CN106892635A - A kind of dry powder fiber coating - Google Patents
A kind of dry powder fiber coating Download PDFInfo
- Publication number
- CN106892635A CN106892635A CN201710255997.9A CN201710255997A CN106892635A CN 106892635 A CN106892635 A CN 106892635A CN 201710255997 A CN201710255997 A CN 201710255997A CN 106892635 A CN106892635 A CN 106892635A
- Authority
- CN
- China
- Prior art keywords
- auxiliary agent
- dry powder
- fiber
- mixture
- fiber coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of dry powder fiber coating of the present invention, belongs to building coating technical field, and the coating is into being grouped into by following percentage by weight：Inorganic coagulation material 30%~50%, re-dispersible glue powder 5%~20%, fiber composition 3%~15%, aggregate 20%~50%, filler 10%~30%, pigment 0%~10%, application property auxiliary agent 3%~10% and functional aid 0%~10%；Compared with prior art, the dry powder fiber coating raw material that the present invention is provided are mainly natural inorganic material, and excellent storage stability is easy to long-term storage and transport.Solvent uses clear water, without organic solvent, does not produce the harmful substances, health environment-friendly such as free formaldehyde, benzene homologues, VOC VOCs, heavy metal in work progress.
Description
Technical field
The invention belongs to building coating technical field, it is related to a kind of interior wall coating, and in particular to a kind of dry powder fiber coating.
Background technology
With the development of interior wall coating diversification, people more focus on the feature of environmental protection of coating, aesthetic property.Fiber coating conduct
A kind of new coating for meeting people's individual demand enters into the people visual field.Current fiber interior wall coating existing on the market is basic
All it is solvent type, adds fiber and some auxiliary agents, there is certain pollution to environment, health is there is also to workmen hidden
Suffer from, and cost of transportation is higher.
Needed badly in the middle of prior art in sum and want a kind of new coating, be used to solve above-mentioned technical problem.
The content of the invention
Use organic solvent not environmentally friendly enough the invention aims to solve existing fiber interior wall coating, and transport inconvenience
Problem, there is provided one kind adds water and use, the dry powder fiber coating of asepsis environment-protecting.
To realize above-mentioned technical purpose, the present invention provides a kind of dry powder fiber coating, it is characterised in that：The coating be by
Following percentage by weight into being grouped into：Inorganic coagulation material 30%~50%, re-dispersible glue powder 5%~20%, fiber group
Compound 3%~15%, aggregate 20%~50%, filler 10%~30%, pigment 0%~10%, application property auxiliary agent 3%~10%
And functional aid 0%~10%；
The inorganic coagulation material be selected from cement, lime, gypsum in any one or a few；
The fiber composition be selected from cotton fiber, synthetic fibers, staple fibre in any one or a few；The aggregate
It is quartz sand and/or natural colour sand；
Described filler is selected from any in carbonate, sulfate, silicate, carbide, sulfide, silica, nitride
One or more；
The application property auxiliary agent is selected from any one in dispersant, thixotropic agent, water-loss reducer, water reducer, thickener or several
Kind；The functional aid be selected from photocatalysis performance auxiliary agent, humidity conditioning function auxiliary agent and antimildew and antibacterial auxiliary agent in any one or
It is several；
Wherein dispersant is sodium polyphosphate；
Wherein thixotropic agent is aerosil or bentonite；
Wherein water-loss reducer is starch ether or cellulose ether；
Wherein water reducer is lignosulfonates or polycarboxylic acids；
Wherein thickener is bentonite or cellulose；
Wherein photocatalysis performance auxiliary agent is nanometer titanium dioxide photocatalysis material；
Wherein humidity conditioning function auxiliary agent is calcium chloride；
Wherein antimildew and antibacterial auxiliary agent be selected from zeolite with carrying silver, copper-loaded zeolite, load zinc zeolite, carry silver-colored diatomite, copper-loaded diatomite,
Carry any one in zinc diatomite and zinc oxide.
