CN106964354A - 一种Fe‑Co‑AC催化材料及其制备方法 - Google Patents
一种Fe‑Co‑AC催化材料及其制备方法 Download PDFInfo
- Publication number
- CN106964354A CN106964354A CN201710263607.2A CN201710263607A CN106964354A CN 106964354 A CN106964354 A CN 106964354A CN 201710263607 A CN201710263607 A CN 201710263607A CN 106964354 A CN106964354 A CN 106964354A
- Authority
- CN
- China
- Prior art keywords
- preparation
- catalysis materials
- solid
- activated charcoal
- activated carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种Fe‑Co‑AC催化材料及其制备方法,涉及活性炭负载型催化剂领域,该制备方法是将活性炭用酸性水溶液浸泡、用水洗涤、烘干,获得预处理活性炭;将预处理活性炭与硝酸铁溶液、硝酸钴溶液、柠檬酸混合,搅拌均匀,得到混合反应液,调节混合反应液的pH值,再在70~90℃下反应得到浆液;将浆液在100~120℃下蒸干,得固体,烘干,得到活性炭固体;向活性炭固体中加入P2O5粉末,混合均匀,于300~700℃焙烧,冷却即得,该制备方法工艺简单,操作方便,成本低,且制得的Fe‑Co‑AC催化材料可用于电催化降解氯离子废水,无需再另外添加其他氧化剂,电解效率高,对氯离子降解率高,有利于大规模产业化应用。
Description
技术领域
本发明涉及一种活性炭负载型催化剂领域,且特别涉及一种Fe-Co-AC催化材料及其制备方法。
背景技术
随着我国经济建设的发展,对水资源的需求量急剧增加,同时,水污染情形也越来越严重。我国《污水综合排放标准(GB8978-1996)》并未对氯化物排放进行限定,大量的氯化物进入环境,会对环境和生物造成严重的危害。目前,有关氯离子的来源、危害及现有处理方法大致如下:
氯离子的来源及危害:Cl-可与Na+、Ca2+、Mg2+、K+等阳离子形成氯化物。地表水中氯化物的来源有自然源和人为源两类,自然源主要有两种:一是水源流过含氯化物地层,导致食盐矿床和其他含氯沉积物溶解于水;二是接近海洋的河流或江水受到潮水和海水吹来的风的影响,导致水中氯化物含量增加。人为源主要有采矿、石油化工、食品、冶金、制革(鞣革)、化学制药、造纸、纺织、油漆、颜料和机械制造等行业所排放的工业废水以及人类生活所产生的生活污水,其中工业排放的工业废水是氯离子最主要来源。
工业废水中氯离子去除技术:目前专门用来去除废水中的氯离子使其达标排放而研发的技术很少,去除氯离子的目的大致有两种:一是为了使废水能满足后续生物处理生物活性要求;二是为了达到废水回用氯化物含量标准。去除氯离子的原理主要有两种:一种是被其它阴离子替代;另一种是同其它阳离子一起去除。根据性质不同,目前常见的去除废水中氯离子的方法可归为四类:沉淀盐方式、分离拦截方式、离子交换方式、氧化还原方式。由于实际含氯离子废水的复杂性与多样性,单纯采用某一种处理方法很难达到预期目的,因此考虑将两种或以上技术联用来处理废水,克服单一方法处理条件苛刻、成本高、效率低的缺陷,以实现高效、经济的目的,因此研究氯离子的去除技术对保护环境和生物都很有意义。
