CN106957564A - A kind of road antiskid coating formula and preparation method - Google Patents
A kind of road antiskid coating formula and preparation method Download PDFInfo
- Publication number
- CN106957564A CN106957564A CN201710240873.3A CN201710240873A CN106957564A CN 106957564 A CN106957564 A CN 106957564A CN 201710240873 A CN201710240873 A CN 201710240873A CN 106957564 A CN106957564 A CN 106957564A
- Authority
- CN
- China
- Prior art keywords
- account
- accounts
- alum
- road
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of road antiskid coating formula and preparation method, it is made up of natural rubber, amorphous state a olefin copolymers, white fused alumina, titanium dioxide, ethylene-vinyl acetate copolymer, propane diols, aluminum stearate, polyurethane resin, sodium carbonate, PVC resin powder, nano-calcium carbonate, alum, acrylic resin, chrome alum, additional thermoplastic elastomer (TPE), sodium metasilicate, polyurethanes and alcohol.Compared with prior art, after the present invention is prepared, it is coated on the road surface theed cement solidifies, stickiness is stained with certain, but without viscosity, similar to the material of rubber tyre, during construction coating, surface is applied as rough surface and is advisable, and preferable skidproof effect can be produced, with higher application value.
Description
Technical field
The present invention relates to a kind of road construction material, more particularly to a kind of road antiskid coating formula and preparation method.
Background technology
Road is exactly the infrastructure for supplying various trackless vehicles and walk from the meaning of a word;It is divided into by its handling characteristics
Highways and streets, backroad, factories and mines road, forestry road, examination road, contest road, automobile test road, workshop
Passage and school's road etc., in the prior art, easy overstocked dust on road, running into rainy day will become wet and slippery.If will
Make coarse surface in road surface, although can solve the problem that vehicle slip problem, but can influence road surface flatness and driving it is comfortable
Property, and running car is on coarse road surface, causes the larger vibrations of automobile tire generation and noise.For such case,
Need to prepare a kind of new ground surface material.
The content of the invention
The purpose of the present invention, which is that, provide a kind of road antiskid coating formula and preparation side to solve the above problems
Method.
The present invention is achieved through the following technical solutions above-mentioned purpose:
A kind of road antiskid coating formula of the present invention, by natural rubber, amorphous state a- olefin copolymers, white fused alumina, titanium white
Powder, ethylene-vinyl acetate copolymer, propane diols, aluminum stearate, polyurethane resin, sodium carbonate, PVC resin powder, nano-calcium carbonate
Calcium, alum, acrylic resin, chrome alum, additional thermoplastic elastomer (TPE), sodium metasilicate, polyurethanes and alcohol composition.
Account for the 2%, white fused alumina preferably, the natural rubber accounts for 30%, the amorphous state a- olefin copolymers and account for
10%th, the titanium dioxide, which accounts for the 8%, ethylene-vinyl acetate copolymer and accounts for the 2%, propane diols, accounts for the 2%, stearic acid
Aluminium, which accounts for the 5%, polyurethane resin and accounts for the 10%, sodium carbonate and account for the 2%, PVC resin powder, accounts for the 2%, nano-calcium carbonate
Calcium, which accounts for the 1%, alum and accounts for the 1%, acrylic resin and account for the 5%, chrome alum, accounts for 2%, the additional thermoplastic elastomer (TPE)
Account for the 5%, sodium metasilicate and account for the 1%, polyurethanes and account for the 2%, alcohol and account for 10%.
A kind of road antiskid coating preparation method of the present invention, comprises the following steps:
(1) white fused alumina, titanium dioxide, aluminum stearate, alum, chrome alum are ground into powder-mixed into A agent;
(2) by natural rubber, amorphous state a- olefin copolymers, ethylene-vinyl acetate copolymer, propane diols, polyurethane tree
Fat, sodium carbonate, PVC resin powder, nano-calcium carbonate, acrylic resin, additional thermoplastic elastomer (TPE), sodium metasilicate, polyurethane
Ester and alcohol are mixed and made into B agent;
(3) A agent and B agent are well mixed when using and constructed, it is to be solidified to come into operation.
