CN106753855A - A kind of good glass cleaner of corrosion-free clean effect - Google Patents
A kind of good glass cleaner of corrosion-free clean effect Download PDFInfo
- Publication number
- CN106753855A CN106753855A CN201611068622.3A CN201611068622A CN106753855A CN 106753855 A CN106753855 A CN 106753855A CN 201611068622 A CN201611068622 A CN 201611068622A CN 106753855 A CN106753855 A CN 106753855A
- Authority
- CN
- China
- Prior art keywords
- parts
- sodium
- vinyl acetate
- corrosion
- clean effect
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of good glass cleaner of corrosion-free clean effect, belong to cleaning agent field, be specifically made up of following material:Modified vinyl acetate polymer, glycerine, OPEO, NPE, polyoxyethylene carboxylate, propylene glycol monomethyl ether, sodium pyrophosphate, sodium alginate, diethyl phosphate, tartaric acid, sodium tetraborate, essence, deionized water.Each material composition collocation of the present invention is reasonable, and obtained glass cleaner has good clean effect, and will not damage glass, and finally glass is cleaned again also without with water, easy to use, there is good promotional value.
Description
Technical field
The invention belongs to cleaning agent field, and in particular to a kind of good glass cleaner of corrosion-free clean effect.
Background technology
Mobile phone has turned into one of present age people instrument essential in living.It is more and more with the development of technology
Mobile phone move towards intelligent, technology sense also constantly strengthens, and makes a general survey of existing most smart mobile phones, and glass board material is mobile phone production material
The most important thing in material, especially display screen, are almost made by glass board material.Mobile phone during normal use most intuitively lacks
Point is exactly that glass board material does not bear dirty, and either fingerprint or dust, cover all at one glance on glass material, reduce the use of people
Impression, it is therefore desirable to clean operation is carried out to glass board material surface, glass cleaner arises at the historic moment.Have in traditional cleaning agent
Using poisonous organic solvent, what is had then easily produces corrosion to other structures, and some cleaning performances are not good.Therefore develop a kind of comprehensive
Close the good glass cleaner of effect and seem particularly necessary.
The content of the invention
The present invention is intended to provide a kind of good glass cleaner of corrosion-free clean effect.
The present invention is achieved through the following technical solutions:
A kind of good glass cleaner of corrosion-free clean effect, is made up of the material of following weight portion:
1.5 ~ 2.5 parts of modified vinyl acetate polymers, 13 ~ 16 parts of glycerine, 3 ~ 5 parts of OPEOs, 2 ~ 4 parts of nonyls
Phenol polyethenoxy ether, 1 ~ 3 part of polyoxyethylene carboxylate, 2 ~ 5 parts of propylene glycol monomethyl ethers, 3 ~ 6 parts of sodium pyrophosphates, 2 ~ 4 parts of alginic acids
Sodium, 1 ~ 3 part of diethyl phosphate, 0.3 ~ 0.5 part of tartaric acid, 0.5 ~ 1 part of sodium tetraborate, 1 ~ 1.5 part of essence, 110 ~ 120 parts go from
Sub- water;The modified vinyl acetate polymer is made up of the material of following weight portion:55 ~ 60 parts of vinyl acetates, 6 ~ 9 parts of acryloyls
Oxy-ethyl-trimethyl salmiac, 4 ~ 7 parts of methyl methacrylates, 3 ~ 5 parts of styrene, 2 ~ 4 parts of triethyl phosphates, 1 ~ 3 part according to ground
Sour calcium sodium.
Preferably, it is made up of the material of following weight portion:
2 parts of modified vinyl acetate polymers, 14 parts of glycerine, 4 parts of OPEOs, 3 parts of NPEs,
2 parts of polyoxyethylene carboxylates, 4 parts of propylene glycol monomethyl ethers, 5 parts of sodium pyrophosphates, 3 parts of sodium alginates, 2 parts of diethyl phosphates, 0.4 part
Tartaric acid, 0.8 part of sodium tetraborate, 1.2 parts of essence, 115 parts of deionized waters;The modified vinyl acetate polymer is by following weight
The material of part is made:57 parts of vinyl acetates, 8 parts of acrylyl oxy-ethyl-trimethyl salmiacs, 6 parts of methyl methacrylates, 4 parts of benzene
Ethene, 3 parts of triethyl phosphates, 2 parts of mosatils.
Further, the preparation method of the modified vinyl acetate polymer is by vinyl acetate, acrylyl oxy-ethyl three
Ammonio methacrylate, methyl methacrylate, styrene, triethyl phosphate, mosatil mix jointly, with ethanol as molten
Agent, azodiisobutyronitrile is initiator, and temperature is to be polymerized under conditions of 65 ~ 67 DEG C.