近年来,通过电化学方法去除氯离子的研究主要集中于电吸附技术(Electro-Sorption Technology,EST),成为该领域的新热点。但目前此技术还停留在实验室阶段,很少工业化,主要是电吸附技术仍然存在一些局限性:①为保证电极有良好的导电性,电吸附技术所使用的电极都很薄,制成的电极厚度一般在1-4mm左右,工业化操作不方便;②用普通吸附材料制成电极时,吸附材料被做成一块块极板,总比表面积无法达到很大,吸附效果不明显;③电极材料自身性能严重影响电吸附技术效果,普通电极材料难以同时满足高比表面积、高电导率、高性价比的要求;④目前电吸附技术所能处理的废水中氯离子浓度远低于工业废水中氯离子实际浓度,所以不能为工业化提供很好的技术支撑。
申请号为201610392863.7的发明专利申请公开了一种三维电极电吸附去除硫酸体系氯离子的方法和应用,该方法是将钛板作为阳极,铅板作为阴极,使用绝缘隔膜将阴极区与阳极区隔离,并将活性炭填充于阳极区,作为第三电极进行阳极极化,该第三电极的工作原理主要是利用活性炭的强吸附性能,以及电极传递的正电荷,即靠阳极钛板把正电荷传递到因水流触碰到阳极钛板的活性炭上,使那些活性炭带正电荷来电吸附去除氯离子。该发明存在以下缺陷:①该发明的整个阳极没有使用有效的氯离子氧化催化剂,通过其规定的电位1.0-1.4V(为了避免析氢)可看出,该发明并不是把氯离子电化学氧化成氯气除掉,而仅仅是把氯离子通过正电荷和活性炭的吸附作用吸附浓缩到活性炭上,来实现去除氯离子的目的。然而,该方法并不是每颗活性炭的表面时时刻刻都触碰到阳极钛板,也就是说并不是每颗活性炭表面都带正电荷,所以整个装置的电吸附效率不是很高。而且,活性炭吸附能力有限,很容易饱和,因此它难以去除高浓度的氯离子废水,通过实施例看出,其试验溶液的氯离子浓度只是1000mg/l,而且其电吸附时间过长,需要2小时才达到吸附稳定,假若废水氯离子浓度过大,使用该方法处理氯离子废水时,必然会用到大量的活性炭,处理时间也会更长。②金属钛在氯离子环境下长时间通电工作易钝化,表面电阻增大,电效率降低,这对电极表面传递正电荷都有很大影响。而且该发明的阳极钛板是一种板式电极,无论如何布置,该阳极的表面积都会受到限制,其表面积不可能很大,阳极电解效率不可能很高。上述缺陷均限制了该方法在实际处理废水中的大规模应用。
发明内容
本发明的目的在于提供一种Fe-Co-AC催化材料的制备方法,该方法工艺简单,操作方便,成本低。
本发明的另一目的在于提供一种Fe-Co-AC催化材料,可用于电催化降解氯离子废水,无需再另外添加其他氧化剂,电解效率高,对氯离子降解率高,有利于大规模产业化应用。
本发明解决其技术问题是采用以下技术方案来实现的。
本发明提出一种Fe-Co-AC催化材料的制备方法,其包括如下步骤:
将活性炭用酸性水溶液浸泡12~36h,过滤得滤饼,将滤饼用水洗涤至pH值为6.5~8.5,将洗涤后的滤饼烘干,获得预处理活性炭;
将预处理活性炭与硝酸铁溶液、硝酸钴溶液、柠檬酸混合,搅拌均匀,得到混合反应液,向混合反应液中滴加碱性水溶液至pH值为6.5~8.5,再在70~90℃水浴条件下反应0.5~1.2h,得到浆液;
将浆液在100~120℃恒温油浴条件下蒸干,得固体,将固体烘干,得到的活性炭固体;向活性炭固体中加入P2O5粉末,混合均匀,于300~700℃焙烧3~7h,冷却即得。
进一步地,在本发明较佳实施例中,酸性水溶液为质量浓度为15%~50%的磷酸水溶液。
进一步地,在本发明较佳实施例中,烘干滤饼的方法是置于60~120℃的干燥箱中进行。
进一步地,在本发明较佳实施例中,混合反应液中铁与钴的浓度摩尔比为3~5:0.5~1.5。
进一步地,在本发明较佳实施例中,混合反应液中铁和钴的总含量按质量百分比占活性炭总质量的1%~10%。
进一步地,在本发明较佳实施例中,活性炭颗粒粒径为5~100目。
进一步地,在本发明较佳实施例中,碱性水溶液为氨水。
