CN106820366A - A kind of fabric with occlusion effect - Google Patents
A kind of fabric with occlusion effect Download PDFInfo
- Publication number
- CN106820366A CN106820366A CN201510874676.8A CN201510874676A CN106820366A CN 106820366 A CN106820366 A CN 106820366A CN 201510874676 A CN201510874676 A CN 201510874676A CN 106820366 A CN106820366 A CN 106820366A
- Authority
- CN
- China
- Prior art keywords
- precoat
- fabric
- yarn
- fiber
- wool
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of fabric with occlusion effect, it is characterised in that：Described fabric includes the first precoat（1）, the second precoat（2）With the 3rd precoat（3）, the second precoat（2）Positioned at the first precoat（1）With the 3rd precoat（3）Between, the second precoat（2）Both sides be provided with section in equilateral triangle projection（4）, the first precoat（1）Towards the second precoat（2）Side be provided with section in equilateral triangle the first groove, the 3rd precoat（3）Towards the second precoat（2）Side be provided with section in equilateral triangle the second groove, the second precoat（2）Projection（4）Respectively with the first precoat（1）The first groove and the 3rd precoat（3）The second fit depressions.A kind of fabric with occlusion effect has good occlusion performance, and without any chemical bonding agent is used, the feature of environmental protection is strong, and soft texture is comfortable and easy to wear.
Description
Technical field
The present invention relates to a kind of fabric with occlusion effect, belong to fabric technical field.
Background technology
With the raising of human living standard, people are to being made the performance requirement also more and more higher of the fabric of clothing.The primary requirement of people is exactly the feature of environmental protection of dress material, it is desirable to which dress material is tried one's best few with or without pollution chemical substance high, such as chemical bonding agent.At present, the Multilayer plus material major part of in the market is bonded using chemical bonding agent.So, the environmental-protecting performance of clothes is not just high.Novel clothes generally require to dry for a long time, could wear.This certainly will influence people to use the normal of clothing.Accordingly it is desirable to be made the fabric of clothes as far as possible less with chemical bonding agent, the environmental-protecting performance of clothes is improved.
The content of the invention
It is an object of the invention to overcome above-mentioned deficiency, there is provided do not use chemical bonding agent, a kind of environmental-protecting performance fabric with occlusion effect high.
The object of the present invention is achieved like this：
A kind of fabric with occlusion effect, including the first precoat, second precoat and the 3rd precoat, second precoat is located between the first precoat and the 3rd precoat, the both sides of the second precoat are provided with projection of the section in equilateral triangle, first precoat is provided with first groove of the section in equilateral triangle towards the side of the second precoat, 3rd precoat is provided with second groove of the section in equilateral triangle towards the side of the second precoat, second precoat it is raised respectively with first groove and the second fit depressions of the 3rd precoat of the first precoat, lower floor's stomata is offered on first precoat, upper strata stomata is offered on 3rd precoat.
Making a kind of process of the fabric with occlusion effect is：
1）, yarn variety design：
From wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre, to wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre carry out anti pilling treatment, ferment treatment and soft treatment, anti pilling treatment is from phosphate antimony oxide mixture as anti pilling agent, phosphate antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system is processed using protease, albumen enzyme dosage is the 0.1-0.2% of wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；
2）, recombing and spinning process：
Wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre recombing are made wool top, then premenstrual spinning-spun yarn-winder-doubling-double twisting-yarn steaming is made yarn, wherein its number of spun yarn is obtained for 81Nm, 780Z twists/m of the twist；Obtained yarn its be number 80Nm double strand yarn, pool capital 810S twists/m of the twist；Weight percent content of the anti-transparent terylene in warp thread and weft yarn is 30；
3）, postfinishing process：
Prepared yarn is carried out as warp thread and weft yarn to weave to obtain wool fabric fabric, fabric fabric is carried out into Final finishing gets product wool worsted face fabric；Postfinishing process is：Singe-braying-crabbing-drying-sizing-decatizing-finished product；Singe：Speed 90m/min, moderate heat, 1 positive 1 is anti-；Braying：Temperature 60 C, speed 20m/min；Crabbing：Temperature is 80 DEG C, and speed is 18 ms/min；Drying：Temperature is 108 DEG C；Sizing：Temperature is 180 DEG C, 25 seconds time；Decatizing：Temperature is 110 DEG C, 6 minutes.
Compared with prior art, the beneficial effects of the invention are as follows：
A kind of fabric with occlusion effect of the present invention has good occlusion performance, without any chemical bonding agent is used in whole process, improves the feature of environmental protection of fabric, and soft texture is comfortable and easy to wear.
Brief description of the drawings
Fig. 1 is a kind of structural representation of the fabric with occlusion effect of the present invention.
Fig. 2 is the schematic diagram of the first precoat in Fig. 1.