The present invention can bring following beneficial effect：The dry powder fiber coating raw material that the present invention is provided are mainly natural nothing
Machine material, excellent storage stability is easy to long-term storage and transport.Solvent uses clear water, without organic solvent, in work progress
The harmful substances, health environment-friendly such as free formaldehyde, benzene homologues, VOC VOCs, heavy metal are not produced.
Specific embodiment
The present invention proposes a kind of dry powder fiber coating, it is characterised in that：The coating is by following percentage by weight
Into being grouped into：Inorganic coagulation material 30%~50%, re-dispersible glue powder 5%~20%, fiber composition 3%~15%, bone
Material 20%~50%, filler 10%~30%, pigment 0%~10%, application property auxiliary agent 3%~10% and functional aid 0%
~10%；The inorganic coagulation material be selected from cement, lime, gypsum in any one or a few；The fiber composition choosing
Any one or a few from cotton fiber, synthetic fibers, staple fibre；The aggregate is quartz sand and/or natural colour sand；Institute
State filler be selected from carbonate, sulfate, silicate, carbide, sulfide, silica, nitride in any one or a few；
The application property auxiliary agent be selected from dispersant, thixotropic agent, water-loss reducer, water reducer, thickener in any one or a few；The work(
Can property auxiliary agent be selected from photocatalysis performance auxiliary agent, humidity conditioning function auxiliary agent and antimildew and antibacterial auxiliary agent any one or a few；
Wherein dispersant is sodium polyphosphate；
Wherein thixotropic agent is aerosil or bentonite；
Wherein water-loss reducer is starch ether or cellulose ether；
Wherein water reducer is lignosulfonates or polycarboxylic acids；
Wherein thickener is bentonite or cellulose；
Wherein photocatalysis performance auxiliary agent is nanometer titanium dioxide photocatalysis material；
Wherein humidity conditioning function auxiliary agent is calcium chloride；
Wherein antimildew and antibacterial auxiliary agent be selected from zeolite with carrying silver, copper-loaded zeolite, load zinc zeolite, carry silver-colored diatomite, copper-loaded diatomite,
Carry any one in zinc diatomite and zinc oxide.
Embodiment 1
A kind of dry powder fiber coating, by following percentage by weight into being grouped into：It is inorganic coagulation material 40%, redispersible
Rubber powder 10%, fiber composition 5%, aggregate 20%, filler 15%, pigment 0%, application property auxiliary agent 5%, functional aid 5%；
In embodiment 1, the inorganic coagulation material is the mixture of lime and cement.The fiber composition is fine cotton
The mixture of peacekeeping polypropylene fibre.The aggregate is quartz sand.Described filler is the mixture of fine particle calcium carbonate and zeolite.The construction
Property auxiliary agent be thixotropic agent and water-loss reducer mixture.The functional aid is photocatalysis performance auxiliary agent and antimildew and antibacterial auxiliary agent
Mixture.
Embodiment 2
A kind of dry powder fiber coating, by following percentage by weight into being grouped into：It is inorganic coagulation material 30%, redispersible
Rubber powder 15%, fiber composition 10%, aggregate 20%, filler 15%, pigment 3%, application property auxiliary agent 5%, functional aid
2%；
In example 2, the inorganic coagulation material is the mixture of lime and cement.The fiber composition is fine cotton
The mixture of dimension, wood-fibred and alumina silicate fibre.The aggregate is natural colour sand.Described filler is coarse whiting, diatomite and zeolite
Mixture.The application property auxiliary agent is the mixture of dispersant, thixotropic agent, water-loss reducer and thickener.The functional aid
It is antimildew and antibacterial auxiliary agent.
