CN106928878A - A kind of weather-proof static-free glue band - Google Patents
A kind of weather-proof static-free glue band Download PDFInfo
- Publication number
- CN106928878A CN106928878A CN201710253134.8A CN201710253134A CN106928878A CN 106928878 A CN106928878 A CN 106928878A CN 201710253134 A CN201710253134 A CN 201710253134A CN 106928878 A CN106928878 A CN 106928878A
- Authority
- CN
- China
- Prior art keywords
- parts
- weather
- mass fraction
- component
- glue band
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of weather-proof static-free glue band, including following mass fraction each component：58 parts of tetraethyl orthosilicate, 10 15 parts of polyethylene glycol, 46 parts of triphenyl phosphate, 15 25 parts of butyl rubber, 20 25 parts of potassium carbonate, 18 24 parts of epoxy resin, to 59 parts of hydroxylated cellulose, 10 15 parts of polypropylene fibre, 20 30 parts of EHMA, 15 20 parts of polyvinyl chloride, 30~40 parts of vinyl phenyl silicone oil, 15~20 parts of silicone, 5~8 parts of dibenzoyl peroxide, 20~30 parts of calcium stearate, 10 15 parts of nitric acid silver powder.The present invention can make adhesive tape with stronger antistatic property, water proofing property is strong, acidproof, alkaline-resisting, stretching resistance is strong, adhesion strength is strong, elongation percentage is higher, under prolonged hot conditions, adhesion strength is also splendid, also be not in cull after adhering to for a long time, peel strength and heat-proof aging rate are high, proterties stabilization, weatherability is strong, beneficial to popularization and application.
Description
【Technical field】
The present invention relates to the technical field of adhesive tape manufacture, particularly a kind of technical field of weather-proof static-free glue band.
【Background technology】
Use of the adhesive in packaging industry has had the history of last 100 yearses.It is gluing with the development of packaging industry
The consumption figure of agent remains level higher, and global packaging industry year glue consumption accounts for the 35% of the total consumption of adhesive, pushes away accordingly
It is probably the maximum consumption market of adhesive to survey packaging industry.Adhesive tape, adhesive tape is made up of base material and binding agent two parts, leads to
Crossing bonding makes two or more disjunct objects link together.One layer of sticker is scribbled on its surface.Sticker can glue
Firmly thing, is that this bond can be molecule firmly because the intermolecular formation of the molecule of itself and article to be connected is bonded
Stick together.With expanding economy and the progress of science and technology, China has turned into the world gluing industry processing factory and consumption
Big country.With reference to supporting experience for many years.Speed with annual 16% increases.Particularly adhesive tape, diaphragm and adhesive sticker are extensive
It is applied to electronics, communication, packaging, building, papermaking, carpenter, Aero-Space, automobile, weaving, metallurgy, machine-building, medical industry
Most active important industry in China's chemical industry is turned into Deng, gluing industry.
【The content of the invention】
The purpose of the present invention is exactly to solve the problems of the prior art, proposes a kind of weather-proof static-free glue band, can make glue
Band has stronger antistatic property, and water proofing property is strong, and acidproof, alkaline-resisting, stretching resistance is strong, adhesion strength is strong, elongation percentage is higher, when long
Between hot conditions under, adhesion strength is also splendid, for a long time adhere to after be also not in cull, peel strength and heat-proof aging rate
Height, proterties stabilization, weatherability is strong, beneficial to popularization and application.
To achieve the above object, the present invention proposes a kind of weather-proof static-free glue band, including following mass fraction each group
Point：Tetraethyl orthosilicate 5-8 parts, polyethylene glycol 10-15 parts, triphenyl phosphate 4-6 parts, butyl rubber 15-25 parts, potassium carbonate 20-
25 parts, epoxy resin 18-24 parts, to hydroxylated cellulose 5-9 parts, polypropylene fibre 10-15 parts, EHMA 20-
30 parts, polyvinyl chloride 15-20 parts, 30~40 parts of vinyl phenyl silicone oil, 15~20 parts of silicone, dibenzoyl peroxide 5~8
Part, 20~30 parts of calcium stearate, 10-15 parts of nitric acid silver powder.
Preferably, the mass fraction of each component is：5 parts of tetraethyl orthosilicate, 10 parts of polyethylene glycol, triphenyl phosphate
4 parts, 15 parts of butyl rubber, 20 parts of potassium carbonate, 18 parts of epoxy resin, to 5 parts of hydroxylated cellulose, 10 parts of polypropylene fibre, methyl
20 parts of Isooctyl acrylate monomer, 15 parts of polyvinyl chloride, 30 parts of vinyl phenyl silicone oil, 15 parts of silicone, 5 parts of dibenzoyl peroxide,
20 parts of calcium stearate, 10 parts of nitric acid silver powder.