进一步地,在本发明较佳实施例中,烘干固体的方法是置于120~150℃的干燥箱中进行。
进一步地,在本发明较佳实施例中,P2O5粉末的加入量占活性炭固体质量的0.5%~5%。
一种Fe-Co-AC催化材料,其采用上述的Fe-Co-AC催化材料的制备方法制得。
本发明实施例的Fe-Co-AC催化材料及其制备方法的有益效果是:本发明实施例的制备方法是将活性炭用酸性水溶液浸泡12~36h,用水洗涤,烘干,获得预处理活性炭;将预处理活性炭与硝酸铁溶液、硝酸钴溶液、柠檬酸混合,搅拌均匀,得到混合反应液,向混合反应液中滴加碱性水溶液至pH值为6.5~8.5,再在70~90℃水浴条件下反应0.5~1.2h,得到浆液;将浆液在100~120℃恒温油浴条件下蒸干,得固体,烘干,得到活性炭固体;向活性炭固体中加入P2O5粉末,混合均匀,于300~700℃焙烧3~7h,冷却即得,该制备方法工艺简单,操作方便,成本低,且制得的Fe-Co-AC催化材料可用于电催化降解氯离子废水,无需再另外添加其他氧化剂,电解效率高,对氯离子降解率高,有利于大规模产业化应用。
附图说明
为了更清楚地说明本发明实施例的技术方案,下面将对实施例中所需要使用的附图作简单地介绍,应当理解,以下附图仅示出了本发明的某些实施例,因此不应被看作是对范围的限定,对于本领域普通技术人员来讲,在不付出创造性劳动的前提下,还可以根据这些附图获得其他相关的附图。
图1为采用本发明实施例1中的电化学反应器与采用普通电化学反应器对氯离子的去除效率变化图。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚,下面将对本发明实施例中的技术方案进行清楚、完整地描述。实施例中未注明具体条件者,按照常规条件或制造商建议的条件进行。所用试剂或仪器未注明生产厂商者,均为可以通过市售购买获得的常规产品。
下面对本发明实施例的Fe-Co-AC催化材料及其制备方法进行具体说明。
本发明实施例提供一种Fe-Co-AC催化材料的制备方法,其包括如下步骤:
S1、将活性炭用酸性水溶液浸泡12~36h,活性炭优选的颗粒粒径为5~100目,酸性水溶液优选为质量浓度为15%~50%的磷酸水溶液,过滤得滤饼;将滤饼用去离子水洗涤至pH值为6.5~8.5,优选洗涤至洗后的洗涤液为中性;将洗涤后的滤饼置于60~120℃,也可于100℃的干燥箱中烘干,获得预处理活性炭,备用。
S2、将预处理活性炭与与硝酸铁溶液、硝酸钴溶液、柠檬酸混合,搅拌均匀,得到混合反应液,混合反应液中铁与钴的浓度摩尔比为3~5:0.5~1.5,混合反应液中铁和钴的总含量按质量百分比占所述活性炭总质量的1%~10%;向混合反应液中逐滴滴加碱性水溶液,碱性水溶液优选为氨水,用于调节混合反应液的pH值,直至pH值为6.5~8.5;再在70~90℃水浴条件下反应0.5~1.2h,反应结束,生成粘稠状的浆液。
本实施例中,加入柠檬酸的主要作用是络合金属离子(主要是铁离子和钴离子),然后在氨水和搅拌作用下,生成质地均匀的溶胶,并沉积到活性炭表面,从而使活性金属离子负载到活性炭上,大大提高了金属离子的负载率。
S3、将浆液在100~120℃恒温油浴条件下蒸干,得固体,将固体置于120~150℃的干燥箱中烘干,得到活性炭固体,该活性炭固体中含有金属铁钴氧化物或金属铁钴氢氧化物。
S4、向活性炭固体中加入P2O5粉末,P2O5粉末的加入量占活性炭固体质量的0.5%~5%,混合均匀,置于300~700℃的马弗炉中焙烧3~7h,在此过程中,由于P2O5粉末在高温条件下会升华成气体,因此可用水吸收该气体,用于制工业磷酸或回收再利用。焙烧完毕后,冷却,即得Fe-Co-AC催化材料。
