CN106947302A - 一种净醛净味界面剂及其制备方法 - Google Patents

一种净醛净味界面剂及其制备方法 Download PDF

Info

Publication number
CN106947302A
CN106947302A CN201710221919.7A CN201710221919A CN106947302A CN 106947302 A CN106947302 A CN 106947302A CN 201710221919 A CN201710221919 A CN 201710221919A CN 106947302 A CN106947302 A CN 106947302A
Authority
CN
China
Prior art keywords
net
interfacial agents
aldehyde
taste
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710221919.7A
Other languages
English (en)
Inventor
卢文书
Original Assignee
卢文书
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 卢文书 filed Critical 卢文书
Priority to CN201710221919.7A priority Critical patent/CN106947302A/zh
Publication of CN106947302A publication Critical patent/CN106947302A/zh
Pending legal-status Critical Current

Abstract

本发明揭示了一种净醛净味界面剂及其制备方法,界面剂按质量计包括:聚乙烯醇,3‑8%;芳香多胺,1‑5%;丙烯酸羟乙酯,1‑5%;流平剂,2‑10%;有机硅助剂,0.3‑0.8%;消泡剂,0.5‑3%;保水剂,1‑6%;增稠剂,2‑10%;粘度调节剂,0.1‑2%;透明填料,1‑5%;去离子水,余量。本发明提出的净醛净味界面剂性能优良,且不含有VOC、甲醛、苯、甲苯、二甲苯和重金属等有害有毒物质。

