CN106978048A - A kind of energy saving paint and preparation method thereof - Google Patents
A kind of energy saving paint and preparation method thereof Download PDFInfo
- Publication number
- CN106978048A CN106978048A CN201710199007.4A CN201710199007A CN106978048A CN 106978048 A CN106978048 A CN 106978048A CN 201710199007 A CN201710199007 A CN 201710199007A CN 106978048 A CN106978048 A CN 106978048A
- Authority
- CN
- China
- Prior art keywords
- parts
- energy saving
- pigment
- acrylate
- monomers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of energy saving paint and preparation method thereof, its composition includes epoxy acrylate, butyl acetate, ethylene glycol, sodium alkyl sulfate, urethane acrylate, polyester acrylate, many official's monomers, pigment, levelling agent and dispersant.After the present invention mixes mentioned component, the paint prepared by processing, with good adhesive force, its lower cost for material, energy-saving and emission-reduction in manufacturing process, raw material are few, raw material sources are extensive, and the paint of this times has certain environment protection significance, it is difficult to fade, environment will not be polluted, with good water-fast function, its bright color, surface is smooth, with good practical function.
Description
Technical field
The invention belongs to decorative materials technology, and in particular to a kind of energy saving paint and preparation method thereof.
Background technology
Paint because of the moistureproof defencive function of its anti-corrosion and decoration function, and favored by finishing person, but it is existing
Paint adds the organic solvents such as benzene mostly, and harm to the human body is larger, also environment can be affected, as people are to ring
The consciousness of guarantor is more and more stronger, and this is accomplished by a kind of more preferable energy-conservation and the paint of environmental protection.
The content of the invention
It is an object of the invention to provide a kind of energy saving paint and preparation method thereof, the present invention has good adhesive force, its
Energy-saving and emission-reduction in lower cost for material, manufacturing process, raw material are few, raw material sources are extensive, and the paint of this times has necessarily
Environment protection significance, it is difficult to fade, and environment will not be polluted, and with good water-fast function, its bright color, surface is put down
It is sliding, with good practical function.
The invention provides following technical scheme：
A kind of energy saving paint, includes the raw material of following parts by weight：25-32 parts of epoxy acrylate, 21-28 parts of butyl acetate, second
It is 20-30 parts of glycol, 25-32 parts of sodium alkyl sulfate, 25-28 parts of urethane acrylate, 24-35 parts of polyester acrylate, many
10-17 parts of 15-20 parts of official's monomer, 10-20 parts of pigment, 12-16 parts of levelling agent and dispersant.
It is preferred that, it is described to include the raw material of following parts by weight：28-30 parts of epoxy acrylate, 24-28 parts of butyl acetate,
22-27 parts of ethylene glycol, 26-30 parts of sodium alkyl sulfate, 26-28 parts of urethane acrylate, 25-31 parts of polyester acrylate,
11-15 parts of many 16-20 parts of official's monomers, 12-17 parts of pigment, 13-16 parts of levelling agent and dispersant.
It is preferred that, it is described to include the raw material of following parts by weight：28 parts of epoxy acrylate, 26 parts of butyl acetate, ethylene glycol
26 parts, 28 parts of sodium alkyl sulfate, 28 parts of urethane acrylate, 30 parts of polyester acrylate, 20 parts of many official's monomers, pigment 15
15 parts of part, 13 parts of levelling agent and dispersant.
It is preferred that, many official's monomers are Pehanorm triacrylate, new penta tetrol triacrylate and two seasons
One or more in the acrylate of penta tetrol six, the lower cost for material advantageously reduces cost of manufacture, and the material system
Danger will not be produced during standby, the security of preparation process can be improved.
It is preferred that, the pigment is talcum powder or titanium dioxide, and the pigment is one kind in the numerous pigment that can generally add,
Appropriate pigment can be added again according to the demand using color.