The beneficial effects of the present invention are:
The present invention is that a kind of road antiskid coating formula and preparation method, compared with prior art, the present invention prepare it
Afterwards, the road surface theed cement solidifies is coated on, with certain stickiness of being stained with, but without viscosity, similar to the material of rubber tyre
Matter, during construction coating, surface is applied as rough surface and is advisable, with anti-skidding effect, with the value promoted the use of.
Embodiment
The invention will be further described below:
A kind of road antiskid coating formula of the present invention, by natural rubber, amorphous state a- olefin copolymers, white fused alumina, titanium white
Powder, ethylene-vinyl acetate copolymer, propane diols, aluminum stearate, polyurethane resin, sodium carbonate, PVC resin powder, nano-calcium carbonate
Calcium, alum, acrylic resin, chrome alum, additional thermoplastic elastomer (TPE), sodium metasilicate, polyurethanes and alcohol composition.
Account for the 2%, white fused alumina preferably, the natural rubber accounts for 30%, the amorphous state a- olefin copolymers and account for
10%th, the titanium dioxide, which accounts for the 8%, ethylene-vinyl acetate copolymer and accounts for the 2%, propane diols, accounts for the 2%, stearic acid
Aluminium, which accounts for the 5%, polyurethane resin and accounts for the 10%, sodium carbonate and account for the 2%, PVC resin powder, accounts for the 2%, nano-calcium carbonate
Calcium, which accounts for the 1%, alum and accounts for the 1%, acrylic resin and account for the 5%, chrome alum, accounts for 2%, the additional thermoplastic elastomer (TPE)
Account for the 5%, sodium metasilicate and account for the 1%, polyurethanes and account for the 2%, alcohol and account for 10%.
A kind of road antiskid coating preparation method of the present invention, comprises the following steps:
(1) white fused alumina, titanium dioxide, aluminum stearate, alum, chrome alum are ground into powder-mixed into A agent;
(2) by natural rubber, amorphous state a- olefin copolymers, ethylene-vinyl acetate copolymer, propane diols, polyurethane tree
Fat, sodium carbonate, PVC resin powder, nano-calcium carbonate, acrylic resin, additional thermoplastic elastomer (TPE), sodium metasilicate, polyurethane
Ester and alcohol are mixed and made into B agent;
(3) A agent and B agent are well mixed when using and constructed, it is to be solidified to come into operation.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, the present invention also have a variety of changes and improvements, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appending claims and its
Equivalent thereof.
Claims (3)
1. a kind of road antiskid coating formula, it is characterised in that:By natural rubber, amorphous statea- olefin copolymer, white fused alumina, titanium
White powder, ethylene-vinyl acetate copolymer, propane diols, aluminum stearate, polyurethane resin, sodium carbonate, PVC resin powder, nano-calcium carbonate
Calcium, alum, acrylic resin, chrome alum, additional thermoplastic elastomer (TPE), sodium metasilicate, polyurethanes and alcohol composition.
2. road antiskid coating formula according to claim 1, it is characterised in that:The natural rubber accounts for 30%, described
Amorphous state a- olefin copolymers account for the 2%, white fused alumina account for the 10%, titanium dioxide account for the 8%, ethene-vinyl acetate be total to
Polymers, which accounts for the 2%, propane diols and accounts for the 2%, aluminum stearate and account for the 5%, polyurethane resin and account for the 10%, sodium carbonate, to be accounted for
2%th, the PVC resin powder account for the 2%, nano-calcium carbonate account for the 1%, alum account for the 1%, acrylic resin account for 5%,
The chrome alum, which accounts for 2%, the additional thermoplastic elastomer (TPE) and accounts for the 5%, sodium metasilicate and account for the 1%, polyurethanes, to be accounted for
2%th, the alcohol accounts for 10%.
3. a kind of road antiskid coating preparation method, it is characterised in that:Comprise the following steps:
(1) white fused alumina, titanium dioxide, aluminum stearate, alum, chrome alum are ground into powder-mixed into A agent;
(2) by natural rubber, amorphous state a- olefin copolymers, ethylene-vinyl acetate copolymer, propane diols, polyurethane resin, carbon
Sour sodium, PVC resin powder, nano-calcium carbonate, acrylic resin, additional thermoplastic elastomer (TPE), sodium metasilicate, polyurethanes and wine
Essence is mixed and made into B agent;
(3) A agent and B agent are well mixed when using and constructed, it is to be solidified to come into operation.