CN106905838A - A kind of LED curable water-bornes UV furniture house ornamentation paints and preparation method thereof - Google Patents
A kind of LED curable water-bornes UV furniture house ornamentation paints and preparation method thereof Download PDFInfo
- Publication number
- CN106905838A CN106905838A CN201710154906.2A CN201710154906A CN106905838A CN 106905838 A CN106905838 A CN 106905838A CN 201710154906 A CN201710154906 A CN 201710154906A CN 106905838 A CN106905838 A CN 106905838A
- Authority
- CN
- China
- Prior art keywords
- water
- coating
- led
- curable water
- led curable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of LED curable water-bornes UV furniture house ornamentation paints, including：It is attached to furniture house ornamentation surface and the coating I solidified by LED curable water-borne UV adhesion primers；It is attached to the surface of coating I and the coating II solidified by LED curable water-borne UV colouring agents；It is attached to the surface of coating II and the coating III solidified by LED curable water-borne UV protective topcoats.The paint hardness of paint film is high, richness is good, adhesive force is excellent, wearability and anti-stain characteristic can strong, in bright gay color, color inhibitions; with solidifying in good decorative effect and defencive function, and preparation, convenient, speed is fast, and production efficiency is high; energy consumption is low, green pollution-free.
Description
Technical field
The invention belongs to furniture house ornamentation decoration material field, and in particular to a kind of LED curable water-bornes UV furniture house ornamentation paints and
Its preparation method.
Background technology
Traditional paint is mostly one-component coating, two-component coating and baking-type coating, their slow drying speeds, production effect
Rate is low, and containing a large amount of volatile organic solvents, easily environment is polluted.With the raising of people's environmental consciousness, as ring
The water paint of guarantor's type paint is widely used, particularly the field such as finishing, construction material, furniture application indoors.However, existing water
Property paint deficiency is still present in the application, such as weatherability is poor, hardness is low, drying time is long, low production efficiency, it is ornamental not enough
Enrich.LED curable water-borne paints are expected to have the technical characterstic and water that LED curing rates are fast, energy consumption is low, paint film property is excellent concurrently
Property paint is environment friendly and pollution-free, the low advantage of cost.
The content of the invention
It is an object of the invention to provide a kind of LED curable water-bornes UV furniture house ornamentation paints and preparation method thereof.The paint paint film
Hardness is high, richness is good, adhesive force is excellent, wearability and anti-stain characteristic can strong, in bright gay color, color inhibition, with good dress
Decorations effect and defencive function, and solidify convenient, speed in preparation soon, production efficiency is high, and energy consumption is low, green pollution-free.
Specifically, a kind of LED curable water-bornes UV furniture house ornamentation paints, it is characterised in that including：It is attached to furniture house ornamentation table
Face and the coating I solidified by LED curable water-borne UV adhesion primers；It is attached to the surface of coating I and by LED curable water-bornes UV
The coating II of toner solidification；It is attached to the surface of coating II and the coating solidified by LED curable water-borne UV protective topcoats
Ⅲ。
Described LED curable water-borne UV adhesion primers, by weight percentage, comprising：Water-and acrylate prepolymer 10-
70%th, water-soluble active monomer 10-60%, light trigger 1-5%, aqueous promoter 0-5%, filler 0-50% and water 0-50%.
Described LED curable water-borne UV colouring agents, by weight percentage, comprising：Water-and acrylate prepolymer 10-
70%th, water-soluble active monomer 10-60%, light trigger 1-5%, aqueous promoter 0-5%, pigment 0-30% and water 0-30%.
Described LED curable water-borne UV protective topcoats, by weight percentage, comprising：Water-and acrylate prepolymer 10-
70%th, water-soluble active monomer 10-60%, light trigger 1-5%, aqueous promoter 0-5%, filler 0-50% and water 0-50%.
As optimal technical scheme, in above-mentioned LED curable water-bornes UV adhesion primers, UV colouring agents and UV protective topcoats,
Described water-and acrylate prepolymer is selected from aqueous polyurethane acrylate, waterborne epoxy acrylate, waterborne polyester propylene
At least one in acid esters, aqueous amino acrylates, aqueous acrylamide acidifying polyacrylate and water-borne acrylate copolymer.
