CN106752791A - 一种抗老化涂料及其制备方法 - Google Patents

一种抗老化涂料及其制备方法 Download PDF

Info

Publication number
CN106752791A
CN106752791A CN201611080511.4A CN201611080511A CN106752791A CN 106752791 A CN106752791 A CN 106752791A CN 201611080511 A CN201611080511 A CN 201611080511A CN 106752791 A CN106752791 A CN 106752791A
Authority
CN
China
Prior art keywords
component
parts
aging coating
curing agent
aging
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611080511.4A
Other languages
English (en)
Inventor
吴娟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Jingwei Technology Innovation Consulting Co Ltd
Original Assignee
Jiangsu Jingwei Technology Innovation Consulting Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Jingwei Technology Innovation Consulting Co Ltd filed Critical Jiangsu Jingwei Technology Innovation Consulting Co Ltd
Priority to CN201611080511.4A priority Critical patent/CN106752791A/zh
Publication of CN106752791A publication Critical patent/CN106752791A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种抗老化涂料及其制备方法，该涂料包括组分一与组分二，组分一包括：乙烯基甲苯醇酸树脂、膨润土、钛白粉、乙二胺、聚酯纤维、三氧化二铝、钛酸丁酯、丙二醇、醋酸乙酯、二苯甲烷二异氰酸酯和抗老化剂；组分二包括：固化剂和溶剂。其制备方法是先将乙烯基甲苯醇酸树脂、膨润土、钛白粉、乙二胺、钛酸丁酯、丙二醇、醋酸乙酯和二苯甲烷二异氰酸酯加入到反应釜中，然后加入剩余组分，得到组分一；然后将固化剂和溶剂相混合，得到组分二；最后将组分一与组分二混合，得到抗老化涂料。本发明所得抗老化涂料具有抗老化，耐高温，耐腐蚀等特性。

