CN106820360B - A kind of erosion hair technique of tasselled silk scarf - Google Patents
A kind of erosion hair technique of tasselled silk scarf Download PDFInfo
- Publication number
- CN106820360B CN106820360B CN201710009109.5A CN201710009109A CN106820360B CN 106820360 B CN106820360 B CN 106820360B CN 201710009109 A CN201710009109 A CN 201710009109A CN 106820360 B CN106820360 B CN 106820360B
- Authority
- CN
- China
- Prior art keywords
- tasselled
- silk scarf
- silk
- cloth
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of erosion hair techniques of tasselled silk scarf, comprising the following steps: the plain embryo cloth of buying silk material, Bing are cut out and pre-process to it；Stamp processing is carried out to biscuit cloth and evaporates processing, automatic embroidery is then carried out using computerized emboridering machine, obtains embroidery cloth；The processing of cold wave gold is carried out to embroidery cloth, and upper light processing is carried out to gold stamping pattern, then by cloth hemming, and manually sews on tasselled；Deoxygenation processing will be carried out after tasselled silk scarf kiering；Erosion hair processing is carried out to tasselled silk scarf；Will treated that tasselled silk scarf soaped and washing process, and dry to constant weight, passed examination can pack factory.The present invention is when dyeing tasselled silk scarf, addition erosion hair agent, to reduce the tiny hair knot on tasselled silk scarf surface, increase the surface flatness and soft handle degree of tasselled silk scarf, and without hair loss, pilling problem, the present invention ensure that tasselled silk scarf is quality, be worthy to be popularized by being rigid in checking up to substrate and technical process.
Description
Technical field
The present invention relates to silk scarf processing technique field more particularly to a kind of erosion hair techniques of tasselled silk scarf.
Background technique
Silk scarf is made into silk, is trapped among on neck and is played the article that modification is done for clothes of arranging in pairs or groups, different
Style rich in color is various, is suitable for people of different ages group.Silk scarf was early in B.C. 3000, skirt-roof used by Egyptian
In cloth, the longuette for having tasselled, cist generation, twine cotton ready made clothings etc. and can find the trace of similar neckerchief, it may be said that the history of silk scarf
Exactly since a piece of cloth.Silk scarf is initially not intended as decoration and uses, but to keep out the cold for major function.The real shape of modern silk scarf
At being in the '20s, escape goes out traditional usage mode of liripipe and scarf, and the long towel of silk weaving starts to be used, the folding of neckerchief
The skills such as method, connection are slowly taken seriously.The material of the '30s, neckerchief rectangular at that time and long towel prevalence is mostly silk or people
Silk is made, pattern is very bold, and the brand of great design style is especially welcome, and famous Hermes silk scarf is just in this period
It has listed.With the continuous development of society, people have deep love for that degree is also higher and higher, and in recent years, silk scarf receives more to silk scarf
Come pursuing for more young men.Either give gifts or wear, no matter spring, summer, autumn and winter, be all suitable for very much wearing silk scarf.Tasselled are
A kind of sagging with tassel made of multicolored feather or silk thread etc., tasselled silk scarf is liked as one of silk scarf by women.
However existing tasselled silk scarf easily deforms in use, the problems such as hair loss.Based on above statement, the invention proposes
A kind of erosion hair technique of tasselled silk scarf.
Summary of the invention
The purpose of the present invention is to solve disadvantages existing in the prior art, and a kind of erosion hair of the tasselled silk scarf proposed
Technique.
