CN106894239A - A kind of fade-proof method during polyamide fibre fluorescein emgloves impregnation - Google Patents
A kind of fade-proof method during polyamide fibre fluorescein emgloves impregnation Download PDFInfo
- Publication number
- CN106894239A CN106894239A CN201710155389.0A CN201710155389A CN106894239A CN 106894239 A CN106894239 A CN 106894239A CN 201710155389 A CN201710155389 A CN 201710155389A CN 106894239 A CN106894239 A CN 106894239A
- Authority
- CN
- China
- Prior art keywords
- gloves
- impregnation
- dipping
- polyamide fibre
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of method fade-proof during polyamide fibre fluorescein emgloves impregnation, comprise the following steps：Woven gloves core pre-treatment dyeing reduction cleaning resin treatment dehydration cover die dipping impregnation drying washing, dehydration, drying.Impregnation COLOR FASTNESS PROBLEM in order to solve polyamide fibre fluorescence green gloves of the invention, it is that gloves finished product is dyeed to change cheese yarn dyeing, and fixation, improves the color fastness of gloves, and washing fastness reaches more than 4 grades.Resin finishing is carried out in leaching methyl alcohol remote holder set, gloves appearance is formed thin film, prevent methyl alcohol equal solvent and dye contacts, prevent solvent from peeling off dyestuff.The methanol tolerant fastness of fluorescence green gloves is improved, reduces the loss of enterprise, make customer satisfaction.
Description
Technical field
The invention belongs to gloves process field, and in particular to fade-proof side during a kind of polyamide fibre fluorescein emgloves impregnation
Method.
Background technology
Terylene dipped gloves are to impregnate natural emulsion based on the seamless terylene gloves core of 13 pins to produce.The gloves belong to
One kind in dipped gloves safety and industrial gloves.Gloves inherit the comfortableness and gas permeability of terylene gloves, and glue surface inherits genuine milk
The advantage of glue, soft abrasion-resistant.Gloves core is except terylene, also the gloves core of other various fibrous raw materials, such as mitten, polyamide fibre hand
Set, the also such as anti-cutting gloves of some features, fire-retardant gloves, antibacterial gloves.General dipped gloves have PU, PVC, fourth
It is fine to wait latex.And the color of gloves core is various, wherein fluorescence green polyamide fibre gloves are exactly one kind therein, fluorescence green polyamide fibre
After butadiene acrylonitrile rubber is soaked, fluorescent green dye fades serious to gloves core, and pollutes glue, in other position staining of gloves.
The content of the invention
Goal of the invention：The present invention provides a kind of method fade-proof during polyamide fibre fluorescein emgloves impregnation.
Technical scheme：Fade-proof method, comprises the following steps during a kind of polyamide fibre fluorescein emgloves impregnation：Weaving hand
Set core -- -- -- -- -- -- -- wash, take off cover die dipping resin treatment reduction cleaning for dehydration for dyeing for pre-treatment by impregnation -- drying --
Water, drying；Concrete operations are as follows：
(1) woven gloves core：50 danier polyamide fibre low stretch yarns are first made into 13 pin seamless gloves cores；
(2) pre-treatment：Processed before being carried out by degreaser in the garment dyeing machine, 15 are washed by 80 DEG C -85 DEG C -
10-15min is washed in 20min, draining in cold water；The degreaser includes：Degreaser 1-2G/L, soaping agent 2-4G/L；
(3) dye：Coloring agent includes：Scattered fluorescent yellow 8G 3-3.5%, glacial acetic acid 2-3G/L, dispersant 1-2G/L；From
Normal temperature is warmed up to 125 DEG C -130 DEG C, is incubated 25min-30min, cools to 50 DEG C -60 DEG C；
(4) reduction cleaning：Reducing agent includes：Sodium hydrosulfite 4-6G/L, caustic soda 1-2G/L, specially：The water at 80 DEG C -90 DEG C
15-20min, discharge opeing are washed, then enters cold water and wash 10-15min；
(5) resin treatment：Resin pickup；Formaldehyde-free resins YJ-130--40G/L；Normal temperature dipping 10--15min；
(6) it is dehydrated：90 DEG C -- 100 DEG C of 8-10min of drying, then bake 3--5min at 150--160 DEG C；
(7) cover die dipping：Handle sleeve core retainer plate on the glove mould in correspondingly sized (Europe version No. 7-11), immersion barrier liquid,
Glue penetration to the gloves back side is prevented, solution is left after dipping 30S, methyl alcohol is volatilized；Wherein, the obstruct liquid includes：Methyl alcohol
80--90G/L, calcium nitrate 5--8G/L, dispersant 3--5G/L；
(8) impregnation：Gloves after above-mentioned dipping are put into the fine latex of liquid fourth after reconciling, fan is reused after taking out
Slightly blow glue surface；
(9) dry：It is 120 DEG C by oven cooking cycle temperature -- 130 DEG C, the time is 40-60 minutes；
(10) wash, be dehydrated, dry.
