CN106883549B - Exempt from logo printing plasthetics and preparation method thereof - Google Patents
Exempt from logo printing plasthetics and preparation method thereof Download PDFInfo
- Publication number
- CN106883549B CN106883549B CN201710230147.3A CN201710230147A CN106883549B CN 106883549 B CN106883549 B CN 106883549B CN 201710230147 A CN201710230147 A CN 201710230147A CN 106883549 B CN106883549 B CN 106883549B
- Authority
- CN
- China
- Prior art keywords
- plasthetics
- exempting
- laser additive
- logo
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention discloses one kind and exempts from logo printing plasthetics and preparation method thereof, wherein, described to exempt from the ingredient that logo printing plasthetics includes following mass percent: plastic material 96%~98.3%, metal powder or mica powder 1.5%~1.8%, laser additive 0.2%~2.2%.Technical solution provided by the invention solves bring chemical contamination and the technical problem that technique is cumbersome, scrappage is high in existing plasthetics production technology.
Description
Technical field
The present invention relates to plasthetics fields more particularly to one kind to exempt from logo printing plasthetics and preparation method thereof.
Background technique
Currently, the logo of surface of plastic product is realized by printing mostly in the market, traditional logo printing adds
Work mode is that either pass through the film prints out required logo shape to laser engraving.The printing ink that film printing uses is easy
Chemical contamination is caused, the logo weatherability of printing is poor, easy to fall off；And laser engraving is in laser beam high temperature irradiation process, so that
Plasthetics is easily deformed, or even fusing, and plasthetics scrappage is higher, is not easy to the application of plasthetics.
Summary of the invention
The main object of the present invention is to provide one kind and exempts from logo printing plasthetics and preparation method thereof, it is intended to reduce plastic cement
Chemical contamination and scrappage in product logo printing technology.
To achieve the above object, the present invention proposes that one kind exempts from logo printing plasthetics, including following mass percent
Ingredient:
Plastic material 96%~98.3%,
Metal powder or mica powder 1.5%~1.8%,
Laser additive 0.2%~2.2%.
Preferably, the plasthetics for exempting from logo printing includes the ingredient of following mass percent:
Plastic material 96%~96.7%,
Metal powder or mica powder 1.5%~1.8%,
Laser additive 1.8%~2.2%.
Preferably, the plasthetics for exempting from logo printing includes the ingredient of following mass percent:
Plastic material 97.7%~98.3%,
Metal powder or mica powder 1.5%~1.8%,
Laser additive 0.2%~1.5%.
Preferably, the plasthetics for exempting from logo printing includes the ingredient of following mass percent:
Plastic material 96.7%~97.7%,
Metal powder or mica powder 1.5%~1.8%,
Laser additive 0.8%~1.5%.
Preferably, the metal powder is aluminium powder.
The present invention also correspondingly proposes a kind of preparation method for exempting from logo printing plasthetics, comprising the following steps:
Step 1: weighing each ingredient according to setting ratio:
Plastic material 96%~98.3%,
Metal powder or mica powder 1.5%~1.8%,
Laser additive 0.2%~2.2%；
Step 2: will weigh accurate plastic material, metal powder or mica powder, laser additive be added reaction kettle in, stir
It mixes uniformly；
It is squeezed out after mixing Step 3: the mixture in reaction kettle is poured into granulator, and dry pre- under preset temperature
If duration.
Preferably, the preset temperature is 80 DEG C~100 DEG C, and the preset duration is 1~4 hour.
Preferably, in step 1 each ingredient setting ratio are as follows:
Plastic material 96%~96.7%,
Metal powder or mica powder 1.5%~1.8%,
Laser additive 1.8%~2.2%.
Preferably, in step 1 each ingredient setting ratio are as follows:
Plastic material 97.7%~98.3%,
Metal powder or mica powder 1.5%~1.8%,
Laser additive 0.2%~0.5%.
Preferably, in step 1 each ingredient setting ratio are as follows:
Plastic material 96.7%~97.7%,
Metal powder or mica powder 1.5%~1.8%,
Laser additive 0.8%~1.5%.
It is provided by the invention to exempt from logo printing plasthetics to include laser additive, it also allows for the logo that exempts from and prints
Brush plasthetics can form logo after carrying out laser carving according to laser carving parameter by laser carving board, no longer need to carry out film printing,
The operational sequence for saving plasthetics logo printing reduces ink chemistry pollution relative to traditional logo processing method,
Also reduce the scrappage of plasthetics.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiments of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is general
Logical technical staff every other embodiment obtained without creative efforts belongs to what the present invention protected
Range.
It in addition, the technical solution between each embodiment of the present invention can be combined with each other, but must be general with this field
Based on logical technical staff can be realized, it will be understood that when the combination of technical solution appearance is conflicting or cannot achieve this
The combination of technical solution is not present, also not the present invention claims protection scope within.
The present invention proposes that one kind exempts from logo printing plasthetics, and the logo printing plasthetics of exempting from includes following quality hundred
Divide each ingredient of ratio:
Plastic material 96%~98.3%,
Metal powder or mica powder 1.5%~1.8%,
Laser additive 0.2%~2.2%.
