CN106986526A - A kind of glass water-permeable brick and preparation method thereof - Google Patents
A kind of glass water-permeable brick and preparation method thereof Download PDFInfo
- Publication number
- CN106986526A CN106986526A CN201710366633.8A CN201710366633A CN106986526A CN 106986526 A CN106986526 A CN 106986526A CN 201710366633 A CN201710366633 A CN 201710366633A CN 106986526 A CN106986526 A CN 106986526A
- Authority
- CN
- China
- Prior art keywords
- glass
- brick
- permeable brick
- water
- particle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of glass water-permeable brick, component meter by weight, the glass water-permeable brick includes 100 parts of glass particle, the particle diameter of the glass particle is 0.08~15mm, it is mutually cementing between the glass particle, adjacent glass particle is staggered to form hole, is mutually communicated and is uniformly distributed between the hole.Present invention also offers a kind of preparation method of the glass water-permeable brick, comprise the following steps：Glassware is crushed, glass particle is obtained；Glass particle is laid on fireproof die；Fireproof die is placed in heating furnace and is heated to certain temperature, is incubated, then cools down；Fireproof die is removed, glass water-permeable brick is obtained.The preparation method simple production process that the present invention is provided, firing temperature is low, and energy consumption is small, cost is low；The compression strength of the water-permeable brick obtained using the present invention is 25~50MPa, and coefficient of permeability is 1.2~10mm/s；The present invention can effectively improve the cyclic utilization rate of discarded glass.
Description
Technical field
The present invention relates to water-permeable brick technical field, more particularly to a kind of glass water-permeable brick and preparation method thereof.
Background technology
A large amount of scrap glasses can be all produced in industrial production and daily life, because intractability is big, recovery utilization rate is low,
Cullet volume of cargo in storage is also being continuously increased.By taking beer bottle as an example, due to the decline of vial production cost, it is ready that recycling is old
The beer producer of vial is fewer and fewer, causes a large amount of old reluctant situations of beer bottle, burden is brought to environment.In
State patent CN200610159648.9 discloses a kind of method of utilization cullet low-firing crystallizing glass sheet material, using beer
The cullet such as bottle fire crystallizing glass sheet material as raw material.Product made from the method that the patent is provided is devitrified glass, production
Technique is more complicated, and the firing time is long, and high energy consumption, product does not possess pervious function, is mainly used in indoor high-grade decoration functions material
Material field, it is difficult to use on a large scale.
It is at present that the materials such as rubble, cement are mixed compressing using wide common water-permeable brick, is mainly used in
The ground pavement in the places such as common pavement, gardens, the major defect of this water-permeable brick is that product appearance is dull, and texture is common,
Be not suitable for top grade place, wear no resistance, while being made a low multiple use to discarded object.Chinese patent CN201511006789.2 is carried
Supplied a kind of production method of environment friendly composite ceramic water-permeable brick, use waste ceramic and include the industrial residue of combustible for
Raw material prepares water-permeable brick.The production method that the patent is provided will be by the process, raw material such as dispensing, old, shaping, dry, sintering
Composition complexity is, it is necessary to add binding agent, and sintering temperature reaches 1200 DEG C or so, and energy consumption is higher, and technological process is complicated.
The content of the invention
In view of this, the invention provides a kind of technological process is simple, energy consumption is low, can improve post consumer glass products utilization rate
Glass water-permeable brick preparation method, additionally provide a kind of compression strength be 25~50MPa, coefficient of permeability be 1.2~10mm/s,
Porosity is 10%~30% glass water-permeable brick.
The present invention provides a kind of glass water-permeable brick, by weight component meter, and the glass water-permeable brick includes glass particle 100
Part, the particle diameter of the glass particle is mutually cementing between 0.08~15mm, the glass particle, and adjacent glass particle interlocks
It is mutually communicated and is uniformly distributed between arrangement form hole, the hole, a diameter of 0.01~3mm of the hole.
Further, the glass water-permeable brick is included inside upper brick face, lower brick face and brick body, and brick body is internally located at
Between brick face and lower brick face, water is fashionable from upper brick surface current, can pass through hole, along brick body inside go out from lower brick surface current.
Further, the glass water-permeable brick is the polyhedral structure that upper brick face and lower brick face are parallel to each other.
Further, the particle diameter of the glass particle in the upper brick face is less than or equal to the particle diameter of the glass particle in lower brick face.
Further, the thickness of the glass water-permeable brick is 1~300mm.
Further, the porosity of the glass water-permeable brick is 10%~30%.
The present invention also provides a kind of preparation method of the glass water-permeable brick, comprises the following steps：
Glassware is crushed, glass particle is obtained；
Glass particle is laid on fireproof die；
Fireproof die is placed in heating furnace and is heated to certain temperature, is incubated, then cools down；
Fireproof die is removed, glass water-permeable brick is obtained.
Further, the glassware is the article being made up of glass material, and it includes waste and old beer bottle, discarded glass
Tank, the inwall of the fireproof die scribbles high temperature resistant releasing agent or laying incombustible paper.
