CN106892757A - A kind of preparation method of silicon magnesium calcium fertilizer material - Google Patents
A kind of preparation method of silicon magnesium calcium fertilizer material Download PDFInfo
- Publication number
- CN106892757A CN106892757A CN201710234616.9A CN201710234616A CN106892757A CN 106892757 A CN106892757 A CN 106892757A CN 201710234616 A CN201710234616 A CN 201710234616A CN 106892757 A CN106892757 A CN 106892757A
- Authority
- CN
- China
- Prior art keywords
- magnesium calcium
- silicon magnesium
- preparation
- calcium fertilizer
- mother liquor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of silicon magnesium calcium fertilizer material, it is characterised in that by silicon magnesium calcium and urea for active component is formed with auxiliary material combination, preparation method includes the silicon magnesium calcium fertilizer material:Burden process, premix material process, once granulation, compounding process, secondary granulation and drying process, the beneficial effects of the invention are as follows:Fertility persistence is relatively strong, fertility release stabilization and nitrogen content are higher.
Description
Technical field
The invention belongs to technical field of biological fertilizer, relate more specifically to a kind of preparation method of silicon magnesium calcium fertilizer material.
Background technology
Fertilizer be to provide one or more plants necessary to mineral element, improve soil property, increase soil fertility
One class material of level, is one of material base of agricultural production.With the rise and development of modern age chemical industry, various chemistry
Fertilizer is come out one after another.But due to excessively using for chemical fertilizer, soil contamination problem is increasingly severe, soil aciditiy change,
Soil hardening fertility declines and harmful substance is produced to soil and pollutes these soil contamination problems, the life for affecting us at moment
It is living.
In order to solve problem above, bio-feritlizer becomes very powerful and exceedingly arrogant, and bio-feritlizer has little by little entered into our world,
Silicon magnesium calcium fertilizer material is exactly a kind of bio-feritlizer using biological fermentation process production, and country's invention of Patent No. CN1182241C is special
Profit discloses a kind of microbial silicon magnesium calcium fertilizer and its manufacture method, and problem above is solved well, the microbial silicon magnesium calcium fertilizer
Acid, the improved soil structure with 1. sweetening of the soil;2. strengthen the stem tissue of crop, promote plant cell division, make rhizome
Leaf is plump;3. chlorophyll is increased, the vigor of various enzymes in activated plant body improves photosynthesis and operates photosynthate
Ability, promotes the growth of plant;4. disease-resistant, insect pest ability is strengthened;5. improve the yield and quality of crops five are big
Effect.
Particularly silicon magnesium calcium fertilizer material has preferably water solubility, is easily absorbed by plant root, fully solves silicon magnesium calcium
Ion is difficult the problem for absorbing.However, have just because of silicon magnesium calcium fertilizer material it is preferably water-soluble, silicon magnesium calcium fertilizer material easily with
Rain drop erosion is flowed away, and the utilization rate for causing fertilizer is not high, and heavy rain is run into after particularly applying fertilizer, and problem is even more serious.Silicon magnesium calcium
The poor popularization for having had a strong impact on silicon magnesium calcium fertilizer material of fertility persistence of fertilizer, the particularly more southern area of rainwater.How
Improve the fertility persistence of silicon magnesium calcium fertilizer material, on the premise of the fertility for ensureing silicon magnesium calcium fertilizer material normally discharges, strengthen magnesium calcium fertilizer
Material slow release, is the research problem of silicon magnesium calcium fertilizer material.
The content of the invention
To solve the above problems, the deficiencies in the prior art are overcome, the invention provides a kind of fertility persistence relatively strong, fertility
The preparation method of release stabilization and nitrogen content silicon magnesium calcium fertilizer material higher, can effectively solve that fertility persistence is poor and nitrogen contains
The relatively low problem of amount.
