CN108716125A - A kind of crease-resistant integral processing method of fabric waterproof - Google Patents
A kind of crease-resistant integral processing method of fabric waterproof Download PDFInfo
- Publication number
- CN108716125A CN108716125A CN201810631174.6A CN201810631174A CN108716125A CN 108716125 A CN108716125 A CN 108716125A CN 201810631174 A CN201810631174 A CN 201810631174A CN 108716125 A CN108716125 A CN 108716125A
- Authority
- CN
- China
- Prior art keywords
- parts
- fabric
- textile fabric
- wrinkle
- crease
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of crease-resistant integral processing methods of fabric waterproof, include the following steps：（1）Water repellent finish；（2）Drying；（3）Wrinkle resistant pretreatment；（4）It bakes；（5）It soaps；（6）Wrinkle proofing；（7）Post-processing.Compared with prior art, beneficial effects of the present invention are：The wrinkle resistant water-repellent finishing method of the present invention can make textile fabric have excellent water-wash resistance, durability, shrink resistance and water repellency；The wrinkle resistant water-repellent finishing method pollution of the present invention is few, and waterproof, wrinkle-proof effect are notable, and persistence is good, and the polymer formed after arrangement, which securely coagulates, to be closed on the fabric, and fabric structure is soft, maintains good washing style.
Description
Technical field
The present invention relates to fabric post-treatment field, especially a kind of crease-resistant integral processing method of fabric waterproof.
Background technology
Textile fabric needs to carry out final finishing, to reach preferable water repellent, flexible effect；Clothes made of many textile fabrics
Dress washes that rear washing shrinkage is big, fold is serious, keeping and flatiron trouble, and it is difficult removal to be stained with greasy dirt, so, such clothes need to be prevented
It is water, grease proofing, antifouling, non-ironing.Although having many technologies for this respect both at home and abroad to report, in the dressing liquid for soaking clothes
Resin demand and agent for three purposes dosage are larger, and in addition to cost of material consumption is big, for effect nor highly desirable, blowdown is more, not environmentally,
And completed by two step method, it extends the time of production technology, increase production cost.
Invention content
The object of the present invention is to provide a kind of crease-resistant integral processing method of fabric waterproof, with solve it is in the prior art not
Foot, it effectively can carry out wrinkle resistant water repellent finish to textile fabric, while shortening the production time, reducing production cost.
The present invention provides a kind of crease-resistant integral processing methods of fabric waterproof, include the following steps：
（1）Water repellent finish：Water repellent finishing agent is padded, water repellent finishing agent is added to the water to obtain the arrangement that solid content is 60-65%
Textile fabric is immersed in the dressing liquid and pads 45-60min by liquid, and pick-up rate is made to reach 80-85%, the finishing agent include with
The component of lower parts by weight：10-15 parts of 2- acrylamidos -2- methyl propane sulfonic acids, 10-20 parts of vinyl phosphonic dimethyl phthalate are different
5-8 parts of structure tridecanol polyoxyethylene ether, 3-5 parts of sodium hydroxide, 1-3 parts of paraffin, 1-2 parts of stearic acid, 5-8 parts of ammonium hydroxide, aluminium oxide
1-2 parts；
（2）Drying：It is 12-15% that moisture percentage is dried to after preheating；
（3）Wrinkle resistant pretreatment：Dewing is stacked after carrying out friction glazing to the textile fabric after drying；
（4）It bakes：By wrinkle resistant pretreated textile fabric 4-5min will be baked at 170-180 DEG C；
（5）It soaps：It is soaped to textile fabric using soaping agent, is washed after soaping；
（6）Wrinkle proofing：Two leachings two are carried out to textile fabric using wrinkle proofing liquid and roll processing, by textile fabric winding after processing
It is used in combination plastic film to coat, the textile fabric coated is banked up at room temperature, the wrinkle proofing liquid includes following parts by weight
Several components：5-12 parts of citric acid, 3-9 parts of ammonium salt in catalysis agent, 13-16 parts of glutaraldehyde, 4-12 parts of sorbitan monostearate,
12-18 parts of hydroxypropyl methyl cellulose, 4-13 parts of hydroxymethyl-2 dihydroxy-ethylene urea, 10-15 parts of softening agent, four acetal resins
6-15 parts；
（7）Post-processing：6-8h will be placed after textile fabric loose winding after stacking at room temperature, finally carries out washing drying.