Beneficial effect：Specific advantage of the invention is as follows：
1st, in order to solve the impregnation COLOR FASTNESS PROBLEM of polyamide fibre fluorescence green gloves, it is the dyeing of gloves finished product to change cheese yarn dyeing, and
Fixation, improves the color fastness of gloves, and washing fastness reaches more than 4 grades.
2nd, resin finishing is carried out before methyl alcohol is soaked, gloves appearance is formed thin film, prevent methyl alcohol equal solvent and dyestuff
Contact, prevents solvent from peeling off dyestuff.
3rd, the methanol tolerant fastness of fluorescence green gloves is improved, reduces the loss of enterprise, make customer satisfaction.
Specific embodiment
With reference to specific embodiment, the present invention will be described in detail.
Specific embodiment one：
Fade-proof method, comprises the following steps during a kind of polyamide fibre fluorescein emgloves impregnation：Woven gloves core -- it is preceding
Treatment -- dyeing -- reduction cleaning -- resin treatment -- dehydration -- cover die dipping -- impregnation -- drying -- washing, dehydration, drying；Tool
Gymnastics is made as follows：
(1) woven gloves core：50 danier polyamide fibre low stretch yarns are first made into 13 pin seamless gloves cores；
(2) pre-treatment：Processed before being carried out by degreaser in the garment dyeing machine, by 80 DEG C of washing 15min, draining,
10min is washed in cold water；The degreaser includes：Degreaser 1G/L, soaping agent 2G/L；
(3) dye：Coloring agent includes：Scattered fluorescent yellow 8G 3%, glacial acetic acid 2G/L, dispersant 1G/L；Heated up from normal temperature
To 125 DEG C, 25min is incubated, cools to 50 DEG C；
(4) reduction cleaning：Reducing agent includes：Sodium hydrosulfite 4G/L, caustic soda 1G/L, specially：15min is washed at 80 DEG C,
Discharge opeing, then enter cold water and wash 10min；
(5) resin treatment：Resin pickup；Formaldehyde-free resins YJ-130G/L；Normal temperature dipping 10min；
(6) it is dehydrated：90 DEG C of drying 8min, then bake 3min at 150 DEG C；
(7) cover die dipping：To on the glove mould in correspondingly sized (Europe version No. 7), immersion barrier liquid is prevented handle sleeve core retainer plate
Glue penetration leaves solution to the gloves back side after dipping 30S, methyl alcohol is volatilized；Wherein, the obstruct liquid includes：Methyl alcohol 80G/L,
Calcium nitrate 5G/L, dispersant 3G/L；
(8) impregnation：Gloves after above-mentioned dipping are put into the fine latex of liquid fourth after reconciling, fan is reused after taking out
Slightly blow glue surface；
(9) dry：It it is 120 DEG C by oven cooking cycle temperature, the time is 40 minutes；
(10) wash, be dehydrated, dry.
Specific embodiment two：
Fade-proof method, comprises the following steps during a kind of polyamide fibre fluorescein emgloves impregnation：Woven gloves core -- it is preceding
Treatment -- dyeing -- reduction cleaning -- resin treatment -- dehydration -- cover die dipping -- impregnation -- drying -- washing, dehydration, drying；Tool
Gymnastics is made as follows：
(1) woven gloves core：50 danier polyamide fibre low stretch yarns are first made into 13 pin seamless gloves cores；
(2) pre-treatment：Processed before being carried out by degreaser in the garment dyeing machine, by 85 DEG C of washing 20min, draining,
15min is washed in cold water；The degreaser includes：Degreaser 2G/L, soaping agent 4G/L；
(3) dye：Coloring agent includes：Scattered fluorescent yellow 8G 3.5%, glacial acetic acid 3G/L, dispersant 2G/L；From normal temperature liter
Temperature is incubated 30min to 130 DEG C, cools to 60 DEG C；
(4) reduction cleaning：Reducing agent includes：Sodium hydrosulfite 6G/L, caustic soda 2G/L, specially：20min is washed at 90 DEG C,
Discharge opeing, then enter cold water and wash 15min；
(5) resin treatment：Resin pickup；Formaldehyde-free resins YJ-140G/L；Normal temperature dipping 15min；
(6) it is dehydrated：100 DEG C of drying 10min, then bake 5min at 160 DEG C；
(7) cover die dipping：Handle sleeve core retainer plate on the glove mould in correspondingly sized (Europe version No. 11), prevent by immersion barrier liquid
Only glue penetration leaves solution to the gloves back side after dipping 30S, methyl alcohol is volatilized；Wherein, the obstruct liquid includes：Methyl alcohol 90G/
L, calcium nitrate 8G/L, dispersant 5G/L；
(8) impregnation：Gloves after above-mentioned dipping are put into the fine latex of liquid fourth after reconciling, fan is reused after taking out
Slightly blow glue surface；
(9) dry：It it is 130 DEG C by oven cooking cycle temperature, the time is 60 minutes；
(10) wash, be dehydrated, dry.
