CN106883864B - 一种向列相液晶组合物及其应用 - Google Patents

一种向列相液晶组合物及其应用 Download PDF

Info

Publication number
CN106883864B
CN106883864B CN201510934837.8A CN201510934837A CN106883864B CN 106883864 B CN106883864 B CN 106883864B CN 201510934837 A CN201510934837 A CN 201510934837A CN 106883864 B CN106883864 B CN 106883864B
Authority
CN
China
Prior art keywords
general formula
liquid
compound representated
compound
crystal composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510934837.8A
Other languages
English (en)
Other versions
CN106883864A (zh
Inventor
陈卯先
陈海光
姜天孟
储士红
王杰
未欣
张琳
袁瑾
谭小玉
田会强
苏学辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing Bayi Space LCD Technology Co Ltd
Original Assignee
Beijing Bayi Space LCD Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing Bayi Space LCD Technology Co Ltd filed Critical Beijing Bayi Space LCD Technology Co Ltd
Priority to CN201510934837.8A priority Critical patent/CN106883864B/zh
Publication of CN106883864A publication Critical patent/CN106883864A/zh
Application granted granted Critical
Publication of CN106883864B publication Critical patent/CN106883864B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及液晶显示技术领域，特别涉及一种相列液晶组合物及其应用。所述向列相液晶组合物至少包含一种通式I所代表的化合物：R1、R2各自独立地代表C1～C12的直链烷基，其中一个或多个不相邻的CH2可以被O、S或CH＝CH所取代；以及至少包含一种通式II的化合物：R3、R4各自独立地代表C1～C12的直链烷基，其中一个或多个不相邻的CH2可以被O、S或CH＝CH所取代；A1、A2各自独立地代表反式1,4‑环己基或1,4‑亚苯基；优选按重量份计，所述液晶组合物包括1～40份通式I所代表的化合物和1～60份通式II所代表的化合物。本发明提供的液晶组合物具有低的旋转粘度和大的弹性常数，表现为具有较短的响应时间，从而有效地解决液晶显示器响应速度慢的问题。

Description

一种向列相液晶组合物及其应用
技术领域
本发明涉及一种液晶组合物，具体地说是一种向列相液晶组合物，确切地说，本发明所提供的液晶组合物具有负的介电各向异性，更确切地说本发明所提供的液晶组合物具有快的响应时间。
背景技术
目前，液晶在信息显示领域得到了广泛应用，同时在光通讯中的应用也取得了一定的进展(S.T.Wu，D.K.Yang.Reflective Liquid Crystal Displays.Wiley，2001)。近几年，液晶化合物的应用领域已经显著拓宽到各类显示器件、电光器件、电子元件、传感器等，向列型液晶化合物已经在平板显示器中得到最为广泛的应用，特别是用于TFT有源矩阵的系统中。