The present invention solve above-mentioned technical problem concrete technical scheme be:The preparation method of silicon magnesium calcium fertilizer material, its feature exists
In:By silicon magnesium calcium and urea for active component is formed with auxiliary material combination, preparation method includes described silicon magnesium calcium fertilizer material:Dispensing work
Sequence, premix material process, once granulation, compounding process, secondary granulation and drying process, described burden process and premix material process
Including:
Ⅰ:Silicon magnesium calcium and urea are crossed into 60 mesh sieves, ammonium hydrogen carbonate and Diammonium phosphate (DAP) are crossed into 80 mesh, binder and land plaster cross 40 mesh
It is stand-by;
Ⅱ:Precise silicon magnesium calcium and urea, and be 1 according to solid-liquid ratio:2 are configured to mother liquor, then are according to mass ratio by mother liquor
1:5 are divided into mother liquor I and mother liquor II;
Ⅲ:Mother liquor I is added in land plaster, is stirred, obtain preparing softwood;
Described once granulation includes:To prepare softwood add drying and granulating machine in, heating and temperature control:100-120 DEG C, control
Granulation size is 14-18 mesh, crosses 14 mesh sieves and obtains gypsum particle;
Described compounding process includes:
Ⅰ:Binder is added in mother liquor II, 60 DEG C are heated to, bubble 2h is invaded, then ammonium hydrogen carbonate and Diammonium phosphate (DAP) are added to mother
Fully dissolved in liquid II, be eventually adding sawdust and stir, obtain compound;
Ⅱ:Gypsum particle is added in compound, is sufficiently mixed 15 minutes, obtain finished product material;
Described secondary granulation includes:Finished product material is pressed into granulator, it is 4-6 mesh to control granulation size, crosses 4 mesh sieves and obtains into
Product particle;
Described drying process includes:Finished particle is placed in drying machine and is dried, control 100-120 DEG C of drying temperature.
Further, described binder includes:Sodium carboxymethylcellulose or stickiness starch or Lauxite or lignin
Sulfonate one or more mixture.
Further, described sawdust moisture is controlled below 5%.
Further, described granulator uses high-speed mixing granulating machine or fertiliser granulates machine.
Further, described finished particle is one kind of spherical bar-shaped or irregular spheroid, after finished particle is dried
Humidity is less than 5%.
Further, the percentage by weight of described silicon magnesium calcium fertilizer material formula each component is:Silicon magnesium calcium 32-36%, urea
18-28%, sawdust 19-21%, land plaster 5-8%, binder 1-2%, ammonium hydrogen carbonate 3-6%, Diammonium phosphate (DAP) 1-3%, each group
Percentage by weight sum is divided to be 100%.
The beneficial effects of the invention are as follows:Present invention employs the technique pelletized twice, and employ multiple auxiliary materials and carry out
Parcel, on the premise of the fertility that ensure that magnesium calcium fertilizer material normally discharges, strengthens magnesium calcium fertilizer material slow release, and this technique provides one
Seed manure power persistence is relatively strong, fertility release is stable and nitrogen content silicon magnesium calcium fertilizer material higher, and fertility persistence is solved well
The poor and relatively low problem of nitrogen content.
Brief description of the drawings:
The present invention of accompanying drawing 1 schemes with the concentrations versus of silicon magnesium calcium fertilizer silicon magnesium calcium burst size in soil of prior art.
Specific embodiment:
Detail be just for the sake of can fully understand embodiments of the invention in the description of the invention, but as ability
The technical staff in domain will be appreciated that implementation of the invention is not limited to these details.In addition, known 26S Proteasome Structure and Function not by
Detailed description or displaying, to avoid having obscured the main points of the embodiment of the present invention.For one of ordinary skill in the art
Speech, can understand above-mentioned term concrete meaning in the present invention with concrete condition.