Fig. 3 is the schematic diagram of the 3rd precoat in Fig. 1.
In figure：First precoat 1, the second precoat 2, the 3rd precoat 3, raised 4, lower floor's stomata 5, upper strata stomata 6.
Specific embodiment
Referring to Fig. 1 to Fig. 3, the present invention relates to the fabric with meshing functionss, including the first precoat 1, second precoat 2 and the 3rd precoat 3, second precoat 2 is located between the first precoat 1 and the 3rd precoat 3, the both sides of the second precoat 2 are provided with section in raised the 4 of equilateral triangle, first precoat 1 is provided with first groove of the section in equilateral triangle towards the side of the second precoat 2, 3rd precoat 3 is provided with second groove of the section in equilateral triangle towards the side of the second precoat 2, raised the 4 of second precoat 2 respectively with first groove and the second fit depressions of the 3rd precoat 3 of the first precoat 1, lower floor's stomata 5 is offered on first precoat 1, upper strata stomata 6 is offered on 3rd precoat 3.
Making a kind of process of the fabric with occlusion effect is：
1）, yarn variety design：
From wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre, to wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre carry out anti pilling treatment, ferment treatment and soft treatment, anti pilling treatment is from phosphate antimony oxide mixture as anti pilling agent, phosphate antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system is processed using protease, albumen enzyme dosage is the 0.1-0.2% of wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；
2）, recombing and spinning process：
Wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre recombing are made wool top, then premenstrual spinning-spun yarn-winder-doubling-double twisting-yarn steaming is made yarn, wherein its number of spun yarn is obtained for 81Nm, 780Z twists/m of the twist；Obtained yarn its be number 80Nm double strand yarn, pool capital 810S twists/m of the twist；Weight percent content of the anti-transparent terylene in warp thread and weft yarn is 30；
3）, postfinishing process：
Prepared yarn is carried out as warp thread and weft yarn to weave to obtain wool fabric fabric, fabric fabric is carried out into Final finishing gets product wool worsted face fabric；Postfinishing process is：Singe-braying-crabbing-drying-sizing-decatizing-finished product；Singe：Speed 90m/min, moderate heat, 1 positive 1 is anti-；Braying：Temperature 60 C, speed 20m/min；Crabbing：Temperature is 80 DEG C, and speed is 18 ms/min；Drying：Temperature is 108 DEG C；Sizing：Temperature is 180 DEG C, 25 seconds time；Decatizing：Temperature is 110 DEG C, 6 minutes.
Claims (2)
1. a kind of with the fabric for being engaged effect, it is characterised in that：Described fabric includes the first precoat（1）, the second precoat（2）With the 3rd precoat（3）, the second precoat（2）Positioned at the first precoat（1）With the 3rd precoat（3）Between, the second precoat（2）Both sides be provided with section in equilateral triangle projection（4）, the first precoat（1）Towards the second precoat（2）Side be provided with section in equilateral triangle the first groove, the 3rd precoat（3）Towards the second precoat（2）Side be provided with section in equilateral triangle the second groove, the second precoat（2）Projection（4）Respectively with the first precoat（1）The first groove and the 3rd precoat（3）The second fit depressions, first precoat（1）On offer lower floor's stomata（5）, the 3rd precoat（3）On offer upper strata stomata（6）.
2. a kind of process of the fabric with occlusion effect described in claim 1 is made, it is characterised in that：
1）, yarn variety design：
From wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre, to wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre carry out anti pilling treatment, ferment treatment and soft treatment, anti pilling treatment is from phosphate antimony oxide mixture as anti pilling agent, phosphate antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system is processed using protease, albumen enzyme dosage is the 0.1-0.2% of wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；
2）, recombing and spinning process：
Wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre recombing are made wool top, then premenstrual spinning-spun yarn-winder-doubling-double twisting-yarn steaming is made yarn, wherein its number of spun yarn is obtained for 81Nm, 780Z twists/m of the twist；Obtained yarn its be number 80Nm double strand yarn, pool capital 810S twists/m of the twist；Weight percent content of the anti-transparent terylene in warp thread and weft yarn is 30；
3）, postfinishing process：
Prepared yarn is carried out as warp thread and weft yarn to weave to obtain wool fabric fabric, fabric fabric is carried out into Final finishing gets product wool worsted face fabric；Postfinishing process is：Singe-braying-crabbing-drying-sizing-
Decatizing-finished product；Singe：Speed 90m/min, moderate heat, 1 positive 1 is anti-；Braying：Temperature 60 C, speed 20m/min；Crabbing：Temperature be 80 DEG C, speed be 18 meters/
Point；Drying：Temperature is 108 DEG C；Sizing：Temperature is 180 DEG C, 25 seconds time；Decatizing：Temperature is 110 DEG C, 6 minutes.