本实施例中,在含有铁钴氧化物或铁钴氢氧化物的活性炭固体中加入P2O5粉末焙烧,P2O5粉末在高温条件下升华成的气体,该气体在高温条件下膨胀并逸出时,会在活性炭固体内产生许多细小的孔隙,从而增大了活性炭的比表面积和吸附能力。
综上所述,本实施例创造性地提出了铁钴氧化物或铁钴氢氧化物掺杂活性炭上的活性组分,具体是将活性炭与硝酸铁、硝酸钴经溶胶-凝胶后焙烧,形成固溶体结构,该制备方法可以减少反应过程中活性金属组分的溶出量,大大提高了负载催化剂的催化活性,并且其中含有多种活性金属组分,其催化效果优于单一组分金属,因此,按照本制备方法制得的Fe-Co-AC催化材料的催化效率得到很大提高。而且,该工艺简单,操作方便,成本低,硝酸铁与硝酸钴的价格相对于传统氯碱行业在制作成本上节约了150%以上,且制得的催化剂在电催化降解有机废水的过程中无需另外再添加其他氧化剂,有利于大规模产业化应用。
本发明实施例提供一种Fe-Co-AC催化材料,该Fe-Co-AC催化材料是采用上述制备方法制得。在同等条件下,该Fe-Co-AC催化材料相比于传统氯碱行业通过涂布的方式把RuO2\TiO2加工到钛板阳极极板上的催化材料,其催化效率提高了10%~25%。
针对现有技术的不足,并结合氯碱工业生成氯气所需的阳极条件,本发明实施例还提供一种Fe-Co-AC催化材料的应用,具体是应用于电化学反应器中电催化降解废水中氯离子,具体将Fe-Co-AC催化材料填充于塑料或难溶金属制作的网状篮或框里(如钛篮)作为阳极,用于电催化降解废水中氯离子。
该Fe-Co-AC活性炭负载型催化剂的催化反应原理如下:
(1)通过阳极直接对电极上吸附的氯离子催化作用:
阳极反应:
(2)上述吸附氯离子的反应是由在电解过程中阳极电极表面产生的一系列中间反应达成,尖晶石结构的Co3O4以氧氯化合物络合盐类形式参与反应:
Co2+O+Cl-→Co3+OCl+e 电化学步骤;
Co3+OCl→Co2+O+1/2Cl2 催化化学步骤;
2Cl-→Cl2+2e 总电化学反应。
Fe的催化原理同上述Co相似,同样把阳极上浓缩吸附过来的氯离子,又通过Fe-Co-AC催化材料的催化作用而大大降低的氯离子过电位的作用,被阳极氧化成氯气,源源不断地分离出去。通过上述作用,该电化学反应器可以将浓度范围很广的氯离子废水处理达标。
以下结合实施例对本发明的特征和性能作进一步的详细描述。
实施例1
本实施例提供一种Fe-Co-AC催化材料,其按照以下方法制得:
S101、将颗粒粒径为30目的活性炭用质量浓度为40%的磷酸水溶液泡40h,过滤的滤饼;将滤饼用去离子水洗涤至洗后的洗涤液pH值为7;将洗涤后的滤饼在90℃的干燥箱中烘干,获得预处理活性炭,备用。
S102、取20g预处理后的活性炭、40ml丁醇、6.73g的Fe(NO3) 3·9H2O、4.85g的Co(NO3)2·6H2O与2.304g(40ml 0.3M)柠檬酸混合,搅拌均匀,得到混合反应液,然后向混合反应液中逐滴滴加氨水,调节混合反应液的pH值为6.5;再在80℃水浴条件下反应1h,生成粘稠状的浆液。
S103、将浆液在100℃恒温油浴中蒸干得固体,将固体置于120℃的干燥箱中烘干,得到22.61g含Fe/Co氧化物的活性炭固体。
S104、向活性炭固体中加入1.051g的P2O5粉末(加入量为活性炭固体质量的5%),混合均匀,置于马弗炉中于450℃下焙烧5h,冷却,得到Fe-Co-AC催化材料。
采用本实施例制得的Fe-Co-AC催化材料组装电化学反应器,应用于电催化降解废水中氯离子,具体应用方法如下:
(1)设计电化学反应器:该电化学反应器包括阳极和阴极,其中,阳极为钛篮(钛网做成的框),里面填充有本实施例制得的Fe-Co-AC催化材料,阳极中间由碳棒引出导线,并连接至电源正极;阴极由铅板制作而成,电极之间的间距为5cm,阴极由导线连接至电源负极。
