CN106883701A - The heavy antisepsis of resistance to dust storm wind power equipment waterborne metallic paint - Google Patents
The heavy antisepsis of resistance to dust storm wind power equipment waterborne metallic paint Download PDFInfo
- Publication number
- CN106883701A CN106883701A CN201710129748.5A CN201710129748A CN106883701A CN 106883701 A CN106883701 A CN 106883701A CN 201710129748 A CN201710129748 A CN 201710129748A CN 106883701 A CN106883701 A CN 106883701A
- Authority
- CN
- China
- Prior art keywords
- resistance
- wind power
- power equipment
- dust storm
- metallic paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of heavy antisepsis of resistance to dust storm wind power equipment waterborne metallic paint, paint ingredient includes acrylic emulsion, deionized water, organic siliconresin, polyimides, vinyl, nano pulp, composite anti-corrosive pigment, dispersant, wetting agent, defoamer, curing agent, coalescents.The great high and low temperature resistance of polyimides of the present invention, vinyl is highly corrosion-resistant；Organic siliconresin is weather-proof, resistance to wind-powered electricity generation, insulation；Nano pulp selects nano titanium oxide, greatly promotes wear-resisting, resistive Saudi Arabia property of the invention；Product is nontoxic, environmental protection, and its suitable for the resistance to dust storm and anti-corrosion of wind power equipment.
Description
Technical field
The present invention relates to water paint field, and in particular to a kind of heavy antisepsis of resistance to dust storm wind power equipment waterborne metallic paint.
Background technology
Wind-power electricity generation to be become play in recent years in that renewable resource the most rapid, is started from " supplementary source " direction
The direction of " the strategy alternatives energy " is developed.Power station is chronically exposed in harsh climate environment, it is necessary to carry out effective out of my mind
Anti-corrosion protection；The wherein apparatus expensive of large-scale wind electricity equipment, work under bad environment, scene inconvenience carries out detachable maintaining to equipment.
The anticorrosive work of pylon is become to ensure the pith of wind-power electricity generation, therefore for the application in extension pylon life-span is of crucial importance.
With flourishing for domestic Wind Power Generation Industry, and the particular surroundings of Wind Power Generation Industry just becomes for the performance requirement of coating
Obtain extremely strict.Current operating wind power equipment coating is derived from import mostly, high cost and actual motion effect is unsatisfactory；
Therefore in terms of the research and development of wind power equipment coating, reduces cost and performance improvement seem particularly urgent.
The content of the invention
Regarding to the issue above, the invention provides a kind of heavy antisepsis of resistance to dust storm wind power equipment waterborne metallic paint.
The present invention is adopted the technical scheme that：A kind of heavy antisepsis of resistance to dust storm wind power equipment waterborne metallic paint, by quality point
Number includes
46 parts of acrylic emulsion
29 parts of deionized water
22 parts of organic siliconresin
18 parts of polyimides
18 parts of vinyl
10 parts of nano pulp
2 parts of composite anti-corrosive pigment
0.3 part of dispersant
0.5 part of wetting agent
0.4 part of defoamer
0.4 part of curing agent
0.2 part of coalescents.
As a kind of perferred technical scheme：Described organic siliconresin is SN480 or SN600.
As a kind of perferred technical scheme：Described nano pulp is nano titanium oxide.
As a kind of perferred technical scheme：Composite anti-corrosive pigment is preferably composite iron-titanium powder.
As a kind of perferred technical scheme：Described dispersant be SN5040, CY540 in one or two.
As a kind of perferred technical scheme：Described wetting agent be PE100 and H436 in one or two.
As a kind of perferred technical scheme：Described defoamer be SPA202 and D160 in one or two.
As a kind of perferred technical scheme：Described curing agent is diethylenetriamine.
As a kind of perferred technical scheme：Described coalescents are in dipropylene glycol n-butyl ether and ethylene glycol monobutyl ether
One or two.
The beneficial effects of the invention are as follows：（1）The great high and low temperature resistance of polyimides, vinyl is highly corrosion-resistant；Have
Machine silicones is weather-proof, resistance to wind-powered electricity generation, insulation；（2）Nano pulp selects nano titanium oxide, greatly promotes wear-resisting, resistive of the invention
Saudi Arabia's property；Product is nontoxic, environmental protection, and its suitable for the resistance to dust storm and anti-corrosion of wind power equipment.
