CN106752603A - A kind of inner wall decoration acrylic coating and preparation method thereof - Google Patents
A kind of inner wall decoration acrylic coating and preparation method thereof Download PDFInfo
- Publication number
- CN106752603A CN106752603A CN201611187876.7A CN201611187876A CN106752603A CN 106752603 A CN106752603 A CN 106752603A CN 201611187876 A CN201611187876 A CN 201611187876A CN 106752603 A CN106752603 A CN 106752603A
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylic coating
- wall decoration
- decoration acrylic
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Present invention relates particularly to a kind of inner wall decoration acrylic coating；It is made up of the raw material of following parts by weight：20 150 parts of the secondary butyl ester emulsion of 30wt% polymethylacrylic acid, 10 20 parts of nitrocellulose, 5 30 parts of metal dust, 10 50 parts of 15wt% poly-vinyl alcohol solutions, 30 70 parts of ethanol, 25 40 parts of Wastewater by Nanometer Anatase titanium dioxide, 0.5 8 parts of fluorine-containing surfactant, 0.5 10 parts of silicon-containing surfactant, 5 15 parts of zinc oxide, 16 parts of auxiliary agent；The inner wall decoration acrylic coating that the present invention is provided has excellent guarantor's light of metallic luster, color, fast light, weather resistance and shelf-life more long is protected, additionally, present invention also offers the preparation method of supporting high-efficient simple.
Description
Technical field
The present invention relates to interior wall coating production technical field, and in particular to a kind of inner wall decoration acrylic coating and its system
Preparation Method.
Background technology
In coatings industry, acrylate is the more excellent thermoplastic resin of a class performance.Acrylate has
Have the advantage that：Good guarantor's color, Gloss Retention；Excellent color and luster；Good weatherability, impact resistance；Pliability is good etc..Cause
And, the field such as acrylate resin coating is widely used in decorating, decoratees, plastic alloy, packaging.
Acrylate resin coating in the market generally has that adhesive force is inadequate, the shelf-life is short when being used for glass material
Etc. defect, the quality of coating is greatly affected, it is impossible to meet the use demand of growing internal wall finishing.
The content of the invention
In view of the shortcomings of the prior art, the invention provides a kind of excellent guarantor's light with metallic luster, protect color, it is fast light,
The inner wall decoration acrylic coating of weather resistance, and its preparation method.
To realize object above, the present invention is achieved by the following technical programs：
A kind of inner wall decoration acrylic coating, is made up of the raw material of following parts by weight：
Further, described inner wall decoration acrylic coating, is made up of the raw material of following parts by weight：
Further, the degree of polymerization of the nitrocellulose is 1000-1200.
Further, the metal dust is selected from the one of which in copper powder, aluminium powder, zinc powder, copper zinc powder, stainless steel powder.
Further, the auxiliary agent is selected from least one in plasticizer, emulsifying agent, antifreezing agent and mould inhibitor.
A kind of preparation method of inner wall decoration acrylic coating, bag step is as follows：
(1) raw material of above-mentioned weight portion is measured respectively, it is standby；
(2) after being well mixed metal dust, Wastewater by Nanometer Anatase titanium dioxide and zinc oxide, input polymethylacrylic acid is secondary
In butyl ester emulsion, nitrocellulose, ethanol, fluorine-containing surfactant, silicon-containing surfactant and auxiliary agent are subsequently adding, through at a high speed
Dispersion machine is uniformly dispersed, and adds poly-vinyl alcohol solution, and stirring mixing is no less than 30 minutes, obtains final product.
Further, the stir speed (S.S.) in the step (2) is 1000-3000r/min.
The effect of each component is as follows：
Metal dust：Can have coating and brilliant color and luster is shone as gold and silver, will not be dimmed；
Anatase titanium dioxide：Improve coating weatherability；
Zinc oxide：With mould proof, antirust, prevent powdering of paint, moreover it is possible to improve the durability of coating；
Silica：Improve the thixotropy of coating；
Silicon-containing surfactant：Materials safety environmental protection, raising coating levelling, dispersion, wetting and antifoam performance；
Fluorine-containing surfactant：Molecule has high surface, is applied in coating, can obtain coating good
Dispersiveness, helps to extend the storage time of coating, it is to avoid the caking sedimentation of coating, causes failure.
Compared with prior art, the beneficial effects of the present invention are：
The formula that the present invention is provided rationally, and by the organic assembling of each raw material components, has obtained acrylic coating
There is excellent color and luster, protect light, protect color, fast light, weather resistance.
