CN106757710A - A kind of napping fabric and its dyeing and finishing processing method with knitting rib-loop outward appearance - Google Patents
A kind of napping fabric and its dyeing and finishing processing method with knitting rib-loop outward appearance Download PDFInfo
- Publication number
- CN106757710A CN106757710A CN201710107209.1A CN201710107209A CN106757710A CN 106757710 A CN106757710 A CN 106757710A CN 201710107209 A CN201710107209 A CN 201710107209A CN 106757710 A CN106757710 A CN 106757710A
- Authority
- CN
- China
- Prior art keywords
- fabric
- napping
- outward appearance
- yarn
- weft yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a kind of napping fabric with knitting rib-loop outward appearance and its dyeing and finishing processing method, the napping fabric is formed by warp thread and weft yarns, it is characterised in that：Warp thread is cotton yarn, and weft yarn uses two groups of yarns, and weft yarn one is spun polyester thread, and weft yarn two is island composite filament；Fabric tissue uses Warp Satin tissue, and fabric is napping face through face；The island composite filament is that sea island filament and high-shrinkage polyester low stretch yarn are composited, the boiling water shrinkage of the boiling water shrinkage less than island composite filament of the spun polyester thread.Its dyeing and finishing processing method include turning over cloth margin to seam → enzyme desizing → kiering → bleaching → fibrillation → tentering of singing → roll brighten → through the operation of face napping → stamp → evaporate → wash → softness sizing → preshrunk → finished product clot.Not only outward appearance has a knitting rib-loop effect to napping fabric of the invention, and feel fluffy insulation knitting comfort.
Description
Technical field
The invention belongs to household textiles field, and in particular to a kind of napping fabric and its dye with knitting rib-loop outward appearance
Finishing processing method.
Background technology
Weft knitting fabric has ventilative, the excellent elasticity and extensibility and productibility of soft texture, moisture absorption, in clothes
Had a wide range of applications on fabric.Current textile fabric industry of being in, due to knitting fabric preferably softness skin-friendly, is consumed
Person widely likes.But, knitting application of dress material but has certain limitation in home textile industry, and main cause has：1. knitted side
Material is easily decoherenced in itself, crimping, easily hooks silk, sturdy and durable not as good as shuttle-woven fabric；2. a textile fabric is presently mainly and based on wide cut, receives
Equipment limit, the circular knitting machine that can meet door width requirement is less；3. influenceed by the edge-rolling of knitting fabric, the sanction of knitting fabric
The special equipment that need to be equipped with is cut and sews, therefore fabric processing is extremely inconvenient.
Current tatting napping or napping fabric extensively get consumer reception in autumn and winter bed necessaries fabric in the market.Although napping fabric
Possess certain warming and soft comfortable degree, but fiber is in process, is injured by mechanicals efforts and chemical reagent, fiber
Strength is impaired, and napping fabric hair loss phenomenon is than more serious, the serious cleannes that have impact on people bedroom in use, from
And bring puzzlement to life.So fabric would generally be increased through the radical lifting tightness of weft yarn or add finishing agent to reduce
Hair, but the soft degree of fabric can be influenceed.
Therefore, a few tatting napping fabric but also with knitting appearance of soft, hair loss is developed, with very big
Market prospects.
The content of the invention
The technical problem of solution：The purpose of the present invention is the limitation for overcoming knitting application of dress material in home textile industry, napping
The technical problem that fabric hair loss phenomenon is serious, pliability is poor, there is provided a kind of napping fabric and its dye with knitting rib-loop outward appearance
Finishing processing method.
Technical scheme：A kind of napping fabric with knitting rib-loop outward appearance, is formed by warp thread and weft yarns, and warp thread is complete
Cotton, weft yarn uses two groups of yarns, and weft yarn one is spun polyester thread, and weft yarn two is island composite filament；Fabric tissue is used through face
Satin weave, fabric is napping face through face；The island composite filament is that sea island filament and high-shrinkage polyester low stretch yarn are composited,
Boiling water shrinkage of the boiling water shrinkage of the spun polyester thread less than island composite filament.
