CN106893798A - 一种耐蚀钢添加锑的冶炼方法 - Google Patents

一种耐蚀钢添加锑的冶炼方法 Download PDF

Info

Publication number
CN106893798A
CN106893798A CN201710215148.0A CN201710215148A CN106893798A CN 106893798 A CN106893798 A CN 106893798A CN 201710215148 A CN201710215148 A CN 201710215148A CN 106893798 A CN106893798 A CN 106893798A
Authority
CN
China
Prior art keywords
antimony
recovery rate
content
corrosion
time
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201710215148.0A
Other languages
English (en)
Other versions
CN106893798B (zh
Inventor
初仁生
刘金刚
李战军
史志强
马长文
郝宁
王卫华
陈霞
刘建明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shougang Corp
Original Assignee
Shougang Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shougang Corp filed Critical Shougang Corp
Priority to CN201710215148.0A priority Critical patent/CN106893798B/zh
Publication of CN106893798A publication Critical patent/CN106893798A/zh
Application granted granted Critical
Publication of CN106893798B publication Critical patent/CN106893798B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种耐蚀钢添加锑的冶炼方法，属于炼钢技术领域。采用LF合金化方式加入同时在RH精炼过程中严密监控锑含量；在LF初期采用锑锭或锑铁配锑；在RH精炼过程中严密监控锑的含量，严格控制RH的真空度和时间，真空度控制为50Pa～100Pa，深真空时间为10～12min，软吹时间为8～10min，流量控制为0.001～0.0015m3/(min*t)，此时收得率为98％～100％。优点是：解决了锑的添加方法和过程含量的控制方法，明确了炼钢过程中锑的收得率和稳定控制规律，实现了成品锑含量的稳定控制，为耐蚀钢的研发提供了技术保证，也为锑的成分优化提供了研究方法。同时取得较高收得率，降低了合金消耗和稳定控制，降低了冶炼成本。

Description

一种耐蚀钢添加锑的冶炼方法
技术领域
本发明属于炼钢技术领域，特别是涉及耐蚀钢添加锑的冶炼方法，添加锑含量大于0.07重量％。
背景技术
钢铁冶炼过程中，锑作为一个耐蚀性的元素经常被要求加在耐蚀钢的成分设计中，锑遇到强热则燃烧成白色锑的氧化物，因此在炼钢中锑加入后会有一定烧损，同时锑在转炉出钢中添加、LF精炼中添加和RH中收得率和稳定性都有很大的不同。尤其在LF精炼和RH精炼中元素的稳定性不得而知，因此锑作为一种毒性元素怎样添加和控制是炼钢中一直以来的难题，尤其是过程中锑含量的变化和稳定性一直鲜有报道。
目前关于锑的专利都为材料制备领域，对于炼钢领域中锑的添加都鲜有报道，因此急需一种锑的添加方法和过程含量的控制方法，特别是一种耐蚀钢添加锑含量大于0.07％的冶炼方法。这可以为锑的炼钢中添加和过程控制带来指导，同时也为耐蚀钢的研发带来一定的技术保证。
发明内容
本发明的目的是提供一种耐蚀钢添加锑的冶炼方法，添加锑含量大于0.07重量％，成功解决了锑的添加方法和过程含量的控制方法。
本发明专利解决问题所采用的技术方案是：
(1)对锑的加入控制规律为：转炉出钢加入锑的收得率为77％～78％，同时在LF和RH精炼过程中会有一定的损耗，损耗为10％～20％，收得率较低。因此采用LF合金化方式加入同时在RH精炼过程中严密监控锑含量(损耗小于2重量％)，提高收得率和控制稳定性；
(2)在LF初期采用锑锭(或锑铁)配锑，加入量为总量50重量％～80重量％，如果对于后续炼钢要求温度得到保证，则加入50重量％；如果后续炼钢要求温度不能得到保证，则加入80重量％后再升温，此时收得率在87％～90％，在LF精炼中后期，即脱硫结束后加入剩下的锑锭(或锑铁)，此时收得率较高，为95％；
(3)在RH精炼过程中严密监控锑的含量，严格控制RH的真空度和时间，真空度控制为50Pa～100Pa，深真空时间为10～12min，同时严格控制软吹时间和软吹流量，软吹时间为8～10min，流量控制为0.001～0.0015m3/(min*t)，此时收得率为98％～100％。
本发明的优点是：解决了锑的添加方法和过程含量的控制方法，特别是一种耐蚀钢添加锑含量大于0.07重量％高锑的冶炼方法，明确了炼钢过程中锑的收得率和稳定控制规律，实现了成品锑含量的稳定控制，为耐蚀钢的研发提供了技术保证，也为锑的成分优化提供了研究方法。同时取得较高收得率，降低了合金消耗和稳定控制，降低了冶炼成本。
具体实施方式
实施例1：
钢种耐蚀钢A32-RCU，锑成品要求为0.08％，钢包容量100t，冶炼工艺为转炉冶炼→LF炉精炼→RH精炼→连铸，对锑的添加和控制方法为：
(1)采用LF合金化方式加入同时在RH精炼过程中严密监控Sb含量(损耗小于2重量％)，提高收得率和控制稳定性。在LF初期采用锑锭配锑，LF炉到站温度为1596℃，后续炼钢要求温度得到保证，加入50重量％锑锭配锑，此时收得率在89％，在LF精炼中后期，即脱硫结束后加入剩下的锑锭(或锑铁)，此时收得率为95％；
(2)在RH精炼过程中严密监控锑的含量，严格控制RH的真空度和时间，真空度控制为80Pa，深真空时间为11.5min，同时严格控制软吹时间和软吹流量，软吹时间为10min，流量控制为0.0012m3/(min*t)，此时收得率为100％。
经此工艺，最终成品锑含量满足要求，锑的收得率达到92％。成功的解决了锑的添加方法和过程含量的控制方法。

Claims (1)

1.一种耐蚀钢添加锑的冶炼方法，其特征在于，工艺步骤及在工艺中控制的技术参数如下：
(1)采用LF合金化方式加入同时在RH精炼过程中严密监控Sb含量损耗小于2重量％，提高收得率和控制稳定性；
(2)在LF初期采用锑锭或锑铁配锑，加入量为总量50重量％～80重量％，当对于后续炼钢要求温度得到保证，则加入50重量％；当后续炼钢要求温度不能得到保证，则加入80重量％后再升温，此时收得率在87％～90％，在LF精炼中后期，即脱硫结束后加入剩下的锑锭或锑铁，此时收得率较高，为95％；
(3)在RH精炼过程中严密监控锑的含量，严格控制RH的真空度和时间，真空度控制为50Pa～100Pa，深真空时间为10～12min，同时严格控制软吹时间和软吹流量，软吹时间为8～10min，流量控制为0.001～0.0015m3/(min*t)，此时收得率为98％～100％。
CN201710215148.0A 2017-04-02 2017-04-02 一种耐蚀钢添加锑的冶炼方法 Active CN106893798B (zh)