Described water-soluble active monomer preferably is selected from propoxyl group trimethylolpropane trimethacrylate (PO3- TMPTA), first
Base hydroxypropyl acrylate (HPMA), ethoxylated trimethylolpropane triacrylate (EOn- TMPTA, n=3,6,9,15,
20), hydroxy-ethyl acrylate (HEA), methacrylic acid (MAA), pure acrylic acid (AA), hydroxyethyl methacrylate (HEMA) and third
At least one in olefin(e) acid hydroxypropyl acrylate (HPA).
Described light trigger is preferably mercaptan, Ciba 1173, Ciba 184, Ciba 369, Ciba 907, Ciba
819th, one or more the combination in Ciba 651, TPO, ITX.
Described aqueous promoter can be levelling agent, wetting dispersing agent, photosensitivity promotor, adhesion promoter, defoamer,
Polymerization inhibitor, delustering agent, one or more combination of anti-settling agent.
Described pigment can be the one kind or two in carbon black, titanium dioxide, pearly-lustre silver powder, pearly-lustre bronze, iron oxide red, phthalocyanine blue
Plant the combination of the above.
Described filler preferably is selected from talcum powder, flatting silica, aerosil, anti-scratch wax powder, calcium carbonate, barium sulfate, stone
At least one in Ying Fen, kaolin, bentonite.
In above-mentioned LED curable water-bornes UV furniture house ornamentation paints, the thickness of coating I, II and III can be identical, also can be different, excellent
Elect 10-200um, more preferably 10-120um as.With 60 ° of Grossmeters, the coating gloss metering of coating III is preferably 10-120 °
It is adjustable.
The preparation method of LED curable water-bornes UV furniture house ornamentation paints of the invention, comprises the following steps：
1) cleaning furniture house ornamentation surface；
2) in furniture house ornamentation external coating LED curable water-borne UV adhesion primers；
3) first time LED solidifications, form coating I；
4) in the external coating LED curable water-borne UV colouring agents of coating I；
5) second LED solidification, forms coating II；
6) in the external coating LED curable water-borne UV protective topcoats of coating II, infrared levelling or natural levelling；
7) third time LED solidifications, form coating III.
In above-mentioned preparation process, described application can be carried out using usual manner as known in the art, such as blade coating, spray
Painting, dip-coating, brushing, roller coat, showering etc., this is to those skilled in the art easily to determine.
The LED curable water-borne UV adhesion primers of application, UV colouring agents and UV protective topcoats have good sound to LED light source
The wavelength of Ying Xing, applicable LED can be 420nm, 405nm, 390nm, 385nm, 380nm, 375nm, 370nm, 365nm,
One kind in 360nm.Specific photocuring operating process is to those skilled in the art easily to determine.Preferably, institute
The LED solidifications stated use 1-6 branch power to be irradiated for the LED lamp tube of 0.01-5KW, irradiation speed 1-100m/min.
Step 6) in, the temperature of described infrared levelling is preferably 20-150 DEG C, and flow time is preferably 0.1-10min.
In addition to above-mentioned steps 1-7, the preparation method of LED curable water-bornes UV furniture house ornamentation paints of the invention can also be optional
Ground includes the conventional steps such as packaging (specification and requirement according to product are packed to finished product).
LED curable water-bornes UV furniture house ornamentation paints of the invention have that hardness of paint film is high, richness is good, wearability and dirt-resistant
Performance is strong, decorative effect and the features such as excellent defencive function, fully meets the use requirement of building trade furniture upholstery, and
Preparation technology production efficiency is high, energy consumption is low, green non-pollution.
Specific embodiment
The present invention is described in further detail below in conjunction with specific embodiment, but should not be construed as protecting the present invention
Protect the limitation of scope.
Prepare embodiment
The White LED curable water-borne UV furniture house ornamentation paints of embodiment 1.
