CN106752515A - A kind of anti-skid wearable coating for forklift fixture - Google Patents
A kind of anti-skid wearable coating for forklift fixture Download PDFInfo
- Publication number
- CN106752515A CN106752515A CN201611145591.7A CN201611145591A CN106752515A CN 106752515 A CN106752515 A CN 106752515A CN 201611145591 A CN201611145591 A CN 201611145591A CN 106752515 A CN106752515 A CN 106752515A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- skid wearable
- toughener
- stabilizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anti-skid wearable coating for forklift fixture, the anti-skid wearable coating includes following components according to the mass fraction：20 30 parts of Hydroxylated acrylic resin, 15 20 parts of titanium dioxide, 48 parts of organosilicon, 37 parts of silicon dioxide gel, 5 11 parts of filler, 8 13 parts of anti-skid wearable powder, 12 parts of stabilizer, 13 parts of curing agent, 24 parts of toughener, 13 parts of thickener；The present invention possesses good non-skid property and anti-wear performance, and long service life.
Description
Technical field
It is specifically a kind of anti-skid wearable coating for forklift fixture the present invention relates to a kind of coating.
Background technology
The application of non-skid coating is continued to develop with people to the continuous pursuit of quality of life, and military affairs are applied to from earliest
It is widely used in the various aspects of life till now, forklift fixture can be worn and torn in transportation by certain, in transport one
During the more sliding goods in a little surfaces, can easily come off, so needing to add a coating on surface, increase non-skid property, but
Though single non-skid property coating skidproof effect preferably, is with the passing of time used, non-skid property is relatively low, and service life shortens, it is impossible to reach
The skidproof effect of permanent stabilization.
The content of the invention
The technical problems to be solved by the invention are, for the shortcoming that above prior art is present, there is provided one kind possesses good
The good good anti-wear performance of non-skid property, and long service life.
The present invention solve above technical problem technical scheme be：A kind of anti-skid wearable for forklift fixture is provided to apply
Material, the anti-skid wearable coating includes following components according to the mass fraction：Hydroxylated acrylic resin 20-30 parts, titanium dioxide 15-20
Part, organosilicon 4-8 part, silicon dioxide gel 3-7 parts, filler 5-11 parts, 8-13 parts of anti-skid wearable powder, stabilizer 1-2 parts, consolidate
Agent 1-3 parts, toughener 2-4 parts, thickener 1-3 parts；
Described filler includes following components according to the mass fraction：Carbon fiber powder 6-11 parts, nano-silica powder 13-25 parts,
Carbon black 6-12 parts, zinc acrylate resin 13-17 parts, phthalic acid 3-7 parts；Described anti-skid wearable powder is Buddha's warrior attendant
The mixture of sand, hollow ceramic micro mist and gluey graphite powder；The toughener is dioctyl phthalate；The stabilizer is
Zinc stearate；The curing agent is hydroxyalkyl amide；The thickener is dioctyl phthalate or the fourth of phthalic acid two
One kind in ester.
The technical scheme that further limits of the invention is：
Foregoing anti-skid wearable coating includes following components according to the mass fraction：Hydroxylated acrylic resin 23-30 parts, titanium dioxide
17-20 parts, organosilicon 5-8 parts, silicon dioxide gel 5-7 parts, filler 5-9 parts, 10-13 parts of anti-skid wearable powder, stabilizer 1
Part, curing agent 1-2 parts, toughener 2-3 parts, thickener 1-2 parts；
Filler includes following components according to the mass fraction：Carbon fiber powder 8-11 parts, nano-silica powder 13-18 parts, carbon black
8-12 parts, zinc acrylate resin 13-15 parts, phthalic acid 3-4 parts；Described anti-skid wearable powder is diamond dust, hollow
The mixture of ceramic and gluey graphite powder；The toughener is dioctyl phthalate；The stabilizer is stearic acid
Zinc；The curing agent is hydroxyalkyl amide；The thickener is in dioctyl phthalate or dibutyl phthalate
It is a kind of.