Further, weft yarn one and the picking ratio of weft yarn two are 1:1.
Further, the warp thread is the cotton yarn of 20S-60S；The weft yarn one is the polyester low stretch of 75D-250D
Silk, weft yarn two is the island composite filament of 80D-250D.
Further, the F numbers ratio of sea island filament and high-shrinkage polyester low stretch yarn is 2 in the island composite filament:1-4:1.
Further, the yarn count of the sea island filament is 50D-150D, and the yarn count of the high-shrinkage polyester low stretch yarn is 30D-
90D。
The dyeing and finishing processing method of the above-mentioned napping fabric with knitting rib-loop outward appearance, including turn over cloth margin to seam → singe → roll enzyme
Desizing → kiering → bleaching → fibrillation → tentering brightens → through face napping → stamp → evaporate → wash → soft sizing → preshrunk
The operation of → finished product clot；The temperature of working solution is more than 80 DEG C in kiering, bleaching, fibrillation, washing step.
Further, concentration of caustic soda is 50-55g/L in the working solution that the fibrillation operation is used.
Further, in the napping operation, using the rubber of 600 mesh, all platen pressures are 1-2bar, rotating speed
1800-2400r/min。
Further, in the soft shaping process, setting temperature is 140-150 DEG C, shaping time 30-40s.Fluff type
Softening agent 55g/L, smooth type softening agent 8g/L.
Beneficial effect：Napping fabric warp thread with knitting rib-loop outward appearance of the invention uses cotton yarn, weft yarn to use
Two kinds of the close low elastic polyester filament of yarn count and the island composite filament with high-shrinkage polyester low stretch yarn；Using two kinds of boiling water of weft yarn
The difference of shrinkage factor, with reference to fiber opening process and sanding, forming outward appearance has knitting rib-loop effect, the pin of feel fluffy insulation
Knit comfort.
Specific embodiment
Invention is described in further detail below by specific embodiment.It will be apparent, however, to one skilled in the art, that
The following example is merely to illustrate the present invention, and should not be taken as limiting the scope of the invention.Unreceipted particular technique in embodiment
Or condition person, (for example write with reference to Shen Lan duckweeds according to the technology or condition described by document in the art《Fabric construction with set
Meter》, China Textiles Press, 2005) or carried out according to product description.
A kind of napping fabric with knitting rib-loop outward appearance of the present invention, is formed by warp thread and weft yarns, and warp thread is cotton
Yarn, weft yarn uses two groups of yarns, and weft yarn one is spun polyester thread, and weft yarn two is island composite filament；Fabric tissue is used through face satin
Line tissue, fabric is napping face through face；The island composite filament is that sea island filament and high-shrinkage polyester low stretch yarn are composited, institute
State the boiling water shrinkage of the boiling water shrinkage less than island composite filament of spun polyester thread.Preferably, the boiling water shrinkage of weft yarn two is
25%-30%, the boiling water shrinkage of weft yarn one is 3.5-4.5%.
The dyeing and finishing processing method of the napping fabric with knitting rib-loop outward appearance, including turn over cloth margin to seam → singe → roll enzyme desizing
→ kiering → bleaching → fibrillation → tentering brightens → through face napping → stamp → evaporate → wash → soft sizing → preshrunk → into
The operation of product clot；The temperature of working solution is more than 80 DEG C in kiering, bleaching, fibrillation, washing step.
By fiber opening process, the part in sea is thoroughly dissolved sea island filament, leaves the part on island, is formed in the composite filament of island
The superfine single fiber of fiber number, greatly reduces the rigidity of composite filament, is made fabric feeling extremely soft；A large amount of superfine monofilament are each other
Staggeredly, layer structure is formed, filoplume can be locked in the inner space of fabric, be difficult to drop.In kiering, bleaching, fibrillation, washing
Finishing process in, working solution temperature be more than 80 DEG C, because the boiling water shrinkage of weft yarn two is larger, Final finishing can be sent out by high temperature
It is raw to shrink, can form larger song in yarns in worsted fabric and take, form fabric feeling more fluffy.In addition, by Final finishing working solution
Afterwards, the sea part of sea island filament dissolves away in the island composite filament of weft yarn two, the diameter reduction of weft yarn two, weft yarn two simultaneously thinner than weft yarn one
Shrinkage degree is more than weft yarn one, and then drive is subjected to displacement to form knitting rib-loop outward appearance through interlacing point, and contractive effect also makes fabric
With the ductility for being similar to knitting fabric.
