CN106758308A - A kind of thionyl base class solvent-borne type polyamide artificial leather manufacture method - Google Patents

A kind of thionyl base class solvent-borne type polyamide artificial leather manufacture method Download PDF

Info

Publication number
CN106758308A
CN106758308A CN201610132488.2A CN201610132488A CN106758308A CN 106758308 A CN106758308 A CN 106758308A CN 201610132488 A CN201610132488 A CN 201610132488A CN 106758308 A CN106758308 A CN 106758308A
Authority
CN
China
Prior art keywords
artificial leather
paint
borne type
class solvent
base class
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610132488.2A
Other languages
Chinese (zh)
Inventor
朱广和
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangyin Huadong Plastic Products Co Ltd
Original Assignee
Jiangyin Huadong Plastic Products Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangyin Huadong Plastic Products Co Ltd filed Critical Jiangyin Huadong Plastic Products Co Ltd
Publication of CN106758308A publication Critical patent/CN106758308A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of thionyl base class solvent-borne type polyamide artificial leather manufacture method; it is to use thionyl base class solvent-borne type polyamide to configure to cover with paint, lacquer, colour wash, etc. slurry; then slurry will be covered with paint, lacquer, colour wash, etc. to cover with paint, lacquer, colour wash, etc. in artificial leather base fabric surface; the polyamide artificial leather for being dyeed by dyeing treatment again, covering with paint, lacquer, colour wash, etc. slurry includes the component of following mass parts:100 parts of thionyl base class solvent-borne type polyamide, 20~120 parts of dimethylformamide, 20~120 parts of acetone.Thionyl base class solvent-borne type polyamide is used as artificial leather top finishing material; dyeing process can be carried out with dyestuff; color effects by that can obtain dyestuff coloring after dyeing treatment, make product have the characteristics of bright-colored, coating permeability is good, surface color fastness is high, color animal migration is small.

Description

A kind of thionyl base class solvent-borne type polyamide artificial leather manufacture method
Technical field
The invention belongs to polyamide artificial leather preparation method technical field, and in particular to a kind of sulfurous for being easy to dye The manufacture method of acyl group class solvent-borne type polyamide artificial leather.
Background technology
Surface has the artificial leather of dyestuff coloring effect, and its bright in luster, transparency is high, is applied to the fashion such as case and bag women's shoes It is loved by people on product, but conventional synthesis leather generally uses pigment coloring mode, it is impossible to and reaching dyestuff coloring is had Effect, although dyestuff coloring effect can be obtained using the manufacture method that the coloring of dyestuff water colouring agent is added in coating material, But this manufacture method can bring serious colour migration to move, poor color fastness, the problems such as cost price is high, making for product is constrained With.
In traditional synthetic leather manufacturing process, mill base, toner and organic dyestuff, metal network need to be added in coating paste
The coloring materials such as dyestuff are closed, so that assign finished leather different colors, but coat colorization feel is partially hard, and coloring formula is once It is determined that after, coating is presented solid color, and gloss and color and luster are dull, without the stereovision such as the depth, light and shade, new and old.Exploitation is just In dyeing artificial leather be those skilled in the art need thinking problem.
The content of the invention
The technical problems to be solved by the invention are directed to above-mentioned prior art and provide a kind of polyamide people be easy to and dye Fabricate-leather, can be dyeed with dyestuff, and product has the characteristics of bright-colored, coating permeability is good, surface color fastness is high.
The present invention the used technical scheme that solves the above problems is:A kind of thionyl base class solvent-borne type polyamide people Fabricate-leather manufacture method, is to use thionyl base class solvent-borne type polyamide to configure to cover with paint, lacquer, colour wash, etc. slurry, then will cover with paint, lacquer, colour wash, etc. slurry and cover with paint, lacquer, colour wash, etc. In artificial leather base fabric surface, then the polyamide artificial leather dyeed by dyeing treatment;
Covering with paint, lacquer, colour wash, etc. slurry includes the component of following mass parts:
100 parts of thionyl base class solvent-borne type polyamide
20~120 parts of dimethylformamide
20~120 parts of acetone.
Preferably, the covering with paint is to make surface technology by release liners dry method to paste thionyl base class solvent-borne type polyamide surface layer Close in artificial leather wet half-finished product.
Preferably described covering with paint is that thionyl base class solvent-borne type polyamide is covered with paint, lacquer, colour wash, etc. into slurry with surface printing method to cover with paint, lacquer, colour wash, etc. in people Fabricate-leather dry method surface of semi-finished.
Preferably, the covering with paint is that thionyl base class solvent-borne type polyamide is applied into finish coat with rolling method to be coated with to artificial leather Base fabric surface of semi-finished.
Described dyeing
Polyamide artificial leather in the present invention is easy to dyeing, and dyeing processing mode includes pad dyeing, dye gigging, overflow dyeing or gas Stream dyeing.
Compared with prior art, the advantage of the invention is that:Using thionyl base class solvent-borne type polyamide as people Fabricate-leather top finishing material, can carry out dyeing process with dyestuff, the color effect by that can obtain dyestuff coloring after dyeing treatment Really, making product has the characteristics of bright-colored, coating permeability is good, surface color fastness is high, color animal migration is small, with common artificial leather Dyeing is few compared to dyestuff usage amount, and dyeing time is very short, and dyeing can be completed compared with low temperature, dyeing is relatively simple, into This relatively low, energy saving.
Specific embodiment
The present invention is described in further detail with reference to embodiments.
Embodiment 1
Thionyl base class solvent-borne type polyamide artificial leather manufacture method, is to use thionyl base class solvent-borne type polyamide Slurry is covered with paint, lacquer, colour wash, etc. in configuration, then will be covered with paint, lacquer, colour wash, etc. slurry and is covered with paint, lacquer, colour wash, etc. in artificial leather base fabric surface, and foregoing covering with paint is to make face by release liners dry method Technology fits in artificial leather wet half-finished product thionyl base class solvent-borne type polyamide surface layer, then is obtained by pad dyeing treatment The polyamide artificial leather of dyeing.
Covering with paint, lacquer, colour wash, etc. slurry includes the component of following mass parts:
100 parts of thionyl base class solvent-borne type polyamide
100 parts of dimethylformamide
80 parts of acetone.
Embodiment 2
Thionyl base class solvent-borne type polyamide artificial leather manufacture method, is to use thionyl base class solvent-borne type polyamide Slurry is covered with paint, lacquer, colour wash, etc. in configuration, then will be covered with paint, lacquer, colour wash, etc. slurry and be covered with paint, lacquer, colour wash, etc. in artificial leather base fabric surface, and foregoing covering with paint is to use surface printing method by sulfurous Acyl group class solvent-borne type polyamide is covered with paint, lacquer, colour wash, etc. slurry and is covered with paint, lacquer, colour wash, etc. in artificial leather dry method surface of semi-finished, then is dyeed by dye gigging treatment Polyamide artificial leather.
Covering with paint, lacquer, colour wash, etc. slurry includes the component of following mass parts:
100 parts of thionyl base class solvent-borne type polyamide
80 parts of dimethylformamide
60 parts of acetone.
Embodiment 3
Thionyl base class solvent-borne type polyamide artificial leather manufacture method, is to use thionyl base class solvent-borne type polyamide Slurry is covered with paint, lacquer, colour wash, etc. in configuration, then will be covered with paint, lacquer, colour wash, etc. slurry and be covered with paint, lacquer, colour wash, etc. in artificial leather base fabric surface, and foregoing covering with paint is to use rolling method by thionyl Base class solvent-borne type polyamide applies finish coat coating to artificial leather base fabric's surface of semi-finished, then it is to be contaminated to be processed by airflow dyeing The polyamide artificial leather of color.
Covering with paint, lacquer, colour wash, etc. slurry includes the component of following mass parts:
100 parts of thionyl base class solvent-borne type polyamide
80 parts of dimethylformamide
100 parts of acetone.
Embodiment 4
Thionyl base class solvent-borne type polyamide artificial leather manufacture method, is to use thionyl base class solvent-borne type polyamide Slurry is covered with paint, lacquer, colour wash, etc. in configuration, then will be covered with paint, lacquer, colour wash, etc. slurry and be covered with paint, lacquer, colour wash, etc. in artificial leather base fabric surface, and foregoing covering with paint is to use surface printing method by sulfurous Acyl group class solvent-borne type polyamide is covered with paint, lacquer, colour wash, etc. slurry and is covered with paint, lacquer, colour wash, etc. in artificial leather dry method surface of semi-finished, then it is to obtain to be processed by overflow dyeing The polyamide artificial leather of dyeing.
Covering with paint, lacquer, colour wash, etc. slurry includes the component of following mass parts:
100 parts of thionyl base class solvent-borne type polyamide
80 parts of dimethylformamide
60 parts of acetone.

