CN106808623B - 5 microns of thickness non-ignitable ultra-thin polyether-ether-ketone film parting agent specials of high-efficiency environment friendly economy - Google Patents
5 microns of thickness non-ignitable ultra-thin polyether-ether-ketone film parting agent specials of high-efficiency environment friendly economy Download PDFInfo
- Publication number
- CN106808623B CN106808623B CN201611199442.9A CN201611199442A CN106808623B CN 106808623 B CN106808623 B CN 106808623B CN 201611199442 A CN201611199442 A CN 201611199442A CN 106808623 B CN106808623 B CN 106808623B
- Authority
- CN
- China
- Prior art keywords
- ether
- microns
- ignitable
- ultra
- environment friendly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention provides a kind of 5 microns of the thickness that high-efficiency environment friendly economy is non-ignitable ultra-thin polyether-ether-ketone film parting agent specials, perfluoropolyether hydrogen ether, the fluorinated surfactant of 0.1wt%~0.5wt%, the perfluorocarbon solvents of 90wt%~95wt%, the alcoholic solvent of 1wt%~4wt%, the oiliness solubilizer of 0wt%~5wt% and the corrosion inhibiter of 0.01wt%~0.5wt% including 0.1wt%~0.5wt%.Preferably, perfluoropolyether hydrogen ether is selected from CF3CF2CF2O(C3F6O)n‑CHFCF3, wherein 10≤n≤60, n are integer.Fluorinated surfactant is selected from CF3CF2CF2O‑(CF(CF3)CF2O)x‑COOAmBiOCH3, wherein 0≤m≤10,3≤i≤10, A=C3H6O, B=C2H4O.Perfluorocarbon solvents are C6F12.Release agent of the invention is suitable for 5 microns of thickness ultra-thin polyether-ether-ketone diaphragm high efficiency manufactures, so that film slice is not necessarily to secondary reshaping, film surface does not have release agent residue to not influence subsequent and fine copper voice coil cementitiousness, excellent high temperature resistance ability, die surface cleans noncoking, without often cleaning, does not have silicone oil pollution for precision electronic components, and it is ingenious in design, easy, environmental protection is prepared, it is economical, it is non-ignitable, it is suitable for large-scale promotion application.
Description
Technical field
The present invention relates to technical field of mold release, more particularly, to polyether-ether-ketone film technical field of mold release, especially
Refer to a kind of 5 microns of the thickness that high-efficiency environment friendly economy is non-ignitable ultra-thin polyether-ether-ketone film parting agent specials.
Background technique
When manufacturing macromolecule material product, molded method is generally used, melt or molten liquid material are injected into mold,
After curing molding, then it is removed from the molds.It, generally can be on mold in advance using demoulding in order to help to be removed from the molds product
Agent.
Release agent is a kind of functional materials between mold and manufactured goods, be prevent rubber, plastics, elastomer or
Mechanograph, laminated product of other materials etc. are bonded on die surface, play the role of a kind of processing aid for being easy to be detached from.
The usually used release agent of engineering plastics processing film has three kinds of release agents such as petroleum (wax) system, silicon systems and fluorine system:
Petroleum (wax) be it is cheap, adhesion property is preferable, the disadvantage is that being easy pollution mold and manufactured goods;Silicon systems are moderate, isolation
Better performances are small to mold and manufactured goods pollution;Fluorine system is expensive, and isolation performance is very good, almost to mold and manufactured goods
It does not pollute.Wherein fluorine system than silicon systems almost few an order of magnitude in dosage, head works as when for the processing of precise electronic component
It rushes the preferably not siliceous fluorine system releasing agent in ground.
Fluorine-containing demoulding agent is a kind of fluoride-containing PMMA, is high efficient demoulding agent of new generation.With traditional wax class and silicone oil
Class release agent is compared, and fluorine-containing demoulding agent is with low using concentration, effect on environment is small, spraying is once used multiple times, can improve
Production efficiency has good stripping result to high cohesiveness product, and product surface residual is few without polluting product and mold, not shadow
Product secondary operation (such as spray painting is printed, bonding) excellent characteristics is rung, is received by the market.