Preferably, the mass fraction of each component is：8 parts of tetraethyl orthosilicate, 15 parts of polyethylene glycol, triphenyl phosphate
6 parts, 25 parts of butyl rubber, 25 parts of potassium carbonate, 24 parts of epoxy resin, to 9 parts of hydroxylated cellulose, 15 parts of polypropylene fibre, methyl
30 parts of Isooctyl acrylate monomer, 20 parts of polyvinyl chloride, 40 parts of vinyl phenyl silicone oil, 20 parts of silicone, 8 parts of dibenzoyl peroxide,
30 parts of calcium stearate, 15 parts of nitric acid silver powder.
Preferably, the mass fraction of each component is：6 parts of tetraethyl orthosilicate, 11 parts of polyethylene glycol, triphenyl phosphate
4 parts, 22 parts of butyl rubber, 25 parts of potassium carbonate, 20 parts of epoxy resin, to 7 parts of hydroxylated cellulose, 12 parts of polypropylene fibre, methyl
25 parts of Isooctyl acrylate monomer, 20 parts of polyvinyl chloride, 30 parts of vinyl phenyl silicone oil, 15 parts of silicone, 6 parts of dibenzoyl peroxide,
24 parts of calcium stearate, 12 parts of nitric acid silver powder.
The present invention proposes a kind of production technology of weather-proof static-free glue band, comprises the following steps successively：
Step one：According to 18-24 parts of mass fraction accurate weighing epoxy resin, butyl rubber 15-25 given by component
Part, polyvinyl chloride 15-20 parts, to hydroxylated cellulose 5-9 parts, polypropylene fibre 10-15 parts of raw material and uniformly mix, be prepared into
Qualified basement membrane batch；
Step 2：Batch prepared by step one is founded in melt extruder, glass melting temperature is 180~200
DEG C, melting time 1 hour is stirred acceleration in melting process, 20min is incubated after founding, and is extruded by melt extruder, system
Into basement membrane；
Step 3：According to 5-8 parts of mass fraction accurate weighing tetraethyl orthosilicate, polyethylene glycol 10-15 given by component
Part, triphenyl phosphate 4-6 parts, potassium carbonate 20-25 parts, EHMA 20-30 parts, vinyl phenyl silicone oil 30~40
Part, 15~20 parts of silicone, 5~8 parts of dibenzoyl peroxide, 20~30 parts of calcium stearate, 10-15 parts of nitric acid silver powder raw material simultaneously
Uniform mixing, is prepared into qualified adhesive batch；
Step 4：Batch prepared by step 3 is carried out three-stage and founds in melt extruder, glass melting temperature according to
Secondary is 80~120 DEG C, 120~160 DEG C, 160~180 DEG C, and the time founded per the stage is 30min, is stirred in melting process
Acceleration is mixed, to be founded be incubated after end per the stage and is stood 10min and found into next stage, three-stage is incubated after the completion of founding
30min is made adhesive from melt extruder extrusion melt；
Step 5：Say that adhesive prepared by step 4 heats melt coating on basement membrane prepared by step 2, obtain weather-proof
Static-free glue band finished product.
Beneficial effects of the present invention：The present invention can make adhesive tape with stronger antistatic property, and water proofing property is strong, acidproof,
Alkaline-resisting, stretching resistance is strong, adhesion strength is strong, elongation percentage is higher, and under prolonged hot conditions, adhesion strength is also splendid, viscous for a long time
Attached is also not in cull, and peel strength and heat-proof aging rate are high, and proterties stabilization, weatherability is strong, beneficial to popularization and application.
Feature of the invention and advantage will be described in detail by embodiment.
【Specific embodiment】
A kind of weather-proof static-free glue band of the present invention, including following mass fraction each component：Tetraethyl orthosilicate 5-8 parts, it is poly-
Ethylene glycol 10-15 parts, triphenyl phosphate 4-6 parts, butyl rubber 15-25 parts, potassium carbonate 20-25 parts, epoxy resin 18-24 parts,
To hydroxylated cellulose 5-9 parts, polypropylene fibre 10-15 parts, EHMA 20-30 parts, polyvinyl chloride 15-20 parts,
30~40 parts of vinyl phenyl silicone oil, 15~20 parts of silicone, 5~8 parts of dibenzoyl peroxide, 20~30 parts of calcium stearate, nitre
Sour silver powder 10-15 parts.
