CN105734781A - Environment-friendly fabric and water absorption test technology thereof - Google Patents

Abstract

The invention relates to an environment-friendly fabric and a water absorption test technology thereof. As SEE ecological cotton is added between an outer layer fabric body and a lining fabric body, the used fabric has the advantages that biodegradation, environment protection and ecology are achieved, energy is saved, and discharging is improved; the fabric is an ideal environment-friendly warmth keeping fabric.

Description

A kind of environment-friendly plus material and water absorption test technique thereof

Technical field

The present invention relates to a kind of environment-friendly plus material and water absorption test technique thereof, belong to fabric technical field.

Background technology

Along with the progress in epoch, relevant ecology, environmental protection, the green concept such as nuisanceless will become more and more popular.Pollution-free food has been subjected to the favor of consumer, has the fabric dress ornament of green indignant thought therewith, will be shown great attention to, and DEVELOPMENT PROSPECT is boundless, and exploitation competition of the same trade will present multi-faceted, multi-level.But the heat-insulating property of garment material is general at present, can not meet the demand in epoch.

Summary of the invention

It is an object of the invention to overcome above-mentioned deficiency, it is provided that a kind of environment-friendly plus material of high insulating effect and water absorption test technique thereof.

The object of the present invention is achieved like this:

The manufacture method of a kind of environment-friendly plus material is:

1), yarn variety design:

Select wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic, to wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic carry out anti pilling process, ferment treatment and soft treatment, anti pilling processes selects phosphate ester antimony oxide mixture as anti pilling agent, phosphate ester antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system uses protease to process, protease consumption is the 0.1-0.2% of wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；

2), recombing technique:

Wool top is made in wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic recombing；

3), spinning process:

Premenstrual spin-spun yarn-winder-doubling-double twisting-yarn steaming makes yarn, wherein preparing its number of spun yarn is 81Nm, twist 780Z twist/m；The yarn prepared its be the double strand yarn of number 80Nm, pool capital twist 810S twist/m；Anti-transparent terylene weight percent content in warp thread with weft yarn is 30；

4), postfinishing process:

nullFinal finishing includes: singe-mono-boil-braying-bis-boil-dry-photocatalyst working fluid pad-dry-TEFLON three-prevention finishing-bake-ripe repair-bristle-cropping-bristle-dewing-tank steams，Additionally，The consumption 30g/l 50g/l of photocatalyst working fluid，Pick-up rate 75% 85%，Car 25m/min 30m/min is kept when the use of photocatalyst working fluid，Temperature 120 DEG C 135 DEG C，The mangle 75-85% of TEFLON three-prevention finishing processing，Speed keeps 18-22m/min，Temperature 160-180 DEG C，The fabric specification finally prepared is: yarn count 96/2-100/2Nm，Total tightness degree 145-165，End count 615-796 root/10 centimetre，Filling density 400-358 root/10 centimetre，Grammes per square metre 340-390 grams m；

5) test water absorption:

Step one: take two pieces of the sample of 10cm × 10cm on the fabric sample of the logical width of 40cm as test sample；

Step 2: be placed on by sample in washing appearance device, adds 300ml tetrachloroethylene as Dry Cleaners, is put into after dry-cleaning 30 minutes in dry-cleaning instrument and takes out after sealing, then repeated washing twice；

Step 3: the sample after dry-cleaning is flat on desktop, naturally sets level, dropper (precision 0.1ml) distance cloth cover 5 ± 0.5cm, instill 3ml distilled water to cloth cover, press stopwatch (precision >=0.1 second), the time that record drips；

Step 4: water droplet penetrates into inside fabric on cloth cover, fabric can be formed water stain circle print, after dripping 10 seconds, measure the minimum and maximum diameter of circle print, it is accurate to 0.1mm, test result is the meansigma methods of minimum and maximum diameter, and the revision of the convention, to 0.1mm, can obtain the water absorbing properties parameter of this fabric.

Compared with prior art, the invention has the beneficial effects as follows:

One environment-friendly plus material of the present invention and water absorption test technique thereof, by increasing SEE ecological cotton between outer shell fabric and lining fabric, use fabric to have biodegradation, energy-conservation change row, the feature such as environmental and ecological, are a kind of desirable environmental protection thermal fabrics.