PEEK (polyetheretherketone, polyether-ether-ketone) is (former empire of Britain Wei Gesi (Victrex) company
Learn ICI) last century the seventies exploitation a kind of special engineering plastics haveing excellent performance, belong to the crystallization that fusing point is up to 345 DEG C
Property polymer.There are many significant advantages compared with other special engineering plastics, high temperature resistant, mechanical performance be excellent, self-lubrication
It is good, chemicals-resistant burn into is fire-retardant, peel resistance, radioresistance, insulating properties are stable, hydrolysis and easy processing etc., navigate in aviation
It, automobile manufacture, the fields such as electric, medical and food processing are used widely.It is released from summer Wei Gesi in 2007
In the world after first PEEK film line, PEEK film maximum breadth 1.5m, has been used for insulated electro by 3~750 μm of thickness
Line/cable, semiconductor, automobile and aircraft industry can do microphone vibrating diaphragm and pressure-sensitive adhesive band bottom.
But Henkel KGaA Frekote 55-Nc semi-permanent mould release agent is used to process 5 microns of ultra-thin polyether-ether-ketones of thickness
When membrane product, encountering repeatedly needs the problem of rearranging fold after product is removed from the molds, and release agent moves to product
Surface needs secondary cleaning, otherwise can not be with troublesome a series of problems, such as fine copper voice coil bonding endlessly, and the product makes
Release agent is diluted with conventional inflammable and explosive solvent, it is upper heavily regulated in transport.
Accordingly, it is desirable to provide a kind of 5 microns of thickness ultra-thin polyether-ether-ketone film parting agent specials, it is suitable for 5 microns of thickness
Ultra-thin polyether-ether-ketone film manufacture, it is efficient, environmentally friendly, economical, non-ignitable.
Summary of the invention
In order to overcome the disadvantages of the prior art mentioned above, it is an object of the present invention to provide a kind of high-efficiency environment friendly economy
5 microns of thickness non-ignitable ultra-thin polyether-ether-ketone film parting agent specials, it is suitable for 5 microns of thickness ultra-thin polyether-ether-ketone films efficiently to make
It makes, so that film slice is not necessarily to secondary reshaping, it is subsequent viscous with fine copper voice coil to not influence that film surface does not have release agent residue
Knot ability, excellent high temperature resistance ability, die surface clean noncoking, without often cleaning, do not have silicon for precision electronic components
Oily pollution is suitable for large-scale promotion application.
Another object of the present invention is to provide a kind of 5 microns of the thickness that high-efficiency environment friendly economy is non-ignitable ultra-thin polyether-ether-ketone films
Parting agent special, it is ingenious in design, easy, environmental protection is prepared, it is economical, it is non-ignitable, it is suitable for large-scale promotion application.
To achieve the above objectives, 5 microns of thickness non-ignitable ultra-thin polyether-ether-ketone films of high-efficiency environment friendly economy of the invention are dedicated
Release agent, its main feature is that, including following components and its weight percentage:
Preferably, the perfluoropolyether hydrogen ether includes any one compound indicated by following molecular formula or its mixing
Object: CF3CF2CF2O(C3F6O)n-CHFCF3, wherein 10≤n≤60, n are integer.
More preferably, 10≤n≤40.
Further, the perfluoropolyether hydrogen ether is selected from HFPO-2000, HFPO-4000, HFPO-6000 and HFPO-
One of 8000 or a variety of.
Preferably, the perfluoropolyether hydrogen ether is in 121 degree of 24 hours fugitive constituents less than 3% (v/v), the perfluoropolyether hydrogen
Ether does not have flash-point.
