CN106863979A - 一种复合防水卷材及其制备方法 - Google Patents
一种复合防水卷材及其制备方法 Download PDFInfo
- Publication number
- CN106863979A CN106863979A CN201710109284.1A CN201710109284A CN106863979A CN 106863979 A CN106863979 A CN 106863979A CN 201710109284 A CN201710109284 A CN 201710109284A CN 106863979 A CN106863979 A CN 106863979A
- Authority
- CN
- China
- Prior art keywords
- layer
- water
- composite
- coiled material
- proof coiled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种复合防水卷材及其制备方法，涉及卷材领域。其中，所述复合防水卷材包括胎基层、叠加在所述胎基层的上表面上的第一沥青层、叠加在所述胎基层的下表面下的第二沥青层、叠加在所述第一沥青层的上表面上的第一隔离层、叠加在所述第二沥青层的下表面下的第二隔离层；其中，所述第一隔离层和所述第二隔离层均至少包括耐老化的高分子材料和橡胶材料中的一种。本发明中的复合防水卷材相比于传统的卷材防水性能提高。
Description
技术领域
本发明涉及卷材领域，尤其涉及一种复合防水卷材及其制备方法。
背景技术
防水卷材是一种可卷曲成卷状的柔性建材产品，其主要用于建筑墙体、屋面、隧道、公路、以及垃圾填埋场等处，可起到抵御外界雨水、地下水渗漏等作用。可见，防水卷材作为工程基础与建筑物之间的无渗漏连接，是整个工程防水的第一道屏障，对整个工程起着至关重要的作用。
常见的防水卷材为沥青防水卷材，沥青防水卷材的防水原理为通过在屋面等基面上铺设沥青来抵御外界雨水等，但这种沥青防水卷材有一些弊端，例如，沥青材料易老化，当铺设在基面上的沥青防水卷材出现老化时，防水卷材的防水性就会大大降低；又如，沥青材料的耐高温性较差，如果基面所处的环境温度较高时，防水卷材的防水性也会降低。可见，沥青防水卷材的防水性能较差。
发明内容
本发明的目的在于提供一种复合防水卷材及其制备方法，以提高防水卷材的防水性能。
为解决上述技术问题，采用如下技术方案：
一方面，本发明提供了一种复合防水卷材，包括胎基层、叠加在所述胎基层的上表面上的第一沥青层、叠加在所述胎基层的下表面下的第二沥青层、叠加在所述第一沥青层的上表面上的第一隔离层、叠加在所述第二沥青层的下表面下的第二隔离层；其中，所述第一隔离层和所述第二隔离层均至少包括耐老化的高分子材料和橡胶材料中的一种。
本发明中的复合防水卷材包括沥青层和隔离层，沥青层为复合防水卷材的基础防水层，可以实现防水功能，而隔离层中包括耐老化的高分子材料和橡胶材料中的至少一种，因此，隔离层也可以起到防水的作用，同时，隔离层还可起到保护沥青层的作用，可见，复合防水卷材实现了双重防水功效，相比于现有技术，复合防水卷材的防水性能提高。在使用过程中，即使沥青层因外界环境的影响而被破坏掉，使其防水性能降低，隔离层会进一步起到防水作用，以确保复合防水卷材整体的防水性能。而且，本发明中的隔离层采用了高分子材料和\或橡胶材料，使得隔离层具有耐老化、拉伸强度高等优点，在实际运用中，可保证复合防水卷材的使用寿命，从而，进一步提供了复合防水卷材的防水性能。
另一方面，本发明提供了一种复合防水卷材的制备方法，包括：步骤S1：采用聚酯毡、玻纤毡和玻纤增强聚酯毡混合制成胎基层，将胎基层放入油温为120℃的浸油池内浸油20分钟；步骤S2：将沥青原料加入到温度在140℃的配料罐内，同时加入机油、滑石粉，并持续搅拌并加热至175℃，后加入改性剂、古马隆树脂、沥青改性增粘剂、高密度聚乙烯，并胶体磨研磨2.5小时后加入石墨，再继续搅拌15分钟后倒入到搅拌罐，制成沥青层；步骤S3：在浸油后的胎基层的上表面上复合第一沥青层，在浸油后的胎基层的下表面下复合第二沥青层；步骤S4：利用高分子材料和橡胶材料中的至少一种材料，在以上步骤形成的结构的上表面上覆盖第一隔离层，在以上步骤形成的结构的下表面下覆盖第二隔离层；步骤S5：对以上步骤形成的结构进行冷却与缠卷处理，获得复合防水卷材。