(2)处理废水:将某电厂产生的500ml脱硫废水(Cl-浓度为9500mg/L、SO4 2-浓度为3200mg/L,偏碱性)引入上述电化学反应器中,通过电化学工作站在阳极和阴极之间施加恒定电流(电流密度约为800mA/dm2,电压约2~3v),并用磁力搅拌器轻微搅拌脱硫废水,反应30min,处理完毕后静置,取上清液,使用离子色谱法对上清液进行氯离子含量分析,测得上清液中的Cl-浓度为1260mg/L,说明处理后的脱硫废水的氯离子去除率达到了86.7%。
另外,采用普通电化学反应器(阳极为钛板,其余的与上述电化学反应器结构相同),按照相同的工艺处理相同的脱硫废水,分别记录采用本实施例电化学反应器与采用普通电化学反应器对氯离子的去除效率,结果如图1所示,由图可以看出,将本实施例的Fe-Co-AC催化材料应用于电催化降解废水中氯离子的效率明显高于普通电催化降解废水中氯离子的效率,且将本实施例的Fe-Co-AC催化材料应用于电催化降解废水中氯离子的去除率明显高于普通电催化降解废水中氯离子的去除率。
实施例2
本实施例提供一种Fe-Co-AC催化材料,其按照以下方法制得:
S201、将颗粒粒径为5目的活性炭用质量浓度为15%的磷酸水溶液泡36h,过滤的滤饼;将滤饼用去离子水洗涤至洗后的洗涤液pH值为6.5;将洗涤后的滤饼在120℃的干燥箱中烘干,获得预处理活性炭,备用。
S202、取20g预处理活性炭、40ml丁醇、8.28g的Fe(NO3)3·9H2O、5.82g的Co(NO3)2·6H2O与2.304g(40ml 0.3M)柠檬酸混合,搅拌均匀,得到混合反应液,然后向混合反应液中逐滴滴加水合肼,调节混合反应液的pH值为7;再在90℃水浴条件下反应1h,生成粘稠状的浆液。
S203、将浆液在120℃恒温油浴中蒸干得固体,将固体置于120℃的干燥箱中烘干,得到24.41g含Fe/Co氧化物的活性炭固体。
S204、向活性炭固体中加入0.73g的P2O5粉末(加入量为活性炭固体质量的3%),混合均匀,置于马弗炉中于700℃下焙烧4h,冷却,得到Fe-Co-AC催化材料。
采用本实施例制得的Fe-Co-AC催化材料应用于电催化降解废水中氯离子,具体应用方法如下:
(1)组装电化学反应器:该电化学反应器的阳极为塑料框,里面填充有本实施例制得的Fe-Co-AC催化材料,阳极中间由金属引出导线,并连接至电源正极;阴极由不锈钢板制作而成,相邻两块不锈钢板之间的间距为5cm,阴极由导线连接至电源负极。
(2)处理废水:将某电厂产生的500ml脱硫废水(Cl-浓度为9500mg/L、SO4 2-浓度为3200mg/L,偏碱性)引入上述电化学反应器中,通过电化学工作站在阳极和阴极之间施加恒定电流(电流密度约为800mA/dm2,电压约2~3v),并用磁力搅拌器轻微搅拌脱硫废水,反应60min,处理完毕后静置,取上清液,使用离子色谱法对上清液进行氯离子含量分析,测得上清液中的Cl-浓度为905mg/L,说明处理后的脱硫废水的氯离子去除率达到了90.47%。
实施例3
本实施例提供一种Fe-Co-AC催化材料,其按照以下方法制得:
S301、将颗粒粒径为100目的活性炭用质量浓度为40%的磷酸水溶液泡36h,过滤的滤饼;将滤饼用去离子水洗涤至洗后的洗涤液pH值为7;将洗涤后的滤饼在70℃的干燥箱中烘干,获得预处理活性炭,备用。
S302、取20g预处理活性炭、40ml丁醇、4.14g的Fe(NO3)3·9H2O、2.91g的Co(NO3)2·6H2O与2.304g(40ml 0.3M)柠檬酸混合,搅拌均匀,得到混合反应液,然后向混合反应液中逐滴滴加氨水,调节混合反应液的pH值为7;再在90℃水浴条件下反应0.5h,生成粘稠状的浆液。
S303、将浆液在110℃恒温油浴中蒸干得固体,将固体置于130℃的干燥箱中烘干,得到20.847g含Fe/Co氧化物或氢氧化物的活性炭固体。
