CN109159608A - A kind of imitative shellwork and manufacturing process - Google Patents
A kind of imitative shellwork and manufacturing process Download PDFInfo
- Publication number
- CN109159608A CN109159608A CN201811006132.XA CN201811006132A CN109159608A CN 109159608 A CN109159608 A CN 109159608A CN 201811006132 A CN201811006132 A CN 201811006132A CN 109159608 A CN109159608 A CN 109159608A
- Authority
- CN
- China
- Prior art keywords
- shellwork
- imitative
- parts
- release agent
- manufacturing process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of imitative shellwork, each components and mass fraction of the imitative shellwork are as follows: 100 parts of resin, 3-6 parts of promotor, 1-3 parts of curing agent, 15-30 parts of fire clay, 15-20 parts of release agent, 1-3 parts of reinforcing agent.Its preparation process are as follows: (1) prepare release agent；(2) in mould inner surface coating release agent；(3) resin, curing agent, fire clay, talcum powder, promotor are weighed by mass fraction and uniformly mixing is added, cast to coat in the mold of release agent；(4) curing molding obtains imitative shellwork.Imitative shellwork produced by the present invention is low in cost, with short production cycle, and yield is high, rich artistry and energy large-scale production, very promising.
Description
Technical field
The present invention relates to a kind of imitative shellwork, especially a kind of imitative shellwork and manufacturing process.
Background technique
With the continuous promotion of people's living standard, people increasingly pay attention to the raising of quality of the life；Meanwhile in house ring
In border, people are also increasingly particular about the decoration of living environment, arrange some shellworks, in house to promote living environment
Comfort level.However, rare and its hand-built difficulty of traditional shellwork due to raw material resources, so that its production effect
Rate is low, and yield is few, is not able to satisfy the market demand of rapid development；Meanwhile traditional shellwork waste of resource, destroying ecology
System does not meet the demand of national industrial policies and sustainable development, and development will be by increasing restriction.
Summary of the invention
In order to overcome disadvantages described above, the technical problem to be solved in the present invention is to provide a kind of imitative shellwork and manufacture works
Skill, the imitative shellwork as made from the technique is low in cost, with short production cycle, and yield is high, rich artistry and energy scale life
It produces, it is very promising.
The technical scheme adopted by the invention is as follows: a kind of imitative shellwork, it is characterised in that the imitative shellwork
Each component and mass fraction are as follows:
According to still another embodiment of the present invention, a kind of imitative shellwork further comprise the promotor be
Cobalt naphthenate solution.
According to still another embodiment of the present invention, a kind of imitative shellwork further comprises that the curing agent was
Peroxyester.
According to still another embodiment of the present invention, a kind of imitative shellwork further comprises talcum powder, mass fraction
It is 10-20 parts.
According to still another embodiment of the present invention, a kind of imitative shellwork further comprises the group of the release agent
It is divided into 100-120 parts of polyvinyl alcohol, 350-380 parts of alcohol, 6-8 parts of acetone, 1000-1200 parts of water.
The invention also discloses a kind of manufacturing process of imitative shellwork, it is characterised in that walks including following preparation process
It is rapid:
(1) release agent is prepared；
(2) in mould inner surface coating release agent；
(3) resin, curing agent, fire clay, talcum powder, promotor are weighed by mass fraction and uniformly mixing, casting is added
In the mold of coated release agent；
(4) curing molding obtains imitative shellwork.
According to still another embodiment of the present invention, a kind of manufacturing process of imitative shellwork further comprises described
Prepare release agent the specific steps are polyvinyl alcohol is added in 1000-1200 parts of hot water, heated while stirring until complete
Until dissolution, it is then allowed to cool to 60-70 DEG C, is slowly added dropwise alcohol under stiring, alcohol cooled to again after being added 60 DEG C with
Under, then slowly add acetone under stiring, it is stand-by with filtered through gauze after being added dropwise.
According to still another embodiment of the present invention, a kind of manufacturing process of imitative shellwork further comprises described
The mode of curing molding is heating cure.
According to still another embodiment of the present invention, a kind of manufacturing process of imitative shellwork further comprises described
The temperature of curing molding is 30 DEG C -35 DEG C.
According to still another embodiment of the present invention, a kind of manufacturing process of imitative shellwork further comprises described
The time of curing molding is 5-10 hours.
A kind of imitative shellwork provided by the invention, by the way that soil is stained in resin, promotor, curing agent, talcum powder, fire resisting
The curing molding in mold is demoulding to obtain finished product, compared with existing bone carving imitates shellwork, imitative shellwork of the invention
The needs in market can be met with large-scale production；It does not need to economize on resources using sclerotin as raw material.It preserves the ecological environment；Imitative shell work
Skill product are low in cost, with short production cycle, and yield is high, and rich artistry is very promising.
Specific embodiment
Presently in connection with preferred embodiment, the present invention is described in further detail.
Embodiment 1
100 parts of resin, 4 parts of cobalt naphthenate solution, 1 part of cyclohexanone peroxide, 15 parts of fire clay, 15 parts of release agent, enhancing
3 parts of agent.
