CN106805336A - A kind of fabric of anti-drilling hair - Google Patents
A kind of fabric of anti-drilling hair Download PDFInfo
- Publication number
- CN106805336A CN106805336A CN201510838596.7A CN201510838596A CN106805336A CN 106805336 A CN106805336 A CN 106805336A CN 201510838596 A CN201510838596 A CN 201510838596A CN 106805336 A CN106805336 A CN 106805336A
- Authority
- CN
- China
- Prior art keywords
- fabric
- yarn
- fiber
- outer shell
- wool
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of fabric of anti-drilling hair, it is characterised in that：The fabric has fabric（1）, outer shell fabric（2）, the fabric（1）With outer shell fabric（2）A glue-line is sprayed with opposite face（3）, the glue-line（3）It is provided with air-vent（4）, the fabric（1）Upper glue layer air-vent（4）With outer shell fabric（2）Upper glue layer air-vent（4）Position it is interlaced, the fabric（1）With outer shell fabric（2）Periphery is by being stitched together.A kind of fabric of anti-drilling hair passes through, and a glue-line is respectively equipped with by two shell fabrics and on the opposing connecting surface of two shell fabric, and two glue-lines are provided with the air-vent for mutually staggering, and makes the fabric in the case where hair is not gone out, with good moisture permeability.
Description
Technical field
The present invention relates to a kind of fabric of anti-drilling hair, belong to fabric technical field.
Background technology
Clothes is gradually received by most consumers because of its warmth retention property, lightweight flexible, aesthetic property and comfortableness.And some fabrics for being used to manufacture clothes generally occur brill hair phenomenon at present; not only have impact on overall outward appearance; and uncomfortable sensation can be given people; and existing anti-drilling hair is typically to apply one layer of adhesive on fabric; to fill up longitude and latitude intertwined point; to prevent hair from getting out, this structure is airtight, hygroscopicity is poor, and dress for a long time causes discomfort.
The content of the invention
It is an object of the invention to overcome above-mentioned deficiency, there is provided a kind of fabric of comfortable, ventilative a kind of anti-drilling hair.
The object of the present invention is achieved like this：
A kind of fabric of anti-drilling hair, the fabric has fabric, outer shell fabric, a glue-line is sprayed with the fabric and outer shell fabric opposite face, the glue-line is provided with air-vent, the fabric upper glue layer air-vent is interlaced with the position of outer shell fabric upper glue layer air-vent, the fabric, by being stitched together, offers lower floor's stomata with outer shell fabric periphery in the fabric, upper strata stomata is offered on the outer shell fabric.
Making a kind of process of the fabric of anti-drilling hair is：
1）, yarn variety design：
From wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre, to wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre carry out anti pilling treatment, ferment treatment and soft treatment, anti pilling treatment is from phosphate antimony oxide mixture as anti pilling agent, phosphate antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system is processed using protease, albumen enzyme dosage is the 0.1-0.2% of wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；
2）, recombing and spinning process：
Wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre recombing are made wool top, then premenstrual spinning-spun yarn-winder-doubling-double twisting-yarn steaming is made yarn, wherein its number of spun yarn is obtained for 81Nm, 780Z twists/m of the twist；Obtained yarn its be number 80Nm double strand yarn, pool capital 810S twists/m of the twist；Weight percent content of the anti-transparent terylene in warp thread and weft yarn is 30；
3）, postfinishing process：
Prepared yarn is carried out as warp thread and weft yarn to weave to obtain wool fabric fabric, fabric fabric is carried out into Final finishing gets product wool worsted face fabric；Postfinishing process is：Singe-braying-crabbing-drying-sizing-decatizing-finished product；Singe：Speed 90m/min, moderate heat, 1 positive 1 is anti-；Braying：Temperature 60 C, speed 20m/min；Crabbing：Temperature is 80 DEG C, and speed is 18 ms/min；Drying：Temperature is 108 DEG C；Sizing：Temperature is 180 DEG C, 25 seconds time；Decatizing：Temperature is 110 DEG C, 6 minutes.
Compared with prior art, the beneficial effects of the invention are as follows：
A kind of fabric of anti-drilling hair passes through, and a glue-line is respectively equipped with by two shell fabrics and on the opposing connecting surface of two shell fabric, and two glue-lines are provided with the air-vent for mutually staggering, and makes the fabric in the case where eider down is not gone out, with good moisture permeability.
Brief description of the drawings
Fig. 1 is a kind of structural representation of the fabric of anti-drilling hair of the present invention.
