CN106833851A - A kind of cold punching die releasing agent for lifting demoulding efficiency - Google Patents
A kind of cold punching die releasing agent for lifting demoulding efficiency Download PDFInfo
- Publication number
- CN106833851A CN106833851A CN201611230731.0A CN201611230731A CN106833851A CN 106833851 A CN106833851 A CN 106833851A CN 201611230731 A CN201611230731 A CN 201611230731A CN 106833851 A CN106833851 A CN 106833851A
- Authority
- CN
- China
- Prior art keywords
- parts
- releasing agent
- punching die
- cold punching
- die releasing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of cold punching die releasing agent for lifting demoulding efficiency, is made up of the component of following weight portion:19 23 parts of phenyl-trimethylsilicane, 15 18 parts of methyl tribromosilane, 10 15 parts of tetraethyl orthosilicate, 25 28 parts of trimethylsilane alcohol, 0.1 0.2 parts of methylpropene sodium sulfonate, 0.4 0.6 parts of ethylenediamine base propanesulfonate, 24 parts of sodium glycero-phosphate, 0.2 0.4 parts of cocounut oil acyl diglycollic amide, 12 parts of 4 nonyl phenol, 35 parts, No. 46 120 130 parts of machinery oil of isocitric acid trisodium salt, 200 250 parts of deionized water.Obtained cold punching die releasing agent demolding performace of the invention is superior, pollution-free, may be such that the bright and clean pore-free of obtained cast(ing) surface, can greatly reduce the abrasion of casting and mold cavity, protects die cavity, plays a part of lubrication and casting is easy to the demoulding.
Description
Technical field
The invention belongs to releasing agent manufacture field, and in particular to a kind of cold punching die releasing agent of lifting demoulding efficiency.
Background technology
Cold stamping is at normal temperatures, pressure to be applied to plate or hot material on forcing press using stamping die, it is produced modeling
Property deformation or separate so as to obtain a kind of pressure processing method of the part of required shape and size.Cold stamping includes two substantially
Operation:(1)Separation circuit:Stamped workpieces are separated from each other with plate along desired contour line;(2)Forming process:Blank not by
It is plastically deformed under conditions of bad, shape needed for obtaining, the processing method of size and precision.In order that the casting after must being molded
It is easy to depart from, often needs to use releasing agent, releasing agent is a kind of feature processing aid for playing auxiliary disengaging effect, and it is in
Between mould and moulded products, it is prevented from rubber, resin, the product of metal material and glues on the mold surface.In industrial production
In, in order to weaken the adhesion between product and mould or absorption, generally using coating releasing agent in die surface, product connects with mould
Dielectric film layer is formed between contacting surface, the thicknesses of layers is only micron order, and heat endurance is good, the film that is effectively isolated of formation can be with
Die surface is formed and is connected chemically, and isolates mould and product, so that peeling force weakens, allows profiled part quickly to take off easily
Fall.Presently commercially available organosilicon polymer is optimum releasing agent, but it is during use, easily produces acid
Matter, and then corrode metal surface, therefore it is badly in need of a kind of new high performance releasing agent of research and development.
The content of the invention
In order to solve the various drawbacks of existing releasing agent, the present invention provides a kind of lifting demoulding efficiency, wide using scope
Cold punching die releasing agent.
The present invention is achieved by the following technical solutions.
A kind of cold punching die releasing agent for lifting demoulding efficiency, is made up of the component of following weight portion:Phenyl trimethicone
Silane 19-23 parts, 15-18 parts of methyl tribromosilane, tetraethyl orthosilicate 10-15 parts, 25-28 parts of trimethylsilane alcohol, metering system
Sodium sulfonate 0.1-0.2 parts, 0.4-0.6 parts of ethylenediamine base propanesulfonate, sodium glycero-phosphate 2-4 parts, cocounut oil acyl diglycollic amide
0.2-0.4 parts, 1-2 parts of 4- nonyl phenols, 3-5 parts of isocitric acid trisodium salt, No. 46 machinery oil 120-130 parts, deionized water
200-250 parts;
Above-mentioned cocounut oil acyl diglycollic amide pH is 8.5-10.5, and active matter content is 95%, and total amine value is 125-155;
Kinematic viscosity of above-mentioned No. 46 machinery oil at 40 DEG C is 43.2mm2/ s, lightning is 220 DEG C, and pour point is -12 DEG C.
