CN106750596A - A kind of fire resisting oil resistant high-low temperature resistant technically classified rubber - Google Patents
A kind of fire resisting oil resistant high-low temperature resistant technically classified rubber Download PDFInfo
- Publication number
- CN106750596A CN106750596A CN201611165358.5A CN201611165358A CN106750596A CN 106750596 A CN106750596 A CN 106750596A CN 201611165358 A CN201611165358 A CN 201611165358A CN 106750596 A CN106750596 A CN 106750596A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- fire resisting
- oil
- low temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fire resisting oil resistant high-low temperature resistant technically classified rubber, it is made up of following components raw material:Natural rubber, neoprene, nitrile rubber, ceramic, palm oil, adhesive, dimethicone, polyurethane, oleic acid, softening agent, zinc oxide, PEG4000, age resistor.Technically classified rubber of the present invention is had an enormous advantage in the aspect performance such as fire resisting, oil resistant, high temperature resistant, and abrasion rupture, long service life are not susceptible in use, instant component proportioning is scientific and reasonable, safely and effectively, preparation method is easily operated, is adapted to industrially large-scale promotion.
Description
Technical field
The present invention relates to technically classified rubber field, and in particular to a kind of fire resisting oil resistant high-low temperature resistant technically classified rubber.
Background technology
The rubber of early stage is taken from the latex of the plants such as rubber tree, Russian dandelion, be made after processing with elasticity, insulation
Property, the material of impermeable water and air.Elastomeric macromolecular compound.It is divided into two kinds of natural rubber and synthetic rubber.Natural rubber
Glue is made of the extraction colloid post-processing from the plants such as rubber tree, Russian dandelion;Synthetic rubber is then by the aggregated reaction of various monomers
And obtain.Rubber is widely used in industry or life each side.
, with common rubber as main raw material(s), its formula design is often with tear resistance for technically classified rubber in the market
Energy, anti-wear performance and crush resistance can not fully take into account it and use Jie as important considerations in design process is formulated
Matter and working condition, causing existing oil sealing to meet use at aspects such as fire resisting, oil resistant, high-low temperature resistants will
Ask, performance occurs very big change in industrial production use, service life is short.
The content of the invention
In view of the shortcomings of the prior art, the invention provides a kind of fire resisting oil resistant high-low temperature resistant technically classified rubber so that institute
Performance very big change, long service life to the sealing ring of production will not occur in use.
To realize object above, the present invention is achieved by the following technical programs:
The invention provides a kind of oil-resistant high-temperature resistance to oxidation technically classified rubber, it is prepared from the following raw materials in parts by weight:
Natural rubber:30-70 parts, neoprene:15-35 parts, nitrile rubber:15-35 parts, ceramic 5-15 parts, palm oil 1-8
Part, adhesive 1-8 parts, dimethicone 1-5 parts, polyurethane 1-8 parts, oleic acid:0.05-0.2 parts, softening agent:6-15 parts, oxidation
Zinc:1-5 parts, PEG4000:1-6 parts, age resistor:1-4.5 parts..
Preferably, it is prepared from the following raw materials in parts by weight:Natural rubber:35-68 parts, neoprene:16-33 parts, fourth
Nitrile rubber:18-33 parts, ceramic 6-12 parts, palm oil 4-6 parts, adhesive 2-6 parts, dimethicone 2-3 parts, polyurethane
2-6 parts, oleic acid:0.08-0.15 parts, softening agent:7-13 parts, zinc oxide:2-4 parts, PEG4000:2-5 parts, age resistor:2-4 parts.
Preferably, it is prepared from the following raw materials in parts by weight:Natural rubber:36 parts, neoprene:16 parts, nitrile rubber:
18 parts, 6 parts of ceramic, 4 parts of palm oil, 3 parts of adhesive, 3 parts of dimethicone, 4 parts of polyurethane, oleic acid:0.1 part, softening
Agent:9 parts, zinc oxide:3 parts, PEG4000:3 parts, age resistor:3 parts.
Preferably, it is prepared from the following raw materials in parts by weight:Natural rubber:40 parts, neoprene:20 parts, nitrile rubber:
22 parts, 8 parts of ceramic, 5 parts of palm oil, 4 parts of adhesive, 3 parts of dimethicone, 4 parts of polyurethane, oleic acid:0.1 part, softening
Agent:9 parts, zinc oxide:4 parts, PEG4000:4 parts, age resistor:4 parts.
