CN106995623A - A kind of environment-friendlyink ink drier and preparation method thereof - Google Patents
A kind of environment-friendlyink ink drier and preparation method thereof Download PDFInfo
- Publication number
- CN106995623A CN106995623A CN201710365809.8A CN201710365809A CN106995623A CN 106995623 A CN106995623 A CN 106995623A CN 201710365809 A CN201710365809 A CN 201710365809A CN 106995623 A CN106995623 A CN 106995623A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- drier
- nano
- diatomite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environment-friendlyink ink drier and preparation method thereof, drier component includes 10 20 parts of anhydrous calcium chloride, 10 20 parts of plant amylum, 5 12 parts of magnesia, 8 18 parts of diatomite, 8 17 parts of bamboo charcoal powder, 5 12 parts of chitosan, 38 parts of basalt powder, 10 20 parts of bentonite, 14 parts of nano-silver ionic powder by weight.Preparation technology of the present invention is simple, and obtained drier moisture absorption, moisture absorption effect are good, nonpoisonous and tasteless, to human body fanout free region, while it is not in Signs of Mould that can preserve for a long time.
Description
Technical field
The present invention relates to drier preparing technical field, specially a kind of environment-friendlyink ink drier and preparation method thereof.
Background technology
Ink is the important materials printed for packaging material, and it is shown pattern, word on stock by printing,
Ink includes main component and auxiliary element, and they equably mix and form a kind of sticky colloidal fluid through repeat-rolling.
It is made up of pigment, link stuff and auxiliary agent etc..For the various printings such as books and periodicals, packing and decorating, building decoration.As social demand increases
Greatly, ink kind and yield also respective extension and growth.
Drier is also absorbent, is used in protection against the tide, and mould proof aspect plays desiccation, by suction type and reaction product
It is not all point physical absorption drier and chemisorbed drier.The drier taste being traditionally used in ink is heavier, dries
Effect is bad.
The content of the invention
It is an object of the invention to provide a kind of environment-friendlyink ink drier and preparation method thereof, to solve above-mentioned background skill
The problem of being proposed in art.
To achieve the above object, the present invention provides following technical scheme：A kind of environment-friendlyink ink drier, drier component
Include 10-20 parts of anhydrous calcium chloride, 10-20 parts of plant amylum, 5-12 parts of magnesia, 8-18 parts of diatomite, bamboo by weight
8-17 parts of powdered carbon, 5-12 parts of chitosan, 3-8 parts of basalt powder, 10-20 parts of bentonite, 1-4 parts of nano-silver ionic powder.
It is preferred that, composition proportion preferably is：15 parts of anhydrous calcium chloride, 15 parts of plant amylum, 8 parts of magnesia, diatomite
13 parts, 13 parts of bamboo charcoal powder, 8 parts of chitosan, 6 parts of basalt powder, 15 parts of bentonite, 3 parts of nano-silver ionic powder.
It is preferred that, its preparation method comprises the following steps：
A, will anhydrous calcium chloride, plant amylum, magnesia, diatomite, bamboo charcoal powder, basalt powder, bentonite mix after add
Ground in grinder, grinding temperature is 40 DEG C -50 DEG C, and milling time is 20min-30min, obtains mixture A；
B, addition chitosan and nano-silver ionic powder in mixture A, add in stirred tank after mixing and stir, stir speed (S.S.) is
500-1000 revs/min, mixing time is 10min, stands 1h, that is, obtains drier.
Compared with prior art, the beneficial effects of the invention are as follows：Preparation technology of the present invention is simple, and obtained drier is inhaled
Wet, moisture absorption effect is good, nonpoisonous and tasteless, to human body fanout free region；In addition, being added with nano-silver ionic powder, Neng Gouchang in the present invention
Time preservation is not in Signs of Mould.
Embodiment
The technical scheme in the embodiment of the present invention is clearly and completely described below, it is clear that described embodiment
Only a part of embodiment of the invention, rather than whole embodiments.Based on the embodiment in the present invention, the common skill in this area
The every other embodiment that art personnel are obtained under the premise of creative work is not made, belongs to the model that the present invention is protected
Enclose.
The present invention provides following technical scheme：A kind of environment-friendlyink ink drier, drier component includes by weight
10-20 parts of anhydrous calcium chloride, 10-20 parts of plant amylum, 5-12 parts of magnesia, 8-18 parts of diatomite, 8-17 parts of bamboo charcoal powder, shell gather
Sugared 5-12 parts, 3-8 parts of basalt powder, 10-20 parts of bentonite, 1-4 parts of nano-silver ionic powder.
Embodiment one：
Drier component by weight include 10 parts of anhydrous calcium chloride, 10 parts of plant amylum, 5- parts of magnesia, 8 parts of diatomite,
8 parts of bamboo charcoal powder, 5 parts of chitosan, 3 parts of basalt powder, 10 parts of bentonite, 1 part of nano-silver ionic powder.
The preparation method of the present embodiment comprises the following steps：
A, will anhydrous calcium chloride, plant amylum, magnesia, diatomite, bamboo charcoal powder, basalt powder, bentonite mix after add
Ground in grinder, grinding temperature is 40 DEG C, and milling time is 20min, obtains mixture A；
B, addition chitosan and nano-silver ionic powder in mixture A, add in stirred tank after mixing and stir, stir speed (S.S.) is
500 revs/min, mixing time is 10min, stands 1h, that is, obtains drier.
Embodiment two：
Drier component includes 20 parts of anhydrous calcium chloride, 20 parts of plant amylum, 12 parts of magnesia, diatomite 18 by weight
Part, 17 parts of bamboo charcoal powder, 12 parts of chitosan, 8 parts of basalt powder, 20 parts of bentonite, 4 parts of nano-silver ionic powder.