Preferably, step（1）Described in finishing agent include following parts by weight component：2- acrylamido -2- first
15 parts of base propane sulfonic acid, 20 parts of vinyl phosphonic dimethyl phthalate, 8 parts of isomerous tridecanol polyoxyethylene ether, 5 parts of sodium hydroxide, paraffin 3
Part, 2 parts of stearic acid, 8 parts of ammonium hydroxide, 2 parts of aluminium oxide.
Preferably, step（2）Middle preheating temperature is 90~95 DEG C, and preheating time is 1~2min.
Preferably, the wrinkle proofing liquid includes the component of following parts by weight：12 parts of citric acid, ammonium salt in catalysis agent 9
Part, 16 parts of glutaraldehyde, 12 parts of sorbitan monostearate, 18 parts of hydroxypropyl methyl cellulose, dihydroxymethyl dihydroxy ethylene
13 parts of urea, 15 parts of softening agent, four 15 parts of acetal resins.
Preferably, step（6）Described in softening agent be newborn made of polyethanol, organosilicon and soluble polyurethane
Liquid.
Compared with prior art, beneficial effects of the present invention are：The wrinkle resistant water-repellent finishing method of the present invention can make weaving
Fabric has excellent water-wash resistance, durability, shrink resistance and water repellency；The wrinkle resistant water-repellent finishing method pollution of the present invention
Few, waterproof, wrinkle-proof effect are notable, and persistence is good, and the polymer formed after arrangement, which securely coagulates, to be closed on the fabric, fabric structure
Softness maintains good washing style.
Specific implementation mode
A kind of crease-resistant integral processing method of fabric waterproof, includes the following steps：
（1）Water repellent finish：Water repellent finishing agent is padded, water repellent finishing agent is added to the water to obtain the arrangement that solid content is 60-65%
Textile fabric is immersed in the dressing liquid and pads 45-60min by liquid, and pick-up rate is made to reach 80-85%, the finishing agent include with
The component of lower parts by weight：10-15 parts of 2- acrylamidos -2- methyl propane sulfonic acids, 10-20 parts of vinyl phosphonic dimethyl phthalate are different
5-8 parts of structure tridecanol polyoxyethylene ether, 3-5 parts of sodium hydroxide, 1-3 parts of paraffin, 1-2 parts of stearic acid, 5-8 parts of ammonium hydroxide, aluminium oxide
1-2 parts；
（2）Drying：It is 12-15% that moisture percentage is dried to after preheating；
（3）Wrinkle resistant pretreatment：Dewing is stacked after carrying out friction glazing to the textile fabric after drying；
（4）It bakes：By wrinkle resistant pretreated textile fabric 4-5min will be baked at 170-180 DEG C；
（5）It soaps：It is soaped to textile fabric using soaping agent, is washed after soaping；
（6）Wrinkle proofing：Two leachings two are carried out to textile fabric using wrinkle proofing liquid and roll processing, by textile fabric winding after processing
It is used in combination plastic film to coat, the textile fabric coated is banked up at room temperature, the wrinkle proofing liquid includes following parts by weight
Several components：5-12 parts of citric acid, 3-9 parts of ammonium salt in catalysis agent, 13-16 parts of glutaraldehyde, 4-12 parts of sorbitan monostearate,
12-18 parts of hydroxypropyl methyl cellulose, 4-13 parts of hydroxymethyl-2 dihydroxy-ethylene urea, 10-15 parts of softening agent, four acetal resins
6-15 parts；
（7）Post-processing：6-8h will be placed after textile fabric loose winding after stacking at room temperature, finally carries out washing drying.
Preferably, step（1）Described in finishing agent include following parts by weight component：2- acrylamido -2- first
15 parts of base propane sulfonic acid, 20 parts of vinyl phosphonic dimethyl phthalate, 8 parts of isomerous tridecanol polyoxyethylene ether, 5 parts of sodium hydroxide, paraffin 3
Part, 2 parts of stearic acid, 8 parts of ammonium hydroxide, 2 parts of aluminium oxide.