Specifically, the cold punching die releasing agent preparation method of above-mentioned lifting demoulding efficiency is comprised the following steps:(1)By benzene
After base trimethyl silane, methyl tribromosilane, tetraethyl orthosilicate, the mixing of trimethylsilane alcohol, it is put into reactor, stirs 20min
Afterwards, methylpropene sodium sulfonate is added thereto to, controls the temperature of reactor for 75-80 DEG C, mixing speed is 200r/min, reaction
After 3-4h, mixed solution is obtained standby;(2)By ethylenediamine base propanesulfonate, sodium glycero-phosphate, cocounut oil acyl diglycollic amide, 4-
Nonyl phenol, isocitric acid trisodium salt are added in No. 46 machine oil, after persistently stirring 30min using the rotating speed of 300r/min, Xiang Qi
Middle addition deionized water, after continuing to stir 70min, is added thereto to step(1)Gained mixed solution, after continuing to stir 30min,
Cold punching die releasing agent is obtained.
Specifically, above-mentioned cold punching die releasing agent is diluted using preceding with the 65-75 times of clear water for weighing.
Technical scheme more than, the beneficial effects of the invention are as follows:
Obtained cold punching die releasing agent demolding performace of the invention is superior, pollution-free, may be such that obtained cast(ing) surface is bright and clean
Pore-free, can greatly reduce the abrasion of casting and mold cavity, protect die cavity, play lubrication and casting is easy to the work of the demoulding
With.The present invention mixes obtained organosilane polymer and No. 46 machine oil, wherein No. 46 machine oil are main in main releasing agent
Composition, organosilane polymer is assisted demoulding material, and both act synergistically, and can mutually improve respective demolding performace, can be
Cast(ing) surface forms that a layer thickness is uniform, the micron order film of good stability, and can greatly reduce produce during cold stamping
Raw frictional heat, makes metal flow uninterrupted and is avoided that corrugation or is broken, and greatly improves obtained cast(ing) surface
Smoothness, and cause that casting is easy to carry out the operation such as follow-up japanning;Ethylenediamine base propanesulfonate and sodium glycero-phosphate collaboration are made
With, the mobility of releasing agent can be further lifted, the uniformity of micron order film is lifted, and cause that casting is easy to the demoulding, no
Damage mold cavity;4- nonyl phenols and isocitric acid trisodium salt act synergistically, and can extend the holding time of releasing agent, anti-anti-avulsion
Mould agent occurs to aoxidize or assemble to form precipitation during storage, improves the quality of releasing agent.
Specific embodiment
Following examples are used for illustrating the present invention, but can not be used for limiting the scope of the present invention, the reality used in embodiment
The condition of applying can be for further adjustments according to the condition of producer, and unaccounted implementation condition is usually conventional laboratory conditions.
Embodiment 1
A kind of cold punching die releasing agent for lifting demoulding efficiency, is made up of the component of following weight portion:Phenyl-trimethylsilicane
19 parts, 15 parts of methyl tribromosilane, 10 parts of tetraethyl orthosilicate, 25 parts of trimethylsilane alcohol, 0.1 part of methylpropene sodium sulfonate, second two
0.4 part of amido propanesulfonate, 2 parts of sodium glycero-phosphate, 0.2 part of cocounut oil acyl diglycollic amide, 1 part of 4- nonyl phenols, isocitric acid
3 parts, No. 46 120 parts of machinery oil of trisodium salt, 200 parts of deionized water;
Above-mentioned cocounut oil acyl diglycollic amide pH is 8.5, and active matter content is 95%, and total amine value is 125;
Kinematic viscosity of above-mentioned No. 46 machinery oil at 40 DEG C is 43.2mm2/ s, lightning is 220 DEG C, and pour point is -12 DEG C.