Specific embodiment
In order to further illustrate the present invention, the present invention is described in detail below by embodiment, but can not be by it
Be interpreted as limiting the scope of the present invention.
Embodiment 1
A kind of heavy antisepsis of resistance to dust storm wind power equipment waterborne metallic paint, is included by mass fraction
46 parts of acrylic emulsion
29 parts of deionized water
22 parts of SN480
18 parts of polyimides
18 parts of vinyl
10 parts of nano titanium oxide
2 parts of composite iron-titanium powder
0.3 part of SN5040
0.5 part of PE100
0.4 part of SPA202
0.4 part of diethylenetriamine
0.2 part of dipropylene glycol n-butyl ether.
Embodiment 2
A kind of heavy antisepsis of resistance to dust storm wind power equipment waterborne metallic paint, is included by mass fraction
46 parts of acrylic emulsion
29 parts of deionized water
22 parts of SN600
18 parts of polyimides
18 parts of vinyl
10 parts of nano titanium oxide
2 parts of composite iron-titanium powder
0.3 part of CY540
0.5 part of H436
0.4 part of D160
0.4 part of diethylenetriamine
0.2 part of ethylene glycol monobutyl ether.
Embodiment 3
A kind of heavy antisepsis of resistance to dust storm wind power equipment waterborne metallic paint, is included by mass fraction
46 parts of acrylic emulsion
29 parts of deionized water
22 parts of SN600
18 parts of polyimides
18 parts of vinyl
10 parts of nano titanium oxide
2 parts of composite iron-titanium powder
0.2 part of SN5040
0.1 part of CY540
0.2 part of PE100
0.3 part of H436
0.1 part of SPA202
0.3 part of D160
0.4 part of diethylenetriamine
0.15 part of dipropylene glycol n-butyl ether
0.05 part of ethylene glycol monobutyl ether.
It should be noted last that, above example is only used to supplement explaination technical scheme and unrestricted.To the greatest extent
Pipe has been described in detail with reference to embodiment to the present invention, this area it is vast it will be appreciated by the skilled person that to skill of the invention
Art scheme is modified or is replaced on an equal basis, and without departure from the spirit and scope of technical solution of the present invention, it all should cover at this
In the middle of the right of invention.
Claims (9)
1. a kind of heavy antisepsis of resistance to dust storm wind power equipment waterborne metallic paint, it is characterised in that：The heavy antisepsis of resistance to dust storm wind power equipment water
Property metallic paint is included by mass fraction
46 parts of acrylic emulsion
29 parts of deionized water
22 parts of organic siliconresin
18 parts of polyimides
18 parts of vinyl
10 parts of nano pulp
2 parts of composite anti-corrosive pigment
0.3 part of dispersant
0.5 part of wetting agent
0.4 part of defoamer
0.4 part of curing agent
0.2 part of coalescents.
2. a kind of heavy antisepsis of resistance to dust storm wind power equipment waterborne metallic paint according to claim 1, it is characterised in that：It is described
Organic siliconresin be SN480 or SN600.
3. a kind of heavy antisepsis of resistance to dust storm wind power equipment waterborne metallic paint according to claim 1, it is characterised in that：It is described
Nano pulp be nano titanium oxide.
4. a kind of heavy antisepsis of resistance to dust storm wind power equipment waterborne metallic paint according to claim 1, it is characterised in that：It is compound
Anti-corrosion paint is preferably composite iron-titanium powder.
5. a kind of heavy antisepsis of resistance to dust storm wind power equipment waterborne metallic paint according to claim 1, it is characterised in that：It is described
Dispersant be one or two in SN5040, CY540.
6. a kind of heavy antisepsis of resistance to dust storm wind power equipment waterborne metallic paint according to claim 1, it is characterised in that：It is described
Wetting agent be one or two in PE100 and H436.
7. a kind of heavy antisepsis of resistance to dust storm wind power equipment waterborne metallic paint according to claim 1, it is characterised in that：It is described
Defoamer be one or two in SPA202 and D160.
8. a kind of heavy antisepsis of resistance to dust storm wind power equipment waterborne metallic paint according to claim 1, it is characterised in that：It is described
Curing agent be diethylenetriamine.
9. a kind of heavy antisepsis of resistance to dust storm wind power equipment waterborne metallic paint according to claim 1, it is characterised in that：It is described
Coalescents be one or two in dipropylene glycol n-butyl ether and ethylene glycol monobutyl ether.