A kind of erosion hair technique of tasselled silk scarf, comprising the following steps:
S1, the plain embryo cloth for purchasing silk material, are cut into required dimensions, Bing for the plain embryo cloth of quality examination qualification
1~1.8h is impregnated in compositional liquor, completes to take out after impregnating, in drying in 78~95 DEG C of baking oven to constant weight, after obtaining pretreatment
Plain embryo cloth；
S2, thickening agent is prepared according to the design needs, using platen printing machine to biscuit cloth pretreated in step S1
Stamp processing is carried out, then carries out evaporating processing, the style that teacher has designed and produced of making a plate is uploaded to the computer of embroidery machine, is adopted
Automatic embroidery is carried out with computerized emboridering machine, obtains embroidery cloth；
S3, under cold pressing state, to embroidery cloth obtained in step S2 carry out the processing of cold wave gold, and to gold stamping pattern into
Light processing on row, then by cloth surrounding to the side of 2.8~3.2mm of infolding, and using the method manually sewed, the four of cloth
Tasselled are sewed in week and corner, obtain tasselled silk scarf；
S4,0.15~0.35 times of the boiling-off additive that cool water quantity is added in cold water, by tasselled silk obtained in step S3
At 94~100 DEG C of high temperature, kiering handles 30~40min, carries out cooling washing after the completion of kiering, and then adjusting pH value is 5.4
~6.8,0.06~0.12 times of deoxyenzyme of cool water quantity is added, at 48~52 DEG C, impregnates 25~35min；
S5, in mass ratio 0.012~0.018:0.2~0.3:1 will lose hair agent and softening agent is added in dyeing dyestuff, adjust
Saving dyestuff pH value is 4~4.8, and dyestuff is heated to 44~58 DEG C, and tasselled silk scarf obtained in step S4 is soaked in dyestuff
In, the dyeing processing of 30~50min is carried out, after completing dyeing, adjusting dyestuff pH value to 9.2~9.8, and dyestuff is warming up to 68
~82 DEG C, continue 12~18min of immersion, takes out tasselled silk scarf；
S6, tasselled silk scarf obtained in step S5 is soaped and washing process, completes cleaning and is placed on 90~108 DEG C
Baking oven in dry to constant weight, carry out routine examination to the quality of tasselled silk scarf, passed examination can pack factory.
Preferably, the silk material in the step S1 is one in crepe de Chine, plain crepe-back satin, georgette, habotai or weight crape
Kind, and preferred plain crepe-back satin.
Preferably, to be water that mass ratio is 1:0.01~0.03 compound the compositional liquor in the step S1 with bleeding agent
Liquid.
Preferably, the bleeding agent is one of quickly penetrating agent F-134 or alkali-resistant penetrant F-135.
Preferably, the stamp processing method in the step S2 is any one of a, b and c, in which: a, in closed environment
Under, 128~142 DEG C of high temperature evaporate 20~30min of processing；B, under atmospheric pressure environment, 170~180 DEG C of high temperature evaporate processing 12~
18min；C, 200~220 DEG C of 3~8min of baking of high temperature.
Preferably, it is that 1:0.3~0.8:2.6~3.5:1.8~2.2 are anti-that the digesting agent in the step S4, which is mass ratio,
Wrinkle agent, stabilizer, hydrogen peroxide and sodium hydroxide compounding agent.
Preferably, the erosion hair agent in the step S5 is aqueous enzyme HY02, quick hair remover F-256, erosion hair agent RC, loses hair
One of agent BP-CONE and erosion hair agent C-29.
A kind of erosion hair technique of tasselled silk scarf proposed by the present invention uses the plain embryo cloth of silk material to make tasselled for substrate
Silk scarf, using stamp, embroidery, the production of gold stamping, artificial sewing tasselled and dyeing concerned process steps completion tasselled silk scarf, to substrate element
Embryo cloth is pre-processed, and ensure that subsequent decal and bronzing effect, and the present invention is when dyeing tasselled silk scarf, addition erosion hair
Agent increases the surface flatness and soft handle degree of tasselled silk scarf, this hair to reduce the tiny hair knot on tasselled silk scarf surface
The tasselled silk scarf appearance of bright preparation is high-end, atmosphere, and bright in luster, soft, smooth, no hair loss, pilling effect, the present invention mention
Manufacture craft out is easy to operate, and manufacturing conditions are mild, by being rigid in checking up to substrate and technical process, ensure that tasselled silk
Towel is quality, reduces the quality problems due to caused by misoperation in manufacturing process, reproducible, can be produced in batches,
High production efficiency is worthy to be popularized.