液晶显示伴随液晶的发现经历了漫长的发展道路。1888年奥地利植物学家Friedrich Reinitzer发现了第一种液晶材料安息香酸胆固醇(cholesteryl benzoate)。1917年Manguin发明了摩擦定向法，用以制作单畴液晶和研究光学各向异性。1909年E.Bose建立了攒动(Swarm)学说，并得到L.S.Ormstein及F.Zernike等人的实验支持(1918年)，后经De Gennes论述为统计性起伏。G.W.Oseen和H.Zocher在1933年创立连续体理论，并得到F.C.Frank完善(1958年)。M.Born(1916年)和K.Lichtennecker(1926年)发现并研究了液晶的介电各向异性。1932年，W.Kast据此将向列相分为正、负性两大类。1927年，V.Freedericksz和V.Zolinao发现向列相液晶在电场或磁场作用下，发生形变并存在电压阈值(Freederichsz转变)。这一发现为液晶显示器的制作提供了依据。
1968年美国RCA公司R.Williams发现向列相液晶在电场作用下形成条纹畴，并有光散射现象。G.H.Heilmeir随即将其发展成动态散射显示模式，并制成世界上第一个液晶显示器(LCD)。七十年代初，Helfrich及Schadt发明了TN原理，人们利用TN光电效应和集成电路相结合，将其做成显示器件(TN-LCD)，为液晶的应用开拓了广阔的前景。七十年代以来，由于大规模集成电路和液晶材料的发展，液晶在显示方面的应用取得了突破性的发展，1983～1985年T.Scheffer等人先后提出超扭曲向列相(Super Twisred Nematic：STN)模式以及P.Brody在1972年提出的有源矩阵(Active matrix：AM)方式被重新采用。传统的TN-LCD技术已发展为STN-LCD及TFT-LCD技术，尽管STN的扫描线数可达768行以上，但是当温度升高时仍然存在着响应速度、视角以及灰度等问题，因此大面积、高信息量、彩色显示大多采用有源矩阵显示方式。TFT-LCD已经广泛用于直视型电视、大屏幕投影电视、计算机终端显示和某些军用仪表显示，相信TFT-LCD技术具有更为广阔的应用前景。
其中“有源矩阵”包括两种类型：1、在作为基片的硅晶片上的OMS(金属氧化物半导体)或其它二极管。2、在作为基片的玻璃板上的薄膜晶体管(TFT)。
单晶硅作为基片材料限制了显示尺寸，因为各部分显示器件甚至模块组装在其结合处出现许多问题。因而，第二种薄膜晶体管是具有前景的有源矩阵类型，所利用的光电效应通常是TN效应。TFT包括化合物半导体，如Cdse，或以多晶或无定形硅为基础的TFT。
目前，LCD产品技术已经成熟，成功地解决了视角、分辨率、色饱和度等技术难题，其显示性能已经接近或超过CRT显示器。大尺寸和中小尺寸LCD在各自的领域已逐渐占据平板显示器的主流地位。受液晶显示器自身的制约(透过率低，绝对透过率5％左右)，导致需要大幅提升背光模组的亮度来达到良好的显示效果，极大程度地增加了背光模组的功耗，另一方面，由于正性FFS显示模式存在的Flexo(高电压下分子发生弯曲，因FFS电场存在弯曲的电场线，正性液晶分子沿电场线方向排列)效应，导致液晶显示器产生明显的闪烁，降低显示器效果。
发明内容
本发明提供一种具有负介电各向异性的向列相液晶组合物，一方面提升液晶显示器的透过率；另一方面排除液晶显示器存在Flexo(负性液晶分子垂直电场方向排列)效应，从而有效地改善液晶显示的闪烁问题；从而达到良好的显示效果。
本发明提供一种向列相液晶组合物，所述液晶组合物至少包含一种通式I所代表的化合物：
R1、R2各自独立地代表C1～C12的直链烷基，其中一个或多个不相邻的CH2可以被O、S或CH＝CH所取代；
以及至少包含一种通式II的化合物：
R3、R4各自独立地代表C1～C12的直链烷基，其中一个或多个不相邻的CH2可以被O、S或CH＝CH所取代；A1、A2各自独立地代表反式1,4-环己基或1,4-亚苯基；
本发明提供的液晶组合物具有低的旋转粘度和大的弹性常数，表现为具有较短的响应时间，从而有效地解决液晶显示器响应速度慢的问题。
