CN106752436A - Trowelling type interior wall sealing wax and preparation method thereof - Google Patents
Trowelling type interior wall sealing wax and preparation method thereof Download PDFInfo
- Publication number
- CN106752436A CN106752436A CN201710141785.8A CN201710141785A CN106752436A CN 106752436 A CN106752436 A CN 106752436A CN 201710141785 A CN201710141785 A CN 201710141785A CN 106752436 A CN106752436 A CN 106752436A
- Authority
- CN
- China
- Prior art keywords
- parts
- trowelling
- interior wall
- wall sealing
- sealing wax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of trowelling type interior wall sealing wax and preparation method thereof, belong to paint field, component by weight is as follows：180 250 parts of deionized water；23 parts of hydroxyethyl cellulose；46 parts of attapulgite；1.5 3 parts of wetting agent；48 parts of dispersant；35 parts of defoamer；13 parts of amine neutralizer；180 250 parts of titanium dioxide；90 130 parts of kaolin；Except 15 30 parts of aldehyde antibacterial additives；15 30 parts of negative ion powder；180 220 parts of aqueous synthetic-resin emulsion；8 12 parts of thickener.The coating operations simple and fast provided using the present invention, coating surface effect is good, in the absence of the pollution to indoor ornament, can overcome problems of the prior art.
Description
Technical field
The invention belongs to paint field, more particularly to a kind of trowelling type interior wall sealing wax and preparation method thereof.
Background technology
The main form of construction work of current inner wall surface sealing wax is roller coat, spraying and brushes, and brushing mode is constructed paint film effect
It is really poor；Roll coating model construction is significantly increased in paint film effect, but efficiency of construction is slower；Spraying method construction coating surface
Effect is good, and construction is fast, but it is more to occur dust in spraying process, easily pollutes interior decoration.
Meanwhile, technology of the interior wall sealing wax on traditional performance is very ripe, is increasingly intended to functionally develop,
In environmental evaluation, the anion in air is to removing dust and toxic and harmful in air, suppression bacterium and mould
Growth, purify air have extremely important effect.It is the target that people dream of to build one and be incubated temperature control.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of trowelling type interior wall sealing wax, simple and quick, paint film table
Face effect is good, in the absence of the pollution to indoor ornament, can overcome problems of the prior art.
In order to solve the above technical problems, the technical solution used in the present invention is：A kind of trowelling type interior wall sealing wax, by weight
The component of part meter is as follows：Deionized water 180-250 parts；Hydroxyethyl cellulose 2-3 parts；Attapulgite 4-6 parts；Wetting agent 1.5-3
Part；Dispersant 4-8 parts；Defoamer 3-5 parts；Amine neutralizer 1-3 parts；Titanium dioxide 180-250 parts；Kaolin 90-130 parts；Except aldehyde
Antibacterial additives 15-30 parts；Negative ion powder 15-30 parts；Aqueous synthetic-resin emulsion 180-220 parts；Thickener 8-12 parts.
Further, the aqueous synthetic-resin emulsion be styrene-acrylic emulsion by vacuumize process, particle diameter is less than 0.1um,
MFT is less than 3 DEG C.
Further, the attapulgite is acicular texture, and particle diameter is less than 0.3um.
Further, the wetting agent is alkyl polyoxyethylene ether, and the dispersant is Sodium Polyacrylate salt.
Further, the defoamer is any one in polysiloxane-polyether copolymer type of latex type, mineral oils.
Further, the titanium dioxide is the rutile type titanium white of chloridising production.
Further, it is described except aldehyde antibacterial additives particle diameter is less than 15um, it is surface-treated using zinc system, duct complex technique
Synthesis.
Further, the negative ion powder is Si02、Al2O3、B2O3Mixture；The thickener for alkali soluble rise class thickening
Agent.
It is using the beneficial effect produced by above-mentioned technical proposal：（1）Brushing, roller coat and spraying method is solved to apply
The defect of work, the mode constructed using trowelling mode carries out the decoration of interior wall, and simple and quick, coating surface effect is good, no
In the presence of the pollution to indoor ornament.
（2）In addition, trowelling type interior wall sealing wax is provided simultaneously with effect of degradation of formaldehyde, antibacterial and anion releasing,
The drawbacks of greatly solving conventional coating and need to use several functions material, formula is set to reach simplification, while select
Aqueous synthetic-resin emulsion has certain elasticity, can make up tiny crackle.
