CN106579616A - Compound warm-keeping cloth - Google Patents
Compound warm-keeping cloth Download PDFInfo
- Publication number
- CN106579616A CN106579616A CN201510664586.6A CN201510664586A CN106579616A CN 106579616 A CN106579616 A CN 106579616A CN 201510664586 A CN201510664586 A CN 201510664586A CN 106579616 A CN106579616 A CN 106579616A
- Authority
- CN
- China
- Prior art keywords
- fabric
- yarn
- wool fiber
- weaving
- outer shell
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a compound warm-keeping cloth. The fabric is characterized by comprising an outer back fabric (3) with strong reflectivity and an inner front fabric (1) with weak reflectivity, wherein a warm-keeping layer (2) is arranged between the back fabric (3) and the front fabric (1). According to the compound warm-keeping cloth, the front and back sides are respectively made of the back fabric with strong reflectivity and the front fabric with weak reflectivity and can be worn in a turned-over manner, namely, in a region with large diurnal temperature variation, the back fabric with strong reflectivity is worn outside when it is relatively hot in the daytime so as to achieve a cooling effect, and the dark side with weak reflectivity is worn outside when it is relatively cold at night so as to achieve a warm-keeping effect.
Description
Technical field
The present invention relates to a kind of composite thermal fabric, belongs to fabric technical field.
Background technology
Traditional fabric is one use of a clothing, designed according to season, the big area of day and night temperature again, this kind of fabric cannot a clothing dual-purpose, it is easily too hot or catch cold, and it is common such as down jackets, the fabric product such as cotton clothes, it is many that product sewing is carried out using artificial operation sewing machine, by sewing thread trace, form the storage area of eider down or implant, due to the requirement of the particularity and Product Process of product, to ensure product quality and wears effect, there is many requirement and restriction at aspects such as the production materials and production technology for adopting, especially select in manufacture material, sewing tech and there is certain risk in terms of wearing experience.In addition, the fabric for being adopted of traditional making fabric is for cannot two sides use.
The content of the invention
It is an object of the invention to overcome above-mentioned deficiency, there is provided there is no longer heat losses pipeline, a kind of strong composite thermal fabric of thermal property.
The object of the present invention is achieved like this:
A kind of composite thermal fabric, the composite material thermal fabric includes the weak front fabric of the reflexive of the strong rear fabric of the reflexive of outer layer and internal layer, warming layer is provided between the rear fabric and front fabric, the warming layer includes fabric and outer shell fabric, there are between fabric and outer shell fabric the spaced adhesive bands being parallel to each other, fabric and outer shell fabric at adhesive bands is bonded together, packing space is formed between fabric and outer shell fabric between adjacent adhesive bands, the front fabric includes woven fabric and knitting fabric, it is bonded together by binding agent pairing between woven fabric and knitting fabric.
Making a kind of process of composite thermal fabric is:
1), yarn variety design:
From wool fiber, cashmere fiber and Sargassum Carbon fibe, to wool fiber, cashmere fiber and Sargassum Carbon fibe carry out anti pilling process, ferment treatment and soft treatment, anti pilling process is from phosphate ester antimony oxide mixture as anti pilling agent, phosphate ester antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system is processed using protease, 0.1-0.2% of the albumen enzyme dosage for wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, 6-8% of the water-soluble organic silicon softening agent consumption for wool fiber weight;
2), recombing technique:
Sequentially pass through silver mixing-grilling-combing-grilling-recombing is completed into bar operation;
3), spinning process:
Using generally known spinning process, scalp acupuncture-bis- pin-tri- pin-tetra- pin-rove-storage-spun yarn-yarn steaming-is sequentially passed through from winder-doubling-double twisting-yarn steaming operation, make for weaving the yarn of worsted fabric, spinning process adopts compact spinning spun yarn equipment;
4), weaving and repair technology:
Using generally known weaving and repair technology, by yarn weaving into fabric, and fabric nonwoven defect and float are caused by repairing;
5), postfinishing process:
Fabric through singing-open width braying-crabbing-bakings-high speed braying-bakings-increasing depths manages-it is ripe repair-middle inspection-bristle-cropping-tank steaming-decatizing-shrinking processes, make worsted fabric.
Compared with prior art, the invention has the beneficial effects as follows:
A kind of composite material thermal fabric of the present invention, positive and negative are respectively adopted the weak front fabric of the strong rear fabric of reflexive and reflexive and make, and may be reversed counter wearing, the big area of day and night temperature, when daytime is hotter, the one side of reflexive strong rear fabric is through outside, the effect of cooling is reached;When evening is colder, the one side that reflexive weak dark face is come is through outside, the effect of insulation is reached.
Description of the drawings
Fig. 1 is a kind of structural representation of composite thermal fabric of the invention.