Embodiment 3
A kind of dry powder fiber coating, by following percentage by weight into being grouped into：It is inorganic coagulation material 45%, redispersible
Rubber powder 5%, fiber composition 5%, aggregate 25%, filler 10%, pigment 2%, application property auxiliary agent 6%, functional aid 2%；
In embodiment 3, the inorganic coagulation material is the mixture of lime and gypsum.The fiber composition is animal
The mixture of hair.The aggregate is the mixture of natural colour sand and quartz sand.Described filler is diatomite and blanc fixe
Mixture.The application property auxiliary agent is dispersant, thixotropic agent, water-loss reducer, the mixture of thickener.The functional aid is tune
The mixture of wet function additive, antimildew and antibacterial auxiliary agent.
The dry powder fiber coating raw material that the present invention is provided are mainly natural inorganic material, and excellent storage stability is easy to length
Phase storage and transport.Solvent uses clear water, without organic solvent, does not produce free formaldehyde, benzene homologues, VOC in work progress
The harmful substances such as VOC, heavy metal, health environment-friendly.
Specific embodiment of the invention is described above, it is only used as example, the present invention is not restricted to the above and retouches
The specific embodiment stated.For a person skilled in the art, any equivalent modifications carried out to the present invention and modification be also all
Within scope of the invention.Therefore, the impartial variants and modifications for being done without departing from the spirit and scope of the invention, all should
Cover within the scope of the invention.
Claims (7)
1. a kind of dry powder fiber coating, it is characterised in that：The coating is into being grouped into by following percentage by weight：Inorganic glue
Gel material 30%~50%, re-dispersible glue powder 5%~20%, fiber composition 3%~15%, aggregate 20%~50%, fill out
Material 10%~30%, pigment 0%~10%, application property auxiliary agent 3%~10% and functional aid 0%~10%；It is described inorganic
Binder Materials be selected from cement, lime, gypsum in any one or a few；
The fiber composition be selected from cotton fiber, synthetic fibers, staple fibre in any one or a few；The aggregate is stone
Sand and/or natural colour sand；Described filler is selected from carbonate, sulfate, silicate, carbide, sulfide, silica, nitridation
Any one or a few in thing；The application property auxiliary agent is selected from dispersant, thixotropic agent, water-loss reducer, water reducer, thickener
Any one or a few；The functional aid is selected from photocatalysis performance auxiliary agent, humidity conditioning function auxiliary agent and antimildew and antibacterial auxiliary agent
Any one or a few；
Wherein dispersant is sodium polyphosphate；
Wherein thixotropic agent is aerosil or bentonite；
Wherein water-loss reducer is starch ether or cellulose ether；
Wherein water reducer is lignosulfonates or polycarboxylic acids；
Wherein thickener is bentonite or cellulose；
Wherein photocatalysis performance auxiliary agent is nanometer titanium dioxide photocatalysis material；
Wherein humidity conditioning function auxiliary agent is calcium chloride；
Wherein antimildew and antibacterial auxiliary agent is selected from the silver-colored diatomite of zeolite with carrying silver, copper-loaded zeolite, load zinc zeolite, load, copper-loaded diatomite, carries zinc
Any one in diatomite and zinc oxide.
2. a kind of dry powder fiber coating according to claim 1, it is characterized in that：The fiber composition is cotton fiber and gathers
The mixture of tacryl.
3. a kind of dry powder fiber coating according to claim 1, it is characterized in that：The fiber composition is animal hair
Mixture.
4. a kind of dry powder fiber coating according to claim 1, it is characterized in that：The fiber composition is cotton fiber, wood
The mixture of fiber and alumina silicate fibre.
5. a kind of dry powder fiber coating according to claim 1, it is characterized in that：Described filler is the mixing of fine particle calcium carbonate and zeolite
Thing.
6. a kind of dry powder fiber coating according to claim 1, it is characterized in that：Described filler is coarse whiting, diatomite and boiling
The mixture of stone.
7. a kind of dry powder fiber coating according to claim 1, it is characterized in that：Described filler is diatomite and blanc fixe
Mixture.