Specific embodiment
Combined with specific embodiments below the present invention is made further to explain.
Embodiment one
A kind of erosion hair technique of tasselled silk scarf proposed by the present invention, comprising the following steps:
S1, plain crepe-back satin element embryo cloth is purchased, the plain embryo cloth of quality examination qualification is cut into required dimensions, Bing is in matter
Amount is completed to take out after impregnating, in 85 DEG C of baking than being to impregnate 1.4h in the water of 1:0.02 and the compositional liquor of quickly penetrating agent F-134
It dries in case to constant weight, obtains pretreated plain embryo cloth；
S2, thickening agent is prepared according to the design needs, using platen printing machine to biscuit cloth pretreated in step S1
Stamp processing is carried out, is then carried out under atmospheric pressure environment, 175 DEG C of high temperature evaporate processing 15min, the flower that the teacher that makes a plate has been designed and produced
Sample uploads to the computer of embroidery machine, carries out automatic embroidery using computerized emboridering machine, obtains embroidery cloth；
S3, under cold pressing state, to embroidery cloth obtained in step S2 carry out the processing of cold wave gold, and to gold stamping pattern into
Light processing on row, then by cloth surrounding to the side of infolding 3mm, and using the method manually sewed, surrounding and side in cloth
Tasselled in angle seam obtain tasselled silk scarf；
S4,0.25 times of the mass ratio that cool water quantity is added in cold water be the anti-creasing agent of 1:0.5:3:1.8, stabilizer, double
The compounding agent of oxygen water and sodium hydroxide, by tasselled silk obtained in step S3 at 98 DEG C of high temperature, kiering handles 35min, kiering
Cooling washing is carried out after the completion, and then adjusting pH value is 6, and 0.08 times of deoxyenzyme of cool water quantity is added, and at 50 DEG C, is impregnated
30min；
Quick hair remover F-256 and softening agent are added in dyeing dyestuff by S5, in mass ratio 0.015:0.25:1, adjust
Dyestuff pH value is 4.5, and dyestuff is heated to 50 DEG C, and tasselled silk scarf obtained in step S4 is soaked in dyestuff, is carried out
The dyeing of 40min is handled, after completing dyeing, adjusting dyestuff pH value to 9.5, and dyestuff is warming up to 75 DEG C, continue to impregnate
15min takes out tasselled silk scarf；
S6, tasselled silk scarf obtained in step S5 is soaped and washing process, completes the baking that cleaning is placed on 100 DEG C
It dries in case to constant weight, carries out routine examination to the quality of tasselled silk scarf, passed examination can pack factory.
Embodiment two
A kind of erosion hair technique of tasselled silk scarf proposed by the present invention, comprising the following steps:
S1, buying georgette element embryo cloth, are cut into required dimensions for the plain embryo cloth of quality examination qualification, Bing is in matter
Amount is completed to take out after impregnating, in 78 DEG C of baking than being to impregnate 1.8h in the water of 1:0.01 and the compositional liquor of alkali-resistant penetrant F-135
It dries in case to constant weight, obtains pretreated plain embryo cloth；
S2, thickening agent is prepared according to the design needs, using platen printing machine to biscuit cloth pretreated in step S1
Stamp processing is carried out, 210 DEG C of baking 5min of high temperature are then carried out, the style that teacher has designed and produced that will make a plate uploads to embroidery machine
Computer, using computerized emboridering machine carry out automatic embroidery, obtain embroidery cloth；
S3, under cold pressing state, to embroidery cloth obtained in step S2 carry out the processing of cold wave gold, and to gold stamping pattern into
Light processing on row, then by cloth surrounding to the side of infolding 2.8mm, and using the method manually sewed, cloth surrounding and
Tasselled are sewed in corner, obtain tasselled silk scarf；
S4,0.15 times of the mass ratio that cool water quantity is added in cold water be the anti-creasing agent of 1:0.3:2.6:2.2, stabilizer,
The compounding agent of hydrogen peroxide and sodium hydroxide, by tasselled silk obtained in step S3 at 94 DEG C of high temperature, kiering handles 40min, boils
Cooling washing is carried out after the completion of practicing, then adjusting pH value is 5.4,0.1 times of deoxyenzyme of cool water quantity is added, at 48 DEG C, leaching
Steep 25min；
S5, in mass ratio 0.018:0.3:1 will lose hair agent BP-CONE and softening agent is added in dyeing dyestuff, adjust dye
Expect that pH value is 4.2, and dyestuff is heated to 48 DEG C, tasselled silk scarf obtained in step S4 is soaked in dyestuff, 45min is carried out
Dyeing processing, after completing dyeing, adjust dyestuff pH value to 9.2, and dyestuff is warming up to 70 DEG C, continue to impregnate 18min, take out
Tasselled silk scarf；
S6, tasselled silk scarf obtained in step S5 is soaped and washing process, completes the baking that cleaning is placed on 105 DEG C
It dries in case to constant weight, carries out routine examination to the quality of tasselled silk scarf, passed examination can pack factory.