From the glued board of specification 1.2m × 2.44m × 6mm, in one layer of LED curable water-bornes UV of its surface roller coating after cleaning
Adhesion primer, it is the solidification of 15m/min to enter after drying equipped with 2 power 300W, the LED of wavelength 365nm and irradiation speed
Machine, it is the coating I of 20um that thickness is formed after solidification.In I surface roller coating of coating, one layer of LED curable water-borne UV white color agents, do
Enter after dry equipped with 3 power 1KW, the LED of wavelength 395nm and irradiation speed is the curing of 15m/min, formed after solidification
Thickness is the coating II of 25um.It it is 80 DEG C in temperature again in II surface roller coating of coating, one layer of LED curable water-borne UV protective topcoat
Levelling 60s under infrared levelling line, subsequently into equipped with 5 power 2KW, the LED of wavelength 365nm and irradiation speed be 15m/
The curing of min, it is the coating III of 30um that thickness is formed after solidification.Obtain final product White LED curable water-borne UV furniture house ornamentation decorative panels.
Wherein, the percentage by weight composition of LED curable water-bornes UV adhesion primers is：Aqueous polyurethane acrylate 56%,
Hydroxy propyl methacrylate 27.5%, mercaptan 3%, Ciba 1,173 1%, levelling agent (BYK-333) 0.5%, adhesive force promote
Agent (phosphate CN9051) 1.5%, defoamer (BYK-018) 0.5%, water 10%.
The percentage by weight of LED curable water-borne UV white color agents is constituted：Waterborne polyester acrylate 35%, aqueous ammonia
Base acrylate 20%, propoxyl group trimethylolpropane trimethacrylate 20%, mercaptan 3%, TPO 2%, levelling agent (BYK-
380) 0.5%, photosensitivity promotor (reactive amines P-1114) 1%, titanium dioxide 13%, polymerization inhibitor (hydroquinones) 0.5%, water 5%.
The percentage by weight of LED curable water-borne UV protective topcoats is constituted：Waterborne epoxy acrylate 29%, aqueous poly- ammonia
Ester acrylate 36%, hydroxy-ethyl acrylate 19%, mercaptan 4%, levelling agent (BYK-381) 0.5%, defoamer (BYK-022)
0.5%th, adhesion promoter (phosphate CN9051) 1%, talcum powder 10%.
The red LED curable water-borne UV furniture house ornamentation paints of embodiment 2.
It is the solid wood of 1.0m × 2.5m × 10mm from specification, in one layer of LED curable water-bornes UV of its surface showering after cleaning
Adhesion primer, subsequently into equipped with 2 power 1KW, the LED of wavelength 385nm and irradiation speed for 15m/min curing,
It is the coating I of 80um that thickness is formed after solidification.In I surface showering of coating, one layer of LED curable water-borne UV red stain, Ran Houjin
Enter equipped with 3 power 3KW, the LED of wavelength 420nm and irradiation speed is the curing of 15m/min, thickness is formed after solidification is
The coating II of 50um.Again in II surface showering of coating, one layer of LED curable water-borne UV protective topcoat, in the infrared stream that temperature is 80 DEG C
Levelling 60s under horizontal line, subsequently into equipped with 5 power 5KW, the LED of wavelength 405nm and irradiation speed consolidating for 15m/min
Change machine, it is the coating III of 40um that thickness is formed after solidification.Obtain final product red LED curable water-borne UV furniture house ornamentation decorative panels.
Wherein, the percentage by weight composition of LED curable water-bornes UV adhesion primers is：Aqueous acrylamide is acidified polyacrylate
63%th, hydroxyethyl methacrylate 30.5%, mercaptan 4%, wetting dispersing agent (DISPERBYK-180) 0.5%, adhesive force promote
Agent (hydroxy acrylate) 1%, defoamer (BYK-028) 1%.
The percentage by weight of LED curable water-borne UV colouring agents is constituted：Waterborne polyester acrylate 35%, water soluble acrylic acid
Ester copolymer 20%, hydroxypropyl acrylate 21%, mercaptan 2%, TPO3%, levelling agent (BYK-337) 0.5%, photosensitivity promotor
(reactive amines P-1114) 1%, iron oxide red 17%, defoamer (BYK-093) 0.5%.