S304、向活性炭固体中加入2g的P2O5粉末(加入量为活性炭固体质量的1%),混合均匀,置于马弗炉中于700℃下焙烧5h,冷却,得到Fe-Co-AC催化材料。
采用本实施例制得的Fe-Co-AC催化材料应用于电催化降解废水中氯离子,具体应用方法如下:
(1)组装电化学反应器:该电化学反应器包括阳极和阴极,其中,阳极为钛篮,里面填充有本实施例制得的Fe-Co-AC催化材料,阳极中间由碳棒引出导线,并连接至电源正极;阴极由不锈钢板制作而成,相邻两块铅板之间的间距为5cm,阴极由导线连接至电源负极。
(2)处理废水:将某电厂产生的500ml脱硫废水(Cl-浓度为9500mg/L、SO4 2-浓度为3200mg/L,偏碱性)引入上述电化学反应器中,通过电化学工作站在阳极和阴极之间施加恒定电流(电流密度约为800mA/dm2,电压约2~3v),并用磁力搅拌器轻微搅拌脱硫废水,反应60min,处理完毕后静置,取上清液,使用离子色谱法对上清液进行氯离子含量分析,测得上清液中的Cl-浓度为990mg/L,说明处理后的脱硫废水的氯离子去除率达到了89.57%。
综上所述,本发明实施例的Fe-Co-AC催化材料的制备方法工艺简单,操作方便,成本低;制得的Fe-Co-AC催化材料可用于电催化降解氯离子废水,无需再另外添加其他氧化剂,电解效率高,对氯离子降解率高,有利于大规模产业化应用。
以上所描述的实施例是本发明一部分实施例,而不是全部的实施例。本发明的实施例的详细描述并非旨在限制要求保护的本发明的范围,而是仅仅表示本发明的选定实施例。基于本发明中的实施例,本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
Claims (10)
1.一种Fe-Co-AC催化材料的制备方法,其特征在于,其包括如下步骤:
将活性炭用酸性水溶液浸泡12~36h,过滤得滤饼,将所述滤饼用水洗涤至pH值为6.5~8.5,将洗涤后的所述滤饼烘干,获得预处理活性炭;
将所述预处理活性炭与硝酸铁溶液、硝酸钴溶液、柠檬酸混合,搅拌均匀,得到混合反应液,向混合反应液中滴加碱性水溶液至pH值为6.5~8.5,再在70~90℃水浴条件下反应0.5~1.2h,得到浆液;
将所述浆液在100~120℃恒温油浴条件下蒸干,得固体,将所述固体烘干,得到的活性炭固体;向所述活性炭固体中加入P2O5粉末,混合均匀,于300~700℃焙烧3~7h,冷却即得。
2.根据权利要求1所述的Fe-Co-AC催化材料的制备方法,其特征在于,所述酸性水溶液为质量浓度为15%~50%的磷酸水溶液。
3.根据权利要求1所述的Fe-Co-AC催化材料的制备方法,其特征在于,烘干所述滤饼的方法是置于60~120℃的干燥箱中进行。
4.根据权利要求1所述的Fe-Co-AC催化材料的制备方法,其特征在于,所述混合反应液中铁与钴的浓度摩尔比为3~5:0.5~1.5。
5.根据权利要求1所述的Fe-Co-AC催化材料的制备方法,其特征在于,所述混合反应液中铁和钴的总含量按质量百分比占所述活性炭总质量的1%~10%。
6.根据权利要求1所述的Fe-Co-AC催化材料的制备方法,其特征在于,所述活性炭颗粒粒径为5~100目。
7.根据权利要求1所述的Fe-Co-AC催化材料的制备方法,其特征在于,所述碱性水溶液为氨水。
8.根据权利要求1所述的Fe-Co-AC催化材料的制备方法,其特征在于,烘干所述固体的方法是置于120~150℃的干燥箱中进行。
9.根据权利要求1所述的Fe-Co-AC催化材料的制备方法,其特征在于,所述P2O5粉末的加入量占所述活性炭固体质量的0.5%~5%。
10.一种Fe-Co-AC催化材料,其特征在于,其采用如权利要求1至9中任一项所述的Fe-Co-AC催化材料的制备方法制得。