CN106752494A - A kind of environmental protection coating material - Google Patents
A kind of environmental protection coating material Download PDFInfo
- Publication number
- CN106752494A CN106752494A CN201611034837.3A CN201611034837A CN106752494A CN 106752494 A CN106752494 A CN 106752494A CN 201611034837 A CN201611034837 A CN 201611034837A CN 106752494 A CN106752494 A CN 106752494A
- Authority
- CN
- China
- Prior art keywords
- parts
- environmental protection
- coating material
- titanium dioxide
- protection coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of environmental protection coating material, it includes：The component of following mass percent：Lemon oil 1-3 parts, mandarin oil 1-3 parts, titanium dioxide 1-3 parts, carbon black 1-3 parts, portland cement 30-60 parts, water reducer 2-5 parts, algae clay 5-10 parts, solvent 1-3 parts, 20-60 parts, glyoxal 5-10 parts, n-butanol 5-10 parts, ethanol 5-10 parts, methylcellulose 5-10 parts, titanium dioxide 1-3 parts, dispersant 1-3 parts, filler 10-30 parts and water 10-30 parts of acrylic acid elastic resin emulsion；Environmental protection coating material of the present invention has used pure natural raw material, the coating more environmental protection of preparation, and stability is high, and coating adhesion is good, good toughness.
Description
Technical field
The present invention relates to a kind of environmental protection coating material, belong to technical field of environmental protection paint.
Background technology
Existing decoration coating type is a lot, with modern's human-subject test and growth in the living standard, to house ornamentation environmental protection
It is required that more and more higher, to meet the market requirement, coating material production producer to the research of environmental protection coating material also improving constantly, but it is existing
Environmental protection coating material can bring many problems, many coating can give out the harmful material such as formaldehyde after, it is impossible to full
Requirement of the sufficient people to environmental protection.
The content of the invention
（One）The technical problem to be solved
To solve the above problems, the present invention proposes a kind of environmental protection coating material and has used pure natural raw material, and the coating of preparation is more
Environmental protection, and stability is high, coating adhesion is good, the environmental protection coating material of good toughness.
（Two）Technical scheme
A kind of environmental protection coating material of the invention, it is characterised in that：Component including following mass percent：Lemon oil 1-3 parts, tangerine
Seed oil 1-3 parts, titanium dioxide 1-3 parts, carbon black 1-3 parts, portland cement 30-60 parts, water reducer 2-5 parts, algae clay 5-
10 parts, solvent 1-3 parts, 20-60 parts of acrylic acid elastic resin emulsion, glyoxal 5-10 parts, n-butanol 5-10 parts, ethanol
5-10 parts, methylcellulose 5-10 parts, titanium dioxide 1-3 parts, dispersant 1-3 parts, filler 10-30 parts and water 10-30
Part.
Further, comprise the following steps：（1）Lemon oil, mandarin oil, titanium dioxide, carbon black are mixed at normal temperatures
Uniformly；（2）By portland cement, water reducer, algae clay, acrylic acid elastic resin emulsion, glyoxal, n-butanol, ethanol, methyl
Cellulose, titanium dioxide, filler mixing and stirring at normal temperatures；（3）By step（1）And step（2）The product for drawing is poured into
In agitator, solvent, dispersant, water are added, slowly stirred, being gradually raised to 30 DEG C from 0 DEG C can be prepared by described environmental protection coating material.
（Three）Beneficial effect
Compared with prior art, it has the advantages that the present invention：Environmental protection coating material of the present invention has used pure natural original
Material, the coating more environmental protection of preparation, and stability is high, coating adhesion is good, good toughness.
Specific embodiment
Embodiment 1
A kind of environmental protection coating material, it is characterised in that：Component including following mass percent：1 part of lemon oil, 1 part of mandarin oil, titanium white
1 part of powder, 1 part of carbon black, 30 parts of portland cement, 2 parts of water reducer, 5 parts of algae clay, 1 part of solvent, acrylic acid elastic resin emulsion 20
Part, 5 parts of glyoxal, 5 parts of n-butanol, 5 parts of ethanol, 5 parts of methylcellulose, 1 part of titanium dioxide, 1 part of dispersant, 10 parts of filler and
10 parts of water；
Wherein, comprise the following steps：（1）By lemon oil, mandarin oil, titanium dioxide, carbon black mixing and stirring at normal temperatures；（2）
By portland cement, water reducer, algae clay, acrylic acid elastic resin emulsion, glyoxal, n-butanol, ethanol, methylcellulose,
Titanium dioxide, filler mixing and stirring at normal temperatures；（3）By step（1）And step（2）The product for drawing pours into agitator
In, solvent, dispersant, water are added, slowly stir, being gradually raised to 30 DEG C from 0 DEG C can be prepared by described environmental protection coating material.
