CN105671740A - Warm-keeping lace fabric and process thereof - Google Patents
Warm-keeping lace fabric and process thereof Download PDFInfo
- Publication number
- CN105671740A CN105671740A CN201610150413.7A CN201610150413A CN105671740A CN 105671740 A CN105671740 A CN 105671740A CN 201610150413 A CN201610150413 A CN 201610150413A CN 105671740 A CN105671740 A CN 105671740A
- Authority
- CN
- China
- Prior art keywords
- fabric
- yarn
- fiber
- twist
- warm
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a warm-keeping lace fabric and a process thereof. The warm-keeping lace fabric and the process thereof are characterized in that the warm-keeping lace fabric comprises a back fabric with high reflectivity on the outer layer and a front fabric with low reflectivity on the inner layer, and a warm-keeping layer is arranged between the back fabric and the front fabric. According to the warm-keeping lace fabric and the process thereof, the back and the front are made of the back fabric with high reflectivity and the front fabric with low reflectivity respectively, and the fabric can be turned over to be worn reversely; in a region where the day and night temperature difference is large, when it is hot on daytime, the side made of the back fabric with high reflectivity is worn outside to achieve the cooling effect; when it is cold at night, the side made of the deep-color fabric with low reflectivity is worn outside to achieve the warm keeping effect.
Description
Technical field
The present invention relates to warm lace fabric and technique thereof, belong to fabric technical field.
Background technology
Traditional fabric is clothing one use, design according to season, the area that day and night temperature is big again, this kind of fabric cannot be used by a clothing two, easily too hot or catch cold, and it is common such as down jackets, the fabric products such as cotton clothes, many employing manual operation sewing machines carry out product sewing, pass through sewing thread trace, form the storage area of eider down or weighting material, due to the singularity of product and the requirement of Product Process, for ensureing quality product and wear effect, a lot of requirement and restriction is had in the production material adopted and production technique etc., especially select at manufactured materials, sewing tech and wear experience aspect and there is certain risk. in addition, the fabric adopted of traditional making fabric is for using on two sides.
Summary of the invention
It is an object of the invention to overcome above-mentioned deficiency, it is provided that no longer include heat losses pipeline, the warm lace fabric that thermal property is strong and technique thereof.
The object of the present invention is achieved like this:
A kind of warm lace fabric and technique thereof is:
1), yarn variety design:
Select wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic, to wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic carry out anti pilling process, ferment treatment and mellowing, anti pilling process selects phosphoric acid ester antimonous oxide mixture as anti pilling agent, phosphoric acid ester antimonous oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system uses proteolytic enzyme to process, proteolytic enzyme consumption is the 0.1-0.2% of wool fiber weight, the softening agent that mellowing is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight,
2), recombing technique:
Wool top is made in wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic recombing;
3), spinning process:
Premenstrual spin-spun yarn-winder-doubling-doubly twist with the fingers-steam yarn makes yarn, wherein obtained its number of spun yarn is 81Nm, twist 780Z twist/m; Obtained yarn its be the double strand yarn of number 80Nm, pool capital twist 810S twist/m; The weight percent content of anti-transparent terylene in warp thread and weft yarn is 30;
4), postfinishing process:
Final finishing comprises: singe-mono-boil-braying-bis-boil-dry-photocatalyst working fluid pad-dry-TEFLON three-prevention finishing-bake-ripe repair-bristle-cropping-bristle-dewing-tank steams, in addition, the consumption 30g/l 50g/l of photocatalyst working fluid, mangle expression 75% 85%, car 25m/min 30m/min is kept when the use of photocatalyst working fluid, temperature 120 DEG C 135 DEG C, what TEFLON three-prevention finishing was processed rolls liquid 75-85%, the speed of a motor vehicle keeps 18-22m/min, temperature 160-180 DEG C, finally obtained fabric specification is: yarn props up 96/2-100/2Nm, total tightness degree 145-165, through close 615-796 root/10 centimetre, filling density 400-358 root/10 centimetre, gram heavy 340-390 gram/meter.
