CN106994722A - A kind of environmental protection composite board processing technology - Google Patents
A kind of environmental protection composite board processing technology Download PDFInfo
- Publication number
- CN106994722A CN106994722A CN201710227718.8A CN201710227718A CN106994722A CN 106994722 A CN106994722 A CN 106994722A CN 201710227718 A CN201710227718 A CN 201710227718A CN 106994722 A CN106994722 A CN 106994722A
- Authority
- CN
- China
- Prior art keywords
- environmental protection
- composite board
- protection composite
- processing technology
- cold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Present invention design environmental protection composite board processing technique field, is specifically related to a kind of environmental protection composite board processing technology, comprises the following steps:1) selection:Choose outward appearance is regular, nothing collides with breakage substrate, middle plate and veneer;2) dry:Substrate and middle plate are passed through into drying process, it is 10 14% to control moisture content;3) polish:Using the substrate and middle plate after sand paper sanding drying process;4) Puttying:Substrate side surface smear putty, and fine sandpaper sanding is used, then smear one layer of glue;5) it is cold-pressed:By middle plate and baseplate-laminating, cold moudling is cold-pressed the 3h of the time 2;6) cold moudling:Centering plate surface is smeared and watered, then veneer and middle plate are fitted, and cold moudling, the cold pressing time is 3 4h;7) hot pressing:Hot-pressing processing is carried out, environmental protection composite board semi-finished product are made;8) fit:One layer of plastic foil of pressurizing attaching is heated on veneer surface, environmental protection composite board is made.The processing technology of the present invention, technical maturity, service life is long.
Description
Technical field
The present invention relates to sheet fabrication production technical field is installed additional, a kind of environmental protection composite board processing technology is specifically related to.
Background technology
The rapid growth of China's economic, as the powerful tractive force for promoting the composite plate market demand;North China, East China and length
River middle and lower reaches one largely pour into market with fast-growing, high-yield woods timber, and external high-quality broad-leaved wood is continuously replenished, and is China
The raw material that the offer continued to develop of composite plate industry is enriched;Abundant manpower resource, is also the industry of Chinese development composite plate
The key factor that is taken advantage compared with other composite plate producing countries of cost accounting.Chinese composite board product quality in itself,
Have and be substantially improved, competitiveness is more and more stronger in the international market.China is not only composite plate big export country, or the first in the world
Big composite plate producing country.
As the improvement of people's living standards, finishing is also increasingly particular about, wherein, the ring of traditional common wood material
The requirement of user can not be met by protecting composite plate, so the environmental protection composite board of high-end name wood quality is occurred in that, but precious wood
Material is by protection is added, and the exploitation to such timber is restricted.Some environmental protection composite boards are due to defective workmanship, so needing one badly
Plant and both do not need precious timber as base material, the sensation of high-end timber, the ring that combination stability is strong, anticreep performance is good can be reached again
Protect composite plate.
The content of the invention
Not enough for above-mentioned prior art, the present invention provides a kind of environmental protection composite board processing technology, improves product appearance matter
Amount and practicality, are used for a long time indeformable.
The furniture environmental protection composite board processing technology that the present invention is provided is achieved through the following technical solutions:
A kind of environmental protection composite board processing technology, comprises the following steps:
1) selection:Choose outward appearance is regular, nothing collides with breakage substrate, middle plate and veneer;
2) dry:Substrate and middle plate are passed through into drying process, it is 10-14% to control moisture content;
3) polish:Using the substrate and middle plate after sand paper sanding drying process;
4) Puttying:Substrate side surface smear putty, and fine sandpaper sanding is used, then smear one layer of glue;
5) it is cold-pressed:By middle plate and baseplate-laminating, cold moudling is cold-pressed time 2-3h;
6) cold moudling:Centering plate surface is smeared and watered, then veneer and middle plate are fitted, cold moudling, and the cold pressing time is
3-4h;
7) hot pressing:Hot-pressing processing is carried out, environmental protection composite board semi-finished product are made;
8) fit:One layer of plastic foil of pressurizing attaching is heated on veneer surface, environmental protection composite board is made.
It is preferred that, the step 1) in veneer thickness be 0.35-0.7mm.
It is preferred that, the step 3) in sand paper mesh number be 320-400 mesh.