Foregoing anti-skid wearable coating includes following components according to the mass fraction：Hydroxylated acrylic resin 26-30 parts, titanium white
Powder 18-20 parts, organosilicon 7-8 parts, silicon dioxide gel 5-6 parts, filler 5-7 parts, 12-13 parts of anti-skid wearable powder, stabilizer 2
Part, 2 parts of curing agent, 3 parts of toughener, 2 parts of thickener；
Filler includes following components according to the mass fraction：Carbon fiber powder 10-11 parts, nano-silica powder 15-18 parts, charcoal
Black 10-12 parts, zinc acrylate resin 14-15 parts, 3 parts of phthalic acid；Described anti-skid wearable powder be diamond dust, in
The mixture of empty ceramic and gluey graphite powder；The toughener is dioctyl phthalate；The stabilizer is tristearin
Sour zinc；The curing agent is hydroxyalkyl amide；The thickener is in dioctyl phthalate or dibutyl phthalate
One kind.
Foregoing anti-skid wearable preparation method for coating is comprised the following steps：
Step one：By diamond dust, hollow ceramic micro mist and gluey graphite powder co-grinding polishing, 60 mesh sieves are crossed, obtain anti-skidding resistance to
Milling material, it is standby；
Step 2：Add reactor to be uniformly mixed polyacrylate copolymerization liquid solution and phthalic acid, be subsequently adding
Carbon fiber powder, nano-silica powder, carbon black continue to stir, and obtain filler, standby；
Step 3：Hydroxylated acrylic resin, titanium dioxide, organosilicon and nanometer titanium dioxide aluminium are added into reactor according to said ratio
In, stirred with 350-400r/min, 20-30min is stirred, temperature is heated to 65-78 DEG C, is subsequently adding stabilizer, toughener, increasing
Thick dose and curing agent, continue to stir 55-65min with 450-530r/min, and temperature rises to 80-87 DEG C, is incubated 30-40min, then
It is cooled to room temperature, stand for standby use；
Step 4：The filler that the anti-skid wearable powder and step 2 that step one is obtained are obtained is added in step 3 in solution,
1-2h is stirred with 300-400r/min.
The beneficial effects of the invention are as follows：The anti-skid wearable coating that technical solution of the present invention is provided, skid resistance is excellent, while
With good abrasion resistance, nano material is with the addition of, by increasing capacitance it is possible to increase its adhesive ability, improve the mechanical strength of coating；The present invention
Preparation method it is simple, the coating of preparation has good durability.
Specific embodiment
Embodiment 1
The present embodiment provide a kind of anti-skid wearable coating for forklift fixture, anti-skid wearable coating according to the mass fraction include with
Lower component：It is 25 parts of Hydroxylated acrylic resin, 17 parts of titanium dioxide, 6 parts of organosilicon, 5 parts of silicon dioxide gel, 6 parts of filler, anti-skidding resistance to
11 parts of milling material, 1 part of stabilizer, 1 part of curing agent, 2 parts of toughener, 1 part of thickener；
Filler includes following components according to the mass fraction：9 parts of carbon fiber powder, 15 parts of nano-silica powder, 8 parts of carbon black,
13 parts of zinc acrylate resin, 4 parts of phthalic acid；Anti-skid wearable powder is diamond dust, hollow ceramic micro mist and gluey graphite
The mixture of powder；Toughener is dioctyl phthalate；Stabilizer is zinc stearate；The curing agent is hydroxyalkyl amide；
Thickener is dioctyl phthalate.