Specific embodiment of the invention:
Embodiment one:By taking 32kg silicon magnesium calcium raw materials as an example:
1. 32kg silicon magnesium calcium and 28kg urea are crossed into 60 mesh sieves, 6kg ammonium hydrogen carbonate and 3kg Diammonium phosphate (DAP) are crossed into 80 mesh, 1kg bondings
It is stand-by that agent and 8kg land plasters cross 40 mesh;
2. precise silicon magnesium calcium 32kg and urea 28kg, silicon magnesium calcium 32kg and urea 28kg is added in 120kg water, fully
Stirring dissolve obtaining mother liquor;Again by mother liquor according to mass ratio be 1:5 are divided into mother liquor I:30 kg and mother liquor II:150 kg;
3. 8kg land plasters are added in 30 kg mother liquors I, stirred, obtain preparing softwood, softwood addition will be prepared
In fluidized drying pelletizer, heating and temperature control is 100 DEG C, and it is 14 mesh to control granulation size, crosses 14 mesh sieves and obtains gypsum particle;
4. first 1kg sodium carboxymethylcelluloses are added in 150 kg mother liquors II, are heated to 60 DEG C, invade bubble 2h, fully after dissolving,
6kg ammonium hydrogen carbonate and 1kg Diammonium phosphate (DAP) are added in mother liquor II are again fully dissolved, be eventually adding 21kg sawdusts, be sufficiently stirred for
Uniformly, compound is obtained;
5. the gypsum particle in step 3 is added in compound, be sufficiently mixed 15 minutes, obtain finished product material;
6. finished product material is pressed into fertiliser granulates machine, it is 4 mesh to control granulation size, obtains finished product rod-shpaed particle;
7. finished particle is placed in drying machine and be dried, control 120 DEG C of drying temperature, dry 20min, control humidity is 5%
Below.
Embodiment two:By taking 36kg silicon magnesium calcium raw materials as an example:
1. 36kg silicon magnesium calcium and 18kg urea are crossed into 60 mesh sieves, 6kg ammonium hydrogen carbonate and 3kg Diammonium phosphate (DAP) are crossed into 80 mesh, 2kg bondings
It is stand-by that agent and 5kg land plasters cross 40 mesh;
2. precise silicon magnesium calcium 36kg and urea 18kg, silicon magnesium calcium 36kg and urea 18kg is added in 108kg water, fully
Stirring dissolve obtaining mother liquor;Again by mother liquor according to mass ratio be 1:5 are divided into mother liquor I:27 kg and mother liquor II:135 kg;
3. 5kg land plasters are added in 27 kg mother liquors I, stirred, obtain preparing softwood, softwood addition will be prepared
In fluidized drying pelletizer, heating and temperature control is 120 DEG C, and it is 18 mesh to control granulation size, crosses 14 mesh sieves and obtains gypsum particle;
4. first 2kg stickiness starch is added in 135 kg mother liquors II, is heated to 60 DEG C, invade bubble 2h, fully after dissolving, then will
3kg ammonium hydrogen carbonate and 3kg Diammonium phosphate (DAP) fully dissolve in being added to mother liquor II, are eventually adding 19kg sawdusts, stir,
Obtain compound;
5. the gypsum particle in step 3 is added in compound, be sufficiently mixed 15 minutes, obtain finished product material;
6. finished product material is pressed into high-speed mixing granulating machine, it is 4 mesh to control granulation size, obtains finished product spherical particle;
7. finished particle is placed in drying machine and be dried, control 100 DEG C of drying temperature, dry 20min, control humidity is 5%
Below.
