CN106832869A - A kind of Novel oil-resistant rubber - Google Patents
A kind of Novel oil-resistant rubber Download PDFInfo
- Publication number
- CN106832869A CN106832869A CN201510889846.XA CN201510889846A CN106832869A CN 106832869 A CN106832869 A CN 106832869A CN 201510889846 A CN201510889846 A CN 201510889846A CN 106832869 A CN106832869 A CN 106832869A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- oil
- age resistor
- novel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to rubber materials, more particularly to a kind of Novel oil-resistant rubber.It includes the component of following portions by weight：60~80 parts of chlorohydrin rubber, 50~90 parts of nitrile rubber, 10~20 parts of nano zine oxide, 3~5 parts of stearic acid, 1~3 part of carbon black, 2~4 parts of white carbon, 1~3 part of potter's clay, 2~4 parts of dibutyl phthalate, 3~5 parts of coumarone indene resin, 1~5 part of zinc diethyl dithiocarbamate, 4~6 parts of novel environment friendly age resistor.The oil resistant rubber produced of formula provided using the present invention, with oil resistance it is good, air-tightness is high, good insulating, strong corrosion resistance the features such as；Novel environment friendly age resistor is added in rubber, can effectively solve the age resistor of nitrile rubber in current techniques not environmentally, anti-old property difference the problems such as.The Novel oil-resistant rubber that the present invention is provided, it is adaptable to various oil resistant places, the need for effectively meeting in life production.
Description
Technical field
The invention belongs to rubber materials, more particularly to a kind of Novel oil-resistant rubber.
Background technology
Rubber is divided into two kinds of natural rubber and synthetic rubber, and natural rubber is to extract glue from the plants such as rubber tree, Russian dandelion
Matter post-processing is made；Synthetic rubber is then obtained, high resilience at room temperature by the aggregated reaction of various monomers, in very little
External force effect is lower to be produced compared with large deformation, remove resilient after external force.
Rubber is widely used in industry or life each side, and requirement of the different aspect to rubber is different, resistance to the need for having
High temperature, oil resistant the need for having, waterproof the need for having is wear-resisting the need for having, therefore, rubber of the production with difference in functionality
The task of top priority as China's rubber industry.
With ageing process carrying out and develop, rubber and its product properties can gradually be lowered so that and lose use value completely.
The material of ageing process can be suppressed it is necessary to allocate some into rubber to extend the service life of rubber, so as to prolong
The storage period and service life of rubber long and its product.These materials are referred to as age resistor.The age resistor of existing nitrile rubber makes
Nonylphenol class age resistor is used, not environmentally, the usage amount of nitrile rubber is constrained significantly and scope is used.
The content of the invention
To make up the deficiency of current techniques, the present invention provides a kind of Novel oil-resistant rubber.
The technical solution adopted in the present invention：
A kind of Novel oil-resistant rubber, including following portions by weight component：60~80 parts of chlorohydrin rubber, nitrile rubber 50~
90 parts, 10~20 parts of nano zine oxide, 3~5 parts of stearic acid, 1~3 part of carbon black, 2~4 parts of white carbon, potter's clay 1~
3 parts, 2~4 parts of dibutyl phthalate, 3~5 parts of coumarone indene resin, zinc diethyl dithiocarbamate 1~5
Part, 4~6 parts of novel environment friendly age resistor.
The novel environment friendly age resistor constituent and content are：Antioxidant BHT 8%~12%, poly- butyl bis-phenol 20%~30%,
Three (nonyl phenyl) phosphite esters 25%~35%, isproportionated potassium rosinate 30%~40%.
Beneficial effects of the present invention：
The oil resistant rubber produced of formula provided using the present invention, with oil resistance it is good, air-tightness is high, good insulating,
The features such as corrosion resistance is strong；Novel environment friendly age resistor is added in rubber, the anti-of nitrile rubber in current techniques can be effectively solved
The problems such as old agent is not environmentally, anti-old property is poor.The Novel oil-resistant rubber that the present invention is provided, it is adaptable to various oil resistant places, energy
The need for effectively meeting in life production.
Specific embodiment
With reference to specific embodiment, the present invention will be described in detail：
Embodiment 1
A kind of Novel oil-resistant rubber, including following portions by weight component：60 parts of chlorohydrin rubber, 90 parts of nitrile rubber,
10 parts of nano zine oxide, 5 parts of stearic acid, 1 part of carbon black, 4 parts of white carbon, 1 part of potter's clay, dibutyl phthalate
4 parts, 3 parts of coumarone indene resin, 5 parts of zinc diethyl dithiocarbamate, 4 parts of novel environment friendly age resistor.
The novel environment friendly age resistor constituent and content are：Antioxidant BHT 8%, poly- butyl bis-phenol 30%, three (nonyls
Base phenyl) phosphite ester 25%, isproportionated potassium rosinate 37%.
Embodiment 2
A kind of Novel oil-resistant rubber, including following portions by weight component：80 parts of chlorohydrin rubber, 50 parts of nitrile rubber,
20 parts of nano zine oxide, 3 parts of stearic acid, 3 parts of carbon black, 2 parts of white carbon, 3 parts of potter's clay, dibutyl phthalate
2 parts, 5 parts of coumarone indene resin, 1 part of zinc diethyl dithiocarbamate, 6 parts of novel environment friendly age resistor.
The novel environment friendly age resistor constituent and content are：Antioxidant BHT 12%, poly- butyl bis-phenol 20%, three (nonyls
Base phenyl) phosphite ester 35%, isproportionated potassium rosinate 33%.
Embodiment 3
A kind of Novel oil-resistant rubber, including following portions by weight component：70 parts of chlorohydrin rubber, 70 parts of nitrile rubber,
15 parts of nano zine oxide, 4 parts of stearic acid, 2 parts of carbon black, 3 parts of white carbon, 2 parts of potter's clay, dibutyl phthalate
3 parts, 4 parts of coumarone indene resin, 3 parts of zinc diethyl dithiocarbamate, 5 parts of novel environment friendly age resistor.
The novel environment friendly age resistor constituent and content are：Antioxidant BHT 10%, poly- butyl bis-phenol 25%, three (nonyls
Base phenyl) phosphite ester 30%, isproportionated potassium rosinate 35%.
Above are only several specific embodiments of the invention, it is clear that the invention is not restricted to above example, can also have
Many deformations.All deformations that one of ordinary skill in the art can directly derive from present disclosure or associate,
It is considered as protection scope of the present invention.
Claims (2)
1. a kind of Novel oil-resistant rubber, it is characterised in that the component including following portions by weight：Chlorohydrin rubber 60~80
Part, 50~90 parts of nitrile rubber, 10~20 parts of nano zine oxide, 3~5 parts of stearic acid, 1~3 part of carbon black, hard charcoal
Black 2~4 parts, 1~3 part of potter's clay, 2~4 parts of dibutyl phthalate, 3~5 parts of coumarone indene resin, diethyl two
1~5 part of zinc thiocarbamate, 4~6 parts of novel environment friendly age resistor.
2. Novel oil-resistant rubber according to claim 1, it is characterised in that the novel environment friendly age resistor constituent
And content is：Antioxidant BHT 8%~12%, poly- butyl bis-phenol 20%~30%, three (nonyl phenyl) phosphite ester 25%~
35%th, isproportionated potassium rosinate 30%~40%.