为了实现快的响应时间，本发明的液晶组合物，按重量份计，包括1～40份通式I所代表的化合物和1～60份通式II所代表的化合物，优选2～25份通式I所代表的化合物和27～53份通式II所代表的化合物。
本发明提供的通式I所代表的化合物为二苯并呋喃类化合物，该结构具有大的负介电各向异性。
具体的，通式I所代表的化合物选自下式中所代表的化合物的一种或几种：
其中，R1代表C1～C7的直链烷基。
上述通式I所代表的化合物具有大的负介电各向异性，有利于增加液晶组合物的介电各向异性。
作为更理想的技术方案，上述通式I所代表的化合物选自下式中所代表的化合物的一种或几种：
本发明提供的通式II所代表的化合物为双环结构，具体的，所述通式II所代表的化合物选自如下化合物的一种或多种：
其中，R3代表C1～C7的直链烷基；R4代表C1～C7的直链烷基、直链烷氧基或C2～C7的直链烯基。
上述通式II所代表的化合物具有更低的旋转粘度和优异的互溶性，有利于降低液晶组合物的旋转粘度和改善液晶组合物的低温互溶性，进一步得到快响应的液晶组合物。
作为更理想的技术方案，通式II所代表的化合物选自式IIA1～式IIC24所代表的化合物的一种或几种：
本发明所提供的液晶组合物还包含一种或多种选自通式III结构的化合物：
R5、R6各自独立地代表C1～C12的直链烷基，其中一个或多个不相邻的CH2可以被O或CH＝CH取代。
A3各自独立地选自以下结构：
优选地，通式III所代表的化合物选自式IIIA～式IIIC中的一种或多种：
其中，R5代表C2～C10的直链烷基或直链烯基；R6代表C1～C8的直链烷基。
更优选地，通式III所代表化合物选自式IIIA1～式IIIC30结构中的一种或多种：
本发明所提供的液晶组合物还包含一种或多种选自通式IV的化合物：
其中，R7、R8各自独立地代表C1～C12的直链烷基、烷氧基或C2～C12的直链烯基；A4代表1，4-亚环己基或1，4-亚苯基；Z1代表单键、CH2CH2或CH2O。
优选地，通式IV所代表的化合物选自以下化合物中的一种或多种：
其中，R7代表C1～C7的直链烷基或C2～C7的直链烯基；R8代表C1～C7的直链烷基或直链烷氧基。
更优选地，通式IV的化合物选自式IVA1～式IVD16中的一种或多种；
为了进一步改善本发明所述液晶组合物的综合性能，本发明提供的液晶组合物还可以包含一种或多种通式V所代表的化合物：
其中，R9、R10各自独立地代表C1～C12的直链烷基。
优选地，通式V所代表的化合物选自以下结构中的一种或多种：
本发明所提供的液晶组合物还包含一种或多种通式VI所代表的化合物：
其中，R11、R12各自独立地代表C1～C12直链烷基、直链烷氧基；L1各自独立地代表H或F。
优选地，通式VI所代表的化合物选自VIA和VIB中的一种或多种：
其中，R11、R12各自独立地代表C1～C7直链烷基或直链烷氧基；优选C1～C5的直链烷基或直链烷氧基。
本发明所提供的液晶组合物还包含一种或多种通式VII所代表的化合物：
其中R13、R14各自独立地代表C1～C12的直链烷基、直链烷氧基或C2～C12的直链烯基；A5选自以下结构：
A6选自以下结构：
优选地，通式VII所代表的化合物选自以下结构中的一种或多种：
其中，R13各自独立地代表C1～C7的直链烷基或C2～C7的直链烯基，优选C2～C5的直链烷基或直链烯基；R14各自独立地代表C1～C7的直链烷基或直链烷氧基，优选C1～C5的直链烷基或直链烷氧基。
本发明所提供的液晶组合物还包含一种或多种通式VIII所代表的化合物：
其中，R15、R16各自独立地代表C1～C12的直链烷基；L2、L3各自独立地代表H或F；A7各自独立地代表1，4-环己基或1，4-亚苯基。
优选地，通式VIII所代表的化合物选自以下结构的一种或多种：
其中，R15、R16各自独立地代表C1～C7的直链烷基，优选C2～C5的直链烷基。
本发明所提供的液晶组合物还包含一种或多种通式IX所代表的化合物：
其中，R17、R18各自独立地代表C1～C12的直链烷基、直链烷氧基或C2～C12的直链烯基；优选地，R17代表C2～C7的直链烯基或直链烷基，进一步优选C2～C5的直链烷基或直链烯基；R18代表C1～C7的直链烷基或直链烷氧基，进一步优选C1～C5的直链烷基或直链烷氧基。