Further, when the particle diameter of the glass particle is 2.5~15mm or 0.7~2.5mm, glass particle will be covered with
Fireproof die is placed in heating furnace, and heating furnace is warming up into 640~810 DEG C with 5 DEG C/min speed, is incubated 1h.
Further, when the particle diameter of the glass particle is 0.08~0.63mm, the fireproof die of glass particle will be covered with
It is placed in heating furnace, heating furnace is warming up to 640~710 DEG C with 5 DEG C/min speed, is incubated 1h.
Compared with prior art, the present invention uses the glasswares such as discarded glass to prepare glass water-permeable brick for raw material, without
Any other material and additive are added, cost of material is low, effectively increase the cyclic utilization rate of discarded glass；The present invention is provided
Preparation method simple production process, firing temperature is low, and energy consumption is small, cost is low, can widely use；What the present invention was prepared
Glass water-permeable brick surface is frosted shape, and with beautiful outward appearance, density is small, and wearability is good, and permeable sex expression is excellent, compression strength
For 25~50MPa, coefficient of permeability is 1.2~10mm/s；It is small that the glass water-permeable brick that the present invention is provided can be used as shopping mall, house
Area etc. builds the pavior brick in place, not only attractive in appearance, and can effectively prevent surface gathered water.
Brief description of the drawings
Fig. 1 is a kind of schematic diagram of glass water-permeable brick of the invention.
Fig. 2 is Fig. 1 close-up schematic view.
Fig. 3 is a kind of structural representation of embodiment of glass water-permeable brick one of the invention.
Fig. 4 is a kind of schematic flow sheet of the preparation method of glass water-permeable brick of the invention.
Embodiment
To make the object, technical solutions and advantages of the present invention clearer, below in conjunction with accompanying drawing to embodiment party of the present invention
Formula is further described.
Fig. 1-Fig. 3 is refer to, The embodiment provides a kind of glass water-permeable brick, it includes brick face 11, lower brick
13 inside face 12 and brick body, 13 are located between upper brick face 11 and lower brick face 12 inside brick body, by weight component meter, glass water-permeable brick
Including 100 parts of glass particle 14, mutually cementing between glass particle 14, adjacent glass particle 14 is staggered to form hole
15, it is mutually communicated and is uniformly distributed, a diameter of 0.01~3mm of hole 15 between hole 15, the particle diameter of glass particle 14 is
0.08~15mm, the porosity of glass water-permeable brick is 10%~30%.
When glass water-permeable brick is laid on into ground, water is flowed into from upper brick face 11, hole 15 can be passed through, along inside brick body
13 flow out from lower brick face 12, and the particle diameter of the glass particle 14 in upper brick face 11 is less than or equal to the grain of the glass particle 14 in lower brick face 12
Footpath.
The thickness of glass water-permeable brick is 1~300mm.
In the polyhedral structure that glass water-permeable brick is parallel to each other for upper brick face 11 and lower brick face 12, an embodiment, glass is saturating
Water brick is rectangular parallelepiped structure.
Fig. 4 is refer to, embodiments of the invention additionally provide a kind of preparation method of glass water-permeable brick, including following step
Suddenly：
Step S101, is crushed glassware using pulverizer, obtains glass particle 14；Glassware includes waste and old
The article that beer bottle, discarded glass tank etc. are made up of glass material.
Step S102, glass particle 14 is laid on fireproof die, and the inwall of fireproof die scribbles high temperature resistant releasing agent
Or laying incombustible paper.
Step S103, fireproof die is placed in heating furnace and is heated to certain temperature, insulation, is then cooled down；
When the particle diameter of glass particle 14 is 2.5~15mm or 0.7~2.5mm, fireproof die is placed in heating furnace and added
Heat is incubated 1h to 640~810 DEG C；When the particle diameter of glass particle 14 is 0.08~0.63mm, fireproof die is placed in heating furnace
In be heated to 640~710 DEG C, be incubated 1h.
Step S104, removes fireproof die, obtains glass water-permeable brick.
Several embodiments of the preparation method of the glass water-permeable brick of the present invention are given below, in conjunction with the embodiments to above-mentioned preparation
Method is illustrated.
Embodiment 1：
Crushed after color is removed into impurity for the waste and old beer bottle of green, screen out the glass that particle diameter is 0.7~2.5mm
Glass particle；High temperature resistant releasing agent is applied in the inwall of fireproof die, glass particle is laid in fireproof die, laying depth is
30mm；Fireproof die is placed in heating furnace, heating furnace is warming up to 760 DEG C with 5 DEG C/min speed, and is incubated 1h, then
Cooling；Fireproof die is removed, is cut, glass water-permeable brick is obtained.
The thickness of the glass water-permeable brick obtained using embodiment 1 is 24mm, and color is bottle green, and it is saturating to measure glass through experiment
The compression strength of water brick is 45.5MPa, and coefficient of permeability is 2.4mm/s.
