CN106966681B - 一种无机隔热多彩岩片漆及其制备方法 - Google Patents
一种无机隔热多彩岩片漆及其制备方法 Download PDFInfo
- Publication number
- CN106966681B CN106966681B CN201710093775.1A CN201710093775A CN106966681B CN 106966681 B CN106966681 B CN 106966681B CN 201710093775 A CN201710093775 A CN 201710093775A CN 106966681 B CN106966681 B CN 106966681B
- Authority
- CN
- China
- Prior art keywords
- thermal insulation
- sliver
- agent
- colorful
- inorganic thermal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种无机隔热多彩岩片漆及其制备方法，本发明的一种无机隔热多彩岩片漆，所述无机隔热多彩岩片漆包括按质量百分比的如下组分组成：无机粘接剂20‑25％，丙烯酸乳液5‑10％，成膜助剂0.5‑1％，功能性隔热粉体1.5‑2％，pH调节剂0.5‑1％，水28‑32％，润湿剂0.1‑0.2％，防冻剂1‑1.5％，防腐剂0.1‑0.2％，消泡剂0.1‑0.2％，增稠剂1‑1.5％，岩片20‑30％。本发明保温隔热，耐水耐候性能优异，高仿真度，绿色环保，保持了无机涂料的硬度和耐久性。
Description
技术领域
本发明涉及涂料领域，具体涉及一种无机隔热多彩岩片漆及其制备方法。
背景技术
近年来，雾霾，全球变暖已越来越严重，石油煤炭等资源也越来越枯竭，节能减排已成为国家政府一项非常重要的工作，早在20年前就提出隔热保温的技术要求，目前已成为行业规范，尤其在南北方这些极冷极热的地区，建筑隔热保温已成为行业强制性要求。在建筑方面，隔热保温具体措施主要是泡沫板进行挂板施工，但是其施工繁琐，造价高，易脱落开裂，不适宜异性复杂构造的施工等缺陷。
从环境保护的立场看，涂料应向水性化，无公害化，节约能源和资源的方向发展，目前墙面上常用涂料为有机涂料，由于其主要成分为有机物，因此其耐候性，耐水性，耐污性，防霉性较差，无机类外墙涂料近几年开始发展，其优异的耐候保色性及透气性已得到人们的认可。但是无机类涂料不易成膜，易出现龟裂，稳定性也稍差。
花岗岩大理石以其庄重的质感，耐久的品质，多样的色彩受到业主的青睐，但是其昂贵的价格，施工复杂，与保温结合困难，加之负重高，在抗震方面存在很大的安全隐患，使很多用户望而却步。水包水和干挂大理石简单快捷，但是水包水很难在大面积施工上保持花色一致，对操作者要求很严，稍微操作不当颜色就会发花，深浅不一，尤其在修补方面。干挂大理石更容易产生色差，颜色很难保持一致，短时间内会产生透水问题，表面会变得很脏，楼体效果非常难看。
发明内容
为解决上述问题，本发明的目的是提供即在于克服现有技术的缺点，提供一种具有保温隔热功能的无机隔热多彩岩片漆及其制备方法。
为实现上述技术目的，本发明采用的技术方案如下：本发明的一种无机隔热多彩岩片漆，所述无机隔热多彩岩片漆包括按质量百分比的如下组分组成：
进一步地，所述无机粘接剂为采用硅酸锂水溶液，二氧化硅粒子的粒径为1μm，产品清晰透明，粘度低，储存和耐水，耐火，耐候性能十分优异。
进一步地，所述丙烯酸乳液为巴德富的硅丙乳液RS996AD；所述成膜助剂为十二碳醇酯类，如伊士曼的醇酯-12。