Preferably, the perfluoropolyether hydrogen ether at 25 degree surface tension less than 20 dynes per centimeters.
Preferably, the fluorinated surfactant includes any one compound or mixture indicated by following molecular formula:
CF3CF2CF2O-(CF(CF3)CF2O)x-COOAmBiOCH3, wherein 0≤m≤10,3≤i≤10, A=C3H6O, B=C2H4O。
More preferably, 0≤m≤3,5≤i≤8.
Further, the fluorinated surfactant is 350 monomethyl ether of hexafluoropropylene oxide tripolymer polyethylene glycol.
Preferably, the static surface tension of the aqueous solution of the fluorinated surfactant containing 0.1wt% is lower than 20 dynes/li
Rice.
Preferably, solubility is no more than 10wt% to the fluorinated surfactant in water, the fluorinated surfactant is in second
It is all dissolved in alcohol.
Preferably, the boiling point of the perfluorocarbon solvents is at 40 degree or more and at 110 degree hereinafter, the perfluorocarbon solvents do not have
There is flash-point.
Preferably, the perfluorocarbon solvents are the compounds indicated by following molecular formula: C6F12。
Preferably, the alcoholic solvent is selected from the one or more of trifluoroethanol and hexafluoroisopropanol.
Preferably, the oiliness solubilizer is 1,3- m-benzotrifluoride.
Preferably, the corrosion inhibiter includes any one compound or mixture indicated by following molecular formula:
CF3CF2CF2O-(CF(CF3)CF2O)k-CONHCH2CH2CH2N(C2H5)2·CH3I, wherein k=2 or 3.
The beneficial effects of the present invention are:
A. 5 microns of thickness non-ignitable ultra-thin polyether-ether-ketone film parting agent specials of high-efficiency environment friendly economy of the invention, including
The perfluoropolyether hydrogen ether of 0.1wt%~0.5wt%, the fluorinated surfactant of 0.1wt%~0.5wt%, 90wt%~95wt%
Perfluorocarbon solvents, the alcoholic solvent of 1wt%~4wt%, the oiliness solubilizer of 0wt%~5wt% and 0.01wt%~0.5wt%
Corrosion inhibiter, be suitable for 5 microns of thickness ultra-thin polyether-ether-ketone film high efficiency manufactures so that film slice be not necessarily to secondary reshaping, film
It is subsequent with fine copper voice coil cementitiousness to not influence that surface does not have release agent residue, excellent high temperature resistance ability, and die surface is clear
Clean noncoking does not have silicone oil pollution for precision electronic components without often cleaning, is suitable for large-scale promotion application
B. 5 microns of thickness non-ignitable ultra-thin polyether-ether-ketone film parting agent specials of high-efficiency environment friendly economy of the invention, including
The perfluoropolyether hydrogen ether of 0.1wt%~0.5wt%, the fluorinated surfactant of 0.1wt%~0.5wt%, 90wt%~95wt%
Perfluorocarbon solvents, the alcoholic solvent of 1wt%~4wt%, the oiliness solubilizer of 0wt%~5wt% and 0.01wt%~0.5wt%
Corrosion inhibiter, it is ingenious in design, prepare easy, environmental protection, it is economical, it is non-ignitable, be suitable for large-scale promotion application.
These and other objects of the invention, feature and advantage, are filled by following detailed descriptions and claim
Fission is existing, and can be achieved by means, device and the their combination specially pointed out in appended claims.
Specific embodiment
The present invention provides a kind of 5 microns of the thickness that high-efficiency environment friendly economy is non-ignitable ultra-thin polyether-ether-ketone film parting agent specials,
Including following components and its weight percentage: perfluoropolyether hydrogen ether, the 0.1wt%~0.5wt% of 0.1wt%~0.5wt%
Fluorinated surfactant, the perfluorocarbon solvents of 90wt%~95wt%, the alcoholic solvent of 1wt%~4wt%, 0wt%~5wt%
The corrosion inhibiter of oiliness solubilizer and 0.01wt%~0.5wt%.