上述液晶组合物，除通式I和通式II所代表的化合物为必选组分外，其他组分(如通式III～通式IX所示化合物)均为可选组分，可选方式可选择任意组合形式，如只在必选组分中加入上述“其他组分”中的一种、若干种或全部。
具体的而言，为了使液晶组合物满足不同的需求，本发明所提供的液晶组合物按重量份计，包括以下组分：1～11份通式I所代表的化合物，20～50份通式II所代表的化合物，0～15份通式III所代表的化合物，3～20份通式IV所代表的化合物，0～30份通式V所代表的化合物，0～15份通式VI所代表的化合物，5～50份通式VII所代表的化合物，0～40份通式IX所代表的化合物。
优选地，本发明所提供的液晶组合物包括以下组分：2～11份通式I所代表的化合物，27～40份通式II所代表的化合物，0～10份通式III所代表的化合物，5～16份通式IV所代表的化合物，0～25份通式V所代表的化合物，0～10份通式VI所代表的化合物，7～48份通式VII所代表的化合物，0～33份通式IX所代表的化合物。
或本发明所提供的液晶组合物包括以下组分：12～30份通式I所代表的化合物，20～60份通式II所代表的化合物，0～25份通式III所代表的化合物，0～10份通式IV所代表的化合物，0～20份通式V所代表的化合物，0～60份通式VII所代表的化合物，0～10份通式VIII所代表的化合物，0～25份通式IX所代表的化合物。
优选地，本发明所提供的液晶组合物包括以下组分：12～25份通式I所代表的化合物，29～53份通式II所代表的化合物，0～21份通式III所代表的化合物，0～2份通式IV所代表的化合物，0～10份通式V所代表的化合物，0～54份通式VII所代表的化合物，0～8份通式VIII所代表的化合物，0～20份通式IX所代表的化合物。
或本发明所提供的液晶组合物包括以下组分：3～30份通式I所代表的化合物，20～55份通式II所代表的化合物，5～25份通式III所代表的化合物，0～20份通式IV所代表的化合物，0～15份通式V所代表的化合物，0～45份通式VII所代表的化合物，0～10份通式VIII所代表的化合物，0～40份通式IX所代表的化合物。
优选地，本发明所提供的液晶组合物包括以下组分：5～25份通式I所代表的化合物，29～53份通式II所代表的化合物，6～21份通式III所代表的化合物，0～16份通式IV所代表的化合物，0～10份通式V所代表的化合物，0～40份通式VII所代表的化合物，0～8份通式VIII所代表的化合物，0～33份通式IX所代表的化合物。
或本发明所提供的液晶组合物包括以下组分：1～15份通式I所代表的化合物，20～40份通式II所代表的化合物，1～20份通式IV所代表的化合物，0～30份通式V所代表的化合物，0～15份通式VI所代表的化合物，25～60份通式VII所代表的化合物。
优选地，本发明所提供的液晶组合物包括以下组分：2～14份通式I所代表的化合物，27～36份通式II所代表的化合物，2～15份通式IV所代表的化合物，0～25份通式V所代表的化合物，0～10份通式VI所代表的化合物，29～54份通式VII所代表的化合物。
以及，更为理想的配方为：2～14份通式I所代表的化合物，27～36份通式II所代表的化合物，2～14份通式IV所代表的化合物，6～25份通式V所代表的化合物，29～48份通式VII所代表的化合物。
本发明所提供的液晶组合物中通式I所代表的化合物为二苯并呋喃结构的化合物，具有极大的负介电各向异性，可有效地增加液晶组合物的介电各向异性；通式II所代表的化合物为两环结构，该类化合物具极低的旋转粘度，作为降低液晶组合物的旋转粘度的最佳选择；本发明所提供的液晶组合物通过添加第I类化合物增加介电各向异性，以此减少极性单体使用，增加第II类化合物使用，达到降低液晶组合物旋转粘度的目的。
本发明所述液晶组合物的制备方法无特殊限制，可采用常规方法将两种或多种化合物混合进行生产，如通过在高温下混合不同组分并彼此溶解的方法制备，其中，将液晶组合物溶解在用于该化合物的溶剂中并混合，然后在减压下蒸馏出该溶剂；或者本发明所述液晶组合物可按照常规的方法制备，如将其中含量较小的组分在较高的温度下溶解在含量较大的主要组分中，或将各所属组分在有机溶剂中溶解，如丙酮、氯仿或甲醇等，然后将溶液混合去除溶剂后得到。