, specifically be polymerized for modified vinyl acetate by a kind of preparation method of the good glass cleaner of corrosion-free clean effect
Thing, glycerine, OPEO, NPE, polyoxyethylene carboxylate, propylene glycol monomethyl ether, burnt phosphorus
Sour sodium, sodium alginate, diethyl phosphate, tartaric acid, sodium tetraborate, essence and deionized water mix jointly, are put into container, plus
Heat is stirred until homogeneous to 54 ~ 58 DEG C with 700 ~ 900 revs/min of rotating speed.
The present invention has the advantages that:
The present invention rationally adds arranged in pairs or groups APEO, NPE and aliphatic acid with deionized water as solvent
Polyoxyethylene ester composition, enhances the scattered uniformity of each material composition and stability, the modified vinyl acetate polymer of addition
Can strengthen Adsorption effect of the cleaning agent to dirt particle, and can be after cleaning glass surface on form diaphragm, strengthen
Its resistant effect.Under the common mating reaction of each material composition, the obtained glass cleaner of the present invention has good decontamination
Effect, and glass will not be damaged, finally glass is cleaned again also without with water, it is easy to use, have well
Promotional value.
Specific embodiment
Embodiment 1
A kind of good glass cleaner of corrosion-free clean effect, is made up of the material of following weight portion:
1.5 parts of modified vinyl acetate polymers, 13 parts of glycerine, 3 parts of OPEOs, 2 parts of Nonyl phenos
Ether, 1 part of polyoxyethylene carboxylate, 2 parts of propylene glycol monomethyl ethers, 3 parts of sodium pyrophosphates, 2 parts of sodium alginates, 1 part of diethyl phosphate,
0.3 part of tartaric acid, 0.5 part of sodium tetraborate, 1 part of essence, 110 parts of deionized waters;The modified vinyl acetate polymer is by as follows
The material of weight portion is made:55 parts of vinyl acetates, 6 parts of acrylyl oxy-ethyl-trimethyl salmiacs, 4 parts of methyl methacrylates, 3
Part styrene, 2 parts of triethyl phosphates, 1 part of mosatil.
Further, the preparation method of the modified vinyl acetate polymer is by vinyl acetate, acrylyl oxy-ethyl three
Ammonio methacrylate, methyl methacrylate, styrene, triethyl phosphate, mosatil mix jointly, with ethanol as molten
Agent, azodiisobutyronitrile is initiator, and temperature is to be polymerized under conditions of 66 DEG C.
, specifically be polymerized for modified vinyl acetate by a kind of preparation method of the good glass cleaner of corrosion-free clean effect
Thing, glycerine, OPEO, NPE, polyoxyethylene carboxylate, propylene glycol monomethyl ether, burnt phosphorus
Sour sodium, sodium alginate, diethyl phosphate, tartaric acid, sodium tetraborate, essence and deionized water mix jointly, are put into container, plus
Heat is stirred until homogeneous to 56 DEG C with 800 revs/min of rotating speed.
Embodiment 2
A kind of good glass cleaner of corrosion-free clean effect, is made up of the material of following weight portion:
2 parts of modified vinyl acetate polymers, 14 parts of glycerine, 4 parts of OPEOs, 3 parts of NPEs,
2 parts of polyoxyethylene carboxylates, 4 parts of propylene glycol monomethyl ethers, 5 parts of sodium pyrophosphates, 3 parts of sodium alginates, 2 parts of diethyl phosphates, 0.4 part
Tartaric acid, 0.8 part of sodium tetraborate, 1.2 parts of essence, 115 parts of deionized waters;The modified vinyl acetate polymer is by following weight
The material of part is made:57 parts of vinyl acetates, 8 parts of acrylyl oxy-ethyl-trimethyl salmiacs, 6 parts of methyl methacrylates, 4 parts of benzene
Ethene, 3 parts of triethyl phosphates, 2 parts of mosatils.Remaining method and step is with embodiment 1.
Embodiment 3
A kind of good glass cleaner of corrosion-free clean effect, is made up of the material of following weight portion:
2.5 parts of modified vinyl acetate polymers, 16 parts of glycerine, 5 parts of OPEOs, 4 parts of Nonyl phenos
Ether, 3 parts of polyoxyethylene carboxylates, 5 parts of propylene glycol monomethyl ethers, 6 parts of sodium pyrophosphates, 4 parts of sodium alginates, 3 parts of diethyl phosphates,
0.5 part of tartaric acid, 1 part of sodium tetraborate, 1.5 parts of essence, 120 parts of deionized waters;The modified vinyl acetate polymer is by as follows
The material of weight portion is made:60 parts of vinyl acetates, 9 parts of acrylyl oxy-ethyl-trimethyl salmiacs, 7 parts of methyl methacrylates, 5
Part styrene, 4 parts of triethyl phosphates, 3 parts of mosatils.Remaining method and step is with embodiment 1.