Embodiment three:By taking 34kg silicon magnesium calcium raw materials as an example:
1. 34kg silicon magnesium calcium and 24kg urea are crossed into 60 mesh sieves, 6kg ammonium hydrogen carbonate and 3kg Diammonium phosphate (DAP) are crossed into 80 mesh, 2kg bondings
It is stand-by that agent and 8kg land plasters cross 40 mesh;
2. precise silicon magnesium calcium 34kg and urea 24kg, silicon magnesium calcium 34kg and urea 24kg is added in 116kg water, fully
Stirring dissolve obtaining mother liquor;Again by mother liquor according to mass ratio be 1:5 are divided into mother liquor I:29 kg and mother liquor II:145 kg;
3. 7kg land plasters are added in 29 kg mother liquors I, stirred, obtain preparing softwood, softwood addition will be prepared
In fluidized drying pelletizer, heating and temperature control is 110 DEG C, and it is 16 mesh to control granulation size, crosses 14 mesh sieves and obtains gypsum particle;
4. first 2kg lignosulfonates are added in 145 kg mother liquors II, are heated to 60 DEG C, invade bubble 2h, fully after dissolving, then
4kg ammonium hydrogen carbonate and 2kg Diammonium phosphate (DAP) are added in mother liquor II and are fully dissolved, be eventually adding 20kg sawdusts, be sufficiently stirred for
It is even, obtain compound;
5. the gypsum particle in step 3 is added in compound, be sufficiently mixed 15 minutes, obtain finished product material;
6. finished product material is pressed into high-speed mixing granulating machine, it is 5 mesh to control granulation size, obtains finished product spherical particle;
7. finished particle is placed in drying machine and be dried, control 110 DEG C of drying temperature, dry 20min, control humidity is 5%
Below.
In order to more intuitively represent product advantage of the invention, it is special with:
A:The silicon magnesium calcium granulated fertilizer produced using secondary granulating process of the invention;
B:The silicon magnesium calcium fertilizer material produced according to granulating process using inventive formulation, concrete technology is silicon magnesium according to mass ratio
Calcium 34%, urea 26%, sawdust 21%, land plaster 8%, binder 2%, ammonium hydrogen carbonate 6%, Diammonium phosphate (DAP) 3%, precise
Each material, and according to silicon magnesium calcium and 2 times of addition soft water of urea quality, above material is placed in after being well mixed in mixer,
In press-in granulator, it is 4-6 mesh to control granulation size, crosses 4 mesh sieves and obtains finished particle;Finished particle is placed in drying machine
Row drying, controls 110 DEG C of drying temperature, dries 20min;
A, B are contrasted;
Fertilizing operation is carried out to the tomato rice shoot tested using the silicon magnesium calcium granulated fertilizer of both the above technique productions, wherein two
The silicon magnesium calcium fertilizer material of kind of different process implements the silicon magnesium calcium of identical equivalent, and seedling is carried out after 30 days according to varying environment CMC model
Detection high, in tests below group, tomato rice shoot purchasing site, initial height of seedling be with physiological situation it is consistent, and using with
Sample is taken in machine sampling, is tested as follows in experiment greenhouse:
1. using the silicon magnesium calcium granulated fertilizer of secondary granulation production, grant on tomato rice shoot surrounding soil, control normal light
According to, moisture, cultivate 30 days, this test group is A1, and height of seedling detection is carried out after 30 days;
2. using a silicon magnesium calcium granulated fertilizer for granulation production, grant on tomato rice shoot surrounding soil, control normal light
According to, moisture, cultivate 30 days, this test group is A2, and height of seedling detection is carried out after 30 days;
3. using the silicon magnesium calcium granulated fertilizer of secondary granulation production, grant on tomato rice shoot surrounding soil, control normal light
According to, Used in Rainy Seasons of Southern Cities is simulated, it is overcast and rainy(Precipitation was controlled at 10mm/ days), cultivate 30 days continuous overcast and rainy 2 days events of stochastic simulation and be total to
7 times, this test group is B1, and height of seedling detection is carried out after 30 days;
4. using a silicon magnesium calcium granulated fertilizer for granulation production, grant on tomato rice shoot surrounding soil, control normal light
According to, Used in Rainy Seasons of Southern Cities is simulated, it is overcast and rainy(Precipitation was controlled at 10mm/ days), cultivate 30 days continuous overcast and rainy 2 days events of stochastic simulation and be total to
7 times, this test group is B2, and height of seedling detection is carried out after 30 days;Testing result such as table 1.