Description

一种净醛净味界面剂及其制备方法
技术领域
[0001] 本发明涉及到界面剂领域,特别是涉及到一种净醛净味界面剂及其制备方法。
背景技术
[0002] 建筑物在装饰前,其墙体表面经常有许多细小裂纹和毛细孔。在潮湿的环境下,水 及其包含的盐分会沿着细小裂纹和毛细孔渗透入混凝土内部,腐蚀了内部的钢筋,使其生 锈和膨胀,严重影响了建筑物的寿命。为了解决这些问题,很多厂家在施工前,会给墙体涂 上一层界面剂,增强其表面强度。然而,市面上的传统界面剂,只是在墙体表面形成一层膜, 并不能渗入墙体内部,与混凝土结合。该膜层虽能阻挡水分的渗透,但随着时间的推移,容 易老化脱落。而且,传统界面剂常使用到一些含甲醛等有害物质的原料,威胁使用人的健 康。
发明内容
[0003] 本发明的主要目的为提供一种净醛净味界面剂及其制备方法,解决基本附着力 差、装饰层容易脱落、避开墙面开裂等难题,而且不添加甲醛,更环保、更健康。
[0004] 本发明提出的一种净醛净味界面剂,按质量计包括:
[0005] 聚乙烯醇,3-8 %;
[0006] 芳香多胺,1-5%;
[0007] 丙烯酸羟乙酯,1-5%;
[0008] 流平剂,2-10 %;
[0009] 有机硅助剂,0 · 3-0 · 8 % ;
[0010] 消泡剂,0.5-3 %;
[0011] 保水剂,1-6%;
[0012] 增稠剂,2-10 %;
[0013] 粘度调节剂,0.1-2 %;
[0014] 透明填料,1-5%;
[0015] 去离子水,余量。
[0016] 优选地,按质量计包括:
[0017] 聚乙烯醇,4-7 %;
[0018] 芳香多胺,2-4%;
[0019] 丙烯酸羟乙酯,2-4%;
[0020] 流平剂,4-8 %;
[0021] 有机硅助剂,0.4-0.6%;
[0022] 消泡剂,1-2.5%;
[0023]保水剂,2-5 %;
[0024]增稠剂,4-8 %;
[0025] 粘度调节剂,0.2-1.8%;
[0026] 透明填料,2-4 %;
[0027] 去离子水,余量。
[0028] 优选地,按质量计包括:
[0029] 聚乙烯醇,7%;
[0030] 芳香多胺,4%;
[0031] 丙烯酸羟乙酯,3%;
[0032]流平剂,6%;
[0033] 有机硅助剂,0.5%;
[0034]消泡剂,2%;
[0035]保水剂,4%;
[0036] 增稠剂,6%;
[0037] 粘度调节剂,1%;
[0038] 透明填料,3%;
[0039] 去离子水,余量。
[0040] 优选地,所述芳香多胺包括4,4’ -MDA、2,4 ’-MDA、2,2 ’-MDA和多苯基甲烷多胺中的 一种或多种。4,4’ -MDA的中文名称为4,4’_二氨基二苯基甲烷,2,4’-MDA的中文名称为2, 4’_二氨基二苯基甲烷,2,2’-MDA的中文名称为2,2’_二氨基二苯基甲烷。
[0041] 优选地,所述流平剂包括表面活性剂、聚丙烯酸、羧甲基纤维素中的一种或多种。
[0042] 优选地,所述消泡剂包括乳化硅油、高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季 戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚、聚氧丙烯聚氧乙烯甘油醚、聚二甲基 硅氧烷中的一种或多种。
[0043] 优选地,所述保水剂包括聚丙烯酰胺、聚丙烯酸钠、聚丙烯酸钾、聚丙烯酸胺、淀粉 接枝丙烯酸盐中的一种或多种。
[0044] 优选地,所述增稠剂包括白炭黑、钠基膨润土、有机膨润土、娃藻土、凹凸棒土、分 子筛、娃凝胶中的一种或多种。
[0045] 优选地,所述透明填料为透明粉。
[0046] 本发明还提供了上述任意一种净醛净味界面剂的制备方法,包括以下步骤:将聚 乙烯醇、芳香多胺、丙烯酸羟乙酯、流平剂、有机硅助剂、消泡剂、保水剂、增稠剂、粘度调节 剂、透明填料混合后加入50〜60°C的去离子水中,搅拌均匀。
[0047] 本发明提出的净醛净味界面剂及其制备方法,界面剂具有以下优点:
[0048] 1、利用矿物胶凝材料和高分子胶凝材料的有机结合,提高了光滑基体的附着力;
[0049] 2、采用了抗渗透材料,可填充水泥砂浆层表面的空隙,加固了基体的牢固性能;
[0050] 3、使原有光滑的墙体表面获得适合涂装作业的施工面层,从而提高涂装层和原有 基体的稳定性和施工质量;
[0051] 4、不含有V0C、甲醛、苯、甲苯、二甲苯和重金属等有害有毒物质。
具体实施方式
[0052] 应当理解,此处所描述的具体实施例仅仅用以解释本发明,并不用于限定本发明。
[0053] 本发明提出的一种净醛净味界面剂,按质量计包括:
[0054] 聚乙烯醇,3-8 %;
[0055] 芳香多胺,1-5%;
[0056] 丙烯酸羟乙酯,1-5%;
[0057] 流平剂,2-10 %;
[0058] 有机硅助剂,0.3-0.8%;
[0059] 消泡剂,0.5-3 %;
[0060] 保水剂,1-6%;
