CN106884319A - Fabric finishing agent and the method for textile finishing - Google Patents
Fabric finishing agent and the method for textile finishing Download PDFInfo
- Publication number
- CN106884319A CN106884319A CN201710067780.5A CN201710067780A CN106884319A CN 106884319 A CN106884319 A CN 106884319A CN 201710067780 A CN201710067780 A CN 201710067780A CN 106884319 A CN106884319 A CN 106884319A
- Authority
- CN
- China
- Prior art keywords
- fabric
- finishing agent
- finishing
- agent
- fabric finishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of fabric finishing agent, including the following components for mixing by weight:1~10 part of Aloe Vera Gel, 1~5 part of farina, 1~3 part of heteroside of Quercetin 3,1~8 part of cyanidin extract, 2~6 parts of alginates, 3~6 parts of functional treatment auxiliary agents and 80~100 parts of water.The fabric finishing agent is the colloidal solution that intrinsic viscosity is 1.20 1.60L/g, and imbibition rate is low, good water-retaining property, good stability, and the coating scope of the fabric finishing agent can be precisely controlled.Method present invention also offers textile finishing is carried out using above-mentioned fabrics finishing agent, production process is few, and energy resource consumption is few, has saved production cost.
Description
Technical field
The present invention relates to a kind of fabric finishing agent and the method for textile finishing.
Background technology
For most of textile articles, in order to assign its each excellent outward appearance, feel and application performance, often
Need to carry out multistep Final finishing, including soft finish, antistatic finish, hard finishing and anti-crease finishing etc..It is with function clothes
Example, when the inner surface of the clothes function different with outer surface needs, such as inner surface needs antibacterial effect, and outer surface needs anti-purple
Outer or oxidation resistant effect, general functional finishing agent is after finishing auxiliaries is added, to increase the dissolubility of finishing auxiliaries, to add
Plus emulsifier is into using after emulsion, finishing technique be it is point inside and outside be coated arrangements twice, the method complex process is produced
Efficiency is low, and the finishing agent poor water retention property of use, readily permeable fabric causes the waste of finishing agent, improves production cost.
The content of the invention
The invention provides a kind of fabric finishing agent, it is used to solve be difficult to point using existing fabric finishing agent finish fabric
Region arranges the problem for obtaining multiple performance.
In order to solve the above-mentioned technical problem, the technical scheme is that:
A kind of fabric finishing agent, including the following components for mixing by weight:
The cyanidin extract includes anthocyanidin, and the cyanidin extract uses preparation method system of the prior art
It is standby.
Preferably, the fabric finishing agent, including the following components for mixing by weight:
According to the fabric finishing agent prepared by above-mentioned formula, various aspects of performance is excellent, and good water-retaining property, imbibition rate is low, tool
There is excellent finishing effect, after being coated with the fabric finishing agent to fabric two-face, the fabric finishing agent of fabric positive and negative is equal
On the shallow-layer surface of fabric, another side is not infiltrated into, the functional treatment auxiliary agent of fabric positive and negative will not be interfered, fabric
Positive and negative can each carry out finishing functions, and difference in functionality effect is realized in fabric subregion, in addition, the fabric finishing agent is characteristic
Viscosity is the colloidal solution of 1.20-1.60L/g, poor fluidity, can closely subregion be coated on the same face of fabric without
Interfere, difference in functionality effect is realized in fabric subregion.
Preferably, the functional treatment auxiliary agent is antibacterial finishing agent, anti UV finishing agent, water-proof aagent and crease-resistant
One or more in finishing agent etc..
Preferably, the antibacterial finishing agent is commercially available general fabrics antibacterial finishing agent, such as zinc oxide, cupric oxide, phosphorus
The inorganic antibacterial finishing agent such as acid dihydride ammonium and lithium carbonate;Or, such as vanillic aldehyde, ethyl vanillin aldehydes compound organic anti-bacterial are whole
Reason agent.
Preferably, the anti UV finishing agent is commercially available general fabrics anti UV finishing agent, such as salicylic acid esters, benzene
Ketone, benzotriazole, group-substituted acrylonitrile, triazines and hindered amines Compositional type compound, specifically, such as o-hydroxy first
Acid phenenyl ester, 2- (the 2 ˊ-ˊ of hydroxyl-5-aminomethyl phenyl) BTA and 2,4-DihydroxyBenzophenone etc..
