CN106830697A - A kind of method for preparing safety glass - Google Patents
A kind of method for preparing safety glass Download PDFInfo
- Publication number
- CN106830697A CN106830697A CN201710138852.0A CN201710138852A CN106830697A CN 106830697 A CN106830697 A CN 106830697A CN 201710138852 A CN201710138852 A CN 201710138852A CN 106830697 A CN106830697 A CN 106830697A
- Authority
- CN
- China
- Prior art keywords
- glass
- heating furnace
- safety glass
- preparing
- silk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of method for preparing safety glass, it is characterised in that it is comprised the following steps：Decontamination, removal of impurities, silk-screen, sintering, heating, insulation, cooling, machine-shaping treatment, chemical tempering step are processed, and used in sintering step and the good glass of silk-screen is positioned in heating furnace in the way of front and rear surfaces do not contact heating furnace panel.The method that the present invention is used causes glass to burst or metaboly when avoiding contact heating furnace in safety glass surface in traditional handicraft because of temperature Centralized, and pass through hang and heated, further such that glass is heated evenly when heating furnace is sintered, the uniformity of glass glazing can be further improved.
Description
Technical field
The present invention relates to safety glass field, more particularly to a kind of method for preparing safety glass.
Background technology
In traditional safety glass production technology, it is necessary to will be carried out after high-temperature glaze silk-screen to glass surface tempering or heat into
Row sintering, and accordingly broken through because technology does not have, must be placed through for glass and be placed on by traditional sintering technology
Sintered in high temperature plate, but the method may be only available for the larger glass of thickness, and if using thin glass（1mm and following）, meeting
Glass is caused to burst or deform, it is impossible to meet demand.
In addition, in order that there is the effect of surface frosted, traditional way is using chemical etching on thin tempering glass
Method is processed, but undoubtedly engraving method is less efficient, and serious to environmental pollution, fails to meet demand.
The content of the invention
The technical problem to be solved in the present invention is：For above-mentioned the deficiencies in the prior art, there is provided one kind prepares safety glass
Method.
The present invention solve its technical problem solution be：A kind of method for preparing safety glass, it is characterised in that it
Comprise the following steps：
（1）Glass basis is pre-processed, stain, the impurity of glass surface is removed；
（2）Using silk-screen printing technique, feature high temperature glaze is printed on the glass surface；
（3）By the good glass of silk-screen by front and rear surfaces do not contact heating furnace panel in the way of be positioned in heating furnace, after will heating
Furnace temperature was warming up to 500 DEG C -800 DEG C in the way of 5-10 DEG C by 10 minutes, after be incubated 1-5 hours at a temperature of it；
（4）Heating in-furnace temperature was down to room temperature in the way of 5-10 DEG C by 10 minutes；Then glass is taken out；
（5）The glass of taking-up is processed forming processes；
（6）Chemical tempering is integrally carried out to glass, after obtain final safety glass.
As one of preferred technical scheme, it is characterised in that described thickness of glass is 0.1mm-1mm.
As one of preferred technical scheme, it is characterised in that described feature high temperature glaze is have surface after applying
The high temperature glaze of frosted finish effect.
As one of preferred technical scheme, it is characterised in that described step（3）In glass with hang place
In heating furnace.
As one of preferred technical scheme, it is characterised in that described step（5）Using cold-formed treatment.
As one of preferred technical scheme, it is characterised in that described glass basis ordinary plate glass or can carve,
The simple glass of embossing.
The beneficial effects of the invention are as follows：
（1）The present invention uses and the good glass of silk-screen is positioned in heating furnace in the way of front and rear surfaces do not contact heating furnace panel
（Can be further placed in heating furnace by hang）, thus avoid safety glass surface contact heating in traditional handicraft
Cause glass to burst or metaboly because of temperature Centralized during stove, and pass through hang and heated, can be further such that glass
Glass is heated evenly when heating furnace is sintered, and further improves the uniformity of glass glazing；
（2）The present invention is attached to safety glass surface by by the glaze of frosted, is entered with substituting conventionally employed chemical etching mode
Row frosted is processed, and in this way under basis, it can be ensured that while thin tempering glass has frosted finish effect, reduces the shadow to environment
Ring, improve producing feasibility.
Specific embodiment
The technique effect of design of the invention, concrete structure and generation is carried out below with reference to embodiment clear, complete
Ground description, to be completely understood by the purpose of the present invention, feature and effect.Obviously, described embodiment is of the invention one
Section Example, rather than whole embodiments, based on embodiments of the invention, those skilled in the art is not paying creativeness
The other embodiment obtained on the premise of work, belongs to the scope of protection of the invention.