Specific embodiment three：
Fade-proof method, comprises the following steps during a kind of polyamide fibre fluorescein emgloves impregnation：Woven gloves core -- it is preceding
Treatment -- dyeing -- reduction cleaning -- resin treatment -- dehydration -- cover die dipping -- impregnation -- drying -- washing, dehydration, drying；Tool
Gymnastics is made as follows：
(1) woven gloves core：50 danier polyamide fibre low stretch yarns are first made into 13 pin seamless gloves cores；
(2) pre-treatment：Processed before being carried out by degreaser in the garment dyeing machine, by 83 DEG C of washing 17min, draining,
12min is washed in cold water；The degreaser includes：Degreaser 1.5G/L, soaping agent 3G/L；
(3) dye：Coloring agent includes：Scattered fluorescent yellow 8G 3.3%, glacial acetic acid 2.3G/L, dispersant 1.2G/L；From normal
Temperature is warmed up to 128 DEG C, is incubated 27min, cools to 56 DEG C；
(4) reduction cleaning：Reducing agent includes：Sodium hydrosulfite 5G/L, caustic soda 1.2G/L, specially：Washed at 87 DEG C
18min, discharge opeing, then enter cold water and wash 13min；
(5) resin treatment：Resin pickup；Formaldehyde-free resins YJ-134G/L；Normal temperature dipping 13min；
(6) it is dehydrated：97 DEG C of drying 9min, then bake 4min at 156 DEG C；
(7) cover die dipping：To on the glove mould in correspondingly sized (Europe version No. 9), immersion barrier liquid is prevented handle sleeve core retainer plate
Glue penetration leaves solution to the gloves back side after dipping 30S, methyl alcohol is volatilized；Wherein, the obstruct liquid includes：Methyl alcohol 84G/L,
Calcium nitrate 6G/L, dispersant 4G/L；
(8) impregnation：Gloves after above-mentioned dipping are put into the fine latex of liquid fourth after reconciling, fan is reused after taking out
Slightly blow glue surface；
(9) dry：It it is 126 DEG C by oven cooking cycle temperature, the time is 50 minutes；
(10) wash, be dehydrated, dry.
Impregnation COLOR FASTNESS PROBLEM in order to solve polyamide fibre fluorescence green gloves of the invention, it is that gloves finished product is dyeed to change cheese yarn dyeing,
And fixation, improves the color fastness of gloves, and washing fastness reaches more than 4 grades.Resin finishing is carried out in leaching methyl alcohol remote holder set, makes hand
Set appearance forms thin film, prevents methyl alcohol equal solvent and dye contacts, prevents solvent from peeling off dyestuff.Improve fluorescence green gloves
Methanol tolerant fastness, reduces the loss of enterprise, makes customer satisfaction.
The present invention is not limited to above-mentioned preferred forms, and anyone can show that other are various under enlightenment of the invention
The product of form, however, make any change in its shape or structure, it is every with skill identical or similar to the present application
Art scheme, is within the scope of the present invention.
Claims (1)
1. a kind of method fade-proof during polyamide fibre fluorescein emgloves impregnation, it is characterised in that：Comprise the following steps：Weaving hand
Set core -- -- -- -- -- -- -- wash, take off cover die dipping resin treatment reduction cleaning for dehydration for dyeing for pre-treatment by impregnation -- drying --
Water, drying；Concrete operations are as follows：
(1) woven gloves core：50 danier polyamide fibre low stretch yarns are first made into 13 pin seamless gloves cores；
(2) pre-treatment：Processed before being carried out by degreaser in the garment dyeing machine, 15-20min washed by 80 DEG C-85 DEG C,
Draining, washes 10-15min in cold water；The degreaser includes：Degreaser 1-2G/L, soaping agent 2-4G/L；
(3) dye：Coloring agent includes：Scattered fluorescent yellow 8G 3-3.5%, glacial acetic acid 2-3G/L, dispersant 1-2G/L；From normal temperature
125 DEG C -130 DEG C are warmed up to, 25min-30min is incubated, 50 DEG C -60 DEG C are cooled to；
(4) reduction cleaning：Reducing agent includes：Sodium hydrosulfite 4-6G/L, caustic soda 1-2G/L, specially：Washed at 80 DEG C -90 DEG C
15-20min, discharge opeing, then enter cold water and wash 10-15min；
(5) resin treatment：Resin pickup；Formaldehyde-free resins YJ-130--40G/L；Normal temperature dipping 10--15min；
(6) it is dehydrated：90 DEG C -- 100 DEG C of 8-10min of drying, then bake 3--5min at 150--160 DEG C；
(7) cover die dipping：To on the glove mould in correspondingly sized (Europe version No. 7-11), immersion barrier liquid is prevented handle sleeve core retainer plate
Glue penetration leaves solution to the gloves back side after dipping 30S, methyl alcohol is volatilized；Wherein, the obstruct liquid includes：Methyl alcohol 80--
90G/L, calcium nitrate 5--8G/L, dispersant 3--5G/L；
(8) impregnation：Gloves after above-mentioned dipping are put into the fine latex of liquid fourth after reconciling, fan are reused after taking out and is slightly blown
Glue surface；
(9) dry：It is 120 DEG C by oven cooking cycle temperature -- 130 DEG C, the time is 40-60 minutes；
(10) wash, be dehydrated, dry.