A kind of anti-skid wearable preparation method for coating for forklift fixture of the present embodiment is comprised the following steps：
Step one：By diamond dust, hollow ceramic micro mist and gluey graphite powder co-grinding polishing, 60 mesh sieves are crossed, obtain anti-skidding resistance to
Milling material, it is standby；
Step 2：Add reactor to be uniformly mixed polyacrylate copolymerization liquid solution and phthalic acid, be subsequently adding
Carbon fiber powder, nano-silica powder, carbon black continue to stir, and obtain filler, standby；
Step 3：Hydroxylated acrylic resin, titanium dioxide, organosilicon and nanometer titanium dioxide aluminium are added into reactor according to said ratio
In, stirred with 350r/min, 30min is stirred, temperature is heated to 70 DEG C, is subsequently adding stabilizer, toughener, thickener and solidification
Agent, continues to stir 65min with 450r/min, and temperature rises to 83 DEG C, is incubated 37min, is subsequently cooled to room temperature, stand for standby use；
Step 4：The filler that the anti-skid wearable powder and step 2 that step one is obtained are obtained is added in step 3 in solution,
2h is stirred with 320r/min.
Embodiment 2
The present embodiment provide a kind of anti-skid wearable coating for forklift fixture, anti-skid wearable coating according to the mass fraction include with
Lower component：It is 28 parts of Hydroxylated acrylic resin, 19 parts of titanium dioxide, 7 parts of organosilicon, 6 parts of silicon dioxide gel, 7 parts of filler, anti-skidding resistance to
13 parts of milling material, 2 parts of stabilizer, 2 parts of curing agent, 3 parts of toughener, 2 parts of thickener；
Filler includes following components according to the mass fraction：11 parts of carbon fiber powder, 17 parts of nano-silica powder, carbon black 10
Part, 14 parts of zinc acrylate resin, 3 parts of phthalic acid；Anti-skid wearable powder is diamond dust, hollow ceramic micro mist and gluey stone
The mixture of ink powder；Toughener is dioctyl phthalate；Stabilizer is zinc stearate；The curing agent is hydroxyalkyl acyl
Amine；Thickener is dioctyl phthalate.
A kind of anti-skid wearable preparation method for coating for forklift fixture of the present embodiment is comprised the following steps：
Step one：By diamond dust, hollow ceramic micro mist and gluey graphite powder co-grinding polishing, 60 mesh sieves are crossed, obtain anti-skidding resistance to
Milling material, it is standby；
Step 2：Add reactor to be uniformly mixed polyacrylate copolymerization liquid solution and phthalic acid, be subsequently adding
Carbon fiber powder, nano-silica powder, carbon black continue to stir, and obtain filler, standby；
Step 3：Hydroxylated acrylic resin, titanium dioxide, organosilicon and nanometer titanium dioxide aluminium are added into reactor according to said ratio
In, stirred with 400r/min, 24min is stirred, temperature is heated to 78 DEG C, is subsequently adding stabilizer, toughener, thickener and solidification
Agent, continues to stir 55min with 520r/min, and temperature rises to 85 DEG C, is incubated 33min, is subsequently cooled to room temperature, stand for standby use；
Step 4：The filler that the anti-skid wearable powder and step 2 that step one is obtained are obtained is added in step 3 in solution,
1h is stirred with 400r/min.
In addition to the implementation, the present invention can also have other embodiment.All use equivalents or equivalent transformation shape
Into technical scheme, all fall within the protection domain of application claims.
Claims (4)
1. a kind of anti-skid wearable coating for forklift fixture, it is characterised in that the anti-skid wearable coating is according to the mass fraction
Including following components：Hydroxylated acrylic resin 20-30 parts, titanium dioxide 15-20 parts, organosilicon 4-8 parts, silicon dioxide gel 3-7
Part, filler 5-11 parts, 8-13 parts of anti-skid wearable powder, stabilizer 1-2 parts, curing agent 1-3 parts, toughener 2-4 parts, thickener 1-
3 parts；
Described filler includes following components according to the mass fraction：Carbon fiber powder 6-11 parts, nano-silica powder 13-25 parts,
Carbon black 6-12 parts, zinc acrylate resin 13-17 parts, phthalic acid 3-7 parts；Described anti-skid wearable powder is Buddha's warrior attendant
The mixture of sand, hollow ceramic micro mist and gluey graphite powder；The toughener is dioctyl phthalate；The stabilizer is
Zinc stearate；The curing agent is hydroxyalkyl amide；The thickener is dioctyl phthalate or the fourth of phthalic acid two
One kind in ester.