[0061] 增稠剂,2-10 %;
[0062] 粘度调节剂,0.1-2 %;
[0063] 透明填料,1-5 %;
[0064] 去离子水,余量。
[0065] 聚乙烯醇
[0066] 聚乙烯醇,又称PVA,白色片状、絮状或粉末状固体,无味。溶于水(95°C以上),微溶 于二甲基亚砜,不溶于汽油、煤油、植物油、苯、甲苯、二氯乙烷、四氯化碳、丙酮、醋酸乙酯、 甲醇、乙二醇等。聚乙烯醇是重要的化工原料,用于制造聚乙烯醇缩醛、耐汽油管道和维尼 纶合成纤维、织物处理剂、乳化剂、纸张涂层、粘合剂、胶水等。
[0067] 芳香多胺
[0068] 芳香多胺(DAM)为含有4,4’ -MDA、2,4 ’ -MDA、2,2 ’ -MDA和多苯基甲烷多胺的混合 物,常温下为浅黄色固体,溶于大多数有机溶剂和盐酸,不溶于汽油、已烷和水。DAM是一种 重要的化工原料中间体,主要用于制备MDI系列产品,还可用于环氧树脂的固化剂、聚酯树 脂结构化剂等,以代替较为昂贵的钛酸三乙醇胺酯。
[0069] 丙烯酸羟乙酯
[0070] 丙烯酸羟乙酯在油脂工业用作润滑油洗涤的添加剂。电子工业用作电子显微镜的 脱水剂。纺织工业用于制造织物的胶粘剂。分析化学中用作化学试剂。此外,还用于水混溶 的包埋剂等
[0071] 流平剂
[0072] 流平剂是一种常用的涂料助剂,它能促使涂料在干燥成膜过程中形成一个平整、 光滑、均匀的涂膜。能有效降低涂饰液表面张力,提高其流平性和均匀性的一类物质。可改 善涂饰液的渗透性,能减少刷涂时产生斑点和斑痕的可能性,增加覆盖性,使成膜均匀、自 然。主要是表面活性剂,有机溶剂等。流平剂种类很多,不同涂料所用的流平剂种类也不尽 相同。本发明实施例采用表面活性剂或聚丙烯酸、羧甲基纤维素。
[0073] 有机硅助剂
[0074] 有机硅材料具有许多独特的性能,如表面张力低、粘温系数小、压缩性高、气体渗 透性高、耐高低温、电气绝缘、耐氧化稳定性、耐候性、难燃、憎水、耐腐蚀、无毒无味以及生 理惰性。
[0075] 消泡剂
[0076]消泡剂,也称消沫剂,用于降低表面张力,抑制泡沫产生或消除已产生泡沫的添加 剂。本发明实施例采用乳化硅油、高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、 聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚和聚氧丙烯聚氧乙烯甘油醚和\或聚二甲基硅氧 烷。
[0077] 保水剂
[0078] 保水剂使用的是高吸水性树脂,它是一种吸水能力特别强的功能高分子材料。本 发明实施例采用聚丙烯酰胺、聚丙烯酸钠、聚丙烯酸钾、聚丙烯酸胺、淀粉接枝丙烯酸盐中 的一种或多种。
[0079] 增稠剂
[0080] 增稠剂是一种流变助剂,不仅可以使涂料增稠,防止施工中出现流挂现象,而且能 赋予涂料优异的机械性能和贮存稳定性。对于黏度较低的水性涂料来说,是非常重要的一 类助剂。本发明实施例采用白炭黑、钠基膨润土、有机膨润土、硅藻土、凹凸棒土、分子筛和\ 或硅凝胶。
[0081] 粘度调节剂
[0082] 粘度调节剂主要是降低聚合物的黏度。增加流动性。对于热熔胶的制造和使用很 有意义。
[0083] 常用的黏度调节剂有石蜡、微晶蜡、聚乙烯蜡、氧化聚乙烯蜡、聚丙烯蜡、沙索蜡、 超支化聚合物、ΑΡΑ0、亚乙基双硬脂酸酰胺、EVA、尿素、盐酸羟胺、硫酸羟胺、环己醇等。其中 APAO全称为UBETACAPA0,系非晶性旷烯烃,相对密度0.86。软化点129〜146〜C。脆性温度为 35〜18°C。针入度 15〜40。熔融黏度(190°C)8000〜8500mPa · s。
[0084] 透明填料
[0085] 透明粉是一种非金属矿物,透明度高,白度好,无毒无味,耐酸耐腐蚀。具有高透明 性,填充料本身的折光率与绝大多数合成树脂的折光率非常接近,所以填料的填量不影响 成品的透明度;能提高产品的表面光滑性和耐磨耐刮性;低吸油量,填充量大,有利于降低 广品的制造成本。
[0086] 本发明还提供了上述任意一种净醛净味界面剂的制备方法,包括以下步骤:将聚 乙烯醇、芳香多胺、丙烯酸羟乙酯、流平剂、有机硅助剂、消泡剂、保水剂、增稠剂、粘度调节 剂、透明填料混合后加入50〜60°C的去离子水中,搅拌均匀。其主要成份是含镁、铝、钙的复 合硅酸盐,属无机盐。另外含部分硫酸盐和杂质,透明粉是一种新型的功能性的透明填充 料,具有透明度高,硬度好,色相佳,高光泽,抗塌陷性好及使用时扬尘少等特点。
[0087] 本发明实施例还提供了上述任意一种净醛净味界面剂的制备方法,包括以下步 骤:将聚乙烯醇、芳香多胺、丙烯酸羟乙酯、流平剂、有机硅助剂、消泡剂、保水剂、增稠剂、粘 度调节剂、透明填料混合后加入50〜60°C的去离子水中,搅拌均匀。
[0088] 实施例1
[0089] 净醛净味界面剂,按质量计包括:
[0090] 聚乙烯醇,7%;
[0091] 芳香多胺,4%;
[0092] 丙烯酸羟乙酯,3%;
[0093] 聚丙烯酸,6%;