The present invention is applied to the application of indoor wall, outside the key property for meeting conventional interior wall coating, also with anti-
Effect of formaldehyde, anion releasing, while easy construction, quick time saving and energy saving, the advantages of smell is pure and fresh, covering power is excellent.
Another object of the present invention is also to provide a kind of preparation method of trowelling type interior wall sealing wax, and above-mentioned smearing can be obtained
Painting type interior wall sealing wax, comprises the following steps：
（1）In deionized water addition dispersion cylinder by proportioning by precise, stirring to middling speed state is opened, addition ethoxy is fine
Dimension element and attapulgite, stir 2-3min；
（2）Then after sequentially adding wetting agent, dispersant, defoamer, the amine neutralizer stirring 3-5min in formula, titanium white is added
Powder, calcined kaolin, except aldehyde antibacterial additives, negative ion powder, open stirring to fast state, mashing dispersion 10-25min,
（3）Then rotating speed to middling speed state is reduced, aqueous synthetic-resin emulsion is added, 3-5min is stirred, thickener is subsequently adding,
Trowelling type interior wall sealing wax is obtained.
In step（1）In, the stir speed (S.S.) of middling speed state is 700-1000r/min；In step（2）In, fast state
Stir speed (S.S.) is 1500-2000r/min；In step（3）In, thickener rises class thickener for alkali soluble, and it is 12 to control final viscosity
± 1 ring, temperature is 25 ± 1 DEG C.
Specific embodiment
With reference to specific embodiment, the present invention is further detailed explanation.It should be understood that these are implemented
Example is explaination of the invention and citing, and the scope of the present invention is not limited in any form.
A kind of trowelling type interior wall sealing wax provided in an embodiment of the present invention with implementation method, component by weight is such as
Under：Deionized water 180-250 parts；Hydroxyethyl cellulose 2-3 parts；Attapulgite 4-6 parts；Wetting agent 1.5-3 parts；Dispersant 4-8
Part；Defoamer 3-5 parts；Amine neutralizer 1-3 parts；Titanium dioxide 180-250 parts；Kaolin 90-130 parts；Except aldehyde antibacterial additives 15-
30 parts；Negative ion powder 15-30 parts；Aqueous synthetic-resin emulsion 180-220 parts；Thickener 8-12 parts.
It is using the beneficial effect produced by above-mentioned technical proposal：（1）Brushing, roller coat and spraying method is solved to apply
The defect of work, the mode constructed using trowelling mode carries out the decoration of interior wall, and simple and quick, coating surface effect is good, no
In the presence of the pollution to indoor ornament.
（2）Trowelling type interior wall sealing wax is provided simultaneously with effect of degradation of formaldehyde, antibacterial and anion releasing, greatly solves
The drawbacks of conventional coating needs to use several functions material, makes formula reach simplification, while the aqueous synthesis tree selected
Fat liquor has certain elasticity, can make up tiny crackle.
（3）This coating is applied to the application of indoor wall, outside the key property for meeting conventional interior wall coating, also has
Effect of anti-formaldehyde, anion releasing, while easy construction, quick time saving and energy saving, the advantages of smell is pure and fresh, covering power is excellent.
Further, it is described aqueous as trowelling type interior wall sealing wax provided in an embodiment of the present invention with implementation method
Synthetic resin emulsion be styrene-acrylic emulsion by vacuumize process, particle diameter is less than 0.1um, and MFT is less than 3 DEG C, such as bar
The EC0502 of this husband.Styrene-acrylic emulsion (styrene-acrylate emulsion) is through emulsion copolymerization by styrene and acrylate monomer
And obtain.Its is water-fast, alkaline-resisting, scrub resistance can be good, and resistance to outdoor aging is widely used in the fields such as adhesive, coating.
Further, it is described concavo-convex as trowelling type interior wall sealing wax provided in an embodiment of the present invention with implementation method
Rod soil is needle-like, hair-like or filamentary structure, and particle diameter is less than 0.3um, such as Attagl 40 of BASF.
Further, as trowelling type interior wall sealing wax provided in an embodiment of the present invention with implementation method, wetting agent is
The LCN407 of alkyl polyoxyethylene ether, such as Clariant.
Further, as trowelling type interior wall sealing wax provided in an embodiment of the present invention with implementation method, the dispersion
Agent is Sodium Polyacrylate salt, such as P30 of Gao Tai.
