CN106832606A - Rubber compounding - Google Patents
Rubber compounding Download PDFInfo
- Publication number
- CN106832606A CN106832606A CN201510886051.3A CN201510886051A CN106832606A CN 106832606 A CN106832606 A CN 106832606A CN 201510886051 A CN201510886051 A CN 201510886051A CN 106832606 A CN106832606 A CN 106832606A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- rubber compounding
- plasticizer
- coupling agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of rubber compounding, and it is prepared from the following raw materials in parts by weight：Ethylene propylene diene rubber 50-60 parts, 30~40 parts of fire retardant, 10 parts of white carbon, zinc oxide 7-8 parts, plasticizer 4-6 parts, stearic acid 3-8 parts, 9 parts of neoprene, coupling agent 1-3 parts, 5 parts of carbon black, 5 parts of red phosphorus.The present invention prepares simple, the elastomeric material good flame resistance being made, and environmental protection.
Description
Technical field
The present invention relates to a kind of rubber compounding.
Background technology
The rubber of early stage is taken from the latex of the plants such as rubber tree, Russian dandelion, is made after processing
With elasticity, insulating properties, impermeable water and air material.Elastomeric macromolecular compound.
It is divided into two kinds of natural rubber and synthetic rubber.Natural rubber is from plants such as rubber tree, Russian dandelions
Middle extraction colloid post-processing is made；Synthetic rubber is then obtained by the aggregated reaction of various monomers.Rubber
Glue product is widely used in industry or life each side.Rubber：High resiliency with reversible deformation
Polymeric material.High resilience at room temperature, larger shape can be produced under the external force effect of very little
Become, remove resilient after external force.The product poor fire that existing rubber compounding is made,
And not environmentally.
The content of the invention
(1) technical problem to be solved
The problem to be solved in the present invention is to provide a kind of rubber compounding, is hindered in the prior art with overcoming
Poor, the defect not environmentally of combustion property.
(2) technical scheme
To solve the technical problem, the present invention provides a kind of rubber compounding, and it is by following weight
The raw material of number is made：Ethylene propylene diene rubber 50-60 parts, 30~40 parts of fire retardant, hard charcoal
Black 10 parts, zinc oxide 7-8 parts, plasticizer 4-6 parts, stearic acid 3-8 parts, neoprene 9
Part, coupling agent 1-3 parts, 5 parts of carbon black, 5 parts of red phosphorus.
6 parts of stearic acid described further.
2 parts of coupling agent described further.
Further, 5 parts of the plasticizer.
(3) beneficial effect
Rubber compounding of the invention, prepares simple, the elastomeric material good flame resistance being made, and
Environmental protection.
Specific embodiment
With reference to embodiment, specific embodiment of the invention is described in further detail.
Following examples are used to illustrate the present invention, but are not limited to the scope of the present invention.
Embodiment one
A kind of rubber compounding of the invention, it is prepared from the following raw materials in parts by weight：Ternary second
Third 50 parts of rubber, 30 parts of fire retardant, 10 parts of white carbon, 7 parts of zinc oxide, plasticizer 4
Part, 3 parts of stearic acid, 9 parts of neoprene, 1 part of coupling agent, 5 parts of carbon black, 5 parts of red phosphorus.
Embodiment two
A kind of rubber compounding, it is prepared from the following raw materials in parts by weight：Ethylene propylene diene rubber
55 parts, 35 parts of fire retardant, 10 parts of white carbon, 8 parts of zinc oxide, 5 parts of plasticizer, firmly
6 parts of resin acid, 9 parts of neoprene, 2 parts of coupling agent, 5 parts of carbon black, 5 parts of red phosphorus.
In sum, above-mentioned implementation method is not restricted implementation method of the invention, all
Modification or wait that the technical staff in field is carried out on the basis of substance of the invention
Effect deformation, in technology category of the invention.
Claims (4)
1. a kind of rubber compounding, it is characterised in that it is prepared from the following raw materials in parts by weight：
Ethylene propylene diene rubber 50-60 parts, 30~40 parts of fire retardant, 10 parts of white carbon, zinc oxide 7-8
Part, plasticizer 4-6 parts, stearic acid 3-8 parts, 9 parts of neoprene, coupling agent 1-3 parts,
5 parts of carbon black, 5 parts of red phosphorus.
2. rubber compounding according to claim 1, it is characterised in that：The stearic acid
6 parts.
3. rubber compounding according to claim 1, it is characterised in that：The coupling agent
2 parts.
4. rubber compounding according to claim 1, it is characterised in that：The plasticizer
5 parts.