Embodiment：A kind of method for preparing safety glass, it is comprised the following steps：
（1）Glass basis is pre-processed, stain, the impurity of glass surface is removed；
（2）Using silk-screen printing technique, feature high temperature glaze is printed on the glass surface；
（3）By the good glass of silk-screen by front and rear surfaces do not contact heating furnace panel in the way of be positioned in heating furnace, after will heating
Furnace temperature was warming up to 500 DEG C 500 DEG C in the way of 10 DEG C by 10 minutes, after be incubated 3 hours at a temperature of it；
（4）Heating in-furnace temperature was down to room temperature in the way of 10 DEG C by 10 minutes；Then glass is taken out；
（5）The glass of taking-up is processed forming processes；
（6）Chemical tempering is integrally carried out to glass, after obtain final safety glass.
The above method is positioned over by way of using and the good glass of silk-screen is not contacted heating furnace panel with front and rear surfaces
In heating furnace（Can be further placed in heating furnace by hang）, thus avoid safety glass surface in traditional handicraft
Glass is caused to burst or metaboly because of temperature Centralized during contact heating furnace.
As one of preferred embodiment, it is characterised in that described thickness of glass is 0.1mm-1mm.Such as by glass
The method that thickness is positioned over heating furnace panel for the safety glass of 0.1mm-1mm, easily causes that glass is produced in annealing furnace quick-fried
Split or metaboly, and " the good glass of silk-screen is put in the way of front and rear surfaces do not contact heating furnace panel in using embodiment
Put " by avoid contact of the thin glass surface with annealing furnace, it is to avoid explosion or deformation situation.
As one of preferred embodiment, it is characterised in that described feature high temperature glaze after applying to have surface
The high temperature glaze of frosted finish effect.Present embodiment is attached to safety glass surface by by the glaze of frosted, is adopted with substituting tradition
Frosted treatment is carried out with chemical etching mode, in this way under basis, it can be ensured that thin tempering glass has the colleague of frosted finish effect,
The influence to environment is reduced, producing feasibility is improved.
As one of preferred embodiment, it is characterised in that described step（3）In glass with hang place
In heating furnace.Heated by hang, can be further such that glass be heated evenly when heating furnace is sintered, further
Improve the uniformity of glass glazing.
As one of preferred embodiment, it is characterised in that described step（5）Using cold-formed treatment.
As one of preferred embodiment, it is characterised in that described glass basis ordinary plate glass or can carve,
The simple glass of embossing.Which is applicable to the glass baseplate of polymorphic type.
Better embodiment of the invention is illustrated above, but the invention is not limited to the implementation
Example, those of ordinary skill in the art can also make a variety of equivalent modifications or replace on the premise of without prejudice to spirit of the invention
Change, these equivalent modifications or replacement are all contained in the application claim limited range.
Claims (6)
1. a kind of method for preparing safety glass, it is characterised in that it is comprised the following steps：
（1）Glass basis is pre-processed, stain, the impurity of glass surface is removed；
（2）Using silk-screen printing technique, feature high temperature glaze is printed on the glass surface；
（3）By the good glass of silk-screen by front and rear surfaces do not contact heating furnace panel in the way of be positioned in heating furnace, after will heating
Furnace temperature was warming up to 500 DEG C -800 DEG C in the way of 5-10 DEG C by 10 minutes, after be incubated 1-5 hours at a temperature of it；
（4）Heating in-furnace temperature was down to room temperature in the way of 5-10 DEG C by 10 minutes；Then glass is taken out；
（5）The glass of taking-up is processed forming processes；
（6）Chemical tempering is integrally carried out to glass, after obtain final safety glass.
2. the method for preparing safety glass according to claim 1, it is characterised in that described thickness of glass is 0.1mm-
1mm。
3. the method for preparing safety glass according to any one claim of claim 1 or 2, it is characterised in that institute
The feature high temperature glaze stated is the high temperature glaze after applying with surface frosted effect.
4. the method for preparing safety glass according to claim 1, it is characterised in that described step（3）In glass
It is placed in heating furnace with hang.
5. the method for preparing safety glass according to claim 1, it is characterised in that described step（5）Added using cold
Work forming processes.
6. the method for preparing safety glass according to any one claim of claim 1 or 2, it is characterised in that institute
The glass basis ordinary plate glass stated or the simple glass that can be carved, be embossed.