Embodiment 2：
Crushed after color is removed into impurity for the waste and old beer bottle of green, screen out the glass that particle diameter is 2.5~15mm
Glass particle；High temperature resistant releasing agent is applied in the inwall of fireproof die, glass particle is laid in fireproof die, laying depth is
30mm；Fireproof die is placed in heating furnace, heating furnace is warming up to 760 DEG C with 5 DEG C/min speed, and is incubated 1h, then
Cooling；Fireproof die is removed, is cut, glass water-permeable brick is obtained.
The thickness of the glass water-permeable brick obtained using embodiment 2 is 27mm, and color is bottle green, and it is saturating to measure glass through experiment
The compression strength of water brick is 43MPa, and coefficient of permeability is 3.6mm/s.
Embodiment 3：
Crushed after color is removed into impurity for the waste and old beer bottle of green, it is 0.25~0.63mm's to screen out particle diameter
Glass particle；High temperature resistant releasing agent is applied in the inwall of fireproof die, glass particle is laid in fireproof die, laying depth is
30mm；Fireproof die is placed in heating furnace, heating furnace is warming up to 710 DEG C with 5 DEG C/min speed, and is incubated 1h, then
Cooling；Fireproof die is removed, is cut, glass water-permeable brick is obtained.
The thickness of the glass water-permeable brick obtained using embodiment 3 is 22mm, and color is light green color, and it is saturating to measure glass through experiment
The compression strength of water brick is 47MPa, and coefficient of permeability is 1.6mm/s.
The present invention uses the glasswares such as discarded glass to prepare glass water-permeable brick for raw material, without adding any other material
And additive, cost of material is low, effectively increases the cyclic utilization rate of discarded glass；The preparation method production work that the present invention is provided
Skill is simple, and firing temperature is low, and energy consumption is small, cost is low, can widely use；The glass water-permeable brick surface that the present invention is prepared is
Frosted shape, with beautiful outward appearance, density is small, and wearability is good, and permeable sex expression is excellent, and compression strength is 25~50MPa, permeable
Coefficient is 1.2~10mm/s；The glass water-permeable brick that the present invention is provided can be used as the road that place is built in shopping mall, residential quarters etc.
Face brick, it is not only attractive in appearance, and can effectively prevent surface gathered water.
Herein, the involved noun of locality such as forward and backward, upper and lower is to be located at parts in accompanying drawing in figure and zero
The position of part each other is intended merely to the clear of expression technology scheme and conveniently come what is defined.It should be appreciated that the noun of locality
Use should not limit the claimed scope of the application.
In the case where not conflicting, the feature in embodiment and embodiment herein-above set forth can be combined with each other.
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc. should be included in the scope of the protection.
Claims (10)
1. a kind of glass water-permeable brick, it is characterised in that component meter by weight, the glass water-permeable brick includes 100 parts of glass particle,
The particle diameter of the glass particle is glass particle staggered row mutually cementing, adjacent between 0.08~15mm, the glass particle
Row, which are formed between hole, the hole, to be mutually communicated and is uniformly distributed, a diameter of 0.01~3mm of the hole.
2. glass water-permeable brick as claimed in claim 1, it is characterised in that the glass water-permeable brick includes upper brick face, lower brick face
Inside brick body, brick body is internally located between brick face and lower brick face, and water is fashionable from upper brick surface current, can pass through hole,
Go out inside along brick body from lower brick surface current.
3. glass water-permeable brick as claimed in claim 2, it is characterised in that the glass water-permeable brick is upper brick face and lower brick face phase
Mutual parallel polyhedral structure.
4. glass water-permeable brick as claimed in claim 2, it is characterised in that the particle diameter of the glass particle in the upper brick face be less than or
Equal to the particle diameter of the glass particle in lower brick face.
5. glass water-permeable brick as claimed in claim 1, it is characterised in that the thickness of the glass water-permeable brick is 1~300mm.
6. glass water-permeable brick as claimed in claim 1, it is characterised in that the porosity of the glass water-permeable brick is 10%~
30%.
7. the preparation method of the glass water-permeable brick described in a kind of any one of claim 1 to 6, it is characterised in that including following step
Suddenly：
Glassware is crushed, glass particle is obtained；
Glass particle is laid on fireproof die；
Fireproof die is placed in heating furnace and is heated to certain temperature, is incubated, then cools down；
Fireproof die is removed, glass water-permeable brick is obtained.
8. the preparation method of glass water-permeable brick as claimed in claim 7, it is characterised in that the glassware is by glass material
Expect the article that is made, it includes waste and old beer bottle, discarded glass tank, the inwall of the fireproof die scribble high temperature resistant releasing agent or
Lay incombustible paper.
9. the preparation method of glass water-permeable brick as claimed in claim 7, it is characterised in that the particle diameter of the glass particle is
During 2.5~15mm or 0.7~2.5mm, the fireproof die for being covered with glass particle is placed in heating furnace, with 5 DEG C/min speed
Heating furnace is warming up to 640~810 DEG C, 1h is incubated.
10. the preparation method of glass water-permeable brick as claimed in claim 7, it is characterised in that the particle diameter of the glass particle is
During 0.08~0.63mm, the fireproof die for being covered with glass particle is placed in heating furnace, with 5 DEG C/min speed by heating furnace liter
Temperature is incubated 1h to 640~710 DEG C.