The percentage by weight of LED curable water-borne UV protective topcoats is constituted：Aqueous amino acrylates 21%, aqueous poly- ammonia
Ester acrylate 35%, hydroxy propyl methacrylate 12%, ethoxyquin trimethylolpropane trimethacrylate (EO3-TMPTA)
16%th, Ciba184 2%, mercaptan 2%, levelling agent (BYK-387) 0.5%, defoamer (BYK-1610) 0.5%, stabilizer are (right
Hydroxyanisol) 1%, flatting silica (OK500) 10%.
The pearly-lustre of embodiment 3. silver LED curable water-borne UV furniture lacquers
It is three offset plates of 1.2m × 2.4m × 12mm from specification, in one layer of LED curable water-borne of its surface spraying after cleaning
UV adhesion primers, subsequently into equipped with the solidification that 2 power 0.5KW, the LED of wavelength 395nm and irradiation speed are 15m/min
Machine, it is the coating I of 28um that thickness is formed after solidification.In I surface spraying of coating, one layer of LED curable water-borne UV pearly-lustres silver colouring agent,
Subsequently into equipped with the curing that 3 power 3KW, the LED of wavelength 420nm and irradiation speed are 12m/min, formed after solidification
Thickness is the coating II of 32um.It it is 80 DEG C in temperature again in II surface spraying of coating, one layer of LED curable water-borne UV protective topcoat
Levelling 60s under infrared levelling line, subsequently into equipped with 5 power 5KW, the LED of wavelength 365nm and irradiation speed be 15m/
The curing of min, it is the coating III of 30um that thickness is formed after solidification.Obtain final product pearly-lustre silver LED curable water-borne UV furniture house ornamentation decoration
Plate.
Wherein, the percentage by weight composition of LED curable water-bornes UV adhesion primers is：Aqueous polyurethane acrylate 40%,
Aqueous acrylamide acidifying polyacrylate 25.5%, ethoxylated trimethylolpropane triacrylate (EO6- TMPTA) 27.5%,
Mercaptan 4%, levelling agent (BYK-3500) 0.5%, adhesion promoter (phosphate CN9051) 1.5%, defoamer (BYK-
080A) 1%.
The percentage by weight of LED curable water-borne UV colouring agents is constituted：Waterborne polyester acrylate 32%, water-base epoxy third
Olefin(e) acid ester 23%, hydroxy-ethyl acrylate 14%, pure acrylic acid 12%, mercaptan 1%, TPO 3%, levelling agent (BYK-3530)
0.5%th, photosensitivity promotor (reactive amines P-1114) 2%, pearly-lustre silver powder 12%, adhesion promoter (phosphate CN9051)
0.5%.
The percentage by weight of LED curable water-borne UV protective topcoats is constituted：Waterborne epoxy acrylate 20%, waterborne polyester
Acrylate 34%, ethoxylated trimethylolpropane triacrylate (EO15- TMPTA) 14%, third oxidation trihydroxy methyl third
Alkane triacrylate 17%, mercaptan 4%, levelling agent (BYK-333) 0.5%, defoamer (BYK-1615) 0.5%, polymerization inhibitor are (right
Benzenediol) 1%, calcium carbonate 9%.
Performance characterization
With reference to corresponding examination criteria, to three kinds of LED curable water-borne UV furniture house ornamentation decorative panels obtained in above-described embodiment 1-3
Performance detection is carried out, detection project includes hardness of paint film, outward appearance, adhesive force, water resistance, wearability, stain resistance, washability
Property and yellowing resistance.
Testing result is as shown in Table 1 below.
Table 1
The hardness of paint film that can be seen that LED curable water-bornes UV furniture house ornamentation paints of the invention by the testing result of table 1 is high,
Richness is good, and adhesive force is strong, and water resistance, wearability, anti-stain characteristic energy, abrasion resistance and yellowing resistance are excellent, decorative effect and
Defencive function is good, fully meets the use requirement of building trade furniture upholstery, and preparation technology production efficiency is high, energy consumption
Low, green non-pollution.