Preferably, the water-proof aagent is commercially available general fabrics water-proof aagent, such as amino resins class, slaine
Class and Polyamide Epoxy, and its corresponding modified compound, specifically, as melamine resin, zirconium carbonate ammonium and
Polyamide-Polyamsne-Epichlorohydrin resin etc..
Preferably, the crease-shedding finishing agent is commercially available general fabrics crease-shedding finishing agent, such as sodium citrate, aldehyde (acyl) amine
Condensation resin, specifically, such as hydroxymethyl-2 dihydroxy-ethylene urea, trimethylol melamine and dimethylol urea.
Fabric finishing agent Aloe Vera Gel of the present invention, farina, Quercetin -3- heterosides, cyanidin extract, sea
Cooperated between alginates, functional treatment auxiliary agent and water each component, improve the water retention property of the fabric finishing agent, dropped
The low imbibition rate of the fabric finishing agent, the fabric finishing agent can realize that fabric positive and negative each carries out finishing functions,
And fabric the same face closely subregion finishing functions.
Method present invention also offers textile finishing is carried out using above-mentioned fabrics finishing agent, comprises the following steps:By matching somebody with somebody
Above-mentioned fabrics finishing agent is prepared by side, and subregion is coated with the fabric finishing agent on fabric to be arranged, then in turn through vapour
Steam and water-washing step, finally dry fabric and obtain finished product.The concrete operations of the steaming step are as follows:It is coated with the textile finishing
Fabric after agent 20~50min of decatize at 100~120 DEG C so that all kinds of materials in the fabric finishing agent are shifted and made
For fabric.The concrete operations of the baking step are as follows:The dry fabric at 90~110 DEG C, dried fabric is into
Product.
Preferably, the method for the textile finishing also includes roll compacting step, the roll compacting step is in the steaming step
Before, it is necessary to determine whether to carry out roll compacting according to the production of fabric, using padding machine to being coated with knitting after the fabric finishing agent
Thing carries out roll compacting, according to the production to fabric it needs to be determined that the pressure of roll compacting.
The method production process of textile finishing of the present invention is few, and energy resource consumption is few, has saved production cost.
Brief description of the drawings
Fig. 1 and Fig. 2 are fabrics on the fabric of one~example IV of the embodiment of the present invention and one~comparative example of comparative example four
The schematic diagram of finishing agent distributed areas coating.
Shown in figure:1- fabrics.
Specific embodiment
To enable the above objects, features and advantages of the present invention more obvious understandable, below in conjunction with the accompanying drawings to the present invention
Specific embodiment be described in detail.It should be noted that, accompanying drawing of the present invention is in the form of simplification and using non-essence
Accurate ratio, is only used to conveniently, lucidly aid in illustrating the purpose of the embodiment of the present invention.
Embodiment one
A kind of fabric finishing agent, including the following components for mixing by weight:
Embodiment two
A kind of fabric finishing agent, including the following components for mixing by weight:
Embodiment three
A kind of fabric finishing agent, including the following components for mixing by weight:
Example IV
A kind of fabric finishing agent, including the following components for mixing by weight:
Textile finishing scheme one
As shown in figure 1, divide a-quadrant, B regions, C regions and D regions on fabric, correspondence coating Examples one to embodiment
Fabric finishing agent described in four.
Textile finishing scheme two
As shown in Fig. 2 in the fabric finishing agent described in fabric face E regions coating Examples one, the coating of reverse side F regions is real
Apply the fabric finishing agent described in example two.
4 groups of fabric finishing agents with difference in functionality are prepared respectively by the formula of embodiment one to example IV, according to knitting
Thing ordering plan one and textile finishing scheme two are coated with above-mentioned fabrics finishing agent on fabric, and then fabric 1 is by roll compacting, decatize
And water-washing step, finally dry fabric 1 and obtain finished product.
Comparative example one
A kind of fabric finishing agent, including the following components for mixing by weight:
200 parts of water
3 parts of antibacterial finishing agent.
Comparative example two
A kind of fabric finishing agent, including the following components for mixing by weight:
200 parts of water
4 parts of anti UV finishing agent.
Comparative example three
A kind of fabric finishing agent, including the following components for mixing by weight:
200 parts of water
6 parts of crease proofing agent
1 part of magnesium chloride (catalyst).
Comparative example four
A kind of fabric finishing agent, including the following components for mixing by weight:
200 parts of water
6 parts of water-proof aagent.
Textile finishing scheme three
As shown in figure 1, divide a-quadrant, B regions, C regions and D regions on fabric, correspondence coating comparative example one to comparative example
Fabric finishing agent described in four.