Description

一种抗老化涂料及其制备方法
技术领域
本发明属于化工涂料制备技术领域，具体涉及一种抗老化涂料及其制备方法。
背景技术
涂料是用有机或无机材料来以装饰和保护物品的一种混合物。涂料的起源尚无定论。公元前6000年，中国已用无机化合物和有机颜料混合焙烧对涂料加以改进。公元前1500年，在法国和西班牙的山洞里，涂料已用于绘画和装饰。公元前1500年，埃及人用染料如靛蓝和茜草制造蓝色和红色颜料，但这种涂料还很不完善。18世纪，由于对亚麻仁油和氧化锌的开发利用，使涂料工业迅速发展。20世纪，涂料工艺有了重大发展，出现了粘着力更大、光泽度更高、阻燃、抗腐蚀与热稳定性高的各种颜色的涂料涂料早期大多以植物油为主要原料，故被叫做“油漆”，如健康环保原生态的熟桐油。不论是传统的以天然物质为原料的涂料产品，还是现代发展中的以合成化工产品为原料的涂料产品，都属于有机化工高分子材料，所形成的涂膜属于高分子化合物类型。按照现代通行的化工产品的分类，涂料属于精细化工产品。现代的涂料正在逐步成为一类多功能性的工程材料，是化学工业中的一个重要行业。
涂料的抗老化性能一直是其比较重要的一方面，抗老化性能差的涂料在长期使用过程中会产生变色、脱皮等现将，严重影响了使用寿命，现有涂料在抗老化方面虽然具有了一定的保证，但是在特殊应用条件下如高温或高湿条件下的抗老化性能却较差。
发明内容
本发明的目的在于为了克服以上现有技术的不足而提供一种抗老化涂料及其制备方法，使得制备得到的涂料具有很好的高温与高湿条件下的耐老化作用。
本发明是采用以下技术手段实现的：
一种抗老化涂料，包括组分一与组分二，
其中组分一以重量组分计包括：乙烯基甲苯醇酸树脂20-30份，膨润土0.5-1份，钛白粉1-3份，乙二胺2-5份，聚酯纤维4-7份，三氧化二铝1-3份，钛酸丁酯4-7份，丙二醇2-4份、醋酸乙酯6-10份、二苯甲烷二异氰酸酯3-6份，抗老化剂1-3份；
组分二以重量组分计包括：固化剂10-20份，溶剂30-40份。
进一步地，组分一中三氧化二铝为纳米三氧化二铝。
进一步地，组分一中抗老化剂为受阻酚类抗氧化剂。
进一步地，组分二中固化剂为胺类固化剂。
进一步地，组分二中溶剂为甲醇、异丙醇和异丁醇的混合物，其中甲醇、异丙醇和异丁醇的质量比为10:3:5。
上述抗老化涂料的制备方法，包括以下步骤：
步骤一，按照重量份称取各组分；
步骤二，将乙烯基甲苯醇酸树脂、膨润土、钛白粉、乙二胺、钛酸丁酯、丙二醇、醋酸乙酯和二苯甲烷二异氰酸酯加入到反应釜中，在惰性气体保护条件下升温50-60℃，搅拌150-200分钟，得到混合物一；
步骤三，将剩余组分加入到混合物一中，搅拌混合后得到组分一；
步骤四，将固化剂和溶剂相混合，搅拌均匀，得到组分二；
步骤五，将组分一与组分二混合，得到抗老化涂料。
本发明所得抗老化涂料具有抗老化，耐高温，耐腐蚀等特性。
具体实施方式
实施例1
一种抗老化涂料，包括组分一与组分二，
其中组分一以重量组分计包括：乙烯基甲苯醇酸树脂20份，膨润土0.5份，钛白粉1份，乙二胺2份，聚酯纤维4份，三氧化二铝1份，钛酸丁酯4份，丙二醇2份、醋酸乙酯6份、二苯甲烷二异氰酸酯3份，抗老化剂1份；
组分二以重量组分计包括：固化剂10份，溶剂30份。
其中，组分一中三氧化二铝为纳米三氧化二铝，抗老化剂为受阻酚类抗氧化剂；组分二中固化剂为胺类固化剂，溶剂为甲醇、异丙醇和异丁醇的混合物，其中甲醇、异丙醇和异丁醇的质量比为10:3:5。
上述抗老化涂料的制备方法，包括以下步骤：
步骤一，按照重量份称取各组分；
步骤二，将乙烯基甲苯醇酸树脂、膨润土、钛白粉、乙二胺、钛酸丁酯、丙二醇、醋酸乙酯和二苯甲烷二异氰酸酯加入到反应釜中，在惰性气体保护条件下升温50-60℃，搅拌150-200分钟，得到混合物一；
步骤三，将剩余组分加入到混合物一中，搅拌混合后得到组分一；
步骤四，将固化剂和溶剂相混合，搅拌均匀，得到组分二；
步骤五，将组分一与组分二混合，得到抗老化涂料。
实施例2
一种抗老化涂料，包括组分一与组分二，
其中组分一以重量组分计包括：乙烯基甲苯醇酸树脂24份，膨润土0.8份，钛白粉2份，乙二胺4份，聚酯纤维6份，三氧化二铝2份，钛酸丁酯6份，丙二醇3份、醋酸乙酯8份、二苯甲烷二异氰酸酯5份，抗老化剂2份；
组分二以重量组分计包括：固化剂17份，溶剂36份。
其中，组分一中三氧化二铝为纳米三氧化二铝，抗老化剂为受阻酚类抗氧化剂；组分二中固化剂为胺类固化剂，溶剂为甲醇、异丙醇和异丁醇的混合物，其中甲醇、异丙醇和异丁醇的质量比为10:3:5。
上述抗老化涂料的制备方法，包括以下步骤：
步骤一，按照重量份称取各组分；
步骤二，将乙烯基甲苯醇酸树脂、膨润土、钛白粉、乙二胺、钛酸丁酯、丙二醇、醋酸乙酯和二苯甲烷二异氰酸酯加入到反应釜中，在惰性气体保护条件下升温50-60℃，搅拌150-200分钟，得到混合物一；
步骤三，将剩余组分加入到混合物一中，搅拌混合后得到组分一；
步骤四，将固化剂和溶剂相混合，搅拌均匀，得到组分二；
步骤五，将组分一与组分二混合，得到抗老化涂料。
实施例3
一种抗老化涂料，包括组分一与组分二，
其中组分一以重量组分计包括：乙烯基甲苯醇酸树脂30份，膨润土1份，钛白粉3份，乙二胺5份，聚酯纤维7份，三氧化二铝3份，钛酸丁酯7份，丙二醇4份、醋酸乙酯10份、二苯甲烷二异氰酸酯6份，抗老化剂3份；
组分二以重量组分计包括：固化剂20份，溶剂40份。
其中，组分一中三氧化二铝为纳米三氧化二铝，抗老化剂为受阻酚类抗氧化剂；组分二中固化剂为胺类固化剂，溶剂为甲醇、异丙醇和异丁醇的混合物，其中甲醇、异丙醇和异丁醇的质量比为10:3:5。
上述抗老化涂料的制备方法，包括以下步骤：
步骤一，按照重量份称取各组分；
步骤二，将乙烯基甲苯醇酸树脂、膨润土、钛白粉、乙二胺、钛酸丁酯、丙二醇、醋酸乙酯和二苯甲烷二异氰酸酯加入到反应釜中，在惰性气体保护条件下升温50-60℃，搅拌150-200分钟，得到混合物一；
步骤三，将剩余组分加入到混合物一中，搅拌混合后得到组分一；
步骤四，将固化剂和溶剂相混合，搅拌均匀，得到组分二；
步骤五，将组分一与组分二混合，得到抗老化涂料。
将实施例1至3所得涂料进行抗老化实验检测。将涂料涂抹于金属件上，在高温和高湿条件下放置3个月后金属件均出现老化现象。

