CN103756763A - Stainless steel stamping tension lubricating oil - Google Patents
Stainless steel stamping tension lubricating oil Download PDFInfo
- Publication number
- CN103756763A CN103756763A CN201310726159.7A CN201310726159A CN103756763A CN 103756763 A CN103756763 A CN 103756763A CN 201310726159 A CN201310726159 A CN 201310726159A CN 103756763 A CN103756763 A CN 103756763A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- parts
- oil
- stainless steel
- butyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a stainless steel stamping tension lubricating oil which comprises the following components in parts by mass: 1-2 parts of glycerin monostearate, 55 parts of LN32 mechanical oil, 8 parts of chlorinated paraffin, 4 parts of dimethyl silicon oil, 19 parts of phosphorous acid di-n-butyl phosphate, 8 parts of lead naphthenate, 23 parts of triethanolamine oleate, 9 parts of poly(n-butyl) vinyl ether, 35 parts of transformer oil, 17 parts of vulcanized whale oil, 2 parts of 2.6-di-tert-butyl phenol and 1 part of hydroxypropyl methyl cellulose. The stainless steel stamping tension lubricating oil is good in lubrication and cooling property and easy to demold, and is capable of preventing a stamped surface from scratch or rusting, ensuring surface smoothness and cleanness, and meeting the direct assembling requirements.
Description
Technical field
The present invention relates to stainless steel plate punch drawing lube oil.
Background technology
In the plate stamping course of processing, metallic substance produces plasticity shearing strain, between shear surface and the mold work surface producing as generation strong friction, make local generation high temperature and cause " seam " and adhesive wear, need to use and there is the punch drawing lube oil that reduces friction, cools and act on, to form pressure-and heat-resistance and tough and tensile composite lubricating film in metallic surface, newborn shear surface and die-face are separated.There are the following problems for existing stainless steel plate punch drawing lube oil: between workpiece and mould, meeting produces serious adhesion and makes demoulding difficulty, can not realize beat type to work continuously, and affects production efficiency; After workpiece punching stretch forming, must carry out the clean of rear road routine, otherwise workpiece surface can not reach the requirement that direct assembling is used; After workpiece punching stretch, its surface has scuffing and microscopic fibers to tear phenomenon.
Summary of the invention
The object of the present invention is to provide a kind of stainless steel plate punch drawing lube oil, it is lubricated and cooling performance is good, can prevent that scratching from appearring in stamped workpieces surface, corrosion, can guarantee that surface smoothness, degree of cleaning are easy to meet direct matching requirements and the demoulding.
For achieving the above object, technical scheme of the present invention is a kind of stainless steel plate punch drawing lube oil of design, following component, consists of:
1-2 mass parts Zerol,
55 mass parts LN32 machinery oil,
8 mass parts clorafins,
4 mass parts dimethyl silicone oils,
19 mass parts di-n-butyl phosphites,
8 mass parts lead naphthenates,
23 mass parts triethanolamine oleates,
9 mass parts are gathered n-butyl vinyl ether,
35 mass parts transformer oil,
17 mass parts sulfuration haco oils,
2 mass parts 2.6-di-tert-butylphenols,
1 mass parts Vltra tears.
Advantage of the present invention and beneficial effect are: a kind of stainless steel plate punch drawing lube oil is provided, it is lubricated and cooling performance is good, can prevent that scratching from appearring in stamped workpieces surface, corrosion, can guarantee that surface smoothness, degree of cleaning are easy to meet direct matching requirements and the demoulding.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples are only for technical scheme of the present invention is more clearly described, and can not limit the scope of the invention with this.
The concrete technical scheme of implementing of the present invention is:
Embodiment 1
A kind of stainless steel plate punch drawing lube oil, is comprised of following component:
1 mass parts Zerol,
55 mass parts LN32 machinery oil,
8 mass parts clorafins,
4 mass parts dimethyl silicone oils,
19 mass parts di-n-butyl phosphites,
8 mass parts lead naphthenates,
23 mass parts triethanolamine oleates,
9 mass parts are gathered n-butyl vinyl ether,
35 mass parts transformer oil,
17 mass parts sulfuration haco oils,
2 mass parts 2.6-di-tert-butylphenols,
1 mass parts Vltra tears.
Embodiment 2
A kind of stainless steel plate punch drawing lube oil, is comprised of following component:
2 mass parts Zerols,
55 mass parts LN32 machinery oil,
8 mass parts clorafins,
4 mass parts dimethyl silicone oils,
19 mass parts di-n-butyl phosphites,
8 mass parts lead naphthenates,
23 mass parts triethanolamine oleates,
9 mass parts are gathered n-butyl vinyl ether,
35 mass parts transformer oil,
17 mass parts sulfuration haco oils,
2 mass parts 2.6-di-tert-butylphenols,
1 mass parts Vltra tears.
Embodiment 3
A kind of stainless steel plate punch drawing lube oil, is comprised of following component:
1.2 mass parts Zerols,
55 mass parts LN32 machinery oil,
8 mass parts clorafins,
4 mass parts dimethyl silicone oils,
19 mass parts di-n-butyl phosphites,
8 mass parts lead naphthenates,
23 mass parts triethanolamine oleates,
9 mass parts are gathered n-butyl vinyl ether,
35 mass parts transformer oil,
17 mass parts sulfuration haco oils,
2 mass parts 2.6-di-tert-butylphenols,
1 mass parts Vltra tears.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, do not departing under the prerequisite of the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (1)
1. stainless steel plate punch drawing lube oil, is characterized in that, following component, consists of:
1-2 mass parts Zerol,
55 mass parts LN32 machinery oil,
8 mass parts clorafins,
4 mass parts dimethyl silicone oils,
19 mass parts di-n-butyl phosphites,
8 mass parts lead naphthenates,
23 mass parts triethanolamine oleates,
9 mass parts are gathered n-butyl vinyl ether,
35 mass parts transformer oil,
17 mass parts sulfuration haco oils,
2 mass parts 2.6-di-tert-butylphenols,
1 mass parts Vltra tears.