Preferably, step（2）Middle preheating temperature is 90~95 DEG C, and preheating time is 1~2min.
Preferably, the wrinkle proofing liquid includes the component of following parts by weight：12 parts of citric acid, ammonium salt in catalysis agent 9
Part, 16 parts of glutaraldehyde, 12 parts of sorbitan monostearate, 18 parts of hydroxypropyl methyl cellulose, dihydroxymethyl dihydroxy ethylene
13 parts of urea, 15 parts of softening agent, four 15 parts of acetal resins.
Preferably, step（6）Described in softening agent be newborn made of polyethanol, organosilicon and soluble polyurethane
Liquid.
Claims (5)
1. a kind of crease-resistant integral processing method of fabric waterproof, it is characterised in that：Include the following steps：
（1）Water repellent finish：Water repellent finishing agent is padded, water repellent finishing agent is added to the water to obtain the arrangement that solid content is 60-65%
Textile fabric is immersed in the dressing liquid and pads 45-60min by liquid, and pick-up rate is made to reach 80-85%, the finishing agent include with
The component of lower parts by weight：10-15 parts of 2- acrylamidos -2- methyl propane sulfonic acids, 10-20 parts of vinyl phosphonic dimethyl phthalate are different
5-8 parts of structure tridecanol polyoxyethylene ether, 3-5 parts of sodium hydroxide, 1-3 parts of paraffin, 1-2 parts of stearic acid, 5-8 parts of ammonium hydroxide, aluminium oxide
1-2 parts；
（2）Drying：It is 12-15% that moisture percentage is dried to after preheating；
（3）Wrinkle resistant pretreatment：Dewing is stacked after carrying out friction glazing to the textile fabric after drying；
（4）It bakes：By wrinkle resistant pretreated textile fabric 4-5min will be baked at 170-180 DEG C；
（5）It soaps：It is soaped to textile fabric using soaping agent, is washed after soaping；
（6）Wrinkle proofing：Two leachings two are carried out to textile fabric using wrinkle proofing liquid and roll processing, by textile fabric winding after processing
It is used in combination plastic film to coat, the textile fabric coated is banked up at room temperature, the wrinkle proofing liquid includes following parts by weight
Several components：5-12 parts of citric acid, 3-9 parts of ammonium salt in catalysis agent, 13-16 parts of glutaraldehyde, 4-12 parts of sorbitan monostearate,
12-18 parts of hydroxypropyl methyl cellulose, 4-13 parts of hydroxymethyl-2 dihydroxy-ethylene urea, 10-15 parts of softening agent, four acetal resins
6-15 parts；
（7）Post-processing：6-8h will be placed after textile fabric loose winding after stacking at room temperature, finally carries out washing drying.
2. the crease-resistant integral processing method of fabric waterproof according to claim 1, it is characterised in that：Step（1）Described in
Finishing agent includes the component of following parts by weight：15 parts of 2- acrylamido -2- methyl propane sulfonic acids, vinyl phosphonic dimethyl phthalate
20 parts, 8 parts of isomerous tridecanol polyoxyethylene ether, 5 parts of sodium hydroxide, 3 parts of paraffin, 2 parts of stearic acid, 8 parts of ammonium hydroxide, aluminium oxide 2
Part.
3. the crease-resistant integral processing method of fabric waterproof according to claim 1, it is characterised in that：Step（2）Middle preheating
Temperature is 90~95 DEG C, and preheating time is 1~2min.
4. the crease-resistant integral processing method of fabric waterproof according to claim 1, it is characterised in that：The wrinkle proofing liquid
Include the component of following parts by weight：12 parts of citric acid, 9 parts of ammonium salt in catalysis agent, 16 parts of glutaraldehyde, sorbitan monostearate
12 parts, 18 parts of hydroxypropyl methyl cellulose, 13 parts of hydroxymethyl-2 dihydroxy-ethylene urea, 15 parts of softening agent, four acetal resins 15
Part.
5. the crease-resistant integral processing method of fabric waterproof according to claim 1, it is characterised in that：Step（6）Described in
Softening agent is the lotion made of polyethanol, organosilicon and soluble polyurethane.