The acrylic coating that the present invention is provided has good dispersed and mould proof, rustless property, and Storage period is long, compared with market
Or so upper common Storage period half a year long of acrylic coating.
Acrylic coating low toxicity, formaldehydeless volatilization that the present invention is provided, paint film flat smooth, hard, toughness are moderate, adhesive force
By force, it is difficult for drop-off, long service life.
Specific embodiment
To make the purpose, technical scheme and advantage of the embodiment of the present invention clearer, below in conjunction with implementation of the invention
Example, is clearly and completely described to the technical scheme in the embodiment of the present invention.Based on the embodiment in the present invention, this area
The every other embodiment that those of ordinary skill is obtained under the premise of creative work is not made, belongs to protection of the present invention
Scope.
Embodiment 1：
A kind of inner wall decoration acrylic coating, is made up of the raw material of following parts by weight：
Further, the auxiliary agent is selected from least one in plasticizer, emulsifying agent, antifreezing agent and mould inhibitor.
Its preparation method, bag step is as follows：
(1) raw material of above-mentioned weight portion is measured respectively, it is standby；
(2) after being well mixed metal dust, Wastewater by Nanometer Anatase titanium dioxide and zinc oxide, input polymethylacrylic acid is secondary
In butyl ester emulsion, nitrocellulose, ethanol, fluorine-containing surfactant, silicon-containing surfactant and auxiliary agent are subsequently adding, through at a high speed
Dispersion machine is uniformly dispersed, and adds poly-vinyl alcohol solution, and stirring mixing is no less than 30 minutes, obtains final product.
Further, the stir speed (S.S.) in the step (2) is 1000-3000r/min.
Embodiment 2：
A kind of inner wall decoration acrylic coating, is made up of the raw material of following parts by weight：
Its preparation method is with embodiment 1.
Embodiment 3：
A kind of inner wall decoration acrylic coating, is made up of the raw material of following parts by weight：
Its preparation method is with embodiment 1.
Embodiment 4：
A kind of inner wall decoration acrylic coating, is made up of the raw material of following parts by weight：
Its preparation method is with embodiment 1.
Embodiment 5：
A kind of inner wall decoration acrylic coating, is made up of the raw material of following parts by weight：
Its preparation method is with embodiment 1.
The present invention compares compared with the partial properties of conventional acrylic coating, as shown in the table：
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations；Although with reference to the foregoing embodiments
The present invention has been described in detail, it will be understood by those within the art that：It still can be to foregoing each implementation
Technical scheme described in example is modified, or carries out equivalent to which part technical characteristic；And these modification or
Replace, do not make the spirit and scope of the essence disengaging various embodiments of the present invention technical scheme of appropriate technical solution.
Claims (7)
1. a kind of inner wall decoration acrylic coating, it is characterised in that be made up of the raw material of following parts by weight：
2. inner wall decoration acrylic coating as claimed in claim 1, it is characterised in that by the raw material group of following parts by weight
Into：
3. inner wall decoration acrylic coating as claimed in claim 1, it is characterised in that the degree of polymerization of the nitrocellulose
It is 1000-1200.
4. inner wall decoration acrylic coating as claimed in claim 1, it is characterised in that the metal dust be selected from copper powder,
One of which in aluminium powder, zinc powder, copper zinc powder, stainless steel powder.
5. inner wall decoration acrylic coating as claimed in claim 1, it is characterised in that the auxiliary agent is selected from plasticizer, breast
At least one in agent, antifreezing agent and mould inhibitor.
6. a kind of preparation method of inner wall decoration acrylic coating as any one of claim 1-5, its feature exists
In bag step is as follows：
(1) raw material of above-mentioned weight portion is measured respectively, it is standby；
(2) after being well mixed metal dust, Wastewater by Nanometer Anatase titanium dioxide and zinc oxide, the secondary butyl ester of polymethylacrylic acid is put into
In emulsion, nitrocellulose, ethanol, fluorine-containing surfactant, silicon-containing surfactant and auxiliary agent are subsequently adding, disperseed through high speed
Machine is uniformly dispersed, and adds poly-vinyl alcohol solution, and stirring mixing is no less than 30 minutes, obtains final product.
7. the preparation method of inner wall decoration acrylic coating as claimed in claim 6, it is characterised in that the step (2)
In stir speed (S.S.) be 1000-3000r/min.