[0094] 有机硅助剂,0.5%;
[0095] 聚氧丙烯甘油醚,2%;
[0096] 聚丙烯酰胺,4%;
[0097] 有机膨润土,6%;
[0098] 聚乙烯蜡,1%;
[0099] 透明粉,3%;
[0100] 去离子水,余量。
[0101] 实施例2
[0102] 净醛净味界面剂,按质量计包括:
[0103] 聚乙烯醇,3%;
[0104] 芳香多胺,5%;
[0105] 丙烯酸羟乙酯,5%;
[0106] 聚丙烯酸,10%;
[0107] 有机硅助剂,0.8%;
[0108] 聚氧丙烯甘油醚,3%;
[0109] 聚丙烯酰胺,6%;
[0110] 有机膨润土,2%;
[0111] 聚乙烯蜡,0.1%;
[0112] 透明粉,1%;
[0113] 去离子水,余量。
[0114] 实施例3
[0ΊΊ5] 净醛净味界面剂,按质量计包括:
[0116] 聚乙烯醇,8%;
[0117] 芳香多胺,1%;
[0118] 丙烯酸羟乙酯,1%;
[0119] 聚丙烯酸,2%;
[0120] 有机硅助剂,0.3%;
[0121] 聚氧丙烯甘油醚,0.5%;
[0122] 聚丙烯酰胺,1%;
[0123] 有机膨润土,10%;
[0124] 聚乙烯蜡,2%;
[0125] 透明粉,5%;
[0126] 去离子水,余量。
[0127] 实施例4
[0128] 净醛净味界面剂,按质量计包括:
[0129] 聚乙烯醇,7%;
[0130] 芳香多胺,4%;
[0131] 丙烯酸羟乙酯,4%;
[0132] 聚丙烯酸,4%;
[0133] 有机硅助剂,0.4%;
[0134] 聚氧丙烯甘油醚,1%;
[0135] 聚丙烯酰胺,2%;
[0136] 有机膨润土,4%;
[0137] 聚乙烯蜡,0.2%;
[0138] 透明粉,2%;
[0139] 去离子水,余量。
[0140] 实施例5
[0141] 净醛净味界面剂,按质量计包括:
[0142] 聚乙烯醇,4%;
[0143] 芳香多胺,2%;
[0144] 丙烯酸羟乙酯,2%;
[0145] 聚丙烯酸,8%;
[0146] 有机硅助剂,0.6%;
[0147] 聚氧丙烯甘油醚,2.5%;
[0148] 聚丙烯酰胺,5%;
[0149] 有机膨润土,8%;
[0150] 聚乙烯蜡,1.8%;
[0151] 透明粉,4%;
[0152] 去离子水,余量。
[0153] 实施例6
[0Ί54] 净醛净味界面剂,按质量计包括:
[0155] 聚乙烯醇,7%;
[0156] 芳香多胺,4%;
[0157] 丙烯酸羟乙酯,4%;
[0158] 聚丙烯酸,5%;
[0159] 有机硅助剂,0.4%;
[0160] 聚氧丙烯甘油醚,1.5%;
[0161] 聚丙烯酰胺,2%;
[0162] 有机膨润土,7%;
[0163] 聚乙烯蜡,1.2%;
[0164] 透明粉,3.5%;
[0165] 去离子水,余量。
[0166] 实施例7
[0167] 净醛净味界面剂,按质量计包括:
[0168] 聚乙烯醇,6%;
[0169] 芳香多胺,4%;
[0170] 丙烯酸羟乙酯,3%;
[0171] 聚丙烯酸,5%;
[0172] 有机硅助剂,0.5%;
[0173] 聚氧丙烯甘油醚,2%;
[0174] 聚丙烯酰胺,4%;
[0175] 有机膨润土,6%;
[0176] 聚乙烯蜡,1%;
[0177] 透明粉,3%;
[0178] 去离子水,余量。
[0179] 实施例8
[0180] 净醛净味界面剂,按质量计包括:
[0181] 聚乙烯醇,5%;
[0182] 芳香多胺,4%;
[0183] 丙烯酸羟乙酯,3%;
[0184] 聚丙烯酸,4%;
[0185] 有机硅助剂,0.5%;
[0186] 聚氧丙烯甘油醚,2%;
[0187] 聚丙烯酰胺,4%;
[0188] 有机膨润土,6%;
[0189] 聚乙烯蜡,1%;
[0190] 透明粉,4%;
[0191] 去离子水,余量。
[0192] 对实施例1-8的界面剂性能进行测试,其物理力学性能均符合JC/T907-2002的I型 标准。
[0193] 采用GB 18582-2008对实施例1-8的有害物质进行检测,结果如下:
[0194]
Figure CN106947302AD00111
[0195] 本发明提出的净醛净味界面剂及其制备方法,界面剂具有以下优点:
[0196] 1、利用矿物胶凝材料和高分子胶凝材料的有机结合,提高了光滑基体的附着力;
[0197] 2、采用了抗渗透材料,可填充水泥砂浆层表面的空隙,加固了基体的牢固性能;
[0198] 3、使原有光滑的墙体表面获得适合涂装作业的施工面层,从而提高涂装层和原有 基体的稳定性和施工质量;
[0199] 4、不含有V0C、甲醛、苯、甲苯、二甲苯和重金属等有害有毒物质。
[0200] 以上所述仅为本发明的优选实施例,并非因此限制本发明的专利范围,凡是利用 本发明说明书所作的等效结构或等效流程变换,或直接或间接运用在其他相关的技术领 域,均同理包括在本发明的专利保护范围内。