更进一步地，所述功能性隔热粉体为纳米氧化锡锑粉体ATO，蓝灰色，粒径小，所述纳米氧化锡锑粉体的粒子的粒径为100-160nm，由纳米级球形基本粒子聚合而成，可吸收近红外辐射，阻隔传热。
进一步地，所述pH调节剂为美国陶氏化学的AMP-95；所述润湿剂为聚硅氧烷-聚醚共聚物，如tego245或tego270。
进一步地，所述防冻剂为丙二醇或乙二醇中的一种或两种的组合；所述防腐剂为卡松类防腐剂，如索尔的RS或特洛伊MERGAL K9N。
更进一步地，所述消泡剂为矿物油类、有机硅类或聚醚类中的一种或几种的组合，如诺普科SN1360,巴斯夫A10；所述增稠剂为疏水缔合型碱溶胀类增稠剂，如陶氏化学TT935；所述岩片的厚度为0.05-0.4mm，颜色丰富，大小形状随意的岩片，如上海岩彩的岩片系列。
本发明所述的无机隔热多彩岩片漆的制备方法，包括如下步骤：
(1)按所述的质量百分比称取各组分，在备料锅或备料缸中加入无机粘接剂，在低速状态下400-600r/min的状态下，缓慢加入丙烯酸乳液，添加完成后搅拌1-2min，然后按顺序依次加入成膜助剂、功能性隔热粉体、pH调节剂、水、润湿剂、防冻剂、防腐剂和消泡剂，添加完成后搅拌1-2min至混合均匀；
(2)将增稠剂用水稀释后得溶液，调整到合适粘度，搅拌均匀后测试粘度138±2KU，测试合格后倒入搅拌釜；
(3)最后依次添加不同规格和颜色的岩片，加入过程中抱团的岩片要进行分散后再加入，加入时边搅拌边加入，控制在低速率下进行搅拌，避免岩片破损，待所有岩片添加完毕后，将转速提至500r/min搅拌30s，则停止，灌装，制得无机隔热多彩岩片漆。
进一步地，在步骤(2)中，所述增稠剂TT935与去离子水的体积比为1:1，所述测试粘度时的温度为25±3℃；所述搅拌釜为真石漆搅拌釜。
进一步地，在步骤(3)中，所述低速率为100-200r/min。
有益效果：本发明保温隔热，耐水耐候性能优异，高仿真度，绿色环保，保持了无机涂料的硬度和耐久性，便于施工等优势，极具发展前景。
与现有技术相比，本发明具有如下优点：
(1)选用以纳米氧化锡锑粉体(ATO)为功能性隔热粉体，解决涂层隔热保温的问题，能够更有效的节能减排。
(2)选用硅酸锂水溶液为无机粘接剂，同时配以硅丙类有机乳液，去除了无机粘接剂和有机粘接剂的缺陷，使漆膜具备优异的耐水、耐火、耐候性，以达到更长的使用年限和装饰效果。
(3)选用0.05-0.4mm厚度的岩片，在漆膜厚度和效果上与多彩岩片漆无异，但是彩点的强度和稳定性均优于水包水多彩涂料，不会出现渗色问题。
(4)泡沫板进行挂板施工，但是其施工繁琐，造价高，易脱落开裂，不适宜异性复杂构造的施工等缺陷。无机类涂料不易成膜，易出现龟裂，稳定性也稍差。水包水很难在大面积施工上保持花色一致，对操作者要求很严，稍微操作不当颜色就会发花，深浅不一，尤其在修补方面。干挂大理石更容易产生色差，颜色很难保持一致，短时间内会产生透水问题，表面会变得很脏，楼体效果非常难看。
具体实施方式
以下通过实施例进一步说明本发明。应该理解的是，这些实施例是本发明的阐释和举例，并不以任何形式限制本发明的范围。
实施例1
本发明的一种无机隔热多彩岩片漆，包括按质量百分比的如下组分组成：
所述无机粘接剂为采用硅酸锂水溶液，二氧化硅粒子的粒径为1μm，产品清晰透明，粘度低，储存和耐水，耐火，耐候性能十分优异。
所述丙烯酸乳液为巴德富的硅丙乳液RS996AD；所述成膜助剂为十二碳醇酯类，如伊士曼的醇酯-12。
所述功能性隔热粉体为纳米氧化锡锑粉体ATO，蓝灰色，粒径小，所述纳米氧化锡锑粉体的粒子的粒径为130nm，由纳米级球形基本粒子聚合而成，可吸收近红外辐射，阻隔传热。
