CN103756763B - Stainless steel plate punch drawing lube oil - Google Patents
Stainless steel plate punch drawing lube oil Download PDFInfo
- Publication number
- CN103756763B CN103756763B CN201310726159.7A CN201310726159A CN103756763B CN 103756763 B CN103756763 B CN 103756763B CN 201310726159 A CN201310726159 A CN 201310726159A CN 103756763 B CN103756763 B CN 103756763B
- Authority
- CN
- China
- Prior art keywords
- mass parts
- steel plate
- stainless steel
- oil
- plate punch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of stainless steel plate punch drawing lube oil, be made up of following component: 1-2 mass parts Zerol, 55 mass parts LN32 machinery oil, 8 mass parts clorafins, 4 mass parts dimethyl silicone oils, 19 mass parts di-n-butyl phosphites, 8 mass parts lead naphthenates, 23 mass parts triethanolamine oleates, 9 mass parts gather n-butyl vinyl ether, 35 mass parts transformer oil, 17 mass parts sulfuration haco oils, 2 mass parts 2.6-di-tert-butylphenols, 1 mass parts Vltra tears.Stainless steel plate punch drawing lube oil of the present invention, its lubrication and cooling performance good, can prevent stamped workpieces surface from occurring scratching, corrosion, can ensure that surface smoothness, degree of cleaning are to meet direct matching requirements and the demoulding is easy.
Description
Technical field
The present invention relates to stainless steel plate punch drawing lube oil.
Background technology
In the plate stamping course of processing, metallic substance produces plasticity shearing strain, as there is strong friction between the shear surface produced and mold working surface, local is then made to produce high temperature and cause " seam " and adhesive wear, need to use the punch drawing lube oil with minimizing friction, the effect of cooling, to forming pressure-and heat-resistance and tough and tensile composite lubricating film in metallic surface, the shear surface of new life and die-face are separated.There are the following problems for existing stainless steel plate punch drawing lube oil: can produce serious adhesion between workpiece and mould and make demoulding difficulty, can not realize beat type works continuously, and affects production efficiency; After workpiece punching stretch forming, the clean of rear road routine must be carried out, otherwise workpiece surface can not reach the requirement that directly assembling uses; After workpiece punching stretch, its surface has scuffing and microscopic fibers to tear phenomenon.
Summary of the invention
The object of the present invention is to provide a kind of stainless steel plate punch drawing lube oil, its lubrication and cooling performance good, can prevent stamped workpieces surface from occurring scratching, corrosion, can ensure that surface smoothness, degree of cleaning are to meet direct matching requirements and the demoulding is easy.
For achieving the above object, technical scheme of the present invention is a kind of stainless steel plate punch drawing lube oil of design, is made up of following component:
1-2 mass parts Zerol,
55 mass parts LN32 machinery oil,
8 mass parts clorafins,
4 mass parts dimethyl silicone oils,
19 mass parts di-n-butyl phosphites,
8 mass parts lead naphthenates,
23 mass parts triethanolamine oleates,
9 mass parts gather n-butyl vinyl ether,
35 mass parts transformer oil,
17 mass parts sulfuration haco oils,
2 mass parts 2.6-di-tert-butylphenols,
1 mass parts Vltra tears.
Advantage of the present invention and beneficial effect are: provide a kind of stainless steel plate punch drawing lube oil, its lubrication and cooling performance good, can prevent stamped workpieces surface from occurring scratching, corrosion, can ensure that surface smoothness, degree of cleaning are to meet direct matching requirements and the demoulding is easy.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of stainless steel plate punch drawing lube oil, is made up of following component:
1 mass parts Zerol,
55 mass parts LN32 machinery oil,
8 mass parts clorafins,
4 mass parts dimethyl silicone oils,
19 mass parts di-n-butyl phosphites,
8 mass parts lead naphthenates,
23 mass parts triethanolamine oleates,
9 mass parts gather n-butyl vinyl ether,
35 mass parts transformer oil,
17 mass parts sulfuration haco oils,
2 mass parts 2.6-di-tert-butylphenols,
1 mass parts Vltra tears.
Embodiment 2
A kind of stainless steel plate punch drawing lube oil, is made up of following component:
2 mass parts Zerols,
55 mass parts LN32 machinery oil,
8 mass parts clorafins,
4 mass parts dimethyl silicone oils,
19 mass parts di-n-butyl phosphites,
8 mass parts lead naphthenates,
23 mass parts triethanolamine oleates,
9 mass parts gather n-butyl vinyl ether,
35 mass parts transformer oil,
17 mass parts sulfuration haco oils,
2 mass parts 2.6-di-tert-butylphenols,
1 mass parts Vltra tears.
Embodiment 3
A kind of stainless steel plate punch drawing lube oil, is made up of following component:
1.2 mass parts Zerols,
55 mass parts LN32 machinery oil,
8 mass parts clorafins,
4 mass parts dimethyl silicone oils,
19 mass parts di-n-butyl phosphites,
8 mass parts lead naphthenates,
23 mass parts triethanolamine oleates,
9 mass parts gather n-butyl vinyl ether,
35 mass parts transformer oil,
17 mass parts sulfuration haco oils,
2 mass parts 2.6-di-tert-butylphenols,
1 mass parts Vltra tears.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (1)
1. stainless steel plate punch drawing lube oil, is characterized in that, is made up of following component:
1-2 mass parts Zerol,
55 mass parts LN32 machinery oil,
8 mass parts clorafins,
4 mass parts dimethyl silicone oils,
19 mass parts di-n-butyl phosphites,
8 mass parts lead naphthenates,
23 mass parts triethanolamine oleates,
9 mass parts gather n-butyl vinyl ether,
35 mass parts transformer oil,
17 mass parts sulfuration haco oils,
2 mass parts 2.6-di-tert-butylphenols,
1 mass parts Vltra tears.