The preparation method of the present embodiment comprises the following steps：
A, will anhydrous calcium chloride, plant amylum, magnesia, diatomite, bamboo charcoal powder, basalt powder, bentonite mix after add
Ground in grinder, grinding temperature is 50 DEG C, and milling time is 30min, obtains mixture A；
B, addition chitosan and nano-silver ionic powder in mixture A, add in stirred tank after mixing and stir, stir speed (S.S.) is
1000 revs/min, mixing time is 10min, stands 1h, that is, obtains drier.
Embodiment three：
Drier component by weight include 12 parts of anhydrous calcium chloride, 12 parts of plant amylum, 6 parts of magnesia, 9 parts of diatomite,
9 parts of bamboo charcoal powder, 6 parts of chitosan, 4 parts of basalt powder, 12 parts of bentonite, 2 parts of nano-silver ionic powder.
The preparation method of the present embodiment comprises the following steps：
A, will anhydrous calcium chloride, plant amylum, magnesia, diatomite, bamboo charcoal powder, basalt powder, bentonite mix after add
Ground in grinder, grinding temperature is 42 DEG C, and milling time is 22min, obtains mixture A；
B, addition chitosan and nano-silver ionic powder in mixture A, add in stirred tank after mixing and stir, stir speed (S.S.) is
600 revs/min, mixing time is 10min, stands 1h, that is, obtains drier.
Example IV：
Drier component includes 18 parts of anhydrous calcium chloride, 18 parts of plant amylum, 11 parts of magnesia, diatomite 17 by weight
Part, 16 parts of bamboo charcoal powder, 11 parts of chitosan, 7 parts of basalt powder, 18 parts of bentonite, 3 parts of nano-silver ionic powder.
The preparation method of the present embodiment comprises the following steps：
A, will anhydrous calcium chloride, plant amylum, magnesia, diatomite, bamboo charcoal powder, basalt powder, bentonite mix after add
Ground in grinder, grinding temperature is 48 DEG C, and milling time is 28min, obtains mixture A；
B, addition chitosan and nano-silver ionic powder in mixture A, add in stirred tank after mixing and stir, stir speed (S.S.) is
900 revs/min, mixing time is 10min, stands 1h, that is, obtains drier.
Embodiment five：
Drier component includes 16 parts of anhydrous calcium chloride, 16 parts of plant amylum, 10 parts of magnesia, diatomite 15 by weight
Part, 15 parts of bamboo charcoal powder, 10 parts of chitosan, 6 parts of basalt powder, 16 parts of bentonite, 3 parts of nano-silver ionic powder.
The preparation method of the present embodiment comprises the following steps：
A, will anhydrous calcium chloride, plant amylum, magnesia, diatomite, bamboo charcoal powder, basalt powder, bentonite mix after add
Ground in grinder, grinding temperature is 46 DEG C, and milling time is 26min, obtains mixture A；
B, addition chitosan and nano-silver ionic powder in mixture A, add in stirred tank after mixing and stir, stir speed (S.S.) is
800 revs/min, mixing time is 10min, stands 1h, that is, obtains drier.
Embodiment six：
Drier component by weight include 15 parts of anhydrous calcium chloride, 15 parts of plant amylum, 8 parts of magnesia, 13 parts of diatomite,
13 parts of bamboo charcoal powder, 8 parts of chitosan, 6 parts of basalt powder, 15 parts of bentonite, 3 parts of nano-silver ionic powder.
The preparation method of the present embodiment comprises the following steps：
A, will anhydrous calcium chloride, plant amylum, magnesia, diatomite, bamboo charcoal powder, basalt powder, bentonite mix after add
Ground in grinder, grinding temperature is 45 DEG C, and milling time is 25min, obtains mixture A；
B, addition chitosan and nano-silver ionic powder in mixture A, add in stirred tank after mixing and stir, stir speed (S.S.) is
700 revs/min, mixing time is 10min, stands 1h, that is, obtains drier.
Preparation technology of the present invention is simple, and obtained drier moisture absorption, moisture absorption effect are good, nonpoisonous and tasteless, to human body fanout free region；
In addition, being added with nano-silver ionic powder in the present invention, it is not in Signs of Mould that can preserve for a long time.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (3)
1. a kind of environment-friendlyink ink drier, it is characterised in that：Drier component includes anhydrous calcium chloride 10-20 by weight
Part, 10-20 parts of plant amylum, 5-12 parts of magnesia, 8-18 parts of diatomite, 8-17 parts of bamboo charcoal powder, 5-12 parts of chitosan, basalt
3-8 parts of powder, 10-20 parts of bentonite, 1-4 parts of nano-silver ionic powder.
2. a kind of environment-friendlyink ink drier according to claim 1, it is characterised in that：It is preferred that composition proportion be：Nothing
15 parts of water calcium chloride, 15 parts of plant amylum, 8 parts of magnesia, 13 parts of diatomite, 13 parts of bamboo charcoal powder, 8 parts of chitosan, basalt powder
6 parts of end, 15 parts of bentonite, 3 parts of nano-silver ionic powder.
3. realize a kind of preparation method of environment-friendlyink ink drier described in claim 1, it is characterised in that：Its preparation method
Comprise the following steps：
Add and grind after anhydrous calcium chloride, plant amylum, magnesia, diatomite, bamboo charcoal powder, basalt powder, bentonite are mixed
Ground in grinding machine, grinding temperature is 40 DEG C -50 DEG C, and milling time is 20min-30min, obtains mixture A；
Chitosan and nano-silver ionic powder are added in mixture A, adds in stirred tank and stirs after mixing, stir speed (S.S.) is
500-1000 revs/min, mixing time is 10min, stands 1h, that is, obtains drier.