CN105671741A - Bubbling testing method of fabric - Google Patents

Bubbling testing method of fabric Download PDF

Info

Publication number
CN105671741A
CN105671741A CN201610152265.2A CN201610152265A CN105671741A CN 105671741 A CN105671741 A CN 105671741A CN 201610152265 A CN201610152265 A CN 201610152265A CN 105671741 A CN105671741 A CN 105671741A
Authority
CN
China
Prior art keywords
sample
fabric
yarn
fiber
twist
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610152265.2A
Other languages
Chinese (zh)
Inventor
赵平宝
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangyin Chunlan Textile Co Ltd
Original Assignee
Jiangyin Chunlan Textile Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangyin Chunlan Textile Co Ltd filed Critical Jiangyin Chunlan Textile Co Ltd
Priority to CN201610152265.2A priority Critical patent/CN105671741A/en
Publication of CN105671741A publication Critical patent/CN105671741A/en
Pending legal-status Critical Current

Abstract

The invention relates to a bubbling testing method of a fabric. The bubbling testing method is characterized in that a composite heat-insulation fabric comprises a back surface textile on an outer layer and with strong reflectivity and a front surface textile on an inner layer and with weak reflectivity, wherein a heat-insulation layer is arranged between the back surface textile and the front surface textile. According to the composite heat-insulation fabric provided by the invention, the front surface and the back surface are prepared from the back surface textile with the strong reflectivity and the front surface textile with the weak reflectivity respectively, and the fabric can be reversed and worn inside out; in regions with great large temperature differences between day and night, when the temperature in daytime is relatively high, one surface of the back surface textile with the strong reflectivity is worn outside so that the effect of cooling is realized; when the temperature at night is relatively low, one deep-color surface with the weak reflectivity is worn outside, so that the heat-insulation effect is realized.