Comparative example 1
This comparative example 1 compared with Example 1, with etc. weight portion acrylate copolymer substituting modification vinyl acetate be polymerized
Thing, method and step all same in addition.
Comparative example 2
This comparative example 2 compared with Example 2, does not contain modified vinyl acetate polymer in its composition, method in addition
Step all same.
Control group
Existing glass cleaner.
In order to contrast effect of the present invention, as experimental subjects, it is made from the existing common third generation " gorilla " glass
The glass print of a height of 10mm × 7mm of length and width × 1mm, is placed under identical environment natural laying dust 7 days, then respectively with above-mentioned six
The cleaning agent that the method for kind is prepared carries out cleaning treatment to it, and table 1 below is counted for corresponding contrast situation:
Table 1
Cleaning performance is evaluated | There is white point rate in glass print after cleaning(%) | |
Embodiment 1 | It is good | 0.12 |
Embodiment 2 | It is good | 0.09 |
Embodiment 3 | It is good | 0.10 |
Comparative example 1 | Preferably | 0.54 |
Comparative example 2 | Preferably | 0.82 |
Control group | Preferably | 0.89 |
Note:Cleaning performance described in upper table 1 is evaluated using artificial sense, more few better with visible dirt particle number;After cleaning
Glass print occur white point rate refer to the glass print surface after cleaning agent treatment there is white point account for overall ratio, be used to comment
Corrosion and damage characteristic of the valency cleaning agent to glass.
By can be seen that the obtained cleaning agent cleaning performance of the present invention in upper table 1 more preferably, the infringement to glass is smaller, more
Tool popularizing value.
Claims (4)
1. the good glass cleaner of a kind of corrosion-free clean effect, it is characterised in that be made up of the material of following weight portion:
1.5 ~ 2.5 parts of modified vinyl acetate polymers, 13 ~ 16 parts of glycerine, 3 ~ 5 parts of OPEOs, 2 ~ 4 parts of nonyls
Phenol polyethenoxy ether, 1 ~ 3 part of polyoxyethylene carboxylate, 2 ~ 5 parts of propylene glycol monomethyl ethers, 3 ~ 6 parts of sodium pyrophosphates, 2 ~ 4 parts of alginic acids
Sodium, 1 ~ 3 part of diethyl phosphate, 0.3 ~ 0.5 part of tartaric acid, 0.5 ~ 1 part of sodium tetraborate, 1 ~ 1.5 part of essence, 110 ~ 120 parts go from
Sub- water;The modified vinyl acetate polymer is made up of the material of following weight portion:55 ~ 60 parts of vinyl acetates, 6 ~ 9 parts of acryloyls
Oxy-ethyl-trimethyl salmiac, 4 ~ 7 parts of methyl methacrylates, 3 ~ 5 parts of styrene, 2 ~ 4 parts of triethyl phosphates, 1 ~ 3 part according to ground
Sour calcium sodium.
2. the good glass cleaner of a kind of corrosion-free clean effect according to claim 1, it is characterised in that by weighing as follows
The material for measuring part is made:
2 parts of modified vinyl acetate polymers, 14 parts of glycerine, 4 parts of OPEOs, 3 parts of NPEs,
2 parts of polyoxyethylene carboxylates, 4 parts of propylene glycol monomethyl ethers, 5 parts of sodium pyrophosphates, 3 parts of sodium alginates, 2 parts of diethyl phosphates, 0.4 part
Tartaric acid, 0.8 part of sodium tetraborate, 1.2 parts of essence, 115 parts of deionized waters;The modified vinyl acetate polymer is by following weight
The material of part is made:57 parts of vinyl acetates, 8 parts of acrylyl oxy-ethyl-trimethyl salmiacs, 6 parts of methyl methacrylates, 4 parts of benzene
Ethene, 3 parts of triethyl phosphates, 2 parts of mosatils.
3. the good glass cleaner of a kind of corrosion-free clean effect according to claim 1 and 2, it is characterised in that described
The preparation method of modified vinyl acetate polymer is by vinyl acetate, acrylyl oxy-ethyl-trimethyl salmiac, methacrylic acid
Methyl esters, styrene, triethyl phosphate, mosatil mix jointly, and with ethanol as solvent, azodiisobutyronitrile is initiation
Agent, temperature be 65 ~ 67 DEG C under conditions of be polymerized.
4. a kind of preparation method of the good glass cleaner of corrosion-free clean effect as claimed in claim 1 or 2, its feature exists
In specifically by modified vinyl acetate polymer, glycerine, OPEO, NPE, aliphatic acid
Polyoxyethylene ester, propylene glycol monomethyl ether, sodium pyrophosphate, sodium alginate, diethyl phosphate, tartaric acid, sodium tetraborate, essence and go from
Sub- water mixes jointly, is put into container, is heated to 54 ~ 58 DEG C, is stirred until homogeneous with 700 ~ 900 revs/min of rotating speed.