Embodiment one, the mass fraction of each component is：5 parts of tetraethyl orthosilicate, 10 parts of polyethylene glycol, triphenyl phosphate
4 parts, 15 parts of butyl rubber, 20 parts of potassium carbonate, 18 parts of epoxy resin, to 5 parts of hydroxylated cellulose, 10 parts of polypropylene fibre, methyl
20 parts of Isooctyl acrylate monomer, 15 parts of polyvinyl chloride, 30 parts of vinyl phenyl silicone oil, 15 parts of silicone, 5 parts of dibenzoyl peroxide,
20 parts of calcium stearate, 10 parts of nitric acid silver powder.
Embodiment two, the mass fraction of each component is：8 parts of tetraethyl orthosilicate, 15 parts of polyethylene glycol, triphenyl phosphate
6 parts, 25 parts of butyl rubber, 25 parts of potassium carbonate, 24 parts of epoxy resin, to 9 parts of hydroxylated cellulose, 15 parts of polypropylene fibre, methyl
30 parts of Isooctyl acrylate monomer, 20 parts of polyvinyl chloride, 40 parts of vinyl phenyl silicone oil, 20 parts of silicone, 8 parts of dibenzoyl peroxide,
30 parts of calcium stearate, 15 parts of nitric acid silver powder.
Embodiment three, the mass fraction of each component is：6 parts of tetraethyl orthosilicate, 11 parts of polyethylene glycol, triphenyl phosphate
4 parts, 22 parts of butyl rubber, 25 parts of potassium carbonate, 20 parts of epoxy resin, to 7 parts of hydroxylated cellulose, 12 parts of polypropylene fibre, methyl
25 parts of Isooctyl acrylate monomer, 20 parts of polyvinyl chloride, 30 parts of vinyl phenyl silicone oil, 15 parts of silicone, 6 parts of dibenzoyl peroxide,
24 parts of calcium stearate, 12 parts of nitric acid silver powder.
The present invention proposes a kind of production technology of weather-proof static-free glue band, comprises the following steps successively：
Step one：According to 18-24 parts of mass fraction accurate weighing epoxy resin, butyl rubber 15-25 given by component
Part, polyvinyl chloride 15-20 parts, to hydroxylated cellulose 5-9 parts, polypropylene fibre 10-15 parts of raw material and uniformly mix, be prepared into
Qualified basement membrane batch；
Step 2：Batch prepared by step one is founded in melt extruder, glass melting temperature is 180~200
DEG C, melting time 1 hour is stirred acceleration in melting process, 20min is incubated after founding, and is extruded by melt extruder, system
Into basement membrane；
Step 3：According to 5-8 parts of mass fraction accurate weighing tetraethyl orthosilicate, polyethylene glycol 10-15 given by component
Part, triphenyl phosphate 4-6 parts, potassium carbonate 20-25 parts, EHMA 20-30 parts, vinyl phenyl silicone oil 30~40
Part, 15~20 parts of silicone, 5~8 parts of dibenzoyl peroxide, 20~30 parts of calcium stearate, 10-15 parts of nitric acid silver powder raw material simultaneously
Uniform mixing, is prepared into qualified adhesive batch；
Step 4：Batch prepared by step 3 is carried out three-stage and founds in melt extruder, glass melting temperature according to
Secondary is 80~120 DEG C, 120~160 DEG C, 160~180 DEG C, and the time founded per the stage is 30min, is stirred in melting process
Acceleration is mixed, to be founded be incubated after end per the stage and is stood 10min and found into next stage, three-stage is incubated after the completion of founding
30min is made adhesive from melt extruder extrusion melt；
Step 5：Say that adhesive prepared by step 4 heats melt coating on basement membrane prepared by step 2, obtain weather-proof
Static-free glue band finished product.
The present invention can make adhesive tape with stronger antistatic property, and water proofing property is strong, acidproof, alkaline-resisting, and stretching resistance is strong, adhesion
Power is strong, elongation percentage is higher, and under prolonged hot conditions, adhesion strength is also splendid, is also not in cull after adhering to for a long time,
Peel strength and heat-proof aging rate are high, and proterties stabilization, weatherability is strong, beneficial to popularization and application.
Above-described embodiment is the description of the invention, is not limitation of the invention, it is any to simple transformation of the present invention after
Scheme belong to protection scope of the present invention.