Further, as trowelling type interior wall sealing wax provided in an embodiment of the present invention with implementation method, defoamer is
Any one in polysiloxane-polyether copolymer type of latex type, mineral oils, such as peaceful A10 of section.Polysiloxane-polyether copolymerization
Thing type of latex type defoamer, is mainly used in eliminating the foam during production aqueous latex paint, is particularly well-suited to phenylpropyl alcohol, pure third breast
Froth breaking in the emulsions such as liquid, vinyl acetate, has the advantages that consumption is few, froth breaking is fast, the suds time is long, does not influence holiday,
Can be also used for disappearing in the process of producing product such as water-based ink, water reducible resin, aqueous epoxy resins, aqueous color paste, slurry
Bubble.
Further, as trowelling type interior wall sealing wax provided in an embodiment of the present invention with implementation method, titanium dioxide is
The rutile type titanium white of chloridising production, the LR996 of such as imperial boa.Coating industry is the maximum user of titanium dioxide, particularly gold
Red stone-type titanium dioxide, major part is consumed by coatings industry.The coating manufactured with titanium dioxide, bright in luster, covering power is high, coloring
Power is strong, and low-consuming, wide in variety, the stability to medium can play a protective role, and can strengthen mechanical strength and the attachment of paint film
Power, prevents crackle, prevents ultraviolet and moisture from passing through, and extends the paint film life-span.
Further, as trowelling type interior wall sealing wax provided in an embodiment of the present invention with implementation method, except aldehyde antibacterial
Additive particle diameter is less than 15um, is surface-treated using zinc system, the synthesis of duct complex technique, such as TZYP2-01 of the rock in day.
Further, as trowelling type interior wall sealing wax provided in an embodiment of the present invention with implementation method, negative ion powder
It is Si02、Al2O3、B2O3Mixture, such as negative ion powder of the rock in day；The thickener rises class thickener, such as Tao Shi for alkali soluble
ASE60.
Embodiment 1
Trowelling type interior wall sealing wax provided in an embodiment of the present invention, including following components by weight：180 parts of deionized water；
2 parts of hydroxyethyl cellulose；6 parts of attapulgite；1.5 parts of wetting agent；4 parts of dispersant；3 parts of defoamer；1 part of amine neutralizer；Titanium
180 parts of white powder；90 parts of kaolin；Except 15 parts of aldehyde antibacterial additives；15 parts of negative ion powder；180 parts of aqueous synthetic-resin emulsion；Increase
Thick dose 8 parts.
Embodiment 2
Embodiment 2 is with the difference of embodiment 1：Trowelling type interior wall sealing wax provided in an embodiment of the present invention, including by weight
Following components of meter：215 parts of deionized water；2.5 parts of hydroxyethyl cellulose；5 parts of attapulgite；2.25 parts of wetting agent；Dispersant
6 parts；4 parts of defoamer；2 parts of amine neutralizer；215 parts of titanium dioxide；110 parts of kaolin；Except 22.5 parts of aldehyde antibacterial additives；Bear from
22.5 parts of sub- powder；215 parts of aqueous synthetic-resin emulsion；10 parts of thickener.
Embodiment 3
Embodiment 3 is with the difference of embodiment 1：Trowelling type interior wall sealing wax provided in an embodiment of the present invention, including by weight
Following components of meter：250 parts of deionized water；3 parts of hydroxyethyl cellulose；4 parts of attapulgite；3 parts of wetting agent；8 parts of dispersant；
5 parts of defoamer；3 parts of amine neutralizer；250 parts of titanium dioxide；130 parts of kaolin；Except 30 parts of aldehyde antibacterial additives；Negative ion powder 30
Part；220 parts of aqueous synthetic-resin emulsion；12 parts of thickener.
Another object of the present invention is also to provide a kind of preparation method of trowelling type interior wall sealing wax, and above-mentioned smearing can be obtained
Painting type interior wall sealing wax, comprises the following steps：
（1）In deionized water addition dispersion cylinder by proportioning by precise, stirring to middling speed state is opened, addition ethoxy is fine
Dimension element and attapulgite, stir 2-3min；
（2）Then after sequentially adding wetting agent, dispersant, defoamer, the amine neutralizer stirring 3-5min in formula, titanium white is added
Powder, calcined kaolin, except aldehyde antibacterial additives, negative ion powder, open stirring to fast state, mashing dispersion 10-25min,
（3）Then rotating speed to middling speed state is reduced, aqueous synthetic-resin emulsion is added, 3-5min is stirred, thickener is subsequently adding,
Trowelling type interior wall sealing wax is obtained.