Fig. 2 is the schematic diagram of fabric in Fig. 1.
Fig. 3 is the schematic diagram of outer shell fabric in Fig. 1.
In figure：Fabric 1, outer shell fabric 2, glue-line 3, air-vent 4, lower floor's stomata 5, upper strata stomata 6.
Specific embodiment
Referring to Fig. 1 to Fig. 3, the present invention relates to anti-drilling hair side material, the fabric has fabric 1, outer shell fabric 2, a glue-line 3 is sprayed with the fabric 1 and the opposite face of outer shell fabric 2, the glue-line 3 is provided with air-vent 4, the upper glue layer air-vent 4 of the fabric 1 is interlaced with the position of the upper glue layer air-vent 4 of outer shell fabric 2, the fabric 1 is with the periphery of outer shell fabric 2 by being stitched together, lower floor's stomata 5 is offered in the fabric 1, upper strata stomata 6 is offered on the outer shell fabric 2.
Making a kind of process of the fabric of anti-drilling hair is：
1）, yarn variety design：
From wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre, to wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre carry out anti pilling treatment, ferment treatment and soft treatment, anti pilling treatment is from phosphate antimony oxide mixture as anti pilling agent, phosphate antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system is processed using protease, albumen enzyme dosage is the 0.1-0.2% of wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；
2）, recombing and spinning process：
Wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre recombing are made wool top, then premenstrual spinning-spun yarn-winder-doubling-double twisting-yarn steaming is made yarn, wherein its number of spun yarn is obtained for 81Nm, 780Z twists/m of the twist；Obtained yarn its be number 80Nm double strand yarn, pool capital 810S twists/m of the twist；Weight percent content of the anti-transparent terylene in warp thread and weft yarn is 30；
3）, postfinishing process：
Prepared yarn is carried out as warp thread and weft yarn to weave to obtain wool fabric fabric, fabric fabric is carried out into Final finishing gets product wool worsted face fabric；Postfinishing process is：Singe-braying-crabbing-drying-sizing-decatizing-finished product；Singe：Speed 90m/min, moderate heat, 1 positive 1 is anti-；Braying：Temperature 60 C, speed 20m/min；Crabbing：Temperature is 80 DEG C, and speed is 18 ms/min；Drying：Temperature is 108 DEG C；Sizing：Temperature is 180 DEG C, 25 seconds time；Decatizing：Temperature is 110 DEG C, 6 minutes.
Claims (2)
1. a kind of fabric of anti-drilling hair, it is characterised in that：The fabric has fabric（1）, outer shell fabric（2）, the fabric（1）With outer shell fabric（2）A glue-line is sprayed with opposite face（3）, the glue-line（3）It is provided with air-vent（4）, the fabric（1）Upper glue layer air-vent（4）With outer shell fabric（2）Upper glue layer air-vent（4）Position it is interlaced, the fabric（1）With outer shell fabric（2）Periphery passes through to be stitched together, the fabric（1）On offer lower floor's stomata（5）, the outer shell fabric（2）On offer upper strata stomata（6）.
2. make claim 1 described in a kind of anti-drilling hair fabric process, it is characterised in that：
1）, yarn variety design：
From wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre, to wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre carry out anti pilling treatment, ferment treatment and soft treatment, anti pilling treatment is from phosphate antimony oxide mixture as anti pilling agent, phosphate antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system is processed using protease, albumen enzyme dosage is the 0.1-0.2% of wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；
2）, recombing and spinning process：
Wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre recombing are made wool top, then premenstrual spinning-spun yarn-winder-doubling-double twisting-yarn steaming is made yarn, wherein its number of spun yarn is obtained for 81Nm, 780Z twists/m of the twist；Obtained yarn its be number 80Nm double strand yarn, pool capital 810S twists/m of the twist；Weight percent content of the anti-transparent terylene in warp thread and weft yarn is 30；
3）, postfinishing process：
Prepared yarn is carried out as warp thread and weft yarn to weave to obtain wool fabric fabric, fabric fabric is carried out into Final finishing gets product wool worsted face fabric；Postfinishing process is：Singe-braying-crabbing-drying-sizing-
Decatizing-finished product；Singe：Speed 90m/min, moderate heat, 1 positive 1 is anti-；Braying：Temperature 60 C, speed 20m/min；Crabbing：Temperature be 80 DEG C, speed be 18 meters/
Point；Drying：Temperature is 108 DEG C；Sizing：Temperature is 180 DEG C, 25 seconds time；Decatizing：Temperature is 110 DEG C, 6 minutes.