It is to be appreciated that provided by the invention exempt from logo printing plasthetics to include laser additive and metal powder,
When plasthetics carries out laser carving processing, the metal powder and laser additive can absorb laser energy, effectively avoid plastic cement table
The case where face is by laser beam thermal energy calcination prevents plasthetics from deforming the phenomenon that even melting because of high temperature.Relative to tradition
Primer spray, finishing coat, then the technique of laser carving, plasthetics provided by the invention save twice lacquer spraying technique, simplifies processing
Process；And reduce because ink printing causes chemical contamination, scrap of the product caused by manual operation is also reduced, is effectively improved
The product yield and processing efficiency of plasthetics.
It should be noted that it is heretofore described exempt from logo printing each ingredient of plasthetics mass percent can have it is more
Kind combination, the different quality percentage of heterogeneity enable plasthetics to be used for the logo that laser carving forms different colours.
And the proportion by adjusting metal powder and laser additive, the logo that plasthetics is formed show different degrees of
Shade and glossiness.
It is to be appreciated that heretofore described metal powder is aluminium powder；The laser additive is that commercially available common laser adds
Add agent；The plastic material can be ABS (acrylonitrile-butadiene-styrene copolymer), PC (polycarbonate), PP (poly- third
Alkene), PE (polyethylene), PA (polyamide), one or more of engineering plastics such as POM (polyformaldehyde).
Further, the present invention also proposes a kind of preparation method for exempting from logo printing plasthetics, comprising the following steps:
Step 1: weighing each ingredient according to setting ratio:
Plastic material 96%~98.3%,
Metal powder or mica powder 1.5%~1.8%,
Laser additive 0.2%~2.2%；
Step 2: will weigh accurate plastic material, metal powder or mica powder, laser additive be added reaction kettle in, stir
It mixes uniformly；
It is squeezed out after mixing Step 3: the mixture in reaction kettle is poured into granulator, and dry pre- under preset temperature
If duration.
It should be noted that the preset temperature is 80 DEG C~100 DEG C, the preset duration is 1~4 hour.
Plasthetics and preparation method thereof progress will be printed to the logo proposed by the present invention that exempts from by specific embodiment below
It illustrates:
Embodiment one
It is a kind of exempt from logo printing plasthetics, the ingredient including following mass percent: ABS96%, aluminium powder 1.8%,
Laser additive 2.2%.
This preparation method for exempting from logo printing plasthetics, comprising the following steps:
Step 1: weighing each ingredient: ABS96%, aluminium powder 1.8%, laser additive 2.2% according to setting ratio；
It is added in reaction kettle, stirs evenly Step 2: accurate ABS, aluminium powder and laser additive will be weighed；
It is squeezed out after mixing Step 3: the mixture in reaction kettle is poured into granulator, and 2 hours dry under 85 degree.
Embodiment two
A kind of plasthetics for exempting from logo printing, the ingredient including following mass percent: ABS96.7%, aluminium powder
1.5%, laser additive 1.8%.
This preparation method for exempting from logo printing plasthetics, comprising the following steps:
Step 1: weighing each ingredient: ABS96.7%, aluminium powder 1.5%, laser additive 1.8% according to setting ratio；
It is added in reaction kettle, stirs evenly Step 2: accurate ABS, aluminium powder and laser additive will be weighed；
It is squeezed out after mixing Step 3: the mixture in reaction kettle is poured into granulator, and 2 hours dry under 85 degree.
Embodiment three
A kind of plasthetics for exempting from logo printing, the ingredient including following mass percent: ABS97.7%, mica powder
1.8%, laser additive 0.5%.
This preparation method for exempting from logo printing plasthetics, comprising the following steps:
Step 1: weighing each ingredient: ABS97.7%, mica powder 1.8%, laser additive 0.5% according to setting ratio；
It is added in reaction kettle, stirs evenly Step 2: accurate ABS, mica powder and laser additive will be weighed；
It is squeezed out after mixing Step 3: the mixture in reaction kettle is poured into granulator, and 2 hours dry under 85 degree.
Example IV
A kind of plasthetics for exempting from logo printing, the ingredient including following mass percent: ABS98.3%, mica powder
1.5%, laser additive 0.2%.
This preparation method for exempting from logo printing plasthetics, comprising the following steps:
Step 1: weighing each ingredient: ABS98.3%, mica powder 1.5%, laser additive 0.2% according to setting ratio；
It is added in reaction kettle, stirs evenly Step 2: accurate ABS, mica powder and laser additive will be weighed；
It is squeezed out after mixing Step 3: the mixture in reaction kettle is poured into granulator, and 2 hours dry under 85 degree.
Embodiment five
It is a kind of exempt from logo printing plasthetics, the ingredient including following mass percent: PC96.7%, aluminium powder 1.8%,
Laser additive 1.5%.
This preparation method for exempting from logo printing plasthetics, comprising the following steps:
Step 1: weighing each ingredient: PC96.7%, aluminium powder 1.8%, laser additive 1.5% according to setting ratio；
It is added in reaction kettle, stirs evenly Step 2: accurate PC, aluminium powder and laser additive will be weighed；
It is squeezed out after mixing Step 3: the mixture in reaction kettle is poured into granulator, and 2 hours dry under 85 degree.