本发明所述液晶组合物具有低旋转粘度、大的弹性常数、良好的低温互溶性以及快的响应速度，可用于多种显示模式的快响应液晶显示，可用于多种显示模式的快响应液晶显示，优选适用于IPS、FFS或VA型液晶显示装置。本发明所述组合物在上述液晶显示装置，尤其是MVA、PVA、PSVA等类VA型液晶显示装置中的使用能明显改善液晶显示器显示效果。
具体实施方式
以下实施例用于说明本发明，但不用来限制本发明的范围。
除非另有说明，本发明中百分比为重量百分比；温度单位为摄氏度；△n代表光学各向异性(25℃)；△ε代表介电各向异性(25℃，1000Hz)；V10代表阈值电压，是在相对透过率改变10％时的特征电压(V，25℃)；γ1代表旋转粘度(mPa.s，25℃)；Cp代表液晶组合物的清亮点(℃)；K11、K22、K33分别代表展曲、扭曲和弯曲弹性常数(pN，25℃)。
以下各实施例中，液晶化合物中基团结构用表1所示代码表示。
表1：液晶化合物的基团结构代码
以如下化合物结构为例：
表示为：4EO2
表示为：3CPWO1
以下各实施例中，液晶组合物的制备均采用热溶解方法，包括以下步骤：用天平按重量百分比称量液晶化合物，其中称量加入顺序无特定要求，通常以液晶化合物熔点由高到低的顺序依次称量混合，在60～100℃下加热搅拌使得各组分熔解均匀，再经过滤、旋蒸，最后封装即得目标样品。
以下各实施例中，液晶组合物中各组分的重量百分比及液晶组合物的性能参数见下述表格。
以下实施例中，所涉及的所有组分均为已知液晶化合物，可由北京八亿时空提供。
实施例1
表2：液晶组合物中各组分的重量百分比及性能参数
实施例2
表3：液晶组合物中各组分的重量百分比及性能参数
实施例3
表4：液晶组合物中各组分的重量百分比及性能参数
实施例4
表5：液晶组合物中各组分的重量百分比及性能参数
实施例5
表6：液晶组合物中各组分的重量百分比及性能参数
实施例6
表7：液晶组合物中各组分的重量百分比及性能参数
实施例7
表8：液晶组合物中各组分的重量百分比及性能参数
实施例8
表9：液晶组合物中各组分的重量百分比及性能参数
实施例9
表11：液晶组合物中各组分的重量百分比及性能参数
实施例10
表11：液晶组合物中各组分的重量百分比及性能参数
实施例11
表12：液晶组合物中各组分的重量百分比及性能参数
实施例12
表13：液晶组合物中各组分的重量百分比及性能参数
实施例13
表14：液晶组合物中各组分的重量百分比及性能参数
对比例1
表15：液晶组合物中各组分的重量百分比及性能参数
将实施例1与对比例1所得液晶组合物的各性能参数值进行汇总比较，参见表16。
表16：液晶组合物的性能参数比较
△n △ε Cp γ1 K<sub>11</sub> K<sub>22</sub> K<sub>33</sub>
实施例1 0.101 -2.6 75 47 13.6 6.8 13.8
对比例1 0.098 -2.7 76 65 11.8 5.9 13.6
经比较可知：与对比例1相比，实施例1提供的液晶组合物具有低的旋转粘度，即具有更快的的响应时间。
由以上实施例可知，本发明所提供的含有二苯并呋喃液晶化合物的液晶组合物，具有低粘度、高电阻率、适合的光学各向异性、良好的低温互溶性、大的弹性常数以及优异的光稳定性和热稳定性，可降低液晶显示器的响应时间，从而解决液晶显示器响应速度慢的问题。因此，本发明所提供的液晶组合物适用于快响应的IPS及FFS以及MVA、PVA、PSVA等VA型液晶显示装置，特别适用于快响应的液晶显示装置。
虽然，上文中已经用一般性说明及具体实施方案对本发明作了详尽的描述，但在本发明基础上，可以对之作一些修改或改进，这对本领域技术人员而言是显而易见的。因此，在不偏离本发明精神的基础上所做的这些修改或改进，均属于本发明要求保护的范围。

Claims (30)

1.一种向列相液晶组合物，其特征在于：所述液晶组合物按重量份计，包括以下组分：1～11份通式I所代表的化合物，20～50份通式II所代表的化合物，0～15份通式III所代表的化合物，3～20份通式IV所代表的化合物，0～30份通式V所代表的化合物，0～15份通式VI所代表的化合物，5～50份通式VII所代表的化合物，0～40份通式IX所代表的化合物；