Embodiment 2
A kind of environmental protection coating material, it is characterised in that：Component including following mass percent：3 parts of lemon oil, 3 parts of mandarin oil, titanium white
3 parts of powder, 3 parts of carbon black, 60 parts of portland cement, 5 parts of water reducer, 10 parts of algae clay, 3 parts of solvent, acrylic acid elastic resin emulsion
60 parts, 10 parts of glyoxal, 10 parts of n-butanol, 10 parts of ethanol, 10 parts of methylcellulose, 3 parts of titanium dioxide, 3 parts of dispersant, filler
30 parts and 30 parts of water.
Wherein, comprise the following steps：（1）By lemon oil, mandarin oil, titanium dioxide, carbon black mixing and stirring at normal temperatures；
（2）By portland cement, water reducer, algae clay, acrylic acid elastic resin emulsion, glyoxal, n-butanol, ethanol, Methyl cellulose
Element, titanium dioxide, filler mixing and stirring at normal temperatures；（3）By step（1）And step（2）The product for drawing pours into stirring
In bucket, solvent, dispersant, water are added, slowly stirred, being gradually raised to 30 DEG C from 0 DEG C can be prepared by described environmental protection coating material.
Embodiment 3
A kind of environmental protection coating material, it is characterised in that：Component including following mass percent：2 parts of lemon oil, 2 parts of mandarin oil, titanium white
2 parts of powder, 2 parts of carbon black, 50 parts of portland cement, 4 parts of water reducer, 7 parts of algae clay, 2 parts of solvent, acrylic acid elastic resin emulsion 30
Part, 8 parts of glyoxal, 8 parts of n-butanol, 8 parts of ethanol, 8 parts of methylcellulose, 2 parts of titanium dioxide, 2 parts of dispersant, 20 parts of filler and
20 parts of water；
Wherein, comprise the following steps：（1）By lemon oil, mandarin oil, titanium dioxide, carbon black mixing and stirring at normal temperatures；（2）
By portland cement, water reducer, algae clay, acrylic acid elastic resin emulsion, glyoxal, n-butanol, ethanol, methylcellulose,
Titanium dioxide, filler mixing and stirring at normal temperatures；（3）By step（1）And step（2）The product for drawing pours into agitator
In, solvent, dispersant, water are added, slowly stir, being gradually raised to 30 DEG C from 0 DEG C can be prepared by described environmental protection coating material.
Environmental protection coating material of the present invention has used pure natural raw material, the coating more environmental protection of preparation, and stability is high, applies
Layer adhesive force is good, good toughness.
Embodiment described above is only that the preferred embodiment of the present invention is described, not to structure of the invention
Think and model point encloses and is defined.On the premise of design concept of the present invention is not departed from, this area ordinary person is to skill of the invention
The all variations and modifications that art scheme is made, all should drop into protection scope of the present invention, in claimed technology of the invention
Hold, all recorded in detail in the claims.
Claims (2)
1. a kind of environmental protection coating material, it is characterised in that：Component including following mass percent：Lemon oil 1-3 parts, mandarin oil 1-
3 parts, titanium dioxide 1-3 parts, carbon black 1-3 parts, portland cement 30-60 parts, water reducer 2-5 parts, algae clay 5-10 parts, it is molten
Agent 1-3 parts, 20-60 parts of acrylic acid elastic resin emulsion, glyoxal 5-10 parts, n-butanol 5-10 parts, ethanol 5-10 parts,
Methylcellulose 5-10 parts, titanium dioxide 1-3 parts, dispersant 1-3 parts, filler 10-30 parts and water 10-30 parts.
2. the preparation method of a kind of environmental protection coating material according to claim 1, it is characterised in that：Comprise the following steps：
（1）By lemon oil, mandarin oil, titanium dioxide, carbon black mixing and stirring at normal temperatures；
（2）By portland cement, water reducer, algae clay, acrylic acid elastic resin emulsion, glyoxal, n-butanol, ethanol, methyl
Cellulose, titanium dioxide, filler mixing and stirring at normal temperatures；
（3）By step（1）And step（2）The product for drawing is poured into agitator, adds solvent, dispersant, water, is slowly stirred,
Gradually 30 DEG C are raised to from 0 DEG C can be prepared by described environmental protection coating material.