Fabric of the present invention is Warp Satin tissue, mainly participates in napping through face warp thread, and the weft yarn one of fabric uses terylene
Long filament, is not in the phenomenon of hair loss plumage during use.
Weft yarn one is 1 with the picking ratio of weft yarn two:1.Than identical, the shrinkage degree of fabric is most for weft yarn one and the picking of weft yarn two
For uniform, rib-loop is regular, also has best effect to preventing hair loss.
Warp thread is 20S-60S cotton yarns, and the weft yarn one close with the thickness of weft yarn two of weft yarn one is low elastic polyester filament, yarn count
It is 75D-250D, weft yarn two is the composite filament that sea island filament and high-shrinkage polyester low stretch yarn are composited, and yarn count is 80D-250D.
The sea island filament of weft yarn two and the F numbers ratio of high-shrinkage polyester low stretch yarn are 2:1-4:1.Present invention discover that in this F numbers ratio
Example scope interior energy plays the effect of the soft fluffy reduction hair loss that sea island filament brings after fibrillation, and can combine high-shrinkage polyester shape
Into knitting rib-loop appearance.Because in this F number proportion, high-shrinkage polyester F numbers are smaller, are heated after shrinking
Just cause that woven fabric possesses the obvious knitting distinctive extensibility of fabric and resilience.Sea island filament F numbers are larger, during fibrillation
Alkali lye mainly plays a part of to dissolve the part in sea in sea island filament, washs that corrasion is smaller to high convergency, a small number of high-shrinkage polyesters
Can just play a supporting role, reduce the loss of fabric broadwise strength.
Singeing step uses two forward one-reverses, speed 100-110m/min；The fire extinguishing of amylase working solution is padded, bank up 4-6h.
Concentration of caustic soda 30-40g/L in kiering operation kiering working solution.
Hydrogen peroxide concentration is that 8-12g/L steaming boxes are front and rear in bleaching process working solution 6-8 lattice high temperature rinsing bowls, vapour respectively
Steaming time 50-60min, steam temperature is 102-105 DEG C.
Concentration of caustic soda is 50-55g/L in fiber opening process working solution, and refining agent concentration is 4-8g/L, and TF101 concentration is 6g/
L, chelated dispersants concentration 8g/L.
Sanding is 1-2bar, rotating speed 1800-2400r/min using 6 rubbers of 600 mesh, platen pressure.Reduce
The rotating speed of rubber surface particles size and increasing rubber, obtains fine and closely woven down, and the instantaneous touch that reinforcement fabric brings is comfortable
Sense.
Embodiment 1
Warp thread uses 32S cotton yarns, weft yarn one to use the ordinary polyester low stretch yarn of 200D/72F, weft yarn two to use
The island composite filament (sea island filament 150D/48F, high-shrinkage polyester low stretch yarn 60D/12F) of 225D/72F, fabric specification is 108 '/
Cotton 32S* (ordinary polyester low stretch yarn 200D+ island composite filament 225D)/133*65, fabric tissue is 4/1 Warp Satin.
Embodiment 2
Warp thread uses 40S cotton yarns, weft yarn one to use the ordinary polyester low stretch yarn of 150D/48F, weft yarn two to use
The island composite filament (sea island filament 130D/48F, high-shrinkage polyester low stretch yarn 30D/12F) of 160D/60F, fabric specification is 108 '/
Cotton 40S* (ordinary polyester low stretch yarn 150D+ island composite filament 160D)/144*92, fabric tissue is 4/1 Warp Satin.