Detailed description of the invention

The present invention relates to the manufacture method of a kind of environment-friendly plus material is:

1), yarn variety design:

Select wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic, to wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic carry out anti pilling process, ferment treatment and soft treatment, anti pilling processes selects phosphate ester antimony oxide mixture as anti pilling agent, phosphate ester antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system uses protease to process, protease consumption is the 0.1-0.2% of wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；

2), recombing technique:

Wool top is made in wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic recombing；

3), spinning process:

Premenstrual spin-spun yarn-winder-doubling-double twisting-yarn steaming makes yarn, wherein preparing its number of spun yarn is 81Nm, twist 780Z twist/m；The yarn prepared its be the double strand yarn of number 80Nm, pool capital twist 810S twist/m；Anti-transparent terylene weight percent content in warp thread with weft yarn is 30；

4), postfinishing process:

nullFinal finishing includes: singe-mono-boil-braying-bis-boil-dry-photocatalyst working fluid pad-dry-TEFLON three-prevention finishing-bake-ripe repair-bristle-cropping-bristle-dewing-tank steams，Additionally，The consumption 30g/l 50g/l of photocatalyst working fluid，Pick-up rate 75% 85%，Car 25m/min 30m/min is kept when the use of photocatalyst working fluid，Temperature 120 DEG C 135 DEG C，The mangle 75-85% of TEFLON three-prevention finishing processing，Speed keeps 18-22m/min，Temperature 160-180 DEG C，The fabric specification finally prepared is: yarn count 96/2-100/2Nm，Total tightness degree 145-165，End count 615-796 root/10 centimetre，Filling density 400-358 root/10 centimetre，Grammes per square metre 340-390 grams m；

5) test water absorption:

Step one: take two pieces of the sample of 10cm × 10cm on the fabric sample of the logical width of 40cm as test sample；

Step 2: be placed on by sample in washing appearance device, adds 300ml tetrachloroethylene as Dry Cleaners, is put into after dry-cleaning 30 minutes in dry-cleaning instrument and takes out after sealing, then repeated washing twice；

Step 3: the sample after dry-cleaning is flat on desktop, naturally sets level, dropper (precision 0.1ml) distance cloth cover 5 ± 0.5cm, instill 3ml distilled water to cloth cover, press stopwatch (precision >=0.1 second), the time that record drips；

Step 4: water droplet penetrates into inside fabric on cloth cover, fabric can be formed water stain circle print, after dripping 10 seconds, measure the minimum and maximum diameter of circle print, it is accurate to 0.1mm, test result is the meansigma methods of minimum and maximum diameter, and the revision of the convention, to 0.1mm, can obtain the water absorbing properties parameter of this fabric.

Claims (1)

1. an environment-friendly plus material, it is characterised in that: the manufacture method of a kind of environment-friendly plus material is:

1), yarn variety design:

Select wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic, to wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic carry out anti pilling process, ferment treatment and soft treatment, anti pilling processes selects phosphate ester antimony oxide mixture as anti pilling agent, phosphate ester antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system uses protease to process, protease consumption is the 0.1-0.2% of wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；

2), recombing technique:

Wool top is made in wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic recombing；

3), spinning process:

Premenstrual spin-spun yarn-winder-doubling-double twisting-yarn steaming makes yarn, wherein preparing its number of spun yarn is 81Nm, twist 780Z twist/m；The yarn prepared its be the double strand yarn of number 80Nm, pool capital twist 810S twist/m；Anti-transparent terylene weight percent content in warp thread with weft yarn is 30；

4), postfinishing process:

nullFinal finishing includes: singe-mono-boil-braying-bis-boil-dry-photocatalyst working fluid pad-dry-TEFLON three-prevention finishing-bake-ripe repair-bristle-cropping-bristle-dewing-tank steams，Additionally，The consumption 30g/l 50g/l of photocatalyst working fluid，Pick-up rate 75% 85%，Car 25m/min 30m/min is kept when the use of photocatalyst working fluid，Temperature 120 DEG C 135 DEG C，The mangle 75-85% of TEFLON three-prevention finishing processing，Speed keeps 18-22m/min，Temperature 160-180 DEG C，The fabric specification finally prepared is: yarn count 96/2-100/2Nm，Total tightness degree 145-165，End count 615-796 root/10 centimetre，Filling density 400-358 root/10 centimetre，Grammes per square metre 340-390 grams m；

5) test water absorption:

Step one: take two pieces of the sample of 10cm × 10cm on the fabric sample of the logical width of 40cm as test sample；

Step 2: be placed on by sample in washing appearance device, adds 300ml tetrachloroethylene as Dry Cleaners, is put into after dry-cleaning 30 minutes in dry-cleaning instrument and takes out after sealing, then repeated washing twice；

Step 3: the sample after dry-cleaning is flat on desktop, naturally sets level, dropper (precision 0.1ml) distance cloth cover 5 ± 0.5cm, instill 3ml distilled water to cloth cover, press stopwatch (precision >=0.1 second), the time that record drips；

Step 4: water droplet penetrates into inside fabric on cloth cover, fabric can be formed water stain circle print, after dripping 10 seconds, measure the minimum and maximum diameter of circle print, it is accurate to 0.1mm, test result is the meansigma methods of minimum and maximum diameter, and the revision of the convention, to 0.1mm, can obtain the water absorbing properties parameter of this fabric.