所述pH调节剂为美国陶氏化学的AMP-95；所述润湿剂为聚硅氧烷-聚醚共聚物，如tego245或tego270。
所述防冻剂为丙二醇；所述防腐剂为卡松类防腐剂，如索尔的RS或特洛伊MERGALK9N。
所述消泡剂为矿物油类、有机硅类中的两种的组合；所述增稠剂为疏水缔合型碱溶胀类增稠剂，如陶氏化学TT935；所述岩片的厚度为0.05mm，颜色丰富，大小形状随意的岩片，如上海岩彩的岩片系列。
本发明所述的无机隔热多彩岩片漆的制备方法，包括如下步骤：
(1)按所述的质量百分比称取各组分，在备料锅或备料缸中加入无机粘接剂，在低速状态下400r/min的状态下，缓慢加入丙烯酸乳液，添加完成后搅拌1min，然后按顺序依次加入成膜助剂、功能性隔热粉体、pH调节剂、水、润湿剂、防冻剂、防腐剂和消泡剂，添加完成后搅拌2min至混合均匀；
(2)将增稠剂用水稀释后得溶液，调整到合适粘度，搅拌均匀后测试粘度138KU，测试合格后倒入搅拌釜；所述增稠剂TT935与去离子水的体积比为1:1，所述测试粘度时的温度为22℃。所述搅拌釜为真石漆搅拌釜。
(3)最后依次添加不同规格和颜色的岩片，加入过程中抱团的岩片要进行分散后再加入，加入时边搅拌边加入，搅拌速度不能过快，控制在低速率100r/min下进行搅拌，避免岩片破损，待所有岩片添加完毕后，将转速提至500r/min搅拌30s，则停止，灌装，制得无机隔热多彩岩片漆。
实施例2
实施例2与实施例1的区别在于：本发明的一种无机隔热多彩岩片漆，包括按质量百分比的如下组分组成：
所述纳米氧化锡锑粉体的粒子的粒径为100nm。
所述pH调节剂为美国陶氏化学的AMP-95；所述润湿剂为聚硅氧烷-聚醚共聚物，如tego245或tego270。
所述防冻剂为乙二醇；所述防腐剂为卡松类防腐剂，如特洛伊MERGAL K9N。
所述消泡剂为矿物油类、有机硅类和聚醚类中的三种的组合；所述增稠剂为疏水缔合型碱溶胀类增稠剂；所述岩片的厚度为0.4mm，颜色丰富，大小形状随意的岩片。
本发明所述的无机隔热多彩岩片漆的制备方法，包括如下步骤：
在步骤(1)中，按所述的质量百分比称取各组分，在备料锅或备料缸中加入无机粘接剂，在低速状态下500r/min的状态下，缓慢加入丙烯酸乳液，添加完成后搅拌1min，然后按顺序依次加入成膜助剂、功能性隔热粉体、pH调节剂、水、润湿剂、防冻剂、防腐剂和消泡剂，添加完成后搅拌1.5min至混合均匀；
在步骤(2)中，将增稠剂用水稀释后得溶液，调整到合适粘度，搅拌均匀后测试粘度140KU，测试合格后倒入搅拌釜；所述增稠剂TT935与去离子水的体积比为1:1，所述测试粘度时的温度为28℃。
在步骤(3)中，最后依次添加不同规格和颜色的岩片，加入过程中抱团的岩片要进行分散后再加入，加入时边搅拌边加入，搅拌速度不能过快，控制在低速率为180r/min下进行搅拌，待所有岩片添加完毕后，将转速提至500r/min搅拌30s，则停止，灌装，制得无机隔热多彩岩片漆。
实施例3
实施例3与实施例1的区别在于：本发明的一种无机隔热多彩岩片漆，包括按质量百分比的如下组分组成：
所述丙烯酸乳液为巴德富的硅丙乳液RS996AD；所述成膜助剂为十二碳醇酯类。
所述纳米氧化锡锑粉体的粒子的粒径为160nm。
所述pH调节剂为美国陶氏化学的AMP-95；所述润湿剂为聚硅氧烷-聚醚共聚物。
所述防冻剂为丙二醇和乙二醇两种的组合；所述防腐剂为卡松类防腐剂。
所述消泡剂为聚醚类；所述岩片的厚度为0.3mm。
本发明所述的无机隔热多彩岩片漆的制备方法，包括如下步骤：
