CN106827695A - A kind of thermal fabric - Google Patents

A kind of thermal fabric Download PDF

Info

Publication number
CN106827695A
CN106827695A CN201510874521.4A CN201510874521A CN106827695A CN 106827695 A CN106827695 A CN 106827695A CN 201510874521 A CN201510874521 A CN 201510874521A CN 106827695 A CN106827695 A CN 106827695A
Authority
CN
China
Prior art keywords
fabric
yarn
fiber
wool
reflectivity
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510874521.4A
Other languages
Chinese (zh)
Inventor
钟俊杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510874521.4A priority Critical patent/CN106827695A/en
Publication of CN106827695A publication Critical patent/CN106827695A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of thermal fabric, it is characterised in that：The strong rear fabric of reflectivity including outer layer（3）The front fabric weak with the reflectivity of internal layer（1）, the rear fabric（3）With front fabric（1）Between be provided with heat preservation layer（2）.A kind of a kind of thermal fabric of composite material of the present invention, positive and negative is respectively adopted the strong rear fabric of reflectivity and the weak front fabric of reflectivity is made, and may be reversed counter wearing, the big area of day and night temperature, when daytime is hotter, the one side of the strong rear fabric of reflectivity is through outside, reaches the effect of cooling；When evening is colder, the one side that the weak dark face of reflectivity is come is through outside, reaches the effect of insulation.

Description

A kind of thermal fabric
Technical field
The present invention relates to a kind of thermal fabric, belong to fabric technical field.
Background technology
Traditional fabric is the use of a clothing one, designed according to season, the big area of day and night temperature again, this kind of fabric cannot a clothing two use, it is easily too hot or catch cold, and it is common such as down jackets, the fabric product such as cotton clothes, it is many that product sewing is carried out using artificial operation sewing machine, by sewing thread trace, form the storage area of eider down or filler, due to the requirement of the particularity and Product Process of product, to ensure product quality and wears effect, there is many requirement and limitation at aspects such as the production materials and production technology for using, especially selected in manufacture material, sewing tech and wear experience aspect there is certain risk.In addition, the fabric for being used of traditional making fabric for cannot two sides use.
The content of the invention
It is an object of the invention to overcome above-mentioned deficiency, there is provided there is no heat losses pipeline, a kind of strong thermal fabric of thermal property.
The object of the present invention is achieved like this：
A kind of thermal fabric, the weak front fabric of the reflectivity of the strong rear fabric of the reflectivity including outer layer and internal layer, heat preservation layer is provided between the rear fabric and front fabric, the heat preservation layer includes fabric and outer shell fabric, there are the spaced adhesive bands being parallel to each other between fabric and outer shell fabric, fabric and outer shell fabric at adhesive bands are bonded together, packing space is formed between fabric and outer shell fabric between adjacent adhesive bands, the front fabric includes woven fabric and knitting fabric, it is bonded together by adhesive pairing between woven fabric and knitting fabric, upper strata stomata is provided with the front fabric, lower floor's stomata is provided with the rear fabric.
Making a kind of process of thermal fabric is：
1）, yarn variety design：
From wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre, to wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre carry out anti pilling treatment, ferment treatment and soft treatment, anti pilling treatment is from phosphate antimony oxide mixture as anti pilling agent, phosphate antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system is processed using protease, albumen enzyme dosage is the 0.1-0.2% of wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；
2）, recombing and spinning process：
Wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre recombing are made wool top, then premenstrual spinning-spun yarn-winder-doubling-double twisting-yarn steaming is made yarn, wherein its number of spun yarn is obtained for 81Nm, 780Z twists/m of the twist；Obtained yarn its be number 80Nm double strand yarn, pool capital 810S twists/m of the twist；Weight percent content of the anti-transparent terylene in warp thread and weft yarn is 30；
3）, postfinishing process：
Prepared yarn is carried out as warp thread and weft yarn to weave to obtain wool fabric fabric, fabric fabric is carried out into Final finishing gets product wool worsted face fabric；Postfinishing process is：Singe-braying-crabbing-drying-sizing-decatizing-finished product；Singe：Speed 90m/min, moderate heat, 1 positive 1 is anti-；Braying：Temperature 60 C, speed 20m/min；Crabbing：Temperature is 80 DEG C, and speed is 18 ms/min；Drying：Temperature is 108 DEG C；Sizing：Temperature is 180 DEG C, 25 seconds time；Decatizing：Temperature is 110 DEG C, 6 minutes.
Compared with prior art, the beneficial effects of the invention are as follows：
A kind of a kind of thermal fabric of composite material of the present invention, positive and negative is respectively adopted the strong rear fabric of reflectivity and the weak front fabric of reflectivity is made, and may be reversed counter wearing, the big area of day and night temperature, when daytime is hotter, the one side of the strong rear fabric of reflectivity is through outside, reaches the effect of cooling；When evening is colder, the one side that the weak dark face of reflectivity is come is through outside, reaches the effect of insulation.
Brief description of the drawings
Fig. 1 is a kind of structural representation of thermal fabric of the invention.
Fig. 2 is the schematic diagram of heat preservation layer in Fig. 1.
Fig. 3 is the schematic diagram of front fabric in Fig. 1.
Fig. 4 is the schematic diagram of rear fabric in Fig. 1.
In figure：Front fabric 1, heat preservation layer 2, fabric 2.1, outer shell fabric 2.2, adhesive bands 2.3, packing space 2.4, rear fabric 3, lower floor's stomata 4, upper strata stomata 5.
Specific embodiment
Referring to Fig. 1 to Fig. 4,The present invention relates to composite thermal fabric,The weak front fabric 1 of the reflectivity of the strong rear fabric 3 of the reflectivity including outer layer and internal layer,May be reversed counter wearing,Heat preservation layer 2 is provided between the rear fabric 3 and front fabric 1,The heat preservation layer 2 includes the outer shell fabric 2.2 of the high-count high density fabric of the fabric 2.1 and individual layer of the high-count high density fabric with individual layer,Between fabric 2.1 and outer shell fabric 2.2 have it is spaced be parallel to each other and width for 2mm-15mm adhesive bands 2.3,Fabric 2.1 and outer shell fabric 2.2 at adhesive bands 2.3 are bonded together,Being formed between fabric 2.1 and outer shell fabric 2.2 between adjacent adhesive bands 2.3 can house packing material such as eider down,The packing space 2.4 of filler etc.,Upper strata stomata 5 is provided with the front fabric 1,Lower floor's stomata 4 is provided with the rear fabric 3.
Making a kind of process of thermal fabric is：
1）, yarn variety design：
From wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre, to wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre carry out anti pilling treatment, ferment treatment and soft treatment, anti pilling treatment is from phosphate antimony oxide mixture as anti pilling agent, phosphate antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system is processed using protease, albumen enzyme dosage is the 0.1-0.2% of wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；
2）, recombing and spinning process：
Wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre recombing are made wool top, then premenstrual spinning-spun yarn-winder-doubling-double twisting-yarn steaming is made yarn, wherein its number of spun yarn is obtained for 81Nm, 780Z twists/m of the twist；Obtained yarn its be number 80Nm double strand yarn, pool capital 810S twists/m of the twist；Weight percent content of the anti-transparent terylene in warp thread and weft yarn is 30；
3）, postfinishing process：
Prepared yarn is carried out as warp thread and weft yarn to weave to obtain wool fabric fabric, fabric fabric is carried out into Final finishing gets product wool worsted face fabric；Postfinishing process is：Singe-braying-crabbing-drying-sizing-decatizing-finished product；Singe：Speed 90m/min, moderate heat, 1 positive 1 is anti-；Braying：Temperature 60 C, speed 20m/min；Crabbing：Temperature is 80 DEG C, and speed is 18 ms/min；Drying：Temperature is 108 DEG C；Sizing：Temperature is 180 DEG C, 25 seconds time；Decatizing：Temperature is 110 DEG C, 6 minutes.