Claims (10)

1. 一种净醛净味界面剂,其特征在于,按质量计包括: 聚乙烯醇,3-8 %; 芳香多胺,1-5 %; 丙烯酸羟乙酯,1-5%; 流平剂,2-10 %; 有机硅助剂,0.3-0.8%; 消泡剂,0.5-3 %; 保水剂,1-6 %; 增稠剂,2-10 %; 粘度调节剂,0.1-2 %; 透明填料,1-5%; 去尚子水,余量。
2. 根据权利要求1所述的净醛净味界面剂,其特征在于,按质量计包括: 聚乙烯醇,4-7 %; 芳香多胺,2-4 %; 丙烯酸羟乙酯,2-4%; 流平剂,4-8 %; 有机硅助剂,0.4-0.6%; 消泡剂,1-2.5%; 保水剂,2-5 %; 增稠剂,4-8 %; 粘度调节剂,0.2-1.8%; 透明填料,2-4 %; 去尚子水,余量。
3. 根据权利要求1所述的净醛净味界面剂,其特征在于,按质量计包括: 聚乙烯醇,7%; 芳香多胺,4%; 丙烯酸羟乙酯,3%; 流平剂,6 %; 有机硅助剂,0.5%; 消泡剂,2%; 保水剂,4%; 增稠剂,6 %; 粘度调节剂,1%; 透明填料,3%; 去尚子水,余量。
4. 根据权利要求1-3任一项所述的净醛净味界面剂,其特征在于,所述芳香多胺包括4,4’ -MDA、2,4 / -MDA、2,2 / -MDA和多苯基甲烷多胺中的一种或多种。
5. 根据权利要求1-3任一项所述的净醛净味界面剂,其特征在于,所述流平剂包括表面 活性剂、聚丙烯酸、羧甲基纤维素中的一种或多种。
6. 根据权利要求1-3任一项所述的净醛净味界面剂,其特征在于,所述消泡剂包括乳化硅油、高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚、聚氧丙烯聚氧乙烯甘油醚、聚二甲基硅氧烷中的一种或多种。
7. 根据权利要求1-3任一项所述的净醛净味界面剂,其特征在于,所述保水剂包括聚丙烯酰胺、聚丙烯酸钠、聚丙烯酸钾、聚丙烯酸胺、淀粉接枝丙烯酸盐中的一种或多种。
8. 根据权利要求1-3任一项所述的净醛净味界面剂,其特征在于,所述增稠剂包括白炭黑、钠基膨润土、有机膨润土、硅藻土、凹凸棒土、分子筛、硅凝胶中的一种或多种。
9. 根据权利要求1-3任一项所述的净醛净味界面剂,其特征在于,所述透明填料为透明粉。
10. 权利要求1-9任一项所述的净醛净味界面剂的制备方法,其特征在于,包括以下步骤: 将聚乙烯醇、芳香多胺、丙烯酸羟乙酯、流平剂、有机硅助剂、消泡剂、保水剂、增稠剂、粘度调节剂、透明填料混合后加入50〜60°C的去离子水中,搅拌均匀。
CN201710221919.7A 2017-04-06 2017-04-06 一种净醛净味界面剂及其制备方法 Pending CN106947302A (zh)