The perfluoropolyether hydrogen ether is the release main material of demoulding, can be any suitable perfluoropolyether hydrogen ether, preferably,
Perfluoropolyether hydrogen ether (the abbreviation HFPOn) include or mixtures thereof any one compound indicated by following molecular formula:
CF3CF2CF2O(C3F6O)n-CHFCF3, wherein 10≤n≤60, n are integer.More preferably, 10≤n≤40.Further, institute
It states perfluoropolyether hydrogen ether and is selected from one of HFPO-2000, HFPO-4000, HFPO-6000 and HFPO-8000 or a variety of.
HFPO-2000, HFPO-4000, HFPO-6000 and HFPO-8000 respectively represent 2000,4000,6000 and of average molecular weight
8000 perfluoropolyether hydrogen ether.
In order to avoid the high temperature thermal decomposition in molding or minute quantity volatilization, preferably, the perfluoropolyether hydrogen ether is at 121 degree
24 hours fugitive constituents do not have flash-point less than 3% (v/v), the perfluoropolyether hydrogen ether.
It can effectively be sprawled rapidly on surface when in order to guarantee mold clamping, preferably, the perfluoropolyether hydrogen ether is 25
Surface tension is less than 20 dynes per centimeters when spending.
The fluorinated surfactant effectively emulsifies perfluoropolyether hydrogen ether and is dispersed into very thin oil film, low surface tension assisted demoulding
It is release, it can be any suitable fluorinated surfactant, preferably, the fluorinated surfactant includes being indicated by following molecular formula
Any one compound or mixture: CF3CF2CF2O-(CF(CF3)CF2O)x-COOAmBiOCH3, wherein 0≤m≤10,3≤i
≤ 10, A=C3H6O, B=C2H4O.More preferably, 0≤m≤3,5≤i≤8.Further, the fluorinated surfactant is six
350 monomethyl ether of fluorine propylene oxide tripolymer polyethylene glycol, is abbreviated as HFPO (3) mpeg 3 50.
It can effectively be sprawled on surface rapidly when in order to guarantee mold clamping, preferably, the fluorine surface containing 0.1wt%
The static surface tension of the aqueous solution of activating agent is lower than 20 dynes per centimeters.
In order to which hydrophilic lipophilic balance guarantees splendid wetability between 7 to 9, preferably, the fluorinated surfactant exists
Solubility is no more than 10wt% in water, and the fluorinated surfactant all dissolves in ethanol.And select hexafluoropropylene oxide three
350 monomethyl ether of aggressiveness polyethylene glycol, which determines that solubility is no more than 10wt% in water, all molten in ethanol
Solution.
In order to guarantee hot press moulding process safety, while can be evaporated completely within requiring perfluorocarbon solvents room temperature lower 30 seconds
Finish, preferably, the boiling point of the perfluorocarbon solvents is at 40 degree or more and at 110 degree hereinafter, the perfluorocarbon solvents do not dodge
Point.
Zero odp (consumption ozone when the perfluorocarbon solvents are for perfluoropolyether hydrogen ether and fluorinated surfactant mixture
Latent energy value) low GWP (chamber effect potential value) diluent, it can be any suitable perfluorocarbon solvents, preferably, the perfluor
Carbon solvent is the compound indicated by following molecular formula: C6F12。
The alcoholic solvent is less toxic inflammability solvent, and dynamic and static surface tension is low, effectively increases the hydrophilic of perfluorocarbon solvents
Performance reduces cost, can be any suitable alcoholic solvent, preferably, the alcoholic solvent be selected from trifluoroethanol (abbreviation TFE) and
Hexafluoroisopropanol (abbreviation HFIP) it is one or more.