Specifically, the cold punching die releasing agent preparation method of above-mentioned lifting demoulding efficiency is comprised the following steps:(1)By benzene
After base trimethyl silane, methyl tribromosilane, tetraethyl orthosilicate, the mixing of trimethylsilane alcohol, it is put into reactor, stirs 20min
Afterwards, methylpropene sodium sulfonate is added thereto to, controls the temperature of reactor for 75 DEG C, mixing speed is 200r/min, reacts 3-
After 4h, mixed solution is obtained standby;(2)By ethylenediamine base propanesulfonate, sodium glycero-phosphate, cocounut oil acyl diglycollic amide, 4- nonyls
Base phenol, isocitric acid trisodium salt are added in No. 46 machine oil, after persistently stirring 30min using the rotating speed of 300r/min, thereto
Deionized water is added, after continuing to stir 70min, step is added thereto to(1)Gained mixed solution, after continuing to stir 30min, system
Obtain cold punching die releasing agent.
Specifically, above-mentioned cold punching die releasing agent is diluted using preceding with 65 times of clear water of weight.
Embodiment 2
A kind of cold punching die releasing agent for lifting demoulding efficiency, is made up of the component of following weight portion:Phenyl-trimethylsilicane
21 parts, 17 parts of methyl tribromosilane, 13 parts of tetraethyl orthosilicate, 27 parts of trimethylsilane alcohol, 0.1 part of methylpropene sodium sulfonate, second two
0.5 part of amido propanesulfonate, 3 parts of sodium glycero-phosphate, 0.3 part of cocounut oil acyl diglycollic amide, 1 part of 4- nonyl phenols, isocitric acid
4 parts, No. 46 125 parts of machinery oil of trisodium salt, 225 parts of deionized water;
Above-mentioned cocounut oil acyl diglycollic amide pH is 9.0, and active matter content is 95%, and total amine value is 140;
Kinematic viscosity of above-mentioned No. 46 machinery oil at 40 DEG C is 43.2mm2/ s, lightning is 220 DEG C, and pour point is -12 DEG C.
Specifically, the cold punching die releasing agent preparation method of above-mentioned lifting demoulding efficiency is comprised the following steps:(1)By benzene
After base trimethyl silane, methyl tribromosilane, tetraethyl orthosilicate, the mixing of trimethylsilane alcohol, it is put into reactor, stirs 20min
Afterwards, methylpropene sodium sulfonate is added thereto to, controls the temperature of reactor for 78 DEG C, mixing speed is 200r/min, reaction
After 3.5h, mixed solution is obtained standby;(2)By ethylenediamine base propanesulfonate, sodium glycero-phosphate, cocounut oil acyl diglycollic amide, 4-
Nonyl phenol, isocitric acid trisodium salt are added in No. 46 machine oil, after persistently stirring 30min using the rotating speed of 300r/min, Xiang Qi
Middle addition deionized water, after continuing to stir 70min, is added thereto to step(1)Gained mixed solution, after continuing to stir 30min,
Cold punching die releasing agent is obtained.
Specifically, above-mentioned cold punching die releasing agent is diluted using preceding with 70 times of clear water of weight.
Embodiment 3
A kind of cold punching die releasing agent for lifting demoulding efficiency, is made up of the component of following weight portion:Phenyl-trimethylsilicane
23 parts, 18 parts of methyl tribromosilane, 15 parts of tetraethyl orthosilicate, 28 parts of trimethylsilane alcohol, 0.2 part of methylpropene sodium sulfonate, second two
0.6 part of amido propanesulfonate, 4 parts of sodium glycero-phosphate, 0.4 part of cocounut oil acyl diglycollic amide, 2 parts of 4- nonyl phenols, isocitric acid
5 parts, No. 46 130 parts of machinery oil of trisodium salt, 250 parts of deionized water;
Above-mentioned cocounut oil acyl diglycollic amide pH is 10.5, and active matter content is 95%, and total amine value is 155;
Kinematic viscosity of above-mentioned No. 46 machinery oil at 40 DEG C is 43.2mm2/ s, lightning is 220 DEG C, and pour point is -12 DEG C.