A kind of preparation method of energy saving paint, comprises the following steps：
Step 1: by epoxy acrylate, butyl acetate, ethylene glycol, sodium alkyl sulfate, urethane acrylate, polyester third
Olefin(e) acid ester and the mixing of many official's monomers, obtain mixture one；
Step 2: mixture one is put into reactor, pigment is added, is ground, grind 50min, the speed of grinding is
500r/min, the particle diameter of grinding is less than 2mm；
Step 3: adding levelling agent and dispersant in product after being ground to step 2, the reaction temperature of reactor is 120-150
DEG C, 4-6h is reacted, mixture two is obtained；
Step 4: adding organic solvent into mixture two, the viscosity of mixture two is adjusted, is controlled in 100-120s；
Step 5: step 4 product is filtered with 200-300 mesh filter screens, obtained filtrate as finished product.
It is preferred that, the step 3 is reacted in sealed environment, is conducive to accelerating reaction speed, is shortened manufacturing cycle.
It is preferred that, the step 4 organic solvent is butyl acetate, and the solvent will not produce influence to preparation process, and easily
In regulation viscosity, lower cost for material, wide material sources.
The beneficial effects of the invention are as follows：
The many official's monomers added in the present invention can sufficiently slow down the curing rate of paint, and not result in dirt to environment
Dye, can improve the viscosity of paint so that the finished product prepared has difficult for drop-off, waterproof and wear-resisting characteristic, extension oil
The use time of paint, improves the quality of paint, and reaches the effect of energy-saving and emission-reduction in certain preparation process.
The present invention has energy-saving and emission-reduction in good adhesive force, its lower cost for material, manufacturing process, and raw material are few, original
Extensively, the paint of this times has certain environment protection significance to material source, and it is difficult to fade, and environment will not be polluted, had
Good water-fast function, its bright color, surface is smooth, with good practical function.
Embodiment
Embodiment 1
A kind of energy saving paint, includes the raw material of following parts by weight：32 parts of epoxy acrylate, 28 parts of butyl acetate, ethylene glycol 30
Part, 32 parts of sodium alkyl sulfate, 28 parts of urethane acrylate, 35 parts of polyester acrylate, 20 parts of many official's monomers, pigment 20
17 parts of part, 16 parts of levelling agent and dispersant.
Many official's monomers are made up of new penta tetrol triacrylate and dipentaerythritol acrylate, and the cost of material is low for this
Honest and clean, danger will not be produced by advantageously reducing in cost of manufacture, and the material preparation process, can improve the safety of preparation process
Property.
Pigment is talcum powder, and the pigment is one kind in the numerous pigment that can generally add, can be according to use color
Demand adds appropriate pigment again.
A kind of preparation method of energy saving paint, comprises the following steps：
Step 1: by epoxy acrylate, butyl acetate, ethylene glycol, sodium alkyl sulfate, urethane acrylate, polyester third
Olefin(e) acid ester and the mixing of many official's monomers, obtain mixture one；
Step 2: mixture one is put into reactor, pigment is added, is ground, grind 50min, the speed of grinding is
500r/min, the particle diameter of grinding is less than 2mm；
Step 3: adding levelling agent and dispersant in product after being ground to step 2, the reaction temperature of reactor is 150 DEG C,
6h is reacted, mixture two is obtained；
Step 4: adding organic solvent into mixture two, the viscosity of mixture two is adjusted, is controlled in 120s；
Step 5: step 4 product is filtered with 300 mesh filter screens, obtained filtrate as finished product.
Step 3 is reacted in sealed environment, is conducive to accelerating reaction speed, is shortened manufacturing cycle.
Step 4 organic solvent is butyl acetate, and the solvent will not produce influence to preparation process, and can easily be accommodated viscosity,
Lower cost for material, wide material sources.
Embodiment 2
A kind of energy saving paint, includes the raw material of following parts by weight：28 parts of epoxy acrylate, 26 parts of butyl acetate, ethylene glycol 26
Part, 28 parts of sodium alkyl sulfate, 28 parts of urethane acrylate, 30 parts of polyester acrylate, 20 parts of many official's monomers, pigment 15
15 parts of part, 13 parts of levelling agent and dispersant.
Many official's monomers are dipentaerythritol acrylate, and the lower cost for material advantageously reduces cost of manufacture, and
Danger will not be produced in the material preparation process, the security of preparation process can be improved.
Pigment is titanium dioxide, and the pigment is one kind in the numerous pigment that can generally add, can be according to use color
Demand adds appropriate pigment again.