The oiliness solubilizer is less toxic inflammability solvent, and dynamic static surface tension is extremely low, effectively increases perfluorocarbon solvents
Oleophylic performance, reduce cost, can be any suitable oiliness solubilizer, preferably, the oiliness solubilizer be selected from 1,2-
One of the bis- benzotrifluorides of double benzotrifluorides, 1,3- and the bis- benzotrifluorides of 1,4- are a variety of.Their molecular formula is
C6H4C2F6(abbreviation XHF, there is o-XHF (1,2- bis- benzotrifluorides), m-XHF (1,3- bis- benzotrifluorides) and p-XHF (Isosorbide-5-Nitrae-bis- three
Toluene fluoride) three kinds of isomers, preferably m-XHF.
The corrosion inhibiter is both sexes fluorinated surfactant: with fluorinated surfactant compatibility composite emulsifying perfluoropolyether hydrogen ether,
And be beneficial to protect brass precision die smooth finish surface, preferably, the corrosion inhibiter includes indicating any by following molecular formula
A kind of compound or mixture: CF3CF2CF2O-(CF(CF3)CF2O)k-CONHCH2CH2CH2N(C2H5)2·CH3I, wherein k=2
Or 3.CF is selected in embodiment3(CF2)2OCF(CF3)CF2OCF(CF3)CF2OCONH(CH2)3N(C2H5)2·CH3I (is contracted with FC-3
Write) and CF3(CF2)2O(CF(CF3)CF2O)2CF(CF3)CF2OCONH(CH2)3N(C2H5)2·CH3The mixing of I (being abridged with FC-4)
Object is abridged with FC-34.
In order to be more clearly understood that technology contents of the invention, spy lifts following embodiment and is described in detail.All hundred
Divide and be weight percentage than, unless otherwise specified.
HFPO-2000 (Hai Sifu chemical industry Co., Ltd, perfluoropolyether hydrogen ether 2000, purity 100%);
HFPO-4000 (Hai Sifu chemical industry Co., Ltd, perfluoropolyether hydrogen ether 4000, purity 100%);
HFPO-6000 (Hai Sifu chemical industry Co., Ltd, perfluoropolyether hydrogen ether 6000, purity 100%);
HFPO-8000 (Hai Sifu chemical industry Co., Ltd, perfluoropolyether hydrogen ether 8000, purity 100%);
HFPO (3) mpeg 3 50 (Hai Sifu chemical industry Co., Ltd, the poly- second two of hexafluoropropylene oxide tripolymer
350 monomethyl ether of alcohol, purity 95%);
HFPO (3) MPEG550 (Hai Sifu chemical industry Co., Ltd, the poly- second two of hexafluoropropylene oxide tripolymer
550 monomethyl ether of alcohol, purity 95%);
HFPD (Hai Sifu chemical industry Co., Ltd, hexafluoropropylene dimmer, purity 99.9%);
HFIP (Hai Sifu chemical industry Co., Ltd, hexafluoroisopropanol, purity 99.5%);
FC-34 (Hai Sifu chemical industry Co., Ltd, dimerization of hexafluoropropene oxide body amido propyl quaternary ammonium chelated iodine
With hexafluoropropylene oxide tripolymer amido propyl quaternary ammonium chelated iodine mixture, purity 95%);
FC-3 (Hai Sifu chemical industry Co., Ltd, dimerization of hexafluoropropene oxide body amido propyl quaternary ammonium chelated iodine,
Purity 95%);
FC-4 (Hai Sifu chemical industry Co., Ltd, hexafluoropropylene oxide tripolymer amido propyl quaternary ammonium chelated iodine,
Purity 95%).
Embodiment 1:
Said components are uniformly mixed by said ratio and obtain release agent 1.
Embodiment 2:
Said components are uniformly mixed by said ratio and obtain release agent 2.
Embodiment 3:
Said components are uniformly mixed by said ratio and obtain release agent 3.
Embodiment 4:
Said components are uniformly mixed by said ratio and obtain release agent 4.