Preferably, described softening agent is sulfonated oil, carbon number aliphatic acid emulsion high, one kind of silicone oil.
Preferably, described age resistor is N- PBNAs, one kind of p-phenylenediamine.
Beneficial effect of the present invention:
Neoprene has oil resistant, high temperature resistant, resistance to combustion, resistance to daylight, resistance to ozone, acid and alkali-resistance, chemical-resistant reagent etc. good
Physical and mechanical properties, nitrile rubber oil resistivity is fabulous, and wearability is higher, and preferably, bonding force is strong for heat-resisting quantity, and the present invention will be natural
Rubber, neoprene, three kinds of rubber of nitrile rubber cooperate with shared according to a certain percentage can meet synthesized technically classified rubber tool
There is an oil resistant, resistance to combustion, the superperformance of resistance to oxidation, PEG4000 is used as additive, by increasing capacitance it is possible to increase the lubrication of technically classified rubber product
Property and plasticity, the power consumption in process can also be reduced, so as to extend the service life of sealing ring, dimethicone tool
Have excellent antioxidative stabilizer, heat decomposition temperature is high, the small advantage of evaporation loss, by increasing capacitance it is possible to increase technically classified rubber product it is anti-
Oxidisability, ceramic is a kind of lightweight non-metallic multifunctional material, and main component is SiO2 and Al2O3, chemical stability is good,
It is plasticity is good, heat resisting temperature is high, density is small, can improve technically classified rubber product oil resistant, resistance to combustion, resistance to oxidation, corrosion-resistant and resistance to
It is high temperatures.Instant component proportioning is scientific and reasonable, and safely and effectively, preparation method is easily operated, is adapted to industrially push away on a large scale
Extensively.
Specific embodiment
To make the purpose, technical scheme and advantage of the embodiment of the present invention clearer, below in conjunction with implementation of the invention
Example, is clearly and completely described to the technical scheme in the embodiment of the present invention.Based on the embodiment in the present invention, this area
The every other embodiment that those of ordinary skill is obtained under the premise of creative work is not made, belongs to protection of the present invention
Scope.
Embodiment 1:
A kind of oil-resistant high-temperature resistance to oxidation technically classified rubber, is prepared from the following raw materials in parts by weight:Natural rubber:36
Part, neoprene:16 parts, nitrile rubber:18 parts, 4 parts of palm oil, 3 parts of adhesive, 3 parts of dimethicone, 4 parts of polyurethane, oil
Acid:0.1 part, softening agent:9 parts, zinc oxide:3 parts, PEG4000:3 parts, age resistor:3 parts.
Embodiment 2:
A kind of oil-resistant high-temperature resistance to oxidation technically classified rubber, is prepared from the following raw materials in parts by weight:Natural rubber:36
Part, neoprene:20 parts, nitrile rubber:18 parts, 4 parts of palm oil, 3 parts of adhesive, 3 parts of dimethicone, 4 parts of polyurethane, oil
Acid:0.1 part, softening agent:9 parts, zinc oxide:3 parts, PEG4000:3 parts, age resistor:3 parts.
Embodiment 3:
A kind of oil-resistant high-temperature resistance to oxidation technically classified rubber, is prepared from the following raw materials in parts by weight:Natural rubber:40
Part, neoprene:18 parts, nitrile rubber:20 parts, 8 parts of ceramic, 5 parts of palm oil, 4 parts of adhesive, 3 parts of dimethicone,
4 parts of polyurethane, oleic acid:0.08 part, softening agent:8 parts, zinc oxide:4 parts, PEG4000:4 parts, age resistor:3 parts.
Embodiment 4:
A kind of oil-resistant high-temperature resistance to oxidation technically classified rubber, is prepared from the following raw materials in parts by weight:Natural rubber:50
Part, neoprene:30 parts, nitrile rubber:20 parts, 8 parts of ceramic, 5 parts of palm oil, 3 parts of adhesive, 2 parts of dimethicone,
4 parts of polyurethane, oleic acid:0.08 part, softening agent:10 parts, zinc oxide:4 parts, PEG4000:5 parts, age resistor:4 parts.