2. the anti-skid wearable coating for forklift fixture according to claim 1, it is characterised in that the anti-skid wearable is applied
Material includes following components according to the mass fraction：Hydroxylated acrylic resin 23-30 parts, titanium dioxide 17-20 parts, organosilicon 5-8 parts, two
Silica sol 5-7 parts, filler 5-9 parts, 10-13 parts of anti-skid wearable powder, 1 part of stabilizer, curing agent 1-2 parts, toughener 2-3
Part, thickener 1-2 parts；
Described filler includes following components according to the mass fraction：Carbon fiber powder 8-11 parts, nano-silica powder 13-18 parts,
Carbon black 8-12 parts, zinc acrylate resin 13-15 parts, phthalic acid 3-4 parts；Described anti-skid wearable powder is Buddha's warrior attendant
The mixture of sand, hollow ceramic micro mist and gluey graphite powder；The toughener is dioctyl phthalate；The stabilizer is
Zinc stearate；The curing agent is hydroxyalkyl amide；The thickener is dioctyl phthalate or the fourth of phthalic acid two
One kind in ester.
3. the anti-skid wearable coating for forklift fixture according to claim 1, it is characterised in that the anti-skid wearable is applied
Material includes following components according to the mass fraction：Hydroxylated acrylic resin 26-30 parts, titanium dioxide 18-20 parts, organosilicon 7-8 parts, two
Silica sol 5-6 parts, filler 5-7 parts, 12-13 parts of anti-skid wearable powder, 2 parts of stabilizer, 2 parts of curing agent, 3 parts of toughener,
2 parts of thickener；
Described filler includes following components according to the mass fraction：Carbon fiber powder 10-11 parts, nano-silica powder 15-18
Part, carbon black 10-12 parts, zinc acrylate resin 14-15 parts, 3 parts of phthalic acid；Described anti-skid wearable powder is Buddha's warrior attendant
The mixture of sand, hollow ceramic micro mist and gluey graphite powder；The toughener is dioctyl phthalate；The stabilizer is
Zinc stearate；The curing agent is hydroxyalkyl amide；The thickener is dioctyl phthalate or the fourth of phthalic acid two
One kind in ester.
4. the anti-skid wearable coating for forklift fixture according to claim 1, it is characterised in that the anti-skid wearable is applied
Preparation method for material is comprised the following steps：
Step one：By diamond dust, hollow ceramic micro mist and gluey graphite powder co-grinding polishing, 60 mesh sieves are crossed, obtain anti-skidding resistance to
Milling material, it is standby；
Step 2：Add reactor to be uniformly mixed polyacrylate copolymerization liquid solution and phthalic acid, be subsequently adding
Carbon fiber powder, nano-silica powder, carbon black continue to stir, and obtain filler, standby；
Step 3：Hydroxylated acrylic resin, titanium dioxide, organosilicon and nanometer titanium dioxide aluminium are added into reactor according to said ratio
In, stirred with 350-400r/min, 20-30min is stirred, temperature is heated to 65-78 DEG C, is subsequently adding stabilizer, toughener, increasing
Thick dose and curing agent, continue to stir 55-65min with 450-530r/min, and temperature rises to 80-87 DEG C, is incubated 30-40min, then
It is cooled to room temperature, stand for standby use；
Step 4：The filler that the anti-skid wearable powder and step 2 that step one is obtained are obtained is added in step 3 in solution,
1-2h is stirred with 300-400r/min.