Comparative example 1:
HFPO-2000 2.00wt%
HFPD 98.00wt%
Said components are uniformly mixed by said ratio and obtain comparison release agent 1.
Comparative example 2:
HFPO-4000 1.00wt%
HFPD 75.00wt%
M-XHF 24.00wt%
Said components are uniformly mixed by said ratio and obtain comparison release agent 2.
Comparative example 3:
Said components are uniformly mixed by said ratio and obtain comparison release agent 3.
Comparative example 4:
Said components are uniformly mixed by said ratio and obtain comparison release agent 4.
Following assessment item is made to above-mentioned various embodiment and comparative examples:
1, flash-point is tested
Water-based solvent and two class material of oil-based solvent are inflammability solvent:
Trifluoroethanol (abbreviation TFE): 73.6 DEG C/flash-point of boiling point, 13 DEG C/25 DEG C 77.3 millimetress of mercury of vapour pressure
Hexafluoroisopropanol (abbreviation HFIP): 59 DEG C/flash-point of boiling point, 4.4 DEG C/20 DEG C 120 millimetress of mercury of vapour pressure
Between double benzotrifluorides (abbreviation XHF): 218.7 DEG C/flash-point of boiling point, 95.9 DEG C/25 DEG C 0.183 millimetress of mercury of vapour pressure
According to Chinese invention patent CN102985506B (application number 201180033889.8, denomination of invention: noninflammability solvent
And surface treating agent) describe, three of the above solvent is used in mixed way constantly with HFE class or PFC class fluorocarbon solvent, noninflammability accounting
Between 3.75-10wt%, so embodiment and comparative example can be assessed with flash-point test.
Flash-point is tested in two steps, and sequence arrangement from low to high, flash-point uses the silent agar diffusion method of Bin Siji-Martin lower than 79 DEG C
(GB/T261-2008 standard), 79 DEG C or less can not measure flash-point and then use Cleveland opening agar diffusion method (GB/T3536-2008 mark
It is quasi-).
2, demolding performace is tested
To evaluate detachability, mold release compositions of the invention are sprayed to (5 centimetres of size (width) * 7 centimetres of latten(-tin)
* 0.3 centimetre of (length) (thickness)), precoating part sample then is made after sufficiently dry solvent.This is not sprayed by another with all-purpose adhesive
The latten(-tin) of the mold release compositions of invention is mutually bonded with the precoating part sample, if the shearing peeling force of adhesive layer is less than
The composition of 100 every square metre of gram forces is indicated with √, otherwise is greater than composition use × expression of 100 every square metre of gram forces.
3, life test is demoulded
Sticking to mould can need shaping again to evaluate with fold occurs when film manufactured goods depanning.Mold release compositions are sprayed
After being coated onto test die head, behind the number of pressing mold will count on sticking to mould next time.Pressing mold number can be used for evaluating holding for release agent
Long property.Mold pressing resin is poly (ether ether ketone) film, 1.5 meters of film breadth, 5 microns of thickness.Sticking mould number does not reach 50 times and uses √
It indicates, sticking mould number is not lower than 50 use × expressions.
4, release agent residue is tested
Bonding due to release agent to PEEK film has residual on just spraying release agent initial film manufactured goods, thin
Film web is 1.5 meters wide, and 5 microns of thickness.When being wiped with absolute alcohol swab stick after less than 3 times moldings not no release agent situation
It is indicated with √, not situation use × expression of release agent after 3 moldings or more.
5, release agent cost compares
Due to selecting hydrofluoroether such as 3M HFE-7100/7200 and ASAHI in Chinese invention patent application CN1799805A
GLASS AE 3000 is obtained because being produced using electrolysis method technique, during which can generate a large amount of wastes, processing cost height also results in
Hydrofluoroether price is very high, and perfluorocarbon solvents obtain and by domestic price cheap hexafluoropropene direct polymerization, with hydrofluoroether
Compared to differing 3 to 5 times in price, there are very big comparative advantages on the market this guarantees the release agent, monovalent cost is lower than
100 yuans are indicated with √, are indicated lower than 250 yuans with 〇 higher than 100 yuans, and are higher than 250 yuans
With × indicate.