Embodiment 5:
A kind of oil-resistant high-temperature resistance to oxidation technically classified rubber, is prepared from the following raw materials in parts by weight:Natural rubber:60
Part, neoprene:33 parts, nitrile rubber:30 parts, 8 parts of ceramic, 4 parts of palm oil, 3 parts of adhesive, 2 parts of dimethicone,
3 parts of polyurethane, oleic acid:0.01 part, softening agent:8 parts, zinc oxide:2 parts, PEG4000:2 parts, age resistor:2 parts.
Embodiment 6:
A kind of oil-resistant high-temperature resistance to oxidation technically classified rubber, is prepared from the following raw materials in parts by weight:Natural rubber:38
Part, neoprene:8 parts, nitrile rubber:20 parts, 8 parts of ceramic, 6 parts of palm oil, 4 parts of adhesive, 3 parts of dimethicone,
4 parts of polyurethane, oleic acid:0.01 part, softening agent:9 parts, zinc oxide:4 parts, PEG4000:3 parts, age resistor:3 parts.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations;Although with reference to the foregoing embodiments
The present invention has been described in detail, it will be understood by those within the art that:It still can be to foregoing each implementation
Technical scheme described in example is modified, or carries out equivalent to which part technical characteristic;And these modification or
Replace, do not make the spirit and scope of the essence disengaging various embodiments of the present invention technical scheme of appropriate technical solution.
Claims (6)
1. a kind of fire resisting oil resistant high-low temperature resistant technically classified rubber, it is characterised in that be prepared from the following raw materials in parts by weight:Naturally
Rubber:30-70 parts, neoprene:15-35 parts, nitrile rubber:15-35 parts, ceramic 5-15 parts, palm oil 1-8 parts, glue
Glutinous 1-8 parts of agent, dimethicone 1-5 parts, polyurethane 1-8 parts, oleic acid:0.05-0.2 parts, softening agent:6-15 parts, zinc oxide:1-
5 parts, PEG4000:1-6 parts, age resistor:1-4.5 parts.
2. fire resisting oil resistant high-low temperature resistant technically classified rubber as claimed in claim 1, it is characterised in that by following parts by weight
Raw material is made:Natural rubber:35-68 parts, neoprene:16-33 parts, nitrile rubber:18-33 parts, ceramic 6-12 parts, palm fibre
4-6 parts of palmitic acid oil, adhesive 2-6 parts, dimethicone 2-3 parts, polyurethane 2-6 parts, oleic acid:0.08-0.15 parts, softening agent:7-
13 parts, zinc oxide:2-4 parts, PEG4000:2-5 parts, age resistor:2-4 parts.
3. fire resisting oil resistant high-low temperature resistant technically classified rubber as claimed in claim 2, it is characterised in that by following parts by weight
Raw material is made:Natural rubber:36 parts, neoprene:16 parts, nitrile rubber:18 parts, 6 parts of ceramic, 4 parts of palm oil, gluing
3 parts of agent, 3 parts of dimethicone, 4 parts of polyurethane, oleic acid:0.1 part, softening agent:9 parts, zinc oxide:3 parts, PEG4000:3 parts, it is anti-
Old agent:3 parts.
4. fire resisting oil resistant high-low temperature resistant technically classified rubber as claimed in claim 2, it is characterised in that by following parts by weight
Raw material is made:Natural rubber:40 parts, neoprene:20 parts, nitrile rubber:22 parts, 8 parts of ceramic, 5 parts of palm oil, gluing
4 parts of agent, 3 parts of dimethicone, 4 parts of polyurethane, oleic acid:0.1 part, softening agent:9 parts, zinc oxide:4 parts, PEG4000:4 parts, it is anti-
Old agent:4 parts.
5. fire resisting oil resistant high-low temperature resistant technically classified rubber as claimed in claim 1, it is characterised in that described softening agent is sulphur
Carburetion, carbon number aliphatic acid emulsion high, one kind of silicone oil.
6. fire resisting oil resistant high-low temperature resistant technically classified rubber as claimed in claim 1, it is characterised in that described age resistor is N-
PBNA, one kind of p-phenylenediamine.