Embodiment six
A kind of plasthetics for exempting from logo printing, the ingredient including following mass percent: ABS97.7%, aluminium powder
1.5%, laser additive 0.8%.
This preparation method for exempting from logo printing plasthetics, comprising the following steps:
Step 1: weighing each ingredient: ABS97.7%, aluminium powder 1.5%, laser additive 0.8% according to setting ratio；
It is added in reaction kettle, stirs evenly Step 2: accurate ABS, aluminium powder and laser additive will be weighed；
It is squeezed out after mixing Step 3: the mixture in reaction kettle is poured into granulator, and 2 hours dry under 85 degree.
Further, it will be carried out in laser carving board by plasthetics prepared by the various embodiments described above according to laser carving parameter
Laser carving is carried out, can be obtained the plasthetics for having different colours logo.Plasthetics laser carving prepared by the various embodiments described above
Logo color afterwards is as follows:
| Embodiment | Logo color |
| One | Ceramics are white |
| Two | It is shallow white |
| Three | It is dark-grey |
| Four | Light gray |
| Five | It is pitch black |
| Six | Somber |
The plasthetics provided by the invention for exempting from logo printing is added by the metal powder and laser that add different ratio
Agent effectively avoids plastic surface so that the metal powder and laser additive can absorb laser energy when carrying out laser carving processing
The case where by laser beam thermal energy calcination, prevents plasthetics from deforming the phenomenon that even melting because of high temperature；And the metal powder
It will not be vaporized by the laser, and then metal powder is deposited in the logo pattern by laser carving, shows special color, by adjusting metal
The proportion of powder and laser additive saves process, avoids so that the logo of different colours is presented in plasthetics surface
Ink prints bring chemical contamination, also reduces plasthetics production cost.
The above description is only a preferred embodiment of the present invention, is not intended to limit the scope of the invention, all at this
Under the inventive concept of invention, the other similar logo that exempts from is obtained using description of the invention and prints plasthetics, is included in
In scope of patent protection of the invention.
Claims (9)
1. one kind exempts from logo printing plasthetics, which is characterized in that the ingredient including following mass percent:
Plastic material 96%~98.3%,
Aluminium powder or mica powder 1.5%~1.8%,
Laser additive 0.2%~2.2%；
By adjusting the proportion of the aluminium powder or mica powder and the laser additive, so that different face are presented in the plasthetics
The logo of color.
2. exempting from logo printing plasthetics as described in claim 1, which is characterized in that the plasthetics for exempting from logo printing
Ingredient including following mass percent:
Plastic material 96%~96.7%,
Aluminium powder or mica powder 1.5%~1.8%,
Laser additive 1.8%~2.2%.
3. exempting from logo printing plasthetics as described in claim 1, which is characterized in that the plasthetics for exempting from logo printing
Ingredient including following mass percent:
Plastic material 97.7%~98.3%,
Aluminium powder or mica powder 1.5%~1.8%,
Laser additive 0.2%~0.5%.
4. exempting from logo printing plasthetics as described in claim 1, which is characterized in that the plasthetics for exempting from logo printing
Ingredient including following mass percent:
Plastic material 96.7%~97.7%,
Aluminium powder or mica powder 1.5%~1.8%,
Laser additive 0.8%~1.5%.
5. a kind of preparation method for exempting from logo printing plasthetics, which comprises the following steps:
Step 1: weighing each ingredient according to setting ratio:
Plastic material 96%~98.3%,
Aluminium powder or mica powder 1.5%~1.8%,
Laser additive 0.2%~2.2%；
Step 2: will weigh accurate plastic material, aluminium powder or mica powder, laser additive be added reaction kettle in, stir evenly；
When being squeezed out after mixing Step 3: the mixture in reaction kettle is poured into granulator, and drying default under preset temperature
It is long；
By adjusting the proportion of the aluminium powder or mica powder and the laser additive, so that different face are presented in the plasthetics
The logo of color.
6. exempting from the preparation method of logo printing plasthetics as claimed in claim 5, which is characterized in that the preset temperature is
80 DEG C~100 DEG C, the preset duration is 1~4 hour.
7. such as the preparation method described in claim 5 or 6 for exempting from logo printing plasthetics, which is characterized in that each in step 1
The setting ratio of ingredient are as follows:
Plastic material 96%~96.7%,
Aluminium powder or mica powder 1.5%~1.8%,
Laser additive 1.8%~2.2%.
8. such as the preparation method described in claim 5 or 6 for exempting from logo printing plasthetics, which is characterized in that each in step 1
The setting ratio of ingredient are as follows:
Plastic material 97.7%~98.3%,
Aluminium powder or mica powder 1.5%~1.8%,
Laser additive 0.2%~0.5%.
9. such as the preparation method described in claim 5 or 6 for exempting from logo printing plasthetics, which is characterized in that each in step 1
The setting ratio of ingredient are as follows:
Plastic material 96.7%~97.7%,
Aluminium powder or mica powder 1.5%~1.8%,
Laser additive 0.8%~1.5%.