CN106746645A - The magnesia porcelain clear frit of one kind improvement - Google Patents
The magnesia porcelain clear frit of one kind improvement Download PDFInfo
- Publication number
- CN106746645A CN106746645A CN201611155803.XA CN201611155803A CN106746645A CN 106746645 A CN106746645 A CN 106746645A CN 201611155803 A CN201611155803 A CN 201611155803A CN 106746645 A CN106746645 A CN 106746645A
- Authority
- CN
- China
- Prior art keywords
- clear frit
- magnesia porcelain
- magnesia
- porcelain
- raw materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of magnesia porcelain clear frit of improvement disclosed by the invention, it is made up of following raw materials by weight：The useless porcelain powder 2~6% of magnesia porcelain；Wash mud 20~24%；Inner Mongol soil 4~8%；Whiten stone 8~12%；Barium carbonate 4~8%；Zinc oxide 5~9%；Albite 13~22%；Potassium feldspar 13~17%；Calcite 10~15%.Transparency is high after magnesia porcelain clear frit of the invention is fired.
Description
Technical field
The present invention relates to domestic ceramics technical field, and in particular to the magnesia porcelain clear frit of one kind improvement.
Background technology
Ceramics counts the history for doing year in the history of human being's production, during domestic ceramics is ceramic various in style
Most ancient and most traditional ceramics.Current porcelain species very abundant, development is even more and makes rapid progress in terms of type, decoration, skill
Art innovation achievement emerges in an endless stream.With the continuous improvement of people's living standard, the practicality and appreciation of ceramic product are needed
Ask more urgent.Ceramic art moulding, artistic decoration, carving product very abundant, various products are constantly brought forth new ideas, are enriched, and enrich
The artistic demand of people.But the art pottery be only limitted to furnishings with decoration, only for the leisure after appreciate it, please it.Practicality and
The ceramic of appreciating one could meet and enrich the material life of people and culture life intension, make people food and drink,
After work, leisure, the Ceramics Culture and Chinese civilization history of China can be appreciated, savoured everywhere.
Magnesia porcelain (reinforcing porcelain) is also a kind of high-grade porcelain, and Britain just makes magnesium early in 18 end of the centurys by primary raw material of talcum
Matter porcelain, so magnesia porcelain is also known as steatite ceramic.Magnesia porcelain porcelain exquisiteness is milky white, thin tire is translucent, have greasy luster.Talcum is magnesium
Hydrosilicate mineral, hand touches with soapy feeling, and slabbing structure, easy slabbing when crushing is difficult to crush.Magnesia porcelain was making
Cheng Zhong, 80-88% is accounted for because its blank is main based on poor material, and plasticity bentonite is less, is burnt in reducing atmosphere condition
More than 1350 DEG C, to be that base substrate has significantly different for its contraction change and common " clay, feldspar, quartz " in sintering process.According to
Known technology cannot be solved at all, and the not high defect of frangible, transparency easily occur in magnesia ceramic products.
The content of the invention
The technical problems to be solved by the invention are the above-mentioned technical problem existing for existing magnesia porcelain clear frit
And a kind of magnesia porcelain clear frit of improvement is provided, transparency is high after the magnesia porcelain clear frit is fired.
The technical solution adopted by the present invention is as follows：
The magnesia porcelain clear frit of one kind improvement, is made up of following raw materials by weight：
In a preferred embodiment of the invention, the magnesia porcelain clear frit, by following raw materials by weight system
Into：
The present invention also provides a kind of preparation method of magnesia porcelain clear frit, comprises the following steps：
(1) pretreatment of raw material：Stone matter raw material are whitened into stone, albite, potassium feldspar, calcite and is processed at least 8 mesh excessively
The powder of sieve；
(2) manufacture：All raw materials are added in the ball mill equipped with abrasive body by formula ratio, adds a certain amount of water to make glaze
In 1.57~1.61g/100ml, more than 240 mesh, i.e., particle diameter is less than ball milling glaze slip to fineness slurry specific gravity control
0.061mm, detects, screen over-size is in 0.03-0.04% for qualified with 320 mesh sieves, you can blowing-mistake screens out iron-store for future use.
Transparency is high after magnesia porcelain clear frit of the invention is fired.
Specific embodiment
Embodiment 1
One kind of the embodiment improves magnesia porcelain clear frit, is made up of following raw materials by weight：
The preparation method of the magnesia porcelain clear frit of improvement of the embodiment, comprises the following steps：
(1) pretreatment of raw material：Stone matter raw material are whitened into stone, albite, potassium feldspar and calcite and is processed at least 8 mesh excessively
The powder of sieve；
(2) manufacture：All raw materials are added in the ball mill equipped with abrasive body by formula ratio, adds a certain amount of water to make glaze
In 1.57g/100ml, more than 240 mesh, i.e., particle diameter is less than 0.061mm to ball milling glaze slip to fineness to slurry specific gravity control, with 320
Mesh sieve detects that screen over-size is 0.03% for qualified, you can blowing-mistake screens out iron-store for future use.
Embodiment 2
Magnesia porcelain clear frit is improved, is made up of following raw materials by weight：
The preparation method of the magnesia porcelain clear frit of improvement of the embodiment, comprises the following steps：
(1) pretreatment of raw material：Stone matter raw material are whitened into stone, albite, potassium feldspar and the powder at least crossing 8 mesh sieves is processed into
Material；
(2) manufacture：All raw materials are added in the ball mill equipped with abrasive body by formula ratio, adds a certain amount of water to make glaze
In 1.55g/100ml, more than 240 mesh, i.e., particle diameter is less than 0.061mm to ball milling glaze slip to fineness to slurry specific gravity control, with 320
Mesh sieve detects that screen over-size is 0.035% for qualified, you can blowing-mistake screens out iron-store for future use.
Embodiment 3
The magnesia porcelain clear frit of improvement of the embodiment, is made up of following raw materials by weight：
The preparation method of the magnesia porcelain clear frit of improvement of the embodiment, comprises the following steps：
(1) pretreatment of raw material：Stone matter raw material are whitened into stone, albite, potassium feldspar and the powder at least crossing 8 mesh sieves is processed into
Material；
(2) manufacture：All raw materials are added in the ball mill equipped with abrasive body by formula ratio, adds a certain amount of water to make glaze
In 1.61g/100ml, more than 240 mesh, i.e., particle diameter is less than 0.061mm to ball milling glaze slip to fineness to slurry specific gravity control, with 320
Mesh sieve detects that screen over-size is 0.04% for qualified, you can blowing-mistake screens out iron-store for future use.
Claims (2)
1. it is a kind of to improve magnesia porcelain clear frit, it is characterised in that to be made up of following raw materials by weight：
2. it is described as claimed in claim 1 to improve magnesia porcelain clear frit, it is characterised in that by following raw materials by weight
It is made：