在步骤(1)中，按所述的质量百分比称取各组分，在备料锅或备料缸中加入无机粘接剂，在低速状态下600r/min的状态下，缓慢加入丙烯酸乳液，添加完成后搅拌1.5min，然后按顺序依次加入成膜助剂、功能性隔热粉体、pH调节剂、水、润湿剂、防冻剂、防腐剂和消泡剂，添加完成后搅拌1min至混合均匀；
在步骤(2)中，将增稠剂用水稀释后得溶液，调整到合适粘度，搅拌均匀后测试粘度136KU，所述测试粘度时的温度为25℃。
在步骤(3)中，最后依次添加不同规格和颜色的岩片，加入过程中抱团的岩片要进行分散后再加入，加入时边搅拌边加入，搅拌速度不能过快，控制在低速率为200r/min下进行搅拌，待所有岩片添加完毕后，将转速提至500r/min搅拌30s，则停止，灌装，制得无机隔热多彩岩片漆。
实施例4
实施例4与实施例1的区别在于：本发明的一种无机隔热多彩岩片漆，其特征在于包括按质量百分比的如下组分组成：
试验1
表1为本发明的实施例测试结果：
表1
由表1所示，本发明的无机隔热多彩岩片漆具有优异的耐水耐碱性，耐老化时间长，装饰效果持久，同时在VOC、重金属等环境指标上均属于未检出的范围，是一种安全、绿色环保的水性涂料。
以上显示和描述了本发明的基本原理，主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，本发明要求保护范围由所附的权利要求书，说明书及其等效物界定。
Claims (8)
1.一种无机隔热多彩岩片漆，其特征在于所述无机隔热多彩岩片漆包括按质量百分比的如下组分组成：
所述的无机隔热多彩岩片漆的制备方法，包括如下步骤：
(1)按所述的质量百分比称取各组分，在备料锅或备料缸中加入无机粘接剂，在低速状态下400-600r/min的状态下，缓慢加入丙烯酸乳液，添加完成后搅拌1-2min，然后按顺序依次加入成膜助剂、功能性隔热粉体、pH调节剂、水、润湿剂、防冻剂、防腐剂和消泡剂，添加完成后搅拌1-2min至混合均匀；
(2)将增稠剂用水稀释后得溶液，调整到合适粘度，搅拌均匀后测试粘度138±2KU，测试合格后倒入搅拌釜；
(3)最后依次添加不同规格和颜色的岩片，加入过程中抱团的岩片要进行分散后再加入，加入时边搅拌边加入，控制在低速率下进行搅拌，避免岩片破损，待所有岩片添加完毕后，将转速提至400-500r/min搅拌20-30s，则停止，灌装，制得无机隔热多彩岩片漆。
2.根据权利要求1所述的无机隔热多彩岩片漆，其特征在于：所述无机粘接剂为采用硅酸锂水溶液，二氧化硅粒子的粒径为1μm；所述丙烯酸乳液为巴德富的硅丙乳液RS996AD；所述成膜助剂为十二碳醇酯类。
3.根据权利要求1所述的无机隔热多彩岩片漆，其特征在于：所述功能性隔热粉体为纳米氧化锡锑粉体ATO，所述纳米氧化锡锑粉体的粒子的粒径为100-160nm。
4.根据权利要求1所述的无机隔热多彩岩片漆，其特征在于：所述pH调节剂为美国陶氏化学的AMP-95；所述润湿剂为聚硅氧烷-聚醚共聚物。
5.根据权利要求1所述的无机隔热多彩岩片漆，其特征在于：所述防冻剂为丙二醇或乙二醇中的一种或两种的组合；所述防腐剂为卡松类防腐剂。
6.根据权利要求1所述的无机隔热多彩岩片漆，其特征在于：所述消泡剂为矿物油类、有机硅类、聚醚类中的一种或几种的组合；所述增稠剂为疏水缔合型碱溶胀类增稠剂；所述岩片的厚度为0.05-0.4mm。
7.根据权利要求1所述的无机隔热多彩岩片漆，其特征在于：在步骤(2)中，选用增稠剂TT935与去离子水的体积比为1:1，所述测试粘度时的温度为25±3℃；所述搅拌釜为真石漆搅拌釜。
8.根据权利要求1所述的无机隔热多彩岩片漆，其特征在于：在步骤(3)中，所述低速率为100-200r/min。