本发明所提供的复合防水卷材的制备方法与上述复合防水卷材的有益效果相同，在此不再赘述。
附图说明
为了更清楚地说明本发明实施例或现有技术中的技术方案，下面将对实施例描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他的附图。
图1为本发明实施例一中的复合防水卷材的第一截面结构图；
图2为本发明实施例一中的复合防水卷材的第二截面结构图；
图3为本发明实施例一中的复合防水卷材的结构示意图；
图4为本发明实施例二中的复合防水卷材的制备方法的第一流程图；
图5为本发明实施例二中的复合防水卷材的制备方法的第二流程图。
附图标记说明：
10—胎基层； 20—第一沥青层； 30—第二沥青层；
40—第一隔离层； 50—第二隔离层； 60—第一加强层；
70—第二加强层； 80—第一隔热层； 90—第二隔热层；
101—第一切割线； 102—第二切割线。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例一
参见图1，本实施例提供了一种复合防水卷材，该复合防水卷材包括胎基层10、叠加在胎基层10的上表面上的第一沥青层20、叠加在胎基层10的下表面下的第二沥青层30、叠加在第一沥青层20的上表面上的第一隔离层40、叠加在第二沥青层30的下表面下的第二隔离层50；其中，第一隔离层40和第二隔离层50均至少包括耐老化的高分子材料和橡胶材料中的一种。
在本实施例中，复合防水卷材包括两层可以起到防水作用的层结构，一层结构是沥青层，另一层结构是隔离层，其中，沥青作为传统的防水材料，可实现沥青层的防水功能，而高分子材料或者橡胶材料作为新型的防水材料，可实现隔离层的防水功能，可见，可实施例中的复合防水卷材可实现双重防水功能，二者的作用相互补充，相互叠加，相比于传统的防水卷材，防水性能明显提高。而且，隔离层还可起到保护复合防水卷材的作用，以使复合防水卷材的使用寿命和功能得到保证。另外，高分子材料或者橡胶材料作为新型材料，具有耐老化、拉伸强度高等特点，从而可延长复合防水卷材的使用寿命，以及改善复合防水卷材的品质。
参见图2，进一步的，复合防水卷材还可包括第一加强层60和第二加强层70，第一加强层60叠加在第一沥青层20和第一隔离层40之间，第二加强层70叠加在第二沥青层30和第二隔离层50之间。优选的，第一加强层60和第二加强层70可为无纺布层。无纺布层的加强层，可减少高分子材料、橡胶材料的变形量，使卷材铺贴更加平整顺直。
继续参见图2，在实际使用中，防水卷材通常会暴露在阳光下，而沥青为深色，深色的沥青会吸收大量的能量，而沥青本身在高温的环境下容易发生融化等现象，本实施例中为了避免上述现象的发生，复合防水卷材还可包括第一隔热层80和第二隔热层90，第一隔热层80叠加在第一沥青层20和第一加强层60之间，第二隔热层90叠加在第二沥青层30和第二加强层70之间。
除此之外，隔热层还可避免基面外侧的温度影响到基面、甚至基面内侧的温度，从而可使基面或者基面内侧保持在一个舒适的恒温环境中。例如，当将复合防水卷材铺贴在建筑物的屋顶上时，外界环境的温度被隔热层阻隔，因此，屋内的温度并不会随着外界环境温度的变化而变化，屋内的人们也就会处在一个相对舒适的环境内。
优选的，隔热层的形成原料可为具有隔热作用的材料，可参考的，隔热层中可包括：环烷油25份～39份、抗氧剂0.5份～1份、硅烷偶联剂1份～1.3份、陶瓷微粒1份～2份、六钛酸钾晶须0.5份～0.7份、苯乙烯-异戊二烯-苯乙烯共聚物30份～35份、竹纤维5份～6份、C5\C9共聚型石油树脂10份～15份、C5加氢石油树脂35份～45份、岩棉纤维5份～6份。