A kind of preparation method of energy saving paint, comprises the following steps：
Step 1: by epoxy acrylate, butyl acetate, ethylene glycol, sodium alkyl sulfate, urethane acrylate, polyester third
Olefin(e) acid ester and the mixing of many official's monomers, obtain mixture one；
Step 2: mixture one is put into reactor, pigment is added, is ground, grind 50min, the speed of grinding is
500r/min, the particle diameter of grinding is less than 2mm；
Step 3: adding levelling agent and dispersant in product after being ground to step 2, the reaction temperature of reactor is 120 DEG C,
4h is reacted, mixture two is obtained；
Step 4: adding organic solvent into mixture two, the viscosity of mixture two is adjusted, is controlled in 100-120s；
Step 5: step 4 product is filtered with 200 mesh filter screens, obtained filtrate as finished product.
Step 3 is reacted in sealed environment, is conducive to accelerating reaction speed, is shortened manufacturing cycle.
Step 4 organic solvent is butyl acetate, and the solvent will not produce influence to preparation process, and can easily be accommodated viscosity,
Lower cost for material, wide material sources.
Embodiment 3
A kind of energy saving paint, includes the raw material of following parts by weight：30 parts of epoxy acrylate, 24 parts of butyl acetate, ethylene glycol 22
Part, 30 parts of sodium alkyl sulfate, 28 parts of urethane acrylate, 25 parts of polyester acrylate, 16 parts of many official's monomers, pigment 17
11 parts of part, 16 parts of levelling agent and dispersant.
Many official's monomers are made up of Pehanorm triacrylate and dipentaerythritol acrylate, the material cost
Cheap, danger will not be produced by advantageously reducing in cost of manufacture, and the material preparation process, can improve the safety of preparation process
Property.
Pigment is titanium dioxide, and the pigment is one kind in the numerous pigment that can generally add, can be according to use color
Demand adds appropriate pigment again.
A kind of preparation method of energy saving paint, comprises the following steps：
Step 1: by epoxy acrylate, butyl acetate, ethylene glycol, sodium alkyl sulfate, urethane acrylate, polyester third
Olefin(e) acid ester and the mixing of many official's monomers, obtain mixture one；
Step 2: mixture one is put into reactor, pigment is added, is ground, grind 50min, the speed of grinding is
500r/min, the particle diameter of grinding is less than 2mm；
Step 3: adding levelling agent and dispersant in product after being ground to step 2, the reaction temperature of reactor is 120 DEG C,
4h is reacted, mixture two is obtained；
Step 4: adding organic solvent into mixture two, the viscosity of mixture two is adjusted, is controlled in 120s；
Step 5: step 4 product is filtered with 300 mesh filter screens, obtained filtrate as finished product.
Step 3 is reacted in sealed environment, is conducive to accelerating reaction speed, is shortened manufacturing cycle.
Step 4 organic solvent is butyl acetate, and the solvent will not produce influence to preparation process, and can easily be accommodated viscosity,
Lower cost for material, wide material sources.
Embodiment 4
A kind of energy saving paint, includes the raw material of following parts by weight：32 parts of epoxy acrylate, 21 parts of butyl acetate, ethylene glycol 30
Part, 25 parts of sodium alkyl sulfate, 28 parts of urethane acrylate, 24 parts of polyester acrylate, 20 parts of many official's monomers, pigment 10
10 parts of part, 16 parts of levelling agent and dispersant.
Many official's monomers are by Pehanorm triacrylate, new penta tetrol triacrylate and the propylene of dipentaerythritol six
Acid esters is constituted, the lower cost for material, and danger will not be produced by advantageously reducing in cost of manufacture, and the material preparation process,
The security of preparation process can be improved.
Pigment is talcum powder, and the pigment is one kind in the numerous pigment that can generally add, can be according to use color
Demand adds appropriate pigment again.