Textile finishing scheme four
As shown in Fig. 2 in the fabric finishing agent described in fabric face E regions coating comparative example one, the coating of reverse side F regions is right
Fabric finishing agent described in ratio two.
4 tissue substance finishing agents are prepared respectively by the formula of comparative example one to comparative example four, according to the He of textile finishing scheme three
Textile finishing scheme four is coated with above-mentioned fabrics finishing agent on fabric, and then fabric is by drying and water-washing step twice, finally
Drying fabric 1 obtains finished product.
Comparative example five
A kind of fabric finishing agent, including the following components for mixing by weight:
Comparative example six
A kind of fabric finishing agent, including the following components for mixing by weight:
Comparative example seven
A kind of fabric finishing agent, including the following components for mixing by weight:
Comparative example eight
A kind of fabric finishing agent, including the following components for mixing by weight:
4 tissue substance finishing agents are prepared respectively by the formula of comparative example five to comparative example eight, are respectively coated on fabric 1, so
Fabric 1 is finally dried fabric 1 and obtains finished product by roll compacting, decatize and water-washing step afterwards.
With Real Silk Habotai fabric (76g/m2) as a example by, using embodiment one to example IV, comparative example five to comparative example
After fabric finishing agent processing and sorting described in eight, performance test is carried out, method of testing is as follows:
Waterproofing tests:The detection and evaluation of GB/T 4745-2012 textile water proof performances get wet method.
Antibiotic property (bacteriostasis rate):The evaluation third portion of GB 20944.3-2008-T antibacterial textile performances:Succusion.
Water retention property is tested:The slurry that 100g is prepared is taken, in 25 DEG C of temperature, in the climatic chamber of humidity 65~75%
After placing 24h, the weight of remaining slurry is weighed.The percentage of initial slurry weight is higher shared by remaining slurry, and water retention property is got over
It is good.
Imbibition rate is tested:3, the square of a diameter of 10cm is formed on fabric by processing, after decatize, washing, drying
Fabric scanned by cat scanner instrument, scanner is set to 600dpi, and brightness is -75, and contrast is 50, and gained image is used
CPAS image processing softwares are analyzed.Area (mm after being processed during graphical analysis can obtain sample2), computing formula is:
Imbibition rate is evaluated and tested with 3 square imbibition rate average values.
Uvioresistant performance (UPF values):According to GB GB/T 18830-2009《The measure of ultraviolet resistance of fabric》It is right
Sample is tested.
Crease resistance:GB/T 3819-1997《The measure of textile fabric wrinkle recovery property》In normal beam technique determine.
Intrinsic viscosity is tested:At 35 ± 0.1 DEG C of temperature, carried out according to classical Huggins equations and Kramer equations double
Extrapolation, determines intrinsic viscosity.(for details, reference can be made to:New method [J] Science of Chemistry of the hot viscosity measurement of the Polymer Solutions such as Liang Yan
Report, 2007,9.853-859.)
Various performance parameters contrast is shown in Table three and table four:
Table three
Table four
As shown in Table 3, comparative example one to comparative example four is common full aquosity fabric finishing agent, the subregion on fabric 1
During coating, fabric finishing agent on fabric diffusion and mix, equivalent to region-wide coating, on fabric present various fabrics it is whole
Manage the function of agent.Embodiment one to example IV is fabric finishing agent of the present invention, and imbibition rate is low, good water-retaining property, stability
It is good.Between a-quadrant, B regions, C regions and D regions, adjacent fabric finishing agent will not mix because of diffusion, it is possible to achieve
Different zones difference in functionality on fabric, further, the fabric finishing agent of difference in functionality is coated with the both sides of fabric 1, side
Fabric finishing agent will not infiltrate into opposite side on fabric, it is possible to achieve fabric positive and negative difference in functionality.
What comparative example five to comparative example eight reflected be in textile finishing agent prescription main component missing to fabric finishing agent
Can influence.
As shown in Table 4, comparative example five to the imbibition rate of the fabric finishing agent of comparative example eight compared with embodiment one to example IV
The imbibition rate of middle fabric finishing agent is high, as described herein fabric finishing agent, can control imbibition rate for 1%~2% when,
The coating scope of fabric finishing agent described in energy precise control.
Further, from embodiment one and comparative example five, without addition aloe in the fabric finishing agent of comparative example five
Glue, the imbibition rate of fabric finishing agent is improved to 6.6% by 1.8% in embodiment one, it will be seen that in the fabric finishing agent, reed
The addition of luxuriant growth glue can slow down speed of the functional finishing adjuvant in fabric finishing agent to infiltration in fabric, so that it is whole to improve fabric
Reason agent is coated with the accuracy of scope.