R1、R2各自独立地代表C1～C12的直链烷基，其中一个或多个不相邻的CH2可以被O、S或CH＝CH所取代；
R3、R4各自独立地代表C1～C12的直链烷基，其中一个或多个不相邻的CH2可以被O、S或CH＝CH所取代；A1、A2各自独立地代表反式1,4-环己基或1,4-亚苯基；
R5、R6各自独立地代表C1～C12的直链烷基，其中一个或多个不相邻的CH2可以被O或CH＝CH取代；
A3选自以下结构：
其中，R7、R8各自独立地代表C1～C12的直链烷基、烷氧基或C2～C12的直链烯基；A4代表1，4-亚环己基或1，4-亚苯基；Z1代表单键、CH2CH2或CH2O；
其中，R9、R10各自独立地代表C1～C12的直链烷基；
其中，R11、R12各自独立地代表C1～C12直链烷基或直链烷氧基；L1代表H或F；
其中R13、R14各自独立地代表C1～C12的直链烷基、直链烷氧基或C2～C12的直链烯基；A5选自以下结构：
A6选自以下结构：
其中，R17、R18各自独立地代表C1～C12的直链烷基、直链烷氧基或C2～C12的直链烯基。
2.根据权利要求1所述的所述液晶组合物，其特征在于：通式I所代表的化合物选自下式中所代表的化合物的一种或几种：
其中，R1、R2各自独立地代表C1～C7的直链烷基。
3.根据权利要求2所述的所述液晶组合物，其特征在于：所述通式I所代表的化合物选自下式中所代表的化合物的一种或几种：
4.根据权利要求1或2所述的液晶组合物，其特征在于：所述通式II所代表的化合物选自如下化合物的一种或多种：
其中，R3代表C1～C7的直链烷基；R4代表C1～C7的直链烷基、直链烷氧基或C2～C7的直链烯基。
5.根据权利要求4所述的液晶组合物，其特征在于：所述通式II所代表的化合物选自式IIA1～式IIC24所代表的化合物的一种或几种：
6.根据权利要求1-3、5中任一项所述的液晶组合物，其特征在于：通式III所代表的化合物选自式IIIA～式IIIC中的一种或多种：
其中，R5代表C2～C10的直链烷基或直链烯基；R6代表C1～C8的直链烷基。
7.根据权利要求6所述的液晶组合物，其特征在于：通式III所代表化合物选自式IIIA1～式IIIC30结构中的一种或多种：
8.根据权利要求1-3、5、7中任一项所述的液晶组合物，其特征在于：
通式IV所代表的化合物选自以下化合物中的一种或多种：
其中，R7代表C1～C7的直链烷基或C2～C7的直链烯基；R8代表C1～C7的直链烷基或直链烷氧基。
9.根据权利要求8所述的液晶组合物，其特征在于：
通式IV的化合物选自式IVA1～式IVD16中的一种或多种；
10.根据权利要求1-3、5、7、9中任一项所述的液晶组合物，其特征在于：通式V所代表的化合物选自以下结构中的一种或多种：
11.根据权利要求1-3、5、7、9中任一项所述的液晶组合物，其特征在于：通式VI所代表的化合物选自VIA和VIB中的一种或多种：
其中，R11、R12各自独立地代表C1～C7直链烷基或直链烷氧基。
12.根据权利要求11所述的液晶组合物，其特征在于：R11、R12各自独立地代表C1～C5的直链烷基或直链烷氧基。
13.根据权利要求1-3、5、7、9、12中任一项所述的液晶组合物，其特征在于：通式VII所代表的化合物选自以下结构中的一种或多种：
其中，R13代表C1～C7的直链烷基或C2～C7的直链烯基；R14代表C1～C7的直链烷基或直链烷氧基。
14.根据权利要求13所述的液晶组合物，其特征在于：R13代表C2～C5的直链烷基或直链烯基；R14代表C1～C5的直链烷基或直链烷氧基。
15.根据权利要求1-3、5、7、9、12、14中任一项所述液晶组合物，其特征在于：所述液晶组合物还包含一种或多种通式VIII所代表的化合物：
其中，R15、R16各自独立地代表C1～C12的直链烷基；L2、L3各自独立地代表H或F；A7代表1，4-环己基或1，4-亚苯基。
16.根据权利要求15所述的液晶组合物，其特征在于：通式VIII所代表的化合物选自以下结构的一种或多种：