It is preferred that, the step 4) in the applying amount of putty be 50-60g/m2, the applying amount of glue is 50-90g/m2。
It is preferred that, the step 5) the middle unit pressure that is cold-pressed is 1-3MPa, and temperature is 40-45 DEG C.
It is preferred that, the step 6) the middle unit pressure that is cold-pressed is 4-6MPa, and temperature is 32-35 DEG C.
It is preferred that, the step 6) in glue applying amount be 65-80g/m2。
It is preferred that, the step 8) in plastic foil be polyethylene film or polypropylene screen.
It is preferred that, the step 8) in temperature control at 35-55 DEG C, Stress control is in 0.07-0.1MPa.
Beneficial effect of the present invention:The present invention is combined into environmental protection composite board using common wood processing, and compound environmental protection is combined
Plate has an outward appearance of the wooden environmental protection composite board of name, and with durable in use, pollution resistance is strong, indeformable advantage.
Embodiment
Embodiment 1
A kind of environmental protection composite board processing technology, comprises the following steps:
1) outward appearance is regular, nothing collides with breakage substrate, middle plate and veneer are chosen;
2) substrate and middle plate are passed through into drying process, it is 10% to control moisture content;
3) using the substrate and middle plate after the sand paper sanding drying process of 320-400 mesh;
4) substrate side surface smear putty, the applying amount of putty is 45g/m2, and fine sandpaper sanding is used, then smear one layer
Glue, the applying amount of glue is 45g/m2;
5) by middle plate and baseplate-laminating, cold moudling, cold pressing unit pressure is 1MPa, and temperature is 35 DEG C, and the time is 2h;
6) centering plate surface is smeared and watered, and the applying amount of glue is 60g/m2, then by veneer and the laminating of middle plate, be cold-pressed into
Type, cold pressing unit pressure is 4MPa, and temperature is 30 DEG C, and the time is 3h;
7) hot-pressing processing is carried out, environmental protection composite board semi-finished product are made;
8) on veneer surface, temperature control is at 35 DEG C, and Stress control is fitted one layer of plastic foil under 0.05MPa, and ring is made
Protect composite plate.
Claims (9)
1. a kind of environmental protection composite board processing technology, comprises the following steps:
1) selection:Choose outward appearance is regular, nothing collides with breakage substrate, middle plate and veneer;
2) dry:Substrate and middle plate are passed through into drying process, it is 10-14% to control moisture content;
3) polish:Using the substrate and middle plate after sand paper sanding drying process;
4) Puttying:Substrate side surface smear putty, and fine sandpaper sanding is used, then smear one layer of glue;
5) it is cold-pressed:By middle plate and baseplate-laminating, cold moudling is cold-pressed time 2-3h;
6) cold moudling:Centering plate surface is smeared and watered, then veneer and middle plate are fitted, and cold moudling, the cold pressing time is 3-4h;
7) hot pressing:Hot-pressing processing is carried out, environmental protection composite board semi-finished product are made;
8) fit:One layer of plastic foil of pressurizing attaching is heated on veneer surface, environmental protection composite board is made.
2. furniture environmental protection composite board processing technology according to claim 1, it is characterised in that:The step 1) in veneer thickness
Spend for 0.35-0.7mm.
3. furniture environmental protection composite board processing technology according to claim 1, it is characterised in that:The step 3) in sand paper mesh number
For 320-400 mesh.
4. furniture environmental protection composite board processing technology according to claim 1, it is characterised in that:The step 4) in putty painting
The amount of smearing is 50-60g/m2, and the applying amount of glue is 50-90g/m2。
5. furniture environmental protection composite board processing technology according to claim 1, it is characterised in that:The step 5) middle cold pressing unit
Pressure is 1-3MPa, and temperature is 40-45 DEG C.
6. furniture environmental protection composite board processing technology according to claim 1, it is characterised in that:The step 6) middle cold pressing unit
Pressure is 4-6MPa, and temperature is 32-35 DEG C.
7. furniture environmental protection composite board processing technology according to claim 1, it is characterised in that:The step 6) in glue painting
The amount of smearing is 65-80g/m2。
8. furniture environmental protection composite board processing technology according to claim 1, it is characterised in that:The step 8) in plastic foil be
Polyethylene film or polypropylene screen.
9. furniture environmental protection composite board processing technology according to claim 1, it is characterised in that:The step 8) in temperature control
At 35-55 DEG C, Stress control is in 0.07-0.1MPa.