Description

The foaming testing method of fabric
Technical field
The present invention relates to the foaming testing method of fabric, belong to fabric technical field.
Background technology
Traditional fabric is clothing one use, design according to season, the area that day and night temperature is big again, this kind of fabric cannot be used by a clothing two, easily too hot or catch cold, and it is common such as down jackets, the fabric products such as cotton clothes, many employing manual operation sewing machines carry out product sewing, pass through sewing thread trace, form the storage area of eider down or weighting material, due to the singularity of product and the requirement of Product Process, for ensureing quality product and wear effect, a lot of requirement and restriction is had in the production material adopted and production technique etc., especially select at manufactured materials, sewing tech and wear experience aspect and there is certain risk. in addition, the fabric adopted of traditional making fabric is for using on two sides.
Summary of the invention
It is an object of the invention to overcome above-mentioned deficiency, it is provided that no longer include heat losses pipeline, the foaming testing method of the fabric that thermal property is strong.
The object of the present invention is achieved like this:
A kind of composite heat insulation fabric, its foaming testing method is:
1), yarn variety design:
Select wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic, to wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic carry out anti pilling process, ferment treatment and mellowing, anti pilling process selects phosphoric acid ester antimonous oxide mixture as anti pilling agent, phosphoric acid ester antimonous oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system uses proteolytic enzyme to process, proteolytic enzyme consumption is the 0.1-0.2% of wool fiber weight, the softening agent that mellowing is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight,
2), recombing technique:
Wool top is made in wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic recombing;
3), spinning process:
Premenstrual spin-spun yarn-winder-doubling-doubly twist with the fingers-steam yarn makes yarn, wherein obtained its number of spun yarn is 81Nm, twist 780Z twist/m; Obtained yarn its be the double strand yarn of number 80Nm, pool capital twist 810S twist/m; The weight percent content of anti-transparent terylene in warp thread and weft yarn is 30;
4), postfinishing process:
Final finishing comprises: singe-mono-boil-braying-bis-boil-dry-photocatalyst working fluid pad-dry-TEFLON three-prevention finishing-bake-ripe repair-bristle-cropping-bristle-dewing-tank steams, in addition, the consumption 30g/l 50g/l of photocatalyst working fluid, mangle expression 75% 85%, car 25m/min 30m/min is kept when the use of photocatalyst working fluid, temperature 120 DEG C 135 DEG C, what TEFLON three-prevention finishing was processed rolls liquid 75-85%, the speed of a motor vehicle keeps 18-22m/min, temperature 160-180 DEG C, finally obtained fabric specification is: yarn props up 96/2-100/2Nm, total tightness degree 145-165, through close 615-796 root/10 centimetre, filling density 400-358 root/10 centimetre, gram heavy 340-390 gram/meter,
5) whipability is tested:
Step one: two pieces, the sample getting 60cm × 60cm on the logical paper web sample of 70cm is as test sample;
Step 2: sample is flat on temperature 20 ± 2 DEG C, balances 2 hours under the envrionment conditions of humidity 65 ± 3%;
Step 3: sample longitudinally folding sample, sample after folding be 30cm(laterally) × 60cm(longitudinally) front is put on pressing machine outwardly, spraying steam 10 seconds, vapor pressure is 6kg, fabric is by deforming after damp and hot, bubble, and folding line or the bubble of different size or different densities is played on surface;
Step 4: after having sprayed steam, takes out fabric after fabric being cooled 5 seconds with air draught, is clipped on trousers clothes hanger horizontal one end of sample, makes sample keep nature vertical;
Step 5: folder is had the trousers hanger of sample in temperature 20 ± 2 DEG C, under the environment of humidity 65 ± 3%, when sample after balance is moved to nature backlight, respectively these two time periods after whole scalding latter 1 hour and after whole boiling hot latter 24 hours, observe the foaming grade that sample appearance change determines sample.
Compared with prior art, the invention has the beneficial effects as follows:
A kind of composite heat insulation fabric of the present invention, pros and cons adopts rear fabric that reflectivity is strong and the weak front fabric of reflectivity to make respectively, turning counter wears, the area that day and night temperature is big, when daytime is hotter, the one side of rear fabric strong for reflectivity is through outside, reaches the effect of cooling; When evening is colder, the one side of dark color weak for reflectivity is through outside, reaches the effect of insulation.
Embodiment
The present invention relates to a kind of composite heat insulation fabric, its foaming testing method is:
1), yarn variety design:
Select wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic, to wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic carry out anti pilling process, ferment treatment and mellowing, anti pilling process selects phosphoric acid ester antimonous oxide mixture as anti pilling agent, phosphoric acid ester antimonous oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system uses proteolytic enzyme to process, proteolytic enzyme consumption is the 0.1-0.2% of wool fiber weight, the softening agent that mellowing is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight,
2), recombing technique:
Wool top is made in wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic recombing;
3), spinning process:
Premenstrual spin-spun yarn-winder-doubling-doubly twist with the fingers-steam yarn makes yarn, wherein obtained its number of spun yarn is 81Nm, twist 780Z twist/m; Obtained yarn its be the double strand yarn of number 80Nm, pool capital twist 810S twist/m; The weight percent content of anti-transparent terylene in warp thread and weft yarn is 30;
4), postfinishing process:
Final finishing comprises: singe-mono-boil-braying-bis-boil-dry-photocatalyst working fluid pad-dry-TEFLON three-prevention finishing-bake-ripe repair-bristle-cropping-bristle-dewing-tank steams, in addition, the consumption 30g/l 50g/l of photocatalyst working fluid, mangle expression 75% 85%, car 25m/min 30m/min is kept when the use of photocatalyst working fluid, temperature 120 DEG C 135 DEG C, what TEFLON three-prevention finishing was processed rolls liquid 75-85%, the speed of a motor vehicle keeps 18-22m/min, temperature 160-180 DEG C, finally obtained fabric specification is: yarn props up 96/2-100/2Nm, total tightness degree 145-165, through close 615-796 root/10 centimetre, filling density 400-358 root/10 centimetre, gram heavy 340-390 gram/meter,
5) whipability is tested:
Step one: two pieces, the sample getting 60cm × 60cm on the logical paper web sample of 70cm is as test sample;
Step 2: sample is flat on temperature 20 ± 2 DEG C, balances 2 hours under the envrionment conditions of humidity 65 ± 3%;
Step 3: sample longitudinally folding sample, sample after folding be 30cm(laterally) × 60cm(longitudinally) front is put on pressing machine outwardly, spraying steam 10 seconds, vapor pressure is 6kg, fabric is by deforming after damp and hot, bubble, and folding line or the bubble of different size or different densities is played on surface;
Step 4: after having sprayed steam, takes out fabric after fabric being cooled 5 seconds with air draught, is clipped on trousers clothes hanger horizontal one end of sample, makes sample keep nature vertical;
Step 5: folder is had the trousers hanger of sample in temperature 20 ± 2 DEG C, under the environment of humidity 65 ± 3%, when sample after balance is moved to nature backlight, respectively these two time periods after whole scalding latter 1 hour and after whole boiling hot latter 24 hours, observe the foaming grade that sample appearance change determines sample.