Claims (2)

1. a kind of thermal fabric, it is characterised in that：The strong rear fabric of reflectivity including outer layer（3）The front fabric weak with the reflectivity of internal layer（1）, the rear fabric（3）With front fabric（1）Between be provided with heat preservation layer（2）, the heat preservation layer（2）Including fabric（2.1）And outer shell fabric（2.2）, fabric（2.1）With outer shell fabric（2.2）Between have the spaced adhesive bands being parallel to each other（2.3）, adhesive bands（2.3）The fabric at place（2.1）And outer shell fabric（2.2）It is bonded together, adjacent adhesive bands（2.3）Between fabric（2.1）And outer shell fabric（2.2）Between form packing space（2.4）, the front fabric included woven fabric and knitting fabric, is bonded together by adhesive pairing between woven fabric and knitting fabric, the front fabric（1）On be provided with upper strata stomata（5）, the rear fabric（3）On be provided with lower floor's stomata（4）.
2. a kind of process of the thermal fabric described in claim 1 is made, it is characterised in that：
1）, yarn variety design：
From wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre, to wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre carry out anti pilling treatment, ferment treatment and soft treatment, anti pilling treatment is from phosphate antimony oxide mixture as anti pilling agent, phosphate antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system is processed using protease, albumen enzyme dosage is the 0.1-0.2% of wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；
2）, recombing and spinning process：
Wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre recombing are made wool top, then premenstrual spinning-spun yarn-winder-doubling-double twisting-yarn steaming is made yarn, wherein its number of spun yarn is obtained for 81Nm, 780Z twists/m of the twist；Obtained yarn its be number 80Nm double strand yarn, pool capital 810S twists/m of the twist；Weight percent content of the anti-transparent terylene in warp thread and weft yarn is 30；
3）, postfinishing process：
Prepared yarn is carried out as warp thread and weft yarn to weave to obtain wool fabric fabric, fabric fabric is carried out into Final finishing gets product wool worsted face fabric；Postfinishing process is：Singe-braying-crabbing-drying-sizing- Decatizing-finished product；Singe：Speed 90m/min, moderate heat, 1 positive 1 is anti-；Braying：Temperature 60 C, speed 20m/min；Crabbing：Temperature be 80 DEG C, speed be 18 meters/ Point；Drying：Temperature is 108 DEG C；Sizing：Temperature is 180 DEG C, 25 seconds time；Decatizing：Temperature is 110 DEG C, 6 minutes.
CN201510874521.4A 2015-12-03 2015-12-03 A kind of thermal fabric Pending CN106827695A (en)