A kind of preparation method of energy saving paint, comprises the following steps：
Step 1: by epoxy acrylate, butyl acetate, ethylene glycol, sodium alkyl sulfate, urethane acrylate, polyester third
Olefin(e) acid ester and the mixing of many official's monomers, obtain mixture one；
Step 2: mixture one is put into reactor, pigment is added, is ground, grind 50min, the speed of grinding is
500r/min, the particle diameter of grinding is less than 2mm；
Step 3: adding levelling agent and dispersant in product after being ground to step 2, the reaction temperature of reactor is 120 DEG C,
4h is reacted, mixture two is obtained；
Step 4: adding organic solvent into mixture two, the viscosity of mixture two is adjusted, is controlled in 100s；
Step 5: step 4 product is filtered with 300 mesh filter screens, obtained filtrate as finished product.
Step 3 is reacted in sealed environment, is conducive to accelerating reaction speed, is shortened manufacturing cycle.
Step 4 organic solvent is butyl acetate, and the solvent will not produce influence to preparation process, and can easily be accommodated viscosity,
Lower cost for material, wide material sources.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, although with reference to foregoing reality
Apply example the present invention is described in detail, for those skilled in the art, it still can be to foregoing each implementation
Technical scheme described in example is modified, or carries out equivalent substitution to which part technical characteristic.All essences in the present invention
God is with principle, and any modification, equivalent substitution and improvements made etc. should be included in the scope of the protection.
Claims (8)
1. a kind of energy saving paint, it is characterised in that include the raw material of following parts by weight：25-32 parts of epoxy acrylate, acetic acid fourth
21-28 parts of ester, 20-30 parts of ethylene glycol, 25-32 parts of sodium alkyl sulfate, 25-28 parts of urethane acrylate, polyester acrylic
10-17 parts of 24-35 parts of ester, 15-20 parts of many official's monomers, 10-20 parts of pigment, 12-16 parts of levelling agent and dispersant.
2. a kind of energy saving paint according to claim 1, it is characterised in that include the raw material of following parts by weight：Epoxy third
28-30 parts of olefin(e) acid ester, 24-28 parts of butyl acetate, 22-27 parts of ethylene glycol, 26-30 parts of sodium alkyl sulfate, polyurethane acroleic acid
26-28 parts of ester, 25-31 parts of polyester acrylate, 16-20 parts of many official's monomers, 12-17 parts of pigment, 13-16 parts of levelling agent and scattered
11-15 parts of agent.
3. a kind of energy saving paint according to claim 1, it is characterised in that include the raw material of following parts by weight：Epoxy third
28 parts of olefin(e) acid ester, 26 parts of butyl acetate, 26 parts of ethylene glycol, 28 parts of sodium alkyl sulfate, 28 parts of urethane acrylate, polyester third
15 parts of 30 parts of olefin(e) acid ester, 20 parts of many official's monomers, 15 parts of pigment, 13 parts of levelling agent and dispersant.
4. a kind of energy saving paint according to claim 1, it is characterised in that many official's monomers are Pehanorm three
One or more in acrylate, new penta tetrol triacrylate and dipentaerythritol acrylate.
5. a kind of energy saving paint according to claim 1, it is characterised in that the pigment is talcum powder or titanium dioxide.
6. the preparation method of a kind of energy saving paint described in claim any one of 1-5, it is characterised in that comprise the following steps：
Step 1: by epoxy acrylate, butyl acetate, ethylene glycol, sodium alkyl sulfate, urethane acrylate, polyester third
Olefin(e) acid ester and the mixing of many official's monomers, obtain mixture one；
Step 2: mixture one is put into reactor, pigment is added, is ground, grind 50min, the speed of grinding is
500r/min, the particle diameter of grinding is less than 2mm；
Step 3: adding levelling agent and dispersant in product after being ground to step 2, the reaction temperature of reactor is 120-150
DEG C, 4-6h is reacted, mixture two is obtained；
Step 4: adding organic solvent into mixture two, the viscosity of mixture two is adjusted, is controlled in 100-120s；
Step 5: step 4 product is filtered with 200-300 mesh filter screens, obtained filtrate as finished product.
7. the preparation method of a kind of energy saving paint according to claim 6, it is characterised in that the step 3 is in sealing ring
Reacted in border.
8. a kind of preparation method of energy saving paint according to claim 6, it is characterised in that the step 4 organic solvent
For butyl acetate.