参见图1～图3，特别的，在第一隔离层40远离第一沥青层20的表面上，每隔一定的长度压制有一条第一切割线101，在第二隔离层50远离第二沥青层30的表面上，每隔一定的长度压制有一条第二切割线102，第一切割线101和第二切割线102的延伸方向均垂直于复合防水卷材的卷绕方向，且第一切割线101的两端分别对应延伸至第一隔离层40的两个边缘，第二切割线102的两端分别对应延伸至第二隔离层50的两个边缘，多条第一切割线101在第一隔离层40上的位置与多条第二切割线102在第二隔离层50上的位置一一对应。
任一组相互对应的两条切割线的设置，使得这两条切割线所在的复合防水卷材的位置处厚度变薄，且切割线的两端一直延伸到隔离层的边缘，从而便于人们根据需要沿切割线处将复合防水卷材分为多块。同时，第一切割线101和第二切割线102的延伸方向均垂直于复合防水卷材的卷绕方向，防水卷材分为多块时，也是规则的形状，通用性好。
除此之外，切割线的分布是均匀的，例如，可每隔10m设置一条切割线，从而通过切割线还可直接量取需要长度的卷材，操作简单，而且精确。
可参考的，第一切割线101和第二切割线102的宽度均可在5mm～15mm之间，这样既方便进行切割，也不会浪费太多的卷材材料。
实施例二
参见图4，本实施例提供了一种复合防水卷材的制备方法，该方法包括：
步骤S1：采用聚酯毡、玻纤毡和玻纤增强聚酯毡混合制成胎基层，将胎基层放入油温为120℃的浸油池内浸油20分钟。
步骤S2：将沥青原料加入到温度在140℃的配料罐内，同时加入机油、滑石粉，并持续搅拌并加热至175℃，后加入改性剂、古马隆树脂、沥青改性增粘剂、高密度聚乙烯，并胶体磨研磨2.5小时后加入石墨，再继续搅拌15分钟后倒入到搅拌罐，制成沥青层。
步骤S3：在浸油后的胎基层的上表面上复合第一沥青层，在浸油后的胎基层的下表面下复合第二沥青层。
步骤S4：利用高分子材料和橡胶材料中的至少一种材料，在以上步骤形成的结构的上表面上覆盖第一隔离层，在以上步骤形成的结构的下表面下覆盖第二隔离层。
步骤S5：对以上步骤形成的结构进行冷却与缠卷处理，获得复合防水卷材。
通过上述方法形成的复合防水卷材包括两层可以起到防水作用的层结构，一层结构是沥青层，另一层结构是隔离层，其中，沥青作为传统的防水材料，可实现沥青层的防水功能，而高分子材料或者橡胶材料作为新型的防水材料，可实现隔离层的防水功能，可见，可实施例中的复合防水卷材可实现双重防水功能，二者的作用相互补充，甚至相互叠加，相比于传统的防水卷材，防水性能明显提高。而且，隔离层还可起到保护复合防水卷材的作用，以使复合防水卷材的的使用寿命和功能得到保证。另外，高分子材料或者橡胶材料作为新型材料，具有耐老化、拉伸强度高等特点，从而可延长复合防水卷材的使用寿命，以及改善复合防水卷材的品质。
参见图5，进一步的，在步骤S3之后，以及在步骤S4之前，还包括：
步骤S6：在以上步骤形成的结构的上表面上形成第一加强层，在以上步骤形成的结构的下表面下形成第二加强层。
在步骤S6中，形成第一加强层和第二加强层所采用的原材料为无纺布。
继续参见图5，在步骤S3和步骤S6之间还包括：
步骤S7：覆压第一隔热层至第一沥青层的上表面上，覆压第二隔热层至第二沥青层的下表面下。
特别的，对于实施例一中提供的隔热层优选方案，其制备方法可为：
在分散反应釜中投入环烷油和抗氧剂，开启搅拌，在高速分散的状态下，加入硅烷偶联剂、陶瓷微粒和六钛酸钾晶须；
将上一步骤中得到的混合液转移至热熔胶反应釜，开启搅拌和加热，当釜内料温达到140℃时，投入苯乙烯-异戊二烯-苯乙烯共聚物、竹纤维和岩棉纤维，继续升温，保持料温在155℃～165℃的条件下真空搅拌；
当苯乙烯-异戊二烯-苯乙烯共聚物、竹纤维和岩棉纤维熔融化，加入C5\C9共聚型石油树脂和C5加氢石油树脂，140℃～150℃条件下抽真空搅拌50分钟～70分钟；
出料冷却定型。
继续参见图5，在步骤S4之后，以及在步骤S5之前，还包括：
步骤S8：在第一隔离层远离第一沥青层的表面上，每隔一定的长度压制一条第一切割线，在第二隔离层远离第二沥青层的表面上，每隔一定的长度压制一条第二切割线；其中，第一切割线和第二切割线的延伸方向均垂直于复合防水卷材的卷绕方向，且第一切割线的两端分别对应延伸至第一隔离层的两个边缘，第二切割线的两端分别对应延伸至第二隔离层的两个边缘，多条第一切割线在第一隔离层上的位置与多条第二切割线在第二隔离层上的位置一一对应。