5. using the silicon magnesium calcium granulated fertilizer of secondary granulation production, grant on tomato rice shoot surrounding soil, control is normal
Illumination, simulate Used in Rainy Seasons of Southern Cities, it is overcast and rainy(Precipitation was controlled at 10mm/ days), the lasting continuous wet weather of simulation totally 20 days, this experiment
Group is determined to carry out calcium, magnesium, the measure of silicone content and urea content in C1,30 days;
6. using a silicon magnesium calcium granulated fertilizer for granulation production, grant on tomato rice shoot surrounding soil, control normal light
According to, Used in Rainy Seasons of Southern Cities is simulated, it is overcast and rainy(Precipitation was controlled at 10mm/ days), lasting to simulate continuous wet weather totally 20 days, this test group is
Calcium, magnesium, the measure of silicone content and urea content is carried out in C2,30 days to determine.
The plant strain growth contrast in the case of different weather of the silicon magnesium calcium fertilizer of 1 technique of table and prior art
Test group | Initial height of seedling/cm | Cultivated days/day | Final height of seedling/cm | Growth conditions |
A1 | 5 | 30 | 20.3 | Well |
A2 | 5 | 30 | 21.2 | Well |
B1 | 5 | 30 | 19.6 | Well |
B2 | 5 | 30 | 14.3 | Difference |
Data above analysis understands:A1 groups understand with the contrast of A2 groups:The secondary granulating process of the present invention and prior art are once pelletized
The silicon magnesium calcium fertilizer of technique productions, can meet the demand of plant growth, and prior art silicon magnesium calcium fertilizer, the release of silicon magnesium calcium compared with
Good, there was no significant difference with silicon magnesium calcium fertilizer of the invention for plant growth;B1 groups understand with the contrast of B2 groups:Of the invention and existing skill
The silicon magnesium calcium fertilizer of art, it is continuous it is overcast and rainy in the case of, the silicon magnesium calcium fertilizer of this technique, plant growth situation difference is little;Existing skill
The silicon magnesium calcium fertilizer of art, plant growth is suppressed;
Therefore, situation of the silicon magnesium calcium fertilizer for granulating process production of secondary granulating process of the invention and prior art in fine day
Under, can be good at meeting the demand of plant growth;Specifically the silicon magnesium calcium fertilizer of secondary granulating process production of the invention, has
There is preferable slow release effect, be prevented from continuous overcast and rainy causing silicon magnesium calcium to be largely lost in.
In order to more intuitively represent the process advantage of secondary granulating process of the invention, spy is with secondary granulation work of the invention
Under overcast and rainy environmental condition, the release of silicon magnesium calcium is dense in soil for silicon magnesium calcium fertilizer for granulating process production of skill and prior art
Degree is contrasted, and the silicon magnesium calcium fertilizer material of two of which different process implements the silicon magnesium calcium of identical equivalent, according to《NY/T
2272-2012 soil conditioner calcium, magnesium, the measure of silicone content》Measure on calcium, magnesium, silicone content in soil is respectively to contrast
Group tomato rice shoot Soil Surrounding is sampled, and after abandoning topsoil, takes difference deep soil 500g, dries, and drying is laggard
Row detection, obtains the concentrations versus of the present invention and silicon magnesium calcium fertilizer silicon magnesium calcium burst size in soil of prior art, such as accompanying drawing 1.
Data above analysis understands:Initial silicon magnesium calcium content is about 2.0 g/kg in soil, is used when using this technique
After the silicon magnesium calcium fertilizer of secondary granulation production uses the silicon magnesium calcium fertilizer once pelletized with prior art, in 1-2 days after fertilising
Maximum burst size can be reached, it is 5.9g/kg that wherein this technique uses the maximum burst size of the silicon magnesium calcium fertilizer of secondary granulation production,
It is 8.0g/kg that prior art uses the maximum burst size of the silicon magnesium calcium fertilizer once pelletized;
By it is continuous it is overcast and rainy after, the silicon magnesium calcium fertilizer of prior art it is continuous it is overcast and rainy in, silicon magnesium calcium content is quickly reduced, finally
The initial value of 2.0 g/kg is reduced to, but the silicon magnesium calcium content of 2.0 g/kg can not maintain the demand of plant growth;This work
The silicon magnesium calcium fertilizer of skill production it is continuous it is overcast and rainy in, silicon magnesium calcium content can be maintained at the scope of the stabilization of 5.0 more than g/kg,
So as to meet the demand of plant growth.