Embodiment three
A kind of erosion hair technique of tasselled silk scarf proposed by the present invention, comprising the following steps:
S1, buying habotai element embryo cloth, are cut into required dimensions for the plain embryo cloth of quality examination qualification, Bing is in matter
Amount is completed to take out after impregnating, in 92 DEG C of baking oven than being to impregnate 1h in the water of 1:0.03 and the compositional liquor of quickly penetrating agent F-134
Interior drying obtains pretreated plain embryo cloth to constant weight；
S2, thickening agent is prepared according to the design needs, using platen printing machine to biscuit cloth pretreated in step S1
Stamp processing is carried out, then under closed environment, 135 DEG C of high temperature evaporate processing 25min, the style that the teacher that makes a plate has been designed and produced
The computer for uploading to embroidery machine carries out automatic embroidery using computerized emboridering machine, obtains embroidery cloth；
S3, under cold pressing state, to embroidery cloth obtained in step S2 carry out the processing of cold wave gold, and to gold stamping pattern into
Light processing on row, then by cloth surrounding to the side of infolding 3.2mm, and using the method manually sewed, cloth surrounding and
Tasselled are sewed in corner, obtain tasselled silk scarf；
S4,0.35 times of the mass ratio that cool water quantity is added in cold water be the anti-creasing agent of 1:0.8:3.5:2, stabilizer, double
The compounding agent of oxygen water and sodium hydroxide, by tasselled silk obtained in step S3 at 100 DEG C of high temperature, kiering handles 30min, kiering
Cooling washing is carried out after the completion, and then adjusting pH value is 6.8, and 0.12 times of deoxyenzyme of cool water quantity is added, and at 52 DEG C, is impregnated
35min；
Aqueous enzyme HY02 and softening agent are added in dyeing dyestuff by S5, in mass ratio 0.012:0.2:1, adjust dyestuff pH
Value is 4.8, and dyestuff is heated to 55 DEG C, and tasselled silk scarf obtained in step S4 is soaked in dyestuff, the dye of 35min is carried out
Color processing, after completing dyeing, adjusting dyestuff pH value to 9.8, and dyestuff is warming up to 80 DEG C, continue to impregnate 12min, takes out tasselled
Silk scarf；
S6, tasselled silk scarf obtained in step S5 is soaped and washing process, completes the baking that cleaning is placed on 95 DEG C
It dries in case to constant weight, carries out routine examination to the quality of tasselled silk scarf, passed examination can pack factory.