Claims (1)

1. a composite heat insulation fabric, it is characterised in that: a kind of composite heat insulation fabric, its foaming testing method is:
1), yarn variety design:
Select wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic, to wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic carry out anti pilling process, ferment treatment and mellowing, anti pilling process selects phosphoric acid ester antimonous oxide mixture as anti pilling agent, phosphoric acid ester antimonous oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system uses proteolytic enzyme to process, proteolytic enzyme consumption is the 0.1-0.2% of wool fiber weight, the softening agent that mellowing is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight,
2), recombing technique:
Wool top is made in wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic recombing;
3), spinning process:
Premenstrual spin-spun yarn-winder-doubling-doubly twist with the fingers-steam yarn makes yarn, wherein obtained its number of spun yarn is 81Nm, twist 780Z twist/m; Obtained yarn its be the double strand yarn of number 80Nm, pool capital twist 810S twist/m; The weight percent content of anti-transparent terylene in warp thread and weft yarn is 30;
4), postfinishing process:
Final finishing comprises: singe-mono-boil-braying-bis-boil-dry-photocatalyst working fluid pad-dry-TEFLON three-prevention finishing-bake-ripe repair-bristle-cropping-bristle-dewing-tank steams, in addition, the consumption 30g/l 50g/l of photocatalyst working fluid, mangle expression 75% 85%, car 25m/min 30m/min is kept when the use of photocatalyst working fluid, temperature 120 DEG C 135 DEG C, what TEFLON three-prevention finishing was processed rolls liquid 75-85%, the speed of a motor vehicle keeps 18-22m/min, temperature 160-180 DEG C, finally obtained fabric specification is: yarn props up 96/2-100/2Nm, total tightness degree 145-165, through close 615-796 root/10 centimetre, filling density 400-358 root/10 centimetre, gram heavy 340-390 gram/meter,
5) whipability is tested:
Step one: two pieces, the sample getting 60cm × 60cm on the logical paper web sample of 70cm is as test sample;
Step 2: sample is flat on temperature 20 ± 2 DEG C, balances 2 hours under the envrionment conditions of humidity 65 ± 3%;
Step 3: sample longitudinally folding sample, sample after folding be 30cm(laterally) × 60cm(longitudinally) front is put on pressing machine outwardly, spraying steam 10 seconds, vapor pressure is 6kg, fabric is by deforming after damp and hot, bubble, and folding line or the bubble of different size or different densities is played on surface;
Step 4: after having sprayed steam, takes out fabric after fabric being cooled 5 seconds with air draught, is clipped on trousers clothes hanger horizontal one end of sample, makes sample keep nature vertical;
Step 5: folder is had the trousers hanger of sample in temperature 20 ± 2 DEG C, under the environment of humidity 65 ± 3%, when sample after balance is moved to nature backlight, respectively these two time periods after whole scalding latter 1 hour and after whole boiling hot latter 24 hours, observe the foaming grade that sample appearance change determines sample.
CN201610152265.2A 2016-03-17 2016-03-17 Bubbling testing method of fabric Pending CN105671741A (en)