From embodiment two and comparative example six, fabric finishing agent does not add the good Ma Ling of water retention property in comparative example six
Sweet potato starch, the water retention property of fabric finishing agent declines substantially, and imbibition rate is by 1.8% improve in embodiment two to 8.5%, positioning
Processing effect declines.
From embodiment two and comparative example seven, after fabric finishing agent places 48h in comparative example seven, with respect to embodiment two,
The intrinsic viscosity of fabric finishing agent have dropped 30%, and intrinsic viscosity influence of the Quercetin -3- heterosides on fabric finishing agent is larger,
The intrinsic viscosity of fabric finishing agent declines, and the stabilising system of fabric finishing agent changes, influence positioning machining accuracy.
From embodiment two and comparative example eight, fabric finishing agent is placed and gelatin phenomenon occurs more than 24h in comparative example eight,
The stability of fabric finishing agent declines, but fabric finishing agent places 48h changes less in embodiment two, it follows that anthocyanidin
Extract component is larger to the stability influence of fabric finishing agent.
From comparative example one to comparative example four, water-retaining property, imbibition of the functional treatment auxiliary agent to fabric finishing agent
Rate and stability without influence, it can thus be appreciated that the hypotonic rate of fabric finishing agent is by Aloe Vera Gel, farina, Quercetin -3- Portugals
Grape glycosides and cyanidin extract interact, and cooperate and produce.
In sum, using fabric finishing agent of the invention, including 1~10 part of Aloe Vera Gel, 1~5 part of farina, 1
~3 parts of Quercetin -3- heterosides, 1~8 part of cyanidin extract, 2~6 parts of alginates, 2~6 parts of functional treatment auxiliary agents and
80~100 parts of water, imbibition rate is low, good water-retaining property, good stability, during for function clothes, it is possible to achieve clothes surfaces externally and internally has
There is difference in functionality, while can also realize that clothes different parts have difference in functionality, such as neckline, cuff has antibacterial effect, clothing
Body has UVResistant effect, and the fabric finishing agent can be also used for electronic product function pad, can be according to circuit requirements so that
The position of same pad has different effects, such as electric conductivity, water resistance.
Those skilled in the art can carry out various changes and modification without deviating from spirit of the invention and model to invention
Enclose.So, if these modifications of the invention and modification belong within the scope of the claims in the present invention and its equivalent technologies, then
The present invention is also intended to including including these changes and modification.
Claims (9)
1. a kind of fabric finishing agent, it is characterised in that including the following components for mixing by weight:
The cyanidin extract includes anthocyanidin.
2. fabric finishing agent according to claim 1, it is characterised in that including the following components for mixing by weight:
3. fabric finishing agent according to claim 1, it is characterised in that the functional treatment auxiliary agent is antibiotic finish
One or more in agent, anti UV finishing agent, water-proof aagent and crease-shedding finishing agent.
4. fabric finishing agent according to claim 3, it is characterised in that the antibacterial finishing agent be zinc oxide, cupric oxide,
One or more in ammonium dihydrogen phosphate and vanillic aldehyde.
5. fabric finishing agent according to claim 3, it is characterised in that the anti UV finishing agent is septichen
One or more in phenyl ester, 2- (the 2 ˊ-ˊ of hydroxyl-5-aminomethyl phenyl) BTA and 2,4-DihydroxyBenzophenone.
6. fabric finishing agent according to claim 3, it is characterised in that the water-proof aagent is melamino-formaldehyde tree
One or more of fat, zirconium carbonate ammonium and Polyamide-Polyamsne-Epichlorohydrin resin.
7. fabric finishing agent according to claim 3, it is characterised in that the crease-shedding finishing agent is sodium citrate, dihydroxy
One or more of methyl dihydroxy ethylene urea, trimethylol melamine and dimethylol urea.
8. a kind of method that fabric finishing agent using as described in claim 1~7 is any carries out textile finishing, its feature exists
In comprising the following steps:The fabric finishing agent is prepared by formula, the subregion coating fabric is whole on fabric to be arranged
Reason agent, then in turn through decatize and water-washing step, finally dries fabric and obtains finished product.
9. the method for textile finishing according to claim 8, it is characterised in that the method for the textile finishing also includes rolling
Pressure step, before the steaming step, the roll compacting step is using padding machine to being coated with the textile finishing for the roll compacting step
Fabric after agent carries out roll compacting.