其中，R15、R16各自独立地代表C1～C7的直链烷基。
17.根据权利要求16所述的液晶组合物，其特征在于：R15、R16各自独立地代表C2～C5的直链烷基。
18.根据权利要求1所述的液晶组合物，其特征在于：R17代表C2～C7的直链烯基或直链烷基，R18代表C1～C7的直链烷基或直链烷氧基。
19.根据权利要求18所述的液晶组合物，其特征在于：R17代表C2～C5的直链烷基或直链烯基；R18代表C1～C5的直链烷基或直链烷氧基。
20.根据权利要求1-3、5、7、9、12、14、16-19任一项所述液晶组合物，其特征在于：包括以下组分：2～11份通式I所代表的化合物，27～40份通式II所代表的化合物，0～10份通式III所代表的化合物，5～16份通式IV所代表的化合物，0～25份通式V所代表的化合物，0～10份通式VI所代表的化合物，7～48份通式VII所代表的化合物，0～33份通式IX所代表的化合物。
21.根据权利要求15所述液晶组合物，其特征在于：所述液晶组合物按重量份计，包括以下组分：12～30份通式I所代表的化合物，20～60份通式II所代表的化合物，0～25份通式III所代表的化合物，0～10份通式IV所代表的化合物，0～20份通式V所代表的化合物，0～60份通式VII所代表的化合物，0～10份通式VIII所代表的化合物，0～25份通式IX所代表的化合物。
22.根据权利要求21所述液晶组合物，其特征在于：包括以下组分：12～25份通式I所代表的化合物，29～53份通式II所代表的化合物，0～21份通式III所代表的化合物，0～2份通式IV所代表的化合物，0～10份通式V所代表的化合物，0～54份通式VII所代表的化合物，0～8份通式VIII所代表的化合物，0～20份通式IX所代表的化合物。
23.根据权利要求15所述液晶组合物，其特征在于：所述液晶组合物按重量份计，包括以下组分：3～30份通式I所代表的化合物，20～55份通式II所代表的化合物，5～25份通式III所代表的化合物，0～20份通式IV所代表的化合物，0～15份通式V所代表的化合物，0～45份通式VII所代表的化合物，0～10份通式VIII所代表的化合物，0～40份通式IX所代表的化合物。
24.根据权利要求23所述液晶组合物，其特征在于：所述液晶组合物包括以下组分：5～25份通式I所代表的化合物，29～53份通式II所代表的化合物，6～21份通式III所代表的化合物，0～16份通式IV所代表的化合物，0～10份通式V所代表的化合物，0～40份通式VII所代表的化合物，0～8份通式VIII所代表的化合物，0～33份通式IX所代表的化合物。
25.根据权利要求1-3、5、7、9、12、14、16-19任一项所述液晶组合物，其特征在于：所述液晶组合物按重量份计，包括以下组分：1～15份通式I所代表的化合物，20～40份通式II所代表的化合物，1～20份通式IV所代表的化合物，0～30份通式V所代表的化合物，0～15份通式VI所代表的化合物，25～60份通式VII所代表的化合物。
26.根据权利要求25所述液晶组合物，其特征在于：所述液晶组合物包括以下组分：2～14份通式I所代表的化合物，27～36份通式II所代表的化合物，2～15份通式IV所代表的化合物，0～25份通式V所代表的化合物，0～10份通式VI所代表的化合物，29～54份通式VII所代表的化合物。
27.根据权利要求26所述液晶组合物，其特征在于：所述液晶组合物包括以下组分：2～14份通式I所代表的化合物，27～36份通式II所代表的化合物，2～14份通式IV所代表的化合物，6～25份通式V所代表的化合物，29～48份通式VII所代表的化合物。
28.权利要求1-27中任一项所述液晶组合物在液晶显示装置中的应用。
29.根据权利要求28所述的应用，其特征在于：所述的液晶显示装置为IPS、FFS或VA型液晶显示器。
30.根据权利要求29所述的应用，其特征在于：所述VA型液晶显示器为MVA、PVA或PSVA型液晶显示器。
CN201510934837.8A 2015-12-15 2015-12-15 一种向列相液晶组合物及其应用 Active CN106883864B (zh)