Specifically, the cold punching die releasing agent preparation method of above-mentioned lifting demoulding efficiency is comprised the following steps:(1)By benzene
After base trimethyl silane, methyl tribromosilane, tetraethyl orthosilicate, the mixing of trimethylsilane alcohol, it is put into reactor, stirs 20min
Afterwards, methylpropene sodium sulfonate is added thereto to, controls the temperature of reactor for 80 DEG C, mixing speed is 200r/min, reacts 3-
After 4h, mixed solution is obtained standby;(2)By ethylenediamine base propanesulfonate, sodium glycero-phosphate, cocounut oil acyl diglycollic amide, 4- nonyls
Base phenol, isocitric acid trisodium salt are added in No. 46 machine oil, after persistently stirring 30min using the rotating speed of 300r/min, thereto
Deionized water is added, after continuing to stir 70min, step is added thereto to(1)Gained mixed solution, after continuing to stir 30min, system
Obtain cold punching die releasing agent.
Specifically, above-mentioned cold punching die releasing agent is diluted using preceding with 75 times of clear water of weight.
By commercially available common releasing agent in obtained releasing agent in embodiment in the present invention 1,2,3 and comparative example in Anhui horse
The Metal Processing Factory of Anshan one is tested, and its performance comparison result is as shown in table 1:
The performance characteristics of the different releasing agents of table 1
Project | Demolding performace | Cast(ing) surface brightness | Percent defective |
Embodiment 1 | It is excellent | It is excellent | It is low |
Embodiment 2 | It is excellent | It is excellent | It is low |
Embodiment 3 | It is excellent | It is excellent | It is low |
Comparative example | In | In | It is high |
As shown in Table 1, the obtained cold punching die releasing agent of the present invention, stripping result is notable, and obtained casting quality is preferably,
Surface gloss is good, does not have any influence on post-production.
It should be appreciated that application of the invention is not limited to above-mentioned citing, and for those of ordinary skills, can
To be improved according to the above description or converted, all these modifications and variations should all belong to the guarantor of appended claims of the present invention
Shield scope.
Claims (3)
1. it is a kind of lifted demoulding efficiency cold punching die releasing agent, it is characterised in that be made up of the component of following weight portion:Benzene
19-23 parts of base trimethyl silane, 15-18 parts of methyl tribromosilane, tetraethyl orthosilicate 10-15 parts, 25-28 parts of trimethylsilane alcohol,
Methylpropene sodium sulfonate 0.1-0.2 parts, 0.4-0.6 parts of ethylenediamine base propanesulfonate, sodium glycero-phosphate 2-4 parts, cocounut oil acyl diethyl
Alkylolamides 0.2-0.4 parts, 1-2 parts of 4- nonyl phenols, 3-5 parts of isocitric acid trisodium salt, No. 46 machinery oil 120-130 parts, go from
Sub- water 200-250 parts;
Above-mentioned cocounut oil acyl diglycollic amide pH is 8.5-10.5, and active matter content is 95%, and total amine value is 125-155;
Kinematic viscosity of above-mentioned No. 46 machinery oil at 40 DEG C is 43.2mm2/ s, lightning is 220 DEG C, and pour point is -12 DEG C.
2. the cold punching die releasing agent of a kind of lifting demoulding efficiency according to claim 1, it is characterised in that prepare
Method is comprised the following steps:(1)Phenyl-trimethylsilicane, methyl tribromosilane, tetraethyl orthosilicate, trimethylsilane alcohol are mixed
Afterwards, it is put into reactor, after stirring 20min, is added thereto to methylpropene sodium sulfonate, the temperature for controlling reactor is 75-80
DEG C, mixing speed is 200r/min, after reaction 3-4h, mixed solution is obtained standby;(2)By ethylenediamine base propanesulfonate, glycerine
Sodium phosphate, cocounut oil acyl diglycollic amide, 4- nonyl phenols, isocitric acid trisodium salt are added in No. 46 machine oil, using 300r/min
Rotating speed persistently stir 30min after, be added thereto to deionized water, after continuing to stir 70min, be added thereto to step(1)Institute
Mixed solution is obtained, after continuing to stir 30min, cold punching die releasing agent is obtained.
3. the cold punching die releasing agent of a kind of lifting demoulding efficiency according to claim 1, it is characterised in that above-mentioned
Cold punching die releasing agent is diluted using preceding with the 65-75 times of clear water for weighing.