Claims (5)
1. a kind of weather-proof static-free glue band, it is characterised in that：Each component including following mass fraction：Including following mass fraction
Each component：Tetraethyl orthosilicate 5-8 parts, polyethylene glycol 10-15 parts, triphenyl phosphate 4-6 parts, butyl rubber 15-25 parts, carbonic acid
Potassium 20-25 parts, epoxy resin 18-24 parts, to hydroxylated cellulose 5-9 parts, polypropylene fibre 10-15 parts, methacrylic acid it is different pungent
Ester 20-30 parts, polyvinyl chloride 15-20 parts, 30~40 parts of vinyl phenyl silicone oil, 15~20 parts of silicone, dibenzoyl peroxide 5
~8 parts, 20~30 parts of calcium stearate, 10-15 parts of nitric acid silver powder.
2. a kind of weather-proof static-free glue band as claimed in claim 1, it is characterised in that：The mass fraction of each component is：
5 parts of tetraethyl orthosilicate, 10 parts of polyethylene glycol, 4 parts of triphenyl phosphate, 15 parts of butyl rubber, 20 parts of potassium carbonate, epoxy resin 18
Part, to 5 parts of hydroxylated cellulose, 10 parts of polypropylene fibre, 20 parts of EHMA, 15 parts of polyvinyl chloride, vinyl benzene
30 parts of base silicone oil, 15 parts of silicone, 5 parts of dibenzoyl peroxide, 20 parts of calcium stearate, 10 parts of nitric acid silver powder.
3. a kind of weather-proof static-free glue band as claimed in claim 1, it is characterised in that：The mass fraction of each component is：
8 parts of tetraethyl orthosilicate, 15 parts of polyethylene glycol, 6 parts of triphenyl phosphate, 25 parts of butyl rubber, 25 parts of potassium carbonate, epoxy resin 24
Part, to 9 parts of hydroxylated cellulose, 15 parts of polypropylene fibre, 30 parts of EHMA, 20 parts of polyvinyl chloride, vinyl benzene
40 parts of base silicone oil, 20 parts of silicone, 8 parts of dibenzoyl peroxide, 30 parts of calcium stearate, 15 parts of nitric acid silver powder.
4. a kind of weather-proof static-free glue band as claimed in claim 1, it is characterised in that：The mass fraction of each component is：
6 parts of tetraethyl orthosilicate, 11 parts of polyethylene glycol, 4 parts of triphenyl phosphate, 22 parts of butyl rubber, 25 parts of potassium carbonate, epoxy resin 20
Part, to 7 parts of hydroxylated cellulose, 12 parts of polypropylene fibre, 25 parts of EHMA, 20 parts of polyvinyl chloride, vinyl benzene
30 parts of base silicone oil, 15 parts of silicone, 6 parts of dibenzoyl peroxide, 24 parts of calcium stearate, 12 parts of nitric acid silver powder.
5. a kind of production technology of weather-proof static-free glue band, it is characterised in that：Comprise the following steps successively：
Step one：According to 18-24 parts of mass fraction accurate weighing epoxy resin given by component, butyl rubber 15-25 parts, it is poly-
Vinyl chloride 15-20 parts, to hydroxylated cellulose 5-9 parts, polypropylene fibre 10-15 parts of raw material and uniformly mix, it is qualified to be prepared into
Basement membrane batch；
Step 2：Batch prepared by step one is founded in melt extruder, glass melting temperature is 180~200 DEG C, is melted
1 hour time processed, acceleration is stirred in melting process, 20min is incubated after founding, extruded by melt extruder, be made base
Film；
Step 3：According to 5-8 parts of mass fraction accurate weighing tetraethyl orthosilicate given by component, polyethylene glycol 10-15 parts, phosphorus
4-6 parts of triphenyl phosphate ester, potassium carbonate 20-25 parts, EHMA 20-30 parts, 30~40 parts of vinyl phenyl silicone oil, silicon
15~20 parts of ketone, 5~8 parts of dibenzoyl peroxide, 20~30 parts of calcium stearate, the raw material of 10-15 parts of nitric acid silver powder and uniform
Mixing, is prepared into qualified adhesive batch；
Step 4：Batch prepared by step 3 is carried out into three-stage in melt extruder to found, glass melting temperature is followed successively by
80~120 DEG C, 120~160 DEG C, 160~180 DEG C, the time founded per the stage is 30min, is stirred in melting process and added
Speed, to found be incubated after end per the stage and stands 10min and found into next stage, three-stage be incubated after the completion of founding 30min from
Melt extruder extrusion melt, is made adhesive；
Step 5：Say that adhesive prepared by step 4 heats melt coating on basement membrane prepared by step 2, obtain weather-proof anti-quiet
Electric adhesive tape finished product.