The above test result is shown in Table 1.
The evaluation result of 1 release agent of table
Therefore, the present invention provides a kind of 5 microns of thickness ultra-thin polyether-ether-ketone film parting agent specials, have efficiently, environmental protection,
Non-ignitable feature, is characterized in particular in:
1, efficiently: 1) film slice is not necessarily to secondary reshaping;2) after there is no release agent residue because of film surface to not influence
Continuous and fine copper voice coil cementitiousness;3) excellent high temperature resistance ability, die surface clean noncoking, without often cleaning;4) for
Precision electronic components do not have silicone oil pollution.
2, environmental-friendly: 1) perfluoropolyether hydrogen ether (abbreviation HFPOn) is by hexafluoropropylene oxide (abbreviation HFPO) catalytic polymerization
Any perfluorooctanoic acid (abbreviation PFOA) or perfluoro octane sulfonate (contracting are not generated into perfluorocarbon compound, in production process
Write PFOS);2) perfluorocarbon solvents (abbreviation PFC) are selected from hexafluoropropylene dimmer (abbreviation HFPD);3) fluorinated surfactant is gentle
Releasing agent is also the compound being derived via hexafluoropropylene oxide;4) release agent is free of chlorine, bromo element, so will not destroy big
Gas ozone layer.
3, economical: release agent of the invention selects perfluorocarbon solvents, by direct by the cheap hexafluoropropene of domestic price
Polymerization and obtain, it is at low cost, and in Chinese invention patent application CN1799805A select hydrofluoroether such as 3M HFE-7100/7200 with
ASAHI GLASS AE 3000, cost is very high, and perfluorocarbon solvents differ 3 to 5 times compared with hydrofluoroether in price, this
Ensure that release agent of the invention on the market has very big price advantage.
4, non-ignitable: according to Chinese invention patent CN102985506B (application number 201180033889.8, denomination of invention: no
Combustion property solvent and surface treating agent) it describes, three of the above solvent is non-ignitable when being used in mixed way with HFE class or PFC class fluorocarbon solvent
Property accounting is between 3.75-10wt%.
In conclusion 5 microns of the thickness ultra-thin polyether-ether-ketone film parting agent specials that high-efficiency environment friendly economy of the invention is non-ignitable
Suitable for 5 microns of thickness ultra-thin polyether-ether-ketone film high efficiency manufactures, so that film slice is not necessarily to secondary reshaping, film surface does not take off
For mould agent residual to not influence subsequent and fine copper voice coil cementitiousness, excellent high temperature resistance ability, die surface cleans noncoking, nothing
It need to often clean, there is no silicone oil pollution for precision electronic components, and ingenious in design, prepare easy, environmental protection, it is economical, it is non-ignitable, it fits
In large-scale promotion application.
In this description, the present invention is described with reference to its specific embodiment.But it is clear that can still make
Various modifications and alterations are without departing from the spirit and scope of the invention.Therefore, specification should be considered as illustrative rather than limit
Property processed.
Claims (13)
1. a kind of 5 microns of the thickness that high-efficiency environment friendly economy is non-ignitable ultra-thin polyether-ether-ketone film parting agent specials, which is characterized in that including
Following components and its weight percentage:
Wherein, the perfluoropolyether hydrogen ether includes or mixtures thereof any one compound indicated by following molecular formula:
CF3CF2CF2O(C3F6O)n-CHFCF3, wherein 10≤n≤60, n are integer;
The fluorinated surfactant includes any one compound or mixture indicated by following molecular formula: CF3CF2CF2O-
(CF(CF3)CF2O)x-COOAmBiOCH3, wherein 0≤m≤10,3≤i≤10, A=C3H6O, B=C2H4O;
The corrosion inhibiter includes any one compound or mixture indicated by following molecular formula: CF3CF2CF2O-(CF(CF3)
CF2O)k-CONHCH2CH2CH2N(C2H5)2·CH3I, wherein k=2 or 3.