需要说明的是，本实施例中的制备方法特别适用于实施例一中的复合防水卷材，对应的，实施例一中的有益效果在实施例二中的对应部分均可实现，因此，在本实施例中不再赘述。
以上，仅为本发明的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，可轻易想到变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应以权利要求的保护范围为准。
Claims (10)
1.一种复合防水卷材，其特征在于，包括胎基层、叠加在所述胎基层的上表面上的第一沥青层、叠加在所述胎基层的下表面下的第二沥青层、叠加在所述第一沥青层的上表面上的第一隔离层、叠加在所述第二沥青层的下表面下的第二隔离层；其中，所述第一隔离层和所述第二隔离层均至少包括耐老化的高分子材料和橡胶材料中的一种。
2.根据权利要求1所述的复合防水卷材，其特征在于，所述复合防水卷材还包括第一加强层和第二加强层，所述第一加强层叠加在所述第一沥青层和所述第一隔离层之间，所述第二加强层叠加在所述第二沥青层和所述第二隔离层之间。
3.根据权利要求2所述的复合防水卷材，其特征在于，所述第一加强层和所述第二加强层均为无纺布层。
4.根据权利要求2所述的复合防水卷材，其特征在于，所述复合防水卷材还包括第一隔热层和第二隔热层，所述第一隔热层叠加在所述第一沥青层和所述第一加强层之间，所述第二隔热层叠加在所述第二沥青层和所述第二加强层之间。
5.根据权利要求1～4任一项所述的复合防水卷材，其特征在于，在所述第一隔离层远离所述第一沥青层的表面上，每隔一定的长度压制有一条第一切割线，在所述第二隔离层远离所述第二沥青层的表面上，每隔一定的长度压制有一条第二切割线，所述第一切割线和所述第二切割线的延伸方向均垂直于所述复合防水卷材的卷绕方向，且所述第一切割线的两端分别对应延伸至所述第一隔离层的两个边缘，所述第二切割线的两端分别对应延伸至所述第二隔离层的两个边缘，多条所述第一切割线在所述第一隔离层上的位置与多条所述第二切割线在所述第二隔离层上的位置一一对应。
6.一种复合防水卷材的制备方法，其特征在于，包括：
步骤S1：采用聚酯毡、玻纤毡和玻纤增强聚酯毡混合制成胎基层，将胎基层放入油温为120℃的浸油池内浸油20分钟；
步骤S2：将沥青原料加入到温度在140℃的配料罐内，同时加入机油、滑石粉，并持续搅拌并加热至175℃，后加入改性剂、古马隆树脂、沥青改性增粘剂、高密度聚乙烯，并胶体磨研磨2.5小时后加入石墨，再继续搅拌15分钟后倒入到搅拌罐，制成沥青层；
步骤S3：在浸油后的胎基层的上表面上复合第一沥青层，在浸油后的胎基层的下表面下复合第二沥青层；
步骤S4：利用高分子材料和橡胶材料中的至少一种材料，在以上步骤形成的结构的上表面上覆盖第一隔离层，在以上步骤形成的结构的下表面下覆盖第二隔离层；
步骤S5：对以上步骤形成的结构进行冷却与缠卷处理，获得复合防水卷材。
7.根据权利要求6所述的复合防水卷材的制备方法，其特征在于，在所述步骤S3之后，以及在所述步骤S4之前，还包括：
步骤S6：在以上步骤形成的结构的上表面上形成第一加强层，在以上步骤形成的结构的下表面下形成第二加强层。
8.根据权利要求7所述的复合防水卷材的制备方法，其特征在于，在所述步骤S6中，形成第一加强层和第二加强层所采用的原材料为无纺布。
9.根据权利要求7所述的复合防水卷材的制备方法，其特征在于，在所述步骤S3和所述步骤S6之间还包括：
步骤S7：覆压第一隔热层至第一沥青层的上表面上，覆压第二隔热层至第二沥青层的下表面下。
10.根据权利要求6～9任一项所述的复合防水卷材的制备方法，其特征在于，在步骤S4之后，以及在步骤S5之前，还包括：
步骤S8：在第一隔离层远离第一沥青层的表面上，每隔一定的长度压制一条第一切割线，在第二隔离层远离第二沥青层的表面上，每隔一定的长度压制一条第二切割线；其中，第一切割线和第二切割线的延伸方向均垂直于复合防水卷材的卷绕方向，且第一切割线的两端分别对应延伸至第一隔离层的两个边缘，第二切割线的两端分别对应延伸至第二隔离层的两个边缘，多条第一切割线在第一隔离层上的位置与多条第二切割线在第二隔离层上的位置一一对应。