In sum:The present invention disclosure satisfy that the demand of plant growth, and this work using the silicon magnesium calcium fertilizer of secondary granulation
Skill has notable sexual clorminance using the silicon magnesium calcium fertilizer of secondary granulation production relative to the slow release effect of the silicon magnesium calcium fertilizer of prior art,
Therefore, present invention employs the technique pelletized twice, multiple auxiliary materials are employed and is wrapped up, ensure that the fertility of magnesium calcium fertilizer material
On the premise of normal release, strengthen magnesium calcium fertilizer material slow release, discharge steady the invention provides a kind of fertility persistence relatively strong, fertility
Fixed and nitrogen content silicon magnesium calcium fertilizer material higher, solves the problems, such as that fertility persistence is poor and nitrogen content is relatively low well.
Claims (6)
1. a kind of preparation method of silicon magnesium calcium fertilizer material, it is characterised in that:Described silicon magnesium calcium fertilizer material is work by silicon magnesium calcium and urea
Property composition is formed with auxiliary material combination, and preparation method includes:Burden process, once premix material process, granulation, compounding process, secondary
Granulation and drying process, described burden process and premix material process include:
Ⅰ:Silicon magnesium calcium and urea are crossed into 60 mesh sieves, ammonium hydrogen carbonate and Diammonium phosphate (DAP) are crossed into 80 mesh, binder and land plaster cross 40 mesh
It is stand-by;
Ⅱ:Precise silicon magnesium calcium and urea, and be 1 according to solid-liquid ratio:2 are configured to mother liquor, then are according to mass ratio by mother liquor
1:5 are divided into mother liquor I and mother liquor II;
Ⅲ:Mother liquor I is added in land plaster, is stirred, obtain preparing softwood;
Described once granulation includes:To prepare softwood add drying and granulating machine in, heating and temperature control:100-120 DEG C, control
Granulation size is 14-18 mesh, crosses 14 mesh sieves and obtains gypsum particle;
Described compounding process includes:
Ⅰ:Binder is added in mother liquor II, 60 DEG C are heated to, bubble 2h is invaded, then ammonium hydrogen carbonate and Diammonium phosphate (DAP) are added to mother
Fully dissolved in liquid II, be eventually adding sawdust and stir, obtain compound;
Ⅱ:Gypsum particle is added in compound, is sufficiently mixed 15 minutes, obtain finished product material;
Described secondary granulation includes:Finished product material is pressed into granulator, it is 4-6 mesh to control granulation size, crosses 4 mesh sieves and obtains into
Product particle;
Described drying process includes:Finished particle is placed in drying machine and is dried, control 100-120 DEG C of drying temperature.
2. the preparation method of silicon magnesium calcium fertilizer material according to claim 1, it is characterised in that described binder includes:Carboxylic first
Base sodium cellulosate or stickiness starch or Lauxite or lignosulfonates one or more mixtures.
3. the preparation method of silicon magnesium calcium fertilizer material according to claim 1, it is characterised in that described sawdust moisture control
System is below 5%.
4. the preparation method of silicon magnesium calcium fertilizer material according to claim 1, it is characterised in that described granulator is using at a high speed
Mixer-granulator or fertiliser granulates machine.
5. the preparation method of silicon magnesium calcium fertilizer material according to claim 1, it is characterised in that described finished particle is spherical
One kind of bar-shaped or irregular spheroid, humidity is less than 5% after finished particle is dried.
6. the preparation method of the silicon magnesium calcium fertilizer material according to claim 1-5 any one, it is characterised in that described silicon magnesium
The percentage by weight of calcareous fertilisers material formula each component is:Silicon magnesium calcium 32-36%, urea 18-28%, sawdust 19-21%, land plaster 5-
8%, binder 1-2%, ammonium hydrogen carbonate 3-6%, Diammonium phosphate (DAP) 1-3%, each component percentage by weight sum are 100%.