Reference examples 1
Difference with embodiment 1 is that weft yarn one and weft yarn two fineness after Final finishing treatment are approached, and fabric specification is
108 '/cotton 32S* (ordinary polyester low stretch yarn 150D+ island composite filament 225D)/133*66, fabric tissue is 4/1 Warp Satin.
Reference examples 2
It is the polyester filament as weft yarn one and weft yarn two use boiling water shrinkage, fabric with the difference of embodiment 1
Specification is 108 '/cotton 32S* ordinary polyester low stretch yarn 200D/133*68, and fabric tissue is 4/1 Warp Satin.
Each performance indications of finished product fabric
| Testing index | Embodiment 1 | Embodiment 2 | Reference examples 1 | Reference examples 2 |
| Hair shedding rate % | 0.4 | 0.3 | 0.5 | 0.9 |
| Softness | It is soft | It is soft | It is soft | It is harder |
| Fluffy degree | It is fluffy | It is fluffy | It is fluffy | Compared with plate |
| Rib-loop outward appearance | Possess | Possess | Do not possess | Do not possess |
Napping fabric warp thread with knitting rib-loop outward appearance of the invention uses cotton yarn, and weft yarn is close using yarn count
Two kinds of low elastic polyester filament and the island composite filament with high-shrinkage polyester low stretch yarn；Using two kinds of differences of the boiling water shrinkage of weft yarn
Not, with reference to fiber opening process and sanding, forming outward appearance has knitting rib-loop effect, the knitting comfort of feel fluffy insulation.
Claims (9)
1. a kind of napping fabric with knitting rib-loop outward appearance, is formed by warp thread and weft yarns, it is characterised in that：Warp thread is complete
Cotton, weft yarn uses two groups of yarns, and weft yarn one is spun polyester thread, and weft yarn two is island composite filament；Fabric tissue is used through face
Satin weave, fabric is napping face through face；The island composite filament is that sea island filament and high-shrinkage polyester low stretch yarn are composited,
Boiling water shrinkage of the boiling water shrinkage of the spun polyester thread less than island composite filament.
2. the napping fabric with knitting rib-loop outward appearance according to claim 1, it is characterised in that：Weft yarn one and weft yarn two
Picking ratio be 1:1.
3. the napping fabric with knitting rib-loop outward appearance according to claim 1, it is characterised in that：The warp thread is 20S-
The cotton yarn of 60S；The weft yarn one is the low elastic polyester filament of 75D-250D, and weft yarn two is the island composite filament of 80D-250D.
4. the napping fabric with knitting rib-loop outward appearance according to claim 1, it is characterised in that：The island composite filament
The F numbers ratio of middle sea island filament and high-shrinkage polyester low stretch yarn is 2:1-4:1.
5. the napping fabric with knitting rib-loop outward appearance according to claim 1, it is characterised in that：The yarn of the sea island filament
Branch is 50D-150D, and the yarn count of the high-shrinkage polyester low stretch yarn is 30D-90D.
6. the dyeing and finishing processing method of the napping fabric with knitting rib-loop outward appearance described in claim 1, it is characterised in that：Including
Turn over cloth margin to seam → enzyme desizing → kiering → bleaching → fibrillation → tentering of singing → roll brighten → through face napping → stamp → evaporate →
The operation of washing → soft sizing → preshrunk → finished product clot；The temperature of working solution in kiering, bleaching, fibrillation, washing step
More than 80 DEG C.
7. the dyeing and finishing processing method of the napping fabric with knitting rib-loop outward appearance according to claim 6, it is characterised in that：
Concentration of caustic soda is 50-55g/L in the working solution that the fibrillation operation is used.
8. the dyeing and finishing processing method of the napping fabric with knitting rib-loop outward appearance according to claim 6, it is characterised in that：
In the napping operation, using the rubber of 600 mesh, all platen pressures are 1-2bar, rotating speed 1800-2400r/min.
9. the dyeing and finishing processing method of the napping fabric with knitting rib-loop outward appearance according to claim 6, it is characterised in that：
In the soft shaping process, setting temperature is 140-150 DEG C, and shaping time 30-40s, fluff type softening agent 55g/L are smoothed
The g/L of type softening agent 8.