In step（1）In, the stir speed (S.S.) of middling speed state is 700-1000r/min；In step（2）In, fast state
Stir speed (S.S.) is 1500-2000r/min；In step（3）In, thickener rises class thickener for alkali soluble, and it is 12 to control final viscosity
± 1 ring, temperature is 25 ± 1 DEG C.
Additionally, the present invention carries out performance detection for the trowelling type interior wall sealing wax made by above-described embodiment, what is measured is each
Item technical indicator see the table below：
By upper table as can be seen that the trowelling type interior wall sealing wax that the present invention is provided meets the performance indications of conventional interior wall, and tool
There is construction simple and fast, have antibacterial and mouldproof performance, while being capable of effect of anion releasing.
The technical scheme that the present invention is provided is described in detail above, application specific case is to the present invention in the present invention
Implementation method be set forth, the explanation of above example is only intended to help and understands the present invention, it is noted that for this skill
For the technical staff in art field, under the premise without departing from the principles of the invention, can also some improvement be carried out to the present invention, these
Improvement is also fallen into the protection domain of the claims in the present invention.
Claims (10)
1. a kind of trowelling type interior wall sealing wax, it is characterised in that component by weight is as follows：Deionized water 180-250 parts；Hydroxyl
Ethyl cellulose 2-3 parts；Attapulgite 4-6 parts；Wetting agent 1.5-3 parts；Dispersant 4-8 parts；Defoamer 3-5 parts；Amine neutralizer
1-3 parts；Titanium dioxide 180-250 parts；Kaolin 90-130 parts；Except 15-30 parts of aldehyde antibacterial additives；Negative ion powder 15-30 parts；Water
180-220 parts of synthetic resin emulsion of property；Thickener 8-12 parts.
2. trowelling type interior wall sealing wax according to claim 1, it is characterised in that the aqueous synthetic-resin emulsion is phenylpropyl alcohol
By vacuumize process, particle diameter is less than 0.1um to emulsion, and MFT is less than 3 DEG C.
3. trowelling type interior wall sealing wax according to claim 1, it is characterised in that the attapulgite is acicular texture, grain
Footpath is less than 0.3um.
4. trowelling type interior wall sealing wax according to claim 1, it is characterised in that the wetting agent is alkyl polyoxyethylene
Ether, the dispersant is Sodium Polyacrylate salt.
5. trowelling type interior wall sealing wax according to claim 1, it is characterised in that the defoamer is polysiloxane-polyether
Any one in copolymer emulsion class, mineral oils.
6. trowelling type interior wall sealing wax according to claim 1, it is characterised in that the titanium dioxide is the gold of chloridising production
Red stone-type titanium dioxide.
7. trowelling type interior wall sealing wax according to claim 1, it is characterised in that except aldehyde antibacterial additives particle diameter is less than
15um, is surface-treated using zinc system, the synthesis of duct complex technique.
8. trowelling type interior wall sealing wax according to claim 1, it is characterised in that the negative ion powder is Si02、Al2O3、
B2O3Mixture；The thickener rises class thickener for alkali soluble.
9. a kind of preparation method of trowelling type interior wall sealing wax, it is characterised in that comprise the following steps：
（1）In deionized water addition dispersion cylinder by proportioning by precise, stirring to middling speed state is opened, addition ethoxy is fine
Dimension element and attapulgite, stir 2-3min；
（2）Then after sequentially adding wetting agent, dispersant, defoamer, the amine neutralizer stirring 3-5min in formula, titanium white is added
Powder, calcined kaolin, except aldehyde antibacterial additives, negative ion powder, open stirring to fast state, mashing dispersion 10-25min,
（3）Then rotating speed to middling speed state is reduced, aqueous synthetic-resin emulsion is added, 3-5min is stirred, thickener is subsequently adding,
Trowelling type interior wall sealing wax is obtained.
10. the preparation method of trowelling type interior wall sealing wax according to claim 9, it is characterised in that in step（1）In, in
The stir speed (S.S.) of fast state is 700-1000r/min；In step（2）In, the stir speed (S.S.) of fast state is 1500-2000r/
min；In step（3）In, thickener rises class thickener for alkali soluble, controls final viscosity for 12 ± 1 rings, and temperature is 25 ± 1 DEG C.