Claims (5)

1. a kind of thionyl base class solvent-borne type polyamide artificial leather manufacture method, it is characterised in that:It is to use sulfinyl Slurry is covered with paint, lacquer, colour wash, etc. in the configuration of class solvent-borne type polyamide, then will be covered with paint, lacquer, colour wash, etc. slurry and is covered with paint, lacquer, colour wash, etc. in artificial leather base fabric surface, then by dyeing The polyamide artificial leather that treatment is dyeed,
Covering with paint, lacquer, colour wash, etc. slurry includes the component of following mass parts:
100 parts of thionyl base class solvent-borne type polyamide
20~120 parts of dimethylformamide
20~120 parts of acetone.
2. thionyl base class solvent-borne type polyamide artificial leather manufacture method according to claim 1, it is characterised in that: The covering with paint is to make surface technology by release liners dry method thionyl base class solvent-borne type polyamide surface layer is fitted into artificial leather wet method On semi-finished product.
3. thionyl base class solvent-borne type polyamide artificial leather manufacture method according to claim 1, it is characterised in that: The covering with paint is that thionyl base class solvent-borne type polyamide is covered with paint, lacquer, colour wash, etc. into slurry with surface printing method to cover with paint, lacquer, colour wash, etc. in artificial leather dry method semi-finished product Surface.
4. thionyl base class solvent-borne type polyamide artificial leather manufacture method according to claim 1, it is characterised in that: The covering with paint is that thionyl base class solvent-borne type polyamide is applied into finish coat with rolling method to be coated with to artificial leather base fabric's surface of semi-finished.
5. thionyl base class solvent-borne type polyamide artificial leather manufacture method according to claim 1, it is characterised in that: The dyeing treatment is pad dyeing, dye gigging, overflow dyeing or airflow dyeing.
CN201610132488.2A 2015-11-21 2016-03-10 A kind of thionyl base class solvent-borne type polyamide artificial leather manufacture method Pending CN106758308A (en)