Claims (10)
1. a kind of LED curable water-bornes UV furniture house ornamentation paints, it is characterised in that including：It is attached to furniture house ornamentation surface and is consolidated by LED
Change the coating I of aqueous UV adhesion primers solidification；It is attached to the surface of coating I and by the solidification of LED curable water-borne UV colouring agents
Into coating II；It is attached to the surface of coating II and the coating III solidified by LED curable water-borne UV protective topcoats；
Described LED curable water-borne UV adhesion primers, by weight percentage, comprising：Water-and acrylate prepolymer 10-70%,
Water-soluble active monomer 10-60%, light trigger 1-5%, aqueous promoter 0-5%, filler 0-50% and water 0-50%；
Described LED curable water-borne UV colouring agents, by weight percentage, comprising：Water-and acrylate prepolymer 10-70%, water
Insoluble active monomer 10-60%, light trigger 1-5%, aqueous promoter 0-5%, pigment 0-30% and water 0-30%；
Described LED curable water-borne UV protective topcoats, by weight percentage, comprising：Water-and acrylate prepolymer 10-70%,
Water-soluble active monomer 10-60%, light trigger 1-5%, aqueous promoter 0-5%, filler 0-50% and water 0-50%.
2. LED curable water-bornes UV furniture house ornamentation paints according to claim 1, it is characterised in that：It is attached in LED curable water-bornes UV
In priming paint, UV colouring agents and UV protective topcoats, described water-and acrylate prepolymer be selected from aqueous polyurethane acrylate,
Waterborne epoxy acrylate, waterborne polyester acrylate, aqueous amino acrylates, aqueous acrylamide acidifying polyacrylate and water
At least one in property acrylate copolymer.
3. LED curable water-bornes UV furniture house ornamentation paints according to claim 1, it is characterised in that：Described water-soluble active
Monomer is selected from propoxyl group trimethylolpropane trimethacrylate（PO3-TMPTA）, hydroxy propyl methacrylate（HPMA）, ethyoxyl
Change trimethylolpropane trimethacrylate (EOn- TMPTA, n=3,6,9,15,20）, hydroxy-ethyl acrylate（HEA）, metering system
Acid（MAA）, pure acrylic acid（AA）, hydroxyethyl methacrylate（HEMA）And hydroxypropyl acrylate（HPA）In at least one.
4. LED curable water-bornes UV furniture house ornamentation paints according to claim 1, it is characterised in that：Described light trigger is
One kind in mercaptan, Ciba 1173, Ciba 184, Ciba 369, Ciba 907, Ciba 819, Ciba 651, TPO, ITX or
Two or more combinations.
5. LED curable water-bornes UV furniture house ornamentation paints according to claim 1, it is characterised in that：Described aqueous promoter is
Levelling agent, wetting dispersing agent, photosensitivity promotor, adhesion promoter, defoamer, polymerization inhibitor, delustering agent, one kind of anti-settling agent or
Two or more combinations.
6. LED curable water-bornes UV furniture house ornamentation paints according to claim 1, it is characterised in that：Described pigment be carbon black,
One or more combination in titanium dioxide, pearly-lustre silver powder, pearly-lustre bronze, iron oxide red, phthalocyanine blue；Described filler is selected to be slided
In stone flour, flatting silica, aerosil, anti-scratch wax powder, calcium carbonate, barium sulfate, silica flour, kaolin, bentonite at least
It is a kind of.
7. LED curable water-borne UV furniture house ornamentation paints according to any one of claim 1-6, it is characterised in that：Coating I,
II and III thickness is preferably 10-200 um, more preferably 10-120 um independently of one another.
8. the preparation method of the LED curable water-borne UV furniture house ornamentation paints any one of claim 1-7, including following step
Suddenly：
1）Cleaning furniture house ornamentation surface；
2）In furniture house ornamentation external coating LED curable water-borne UV adhesion primers；
3）First time LED solidifies, and forms coating I；
4）In the external coating LED curable water-borne UV colouring agents of coating I；
5）Second LED solidification, forms coating II；
6）In the external coating LED curable water-borne UV protective topcoats of coating II, infrared levelling or natural levelling；
7）Third time LED solidifies, and forms coating III.
9. preparation method according to claim 8, it is characterised in that：For solidify LED wavelength be 420nm,
One kind in 405nm, 390nm, 385nm, 380nm, 375nm, 370nm, 365nm, 360nm.
10. preparation method according to claim 8, it is characterised in that：Step 6）In, the temperature of described infrared levelling is
20-150 DEG C, flow time is 0.1-10 min.