Compared with prior art, the invention has the beneficial effects as follows:
A kind of warm lace fabric of the present invention and technique thereof, pros and cons adopts rear fabric that reflectivity is strong and the weak front fabric of reflectivity to make respectively, turning counter wear, the area that day and night temperature is big, when daytime is hotter, the one side of rear fabric strong for reflectivity is through outside, reaches the effect of cooling; When evening is colder, the one side that dark face weak for reflectivity is come is through outside, reaches the effect of insulation.
Embodiment
The present invention relates to a kind of warm lace fabric and technique is:
1), yarn variety design:
Select wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic, to wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic carry out anti pilling process, ferment treatment and mellowing, anti pilling process selects phosphoric acid ester antimonous oxide mixture as anti pilling agent, phosphoric acid ester antimonous oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system uses proteolytic enzyme to process, proteolytic enzyme consumption is the 0.1-0.2% of wool fiber weight, the softening agent that mellowing is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight,
2), recombing technique:
Wool top is made in wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic recombing;
3), spinning process:
Premenstrual spin-spun yarn-winder-doubling-doubly twist with the fingers-steam yarn makes yarn, wherein obtained its number of spun yarn is 81Nm, twist 780Z twist/m; Obtained yarn its be the double strand yarn of number 80Nm, pool capital twist 810S twist/m; The weight percent content of anti-transparent terylene in warp thread and weft yarn is 30;
4), postfinishing process:
Final finishing comprises: singe-mono-boil-braying-bis-boil-dry-photocatalyst working fluid pad-dry-TEFLON three-prevention finishing-bake-ripe repair-bristle-cropping-bristle-dewing-tank steams, in addition, the consumption 30g/l 50g/l of photocatalyst working fluid, mangle expression 75% 85%, car 25m/min 30m/min is kept when the use of photocatalyst working fluid, temperature 120 DEG C 135 DEG C, what TEFLON three-prevention finishing was processed rolls liquid 75-85%, the speed of a motor vehicle keeps 18-22m/min, temperature 160-180 DEG C, finally obtained fabric specification is: yarn props up 96/2-100/2Nm, total tightness degree 145-165, through close 615-796 root/10 centimetre, filling density 400-358 root/10 centimetre, gram heavy 340-390 gram/meter.
Claims (1)
1. a warm lace fabric and technique thereof, it is characterised in that: described warm lace fabric and technique thereof is:
1), yarn variety design:
Select wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic, to wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic carry out anti pilling process, ferment treatment and mellowing, anti pilling process selects phosphoric acid ester antimonous oxide mixture as anti pilling agent, phosphoric acid ester antimonous oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system uses proteolytic enzyme to process, proteolytic enzyme consumption is the 0.1-0.2% of wool fiber weight, the softening agent that mellowing is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight,
2), recombing technique:
Wool top is made in wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic recombing;
3), spinning process:
Premenstrual spin-spun yarn-winder-doubling-doubly twist with the fingers-steam yarn makes yarn, wherein obtained its number of spun yarn is 81Nm, twist 780Z twist/m;Obtained yarn its be the double strand yarn of number 80Nm, pool capital twist 810S twist/m; The weight percent content of anti-transparent terylene in warp thread and weft yarn is 30;
4), postfinishing process:
Final finishing comprises: singe-mono-boil-braying-bis-boil-dry-photocatalyst working fluid pad-dry-TEFLON three-prevention finishing-bake-ripe repair-bristle-cropping-bristle-dewing-tank steams, in addition, the consumption 30g/l 50g/l of photocatalyst working fluid, mangle expression 75% 85%, car 25m/min 30m/min is kept when the use of photocatalyst working fluid, temperature 120 DEG C 135 DEG C, what TEFLON three-prevention finishing was processed rolls liquid 75-85%, the speed of a motor vehicle keeps 18-22m/min, temperature 160-180 DEG C, finally obtained fabric specification is: yarn props up 96/2-100/2Nm, total tightness degree 145-165, through close 615-796 root/10 centimetre, filling density 400-358 root/10 centimetre, gram heavy 340-390 gram/meter.