Claims (6)

1.一种抗老化涂料，其特征在于，包括组分一与组分二，
其中组分一以重量组分计包括：乙烯基甲苯醇酸树脂20-30份，膨润土0.5-1份，钛白粉1-3份，乙二胺2-5份，聚酯纤维4-7份，三氧化二铝1-3份，钛酸丁酯4-7份，丙二醇2-4份、醋酸乙酯6-10份、二苯甲烷二异氰酸酯3-6份，抗老化剂1-3份；
组分二以重量组分计包括：固化剂10-20份，溶剂30-40份。
2.根据权利要求1所述的抗老化涂料，其特征在于，组分一中三氧化二铝为纳米三氧化二铝。
3.根据权利要求1所述的抗老化涂料，其特征在于，组分一中抗老化剂为受阻酚类抗氧化剂。
4.根据权利要求1所述的抗老化涂料，其特征在于，组分二中固化剂为胺类固化剂。
5.根据权利要求1所述的抗老化涂料，其特征在于，组分二中溶剂为甲醇、异丙醇和异丁醇的混合物，其中甲醇、异丙醇和异丁醇的质量比为10:3:5。
6.一种权利要求1-5任一项所述的抗老化涂料的制备方法，其特征在于，包括以下步骤：
步骤一，按照重量份称取各组分；
步骤二，将乙烯基甲苯醇酸树脂、膨润土、钛白粉、乙二胺、钛酸丁酯、丙二醇、醋酸乙酯和二苯甲烷二异氰酸酯加入到反应釜中，在惰性气体保护条件下升温50-60℃，搅拌150-200分钟，得到混合物一；
步骤三，将剩余组分加入到混合物一中，搅拌混合后得到组分一；
步骤四，将固化剂和溶剂相混合，搅拌均匀，得到组分二；
步骤五，将组分一与组分二混合，得到抗老化涂料。
CN201611080511.4A 2016-11-30 2016-11-30 一种抗老化涂料及其制备方法 Pending CN106752791A (zh)