2. 5 microns of thickness non-ignitable ultra-thin polyether-ether-ketone film parting agent specials of high-efficiency environment friendly economy according to claim 1,
It is characterized in that, 10≤n≤40.
3. 5 microns of thickness non-ignitable ultra-thin polyether-ether-ketone film parting agent specials of high-efficiency environment friendly economy according to claim 2,
It is characterized in that, the perfluoropolyether hydrogen ether in HFPO-2000, HFPO-4000, HFPO-6000 and HFPO-8000 one
Kind is a variety of.
4. 5 microns of thickness non-ignitable ultra-thin polyether-ether-ketone film parting agent specials of high-efficiency environment friendly economy according to claim 1,
It is characterized in that, the perfluoropolyether hydrogen ether in 121 degree of 24 hours fugitive constituents less than 3% (v/v), the perfluoropolyether hydrogen ether is not
With flash-point.
5. 5 microns of thickness non-ignitable ultra-thin polyether-ether-ketone film parting agent specials of high-efficiency environment friendly economy according to claim 1,
It is characterized in that, the perfluoropolyether hydrogen ether at 25 degree surface tension less than 20 dynes per centimeters.
6. 5 microns of thickness non-ignitable ultra-thin polyether-ether-ketone film parting agent specials of high-efficiency environment friendly economy according to claim 1,
It is characterized in that, 0≤m≤3,5≤i≤8.
7. 5 microns of thickness non-ignitable ultra-thin polyether-ether-ketone film parting agent specials of high-efficiency environment friendly economy according to claim 6,
It is characterized in that, the fluorinated surfactant is 350 monomethyl ether of hexafluoropropylene oxide tripolymer polyethylene glycol.
8. 5 microns of thickness non-ignitable ultra-thin polyether-ether-ketone film parting agent specials of high-efficiency environment friendly economy according to claim 1,
It is characterized in that, the static surface tension of the aqueous solution of the fluorinated surfactant containing 0.1wt% is lower than 20 dynes per centimeters.
9. 5 microns of thickness non-ignitable ultra-thin polyether-ether-ketone film parting agent specials of high-efficiency environment friendly economy according to claim 1,
It is characterized in that, solubility is no more than 10wt% to the fluorinated surfactant in water, the fluorinated surfactant is in ethanol
All dissolutions.
10. 5 microns of the thickness non-ignitable ultra-thin dedicated demouldings of polyether-ether-ketone film of high-efficiency environment friendly economy according to claim 1
Agent, which is characterized in that the boiling point of the perfluorocarbon solvents is at 40 degree or more and at 110 degree hereinafter, the perfluorocarbon solvents do not have
There is flash-point.
11. 5 microns of the thickness non-ignitable ultra-thin dedicated demouldings of polyether-ether-ketone film of high-efficiency environment friendly economy according to claim 1
Agent, which is characterized in that the perfluorocarbon solvents are the compounds indicated by following molecular formula: C6F12。
12. 5 microns of the thickness non-ignitable ultra-thin dedicated demouldings of polyether-ether-ketone film of high-efficiency environment friendly economy according to claim 1
Agent, which is characterized in that the alcoholic solvent is selected from the one or more of trifluoroethanol and hexafluoroisopropanol.
13. 5 microns of the thickness non-ignitable ultra-thin dedicated demouldings of polyether-ether-ketone film of high-efficiency environment friendly economy according to claim 1
Agent, which is characterized in that the oiliness solubilizer is 1,3- m-benzotrifluoride.