The tasselled silk scarf prepared in the erosion hair technique of the tasselled silk scarf proposed in the embodiment of the present invention one~tri- is surveyed respectively
Pilling grading and force of explosion rate of descent, obtain following result:
| Embodiment | One | Two | Three |
| Pilling grading | 4 grades | 4 grades | 4 grades |
| Force of explosion rate of descent (%) | 18.7 | 20.3 | 19.1 |
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (7)
1. a kind of erosion hair technique of tasselled silk scarf, which comprises the following steps:
The plain embryo cloth of quality examination qualification is cut into required dimensions by S1, the plain embryo cloth for purchasing silk material, and Bing is in multiple
It with 1~1.8h is impregnated in liquid, completes to take out after impregnating, in drying in 78~95 DEG C of baking oven to constant weight, obtains pretreated element
Embryo cloth；
S2, thickening agent is prepared according to the design needs, biscuit cloth pretreated in step S1 is carried out using platen printing machine
Stamp processing, then carries out evaporating processing, the style that teacher has designed and produced of making a plate is uploaded to the computer of embroidery machine, using electricity
Brain embroidery machine carries out automatic embroidery, obtains embroidery cloth；
S3, under cold pressing state, the processing of cold wave gold is carried out to embroidery cloth obtained in step S2, and gold stamping pattern is carried out
Light processing, then by cloth surrounding to the side of 2.8~3.2mm of infolding, and using the method manually sewed, cloth surrounding and
Tasselled are sewed in corner, obtain tasselled silk scarf；
S4,0.15~0.35 times of the boiling-off additive that cool water quantity is added in cold water, by tasselled silk obtained in step S3 in height
At 94~100 DEG C of temperature, kiering handles 30~40min, carries out cooling washing after the completion of kiering, then adjust pH value be 5.4~
6.8,0.06~0.12 times of deoxyenzyme of cool water quantity is added, at 48~52 DEG C, impregnates 25~35min；
S5, in mass ratio 0.012~0.018:0.2~0.3:1 will lose hair agent and softening agent is added in dyeing dyestuff, adjust dye
Expect that pH value is 4~4.8, and dyestuff is heated to 44~58 DEG C, tasselled silk scarf obtained in step S4 is soaked in dyestuff, into
The dyeing of 30~50min of row is handled, after completing dyeing, adjusting dyestuff pH value to 9.2~9.8, and dyestuff is warming up to 68~82
DEG C, continue 12~18min of immersion, takes out tasselled silk scarf；
S6, tasselled silk scarf obtained in step S5 is soaped and washing process, completes the baking that cleaning is placed on 90~108 DEG C
It dries in case to constant weight, carries out routine examination to the quality of tasselled silk scarf, passed examination can pack factory.
2. a kind of erosion hair technique of tasselled silk scarf according to claim 1, which is characterized in that the silk in the step S1
Material is one of crepe de Chine, plain crepe-back satin, georgette, habotai or weight crape.
3. a kind of erosion hair technique of tasselled silk scarf according to claim 1, which is characterized in that the compounding in the step S1
Liquid is the compositional liquor of the water that mass ratio is 1:0.01~0.03 and bleeding agent.
4. a kind of erosion hair technique of tasselled silk scarf according to claim 3, which is characterized in that the bleeding agent is quickly to seep
Saturating one of agent F-134 or alkali-resistant penetrant F-135.
5. a kind of erosion hair technique of tasselled silk scarf according to claim 1, which is characterized in that the stamp in the step S2
Processing method is any one of a, b and c, in which: a, under closed environment, 128~142 DEG C of high temperature evaporate processing 20~
30min；B, under atmospheric pressure environment, 170~180 DEG C of high temperature evaporate 12~18min of processing；C, 200~220 DEG C of high temperature bake 3~
8min。
6. a kind of erosion hair technique of tasselled silk scarf according to claim 1, which is characterized in that the kiering in the step S4
Agent is that mass ratio is answering for 1:0.3~0.8:2.6~3.5:1.8~2.2 anti-creasing agent, stabilizer, hydrogen peroxide and sodium hydroxide
Ingredients.
7. a kind of erosion hair technique of tasselled silk scarf according to claim 1, which is characterized in that the erosion hair in the step S5
Agent is aqueous enzyme HY02, quick hair remover F-256, erosion hair agent RC, loses one of hair agent BP-CONE and erosion hair agent C-29.