Its preparation process includes following step of preparation process:
(1) it prepares release agent: polyvinyl alcohol being added in 1000-1200 parts of hot water, is heated while stirring until complete
Until dissolution, it is then allowed to cool to 60-70 DEG C, is slowly added dropwise alcohol under stiring, alcohol cooled to again after being added 60 DEG C with
Under, then slowly add acetone under stiring, it is stand-by with filtered through gauze after being added dropwise.
(2) in mould inner surface coating release agent；
(3) resin, curing agent, fire clay, talcum powder, promotor are weighed by mass fraction and uniformly mixing, casting is added
In the mold of coated release agent；
(4) heating cure, the temperature of curing molding are 30 DEG C -35 DEG C.Time is 10 hours, and curing molding obtains imitative shell
Craftwork.
Embodiment 2
100 parts of resin, 6 parts of cobalt naphthenate solution, 3 parts of cyclohexanone peroxide, 20 parts of fire clay, 18 parts of release agent, enhancing
3 parts of agent.
Its preparation process includes following step of preparation process:
(1) it prepares release agent: polyvinyl alcohol being added in 1000-1200 parts of hot water, is heated while stirring until complete
Until dissolution, it is then allowed to cool to 60-70 DEG C, is slowly added dropwise alcohol under stiring, alcohol cooled to again after being added 60 DEG C with
Under, then slowly add acetone under stiring, it is stand-by with filtered through gauze after being added dropwise.
(2) in mould inner surface coating release agent；
(3) resin, curing agent, fire clay, talcum powder, promotor are weighed by mass fraction and uniformly mixing, casting is added
In the mold of coated release agent；
(4) heating cure, the temperature of curing molding are 30 DEG C -35 DEG C.Time is 8 hours, and curing molding obtains imitative shell work
Skill product.
Embodiment 3
100 parts of resin, 6 parts of cobalt naphthenate solution, 3 parts of cyclohexanone peroxide, 30 parts of fire clay, 20 parts of release agent, enhancing
3 parts of agent.
Its preparation process includes following step of preparation process:
(1) it prepares release agent: polyvinyl alcohol being added in 1000-1200 parts of hot water, is heated while stirring until complete
Until dissolution, it is then allowed to cool to 60-70 DEG C, is slowly added dropwise alcohol under stiring, alcohol cooled to again after being added 60 DEG C with
Under, then slowly add acetone under stiring, it is stand-by with filtered through gauze after being added dropwise.
(2) in mould inner surface coating release agent；
(3) resin, curing agent, fire clay, talcum powder, promotor are weighed by mass fraction and uniformly mixing, casting is added
In the mold of coated release agent；
(4) heating cure, the temperature of curing molding are 30 DEG C -35 DEG C.Time is 5 hours, and curing molding obtains imitative shell work
Skill product.
Taking the above-mentioned ideal embodiment according to the present invention as inspiration, through the above description, relevant staff is complete
Various changes and amendments can be carried out without departing from the scope of the technological thought of the present invention' entirely.The technology of this invention
Property range is not limited to the contents of the specification, it is necessary to which the technical scope thereof is determined according to the scope of the claim.
Claims (10)
1. a kind of imitative shellwork, it is characterised in that each component and mass fraction of the imitative shellwork are as follows:
2. a kind of imitative shellwork according to right 1, it is characterised in that the promotor is cobalt naphthenate solution.
3. a kind of imitative shellwork according to right 1, it is characterised in that the curing agent is cyclohexanone peroxide.
4. a kind of imitative shellwork according to right 1, it is characterised in that further include talcum powder, mass fraction 10-20
Part.
5. a kind of imitative shellwork according to right 1, it is characterised in that the group of the release agent is divided into polyvinyl alcohol
100-120 parts, 350-380 parts of alcohol, 6-8 parts of acetone, 1000-1200 parts of water.
6. a kind of manufacturing process of imitative shellwork, it is characterised in that including following step of preparation process:
(1) release agent is prepared；
(2) in mould inner surface coating release agent；
(3) resin, curing agent, fire clay, talcum powder, promotor are weighed by mass fraction and uniformly mixing is added, cast to coat
In the mold of release agent；
(4) curing molding obtains imitative shellwork.
7. a kind of manufacturing process of imitative shellwork according to claim 6, it is characterised in that the preparation demoulding
Agent the specific steps are polyvinyl alcohol is added in 1000-1200 parts of hot water, heated until being completely dissolved while stirring,
Then allow it to cool to 70 DEG C or less, 60 DEG C or more, be slowly added dropwise alcohol under stiring, alcohol cooled to again after being added 60 DEG C with
Under, then slowly add acetone under stiring, it is stand-by with filtered through gauze after being added dropwise.
8. a kind of manufacturing process of imitative shellwork according to claim 6, it is characterised in that the curing molding
Mode be heating cure.
9. a kind of manufacturing process of imitative shellwork according to claim 7, it is characterised in that the curing molding
Temperature be 30 DEG C -35 DEG C.
10. a kind of manufacturing process of imitative shellwork according to claim 6, it is characterised in that the curing molding
Time be 5-10 hours.