Fig. 2 is the schematic diagram of warming layer in Fig. 1.
In figure:Front fabric 1, warming layer 2, fabric 2.1, outer shell fabric 2.2, adhesive bands 2.3, packing space 2.4, rear fabric 3.
Specific embodiment
Referring to Fig. 1 and Fig. 2,The present invention relates to a kind of composite thermal fabric,Including the weak front fabric 1 of the reflexive of the strong rear fabric 3 of the reflexive of outer layer and internal layer,May be reversed counter wearing,Warming layer 2 is provided between the rear fabric 3 and front fabric 1,The warming layer 2 includes the outer shell fabric 2.2 of the high-count high density fabric of the fabric 2.1 and monolayer of the high-count high density fabric with monolayer,Between fabric 2.1 and outer shell fabric 2.2 have it is spaced be parallel to each other and width for 2mm-15mm adhesive bands 2.3,Fabric 2.1 and outer shell fabric 2.2 at adhesive bands 2.3 is bonded together,Formed between fabric 2.1 and outer shell fabric 2.2 between adjacent adhesive bands 2.3 and can house packing material such as eider down、The packing space 2.4 of implant etc..
Making a kind of process of composite thermal fabric is:
1), yarn variety design:
From wool fiber, cashmere fiber and Sargassum Carbon fibe, to wool fiber, cashmere fiber and Sargassum Carbon fibe carry out anti pilling process, ferment treatment and soft treatment, anti pilling process is from phosphate ester antimony oxide mixture as anti pilling agent, phosphate ester antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system is processed using protease, 0.1-0.2% of the albumen enzyme dosage for wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, 6-8% of the water-soluble organic silicon softening agent consumption for wool fiber weight;
2), recombing technique:
Sequentially pass through silver mixing-grilling-combing-grilling-recombing is completed into bar operation;
3), spinning process:
Using generally known spinning process, scalp acupuncture-bis- pin-tri- pin-tetra- pin-rove-storage-spun yarn-yarn steaming-is sequentially passed through from winder-doubling-double twisting-yarn steaming operation, make for weaving the yarn of worsted fabric, spinning process adopts compact spinning spun yarn equipment;
4), weaving and repair technology:
Using generally known weaving and repair technology, by yarn weaving into fabric, and fabric nonwoven defect and float are caused by repairing;
5), postfinishing process:
Fabric through singing-open width braying-crabbing-bakings-high speed braying-bakings-increasing depths manages-it is ripe repair-middle inspection-bristle-cropping-tank steaming-decatizing-shrinking processes, make worsted fabric.
Claims (2)
1. a kind of composite thermal fabric, it is characterised in that:The composite material thermal fabric includes the strong rear fabric of the reflexive of outer layer(3)The front fabric weak with the reflexive of internal layer(1), the rear fabric(3)With front fabric(1)Between be provided with warming layer(2), the warming layer(2)Including fabric(2.1)And outer shell fabric(2.2), fabric(2.1)With outer shell fabric(2.2)Between have the spaced adhesive bands being parallel to each other(2.3), adhesive bands(2.3)The fabric at place(2.1)And outer shell fabric(2.2)It is bonded together, adjacent adhesive bands(2.3)Between fabric(2.1)And outer shell fabric(2.2)Between form packing space(2.4), the front fabric included woven fabric and knitting fabric, is bonded together by binding agent pairing between woven fabric and knitting fabric.
2. a kind of process of the composite thermal fabric described in claim 1 is made, it is characterised in that:
1), yarn variety design:
From wool fiber, cashmere fiber and Sargassum Carbon fibe, to wool fiber, cashmere fiber and Sargassum Carbon fibe carry out anti pilling process, ferment treatment and soft treatment, anti pilling process is from phosphate ester antimony oxide mixture as anti pilling agent, phosphate ester antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system is processed using protease, 0.1-0.2% of the albumen enzyme dosage for wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, 6-8% of the water-soluble organic silicon softening agent consumption for wool fiber weight;
2), recombing technique:
Sequentially pass through silver mixing-grilling-combing-grilling-recombing is completed into bar operation;
3), spinning process:
Using generally known spinning process, scalp acupuncture-bis- pin-tri- pin-tetra- pin-rove-storage-spun yarn-yarn steaming-is sequentially passed through from winder-doubling-double twisting-yarn steaming operation, make for weaving the yarn of worsted fabric, spinning process adopts compact spinning spun yarn equipment;
4), weaving and repair technology:
Using generally known weaving and repair technology, by yarn weaving into fabric, and fabric nonwoven defect and float are caused by repairing;
5), postfinishing process:
Fabric through singing-open width braying-crabbing-bakings-high speed braying-bakings-increasing depths manages-it is ripe repair-middle inspection-bristle-cropping-tank steaming-decatizing-shrinking processes, make worsted fabric.