CN106738201A - A kind of preparation method of reinforcing fiber magnesium-made fire-proof plate - Google Patents
A kind of preparation method of reinforcing fiber magnesium-made fire-proof plate Download PDFInfo
- Publication number
- CN106738201A CN106738201A CN201611121396.0A CN201611121396A CN106738201A CN 106738201 A CN106738201 A CN 106738201A CN 201611121396 A CN201611121396 A CN 201611121396A CN 106738201 A CN106738201 A CN 106738201A
- Authority
- CN
- China
- Prior art keywords
- reinforcing fiber
- magnesium
- made fire
- proof plate
- kilograms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of preparation method of reinforcing fiber magnesium-made fire-proof plate, the process steps are as follows:Stirring pool is pumped into after 3 tons of magnesium sulfate and 1.6 tons of aquation slurries are put into slurrying pond, 120 kg magnesia, 25 kilograms of sawdust powders, 80 kilograms of magnesium sulfate and 25 kilograms of bamboo fibres are added;Hopper upper strata is put into after stirring, the raw material for stirring is flowed into the template of hopper lower floor grid cloth, pass through drum pressed sizing again, just into reinforcing fiber magnesium-made fire-proof boards half-finished product, then reinforcing fiber magnesium-made fire-proof sheet material semi-finished product are entered into fog room, conserve the temperature of 40 DEG C of constant indoor temperature, and the temperature control baking and curing by 12 hours is molded, reinforcing fiber magnesium-made fire-proof plate is unified into the demoulding after curing molding, finally enter finished room and put one week of maintenance, then cut, be molded, packed.Beneficial effects of the present invention are:Reinforcing fiber magnesium-made fire-proof plate has environmental protection, and fire prevention, waterproof is incubated, not flexible type, antisepsis;Product can do ventilation shaft, dalle, external wall insulation etc..
Description
Technical field
The invention belongs to PLASTIC LAMINATED field, more particularly to a kind of preparation method of reinforcing fiber magnesium-made fire-proof plate.
Background technology
Existing PLASTIC LAMINATED is more and more extensive in the application of building field, but the weak point of common PLASTIC LAMINATED exists
In:Fire-protection rating is low, is easily deformed.
The content of the invention
It is an object of the invention to overcome the shortcomings of that prior art is present, and provide a kind of reinforcing fiber magnesium-made fire-proof plate
Preparation method.
The purpose of the present invention is completed by following technical solution, the making side of this reinforcing fiber magnesium-made fire-proof plate
Method, the process steps are as follows:Stirring pool is pumped into after 3 tons of magnesium sulfate and 1.6 tons of aquation slurries are put into slurrying pond, 120 are added
Kilogram magnesia, 25 kilograms of sawdust powders, 80 kilograms of magnesium sulfate and 25 kilograms of bamboo fibres;Hopper upper strata is put into after stirring, is stirred
It is just magnesia anti-into reinforcing fiber in mixing the template that uniform raw material flows into hopper lower floor grid cloth, then by drum pressed sizing
Then reinforcing fiber magnesium-made fire-proof sheet material semi-finished product are entered fog room by fiery boards half-finished product, conserve the temperature of 40 DEG C of constant indoor temperature,
It is most laggard and the temperature control baking and curing by 12 hours is molded, and reinforcing fiber magnesium-made fire-proof plate is unified into the demoulding after curing molding
Enter finished room and put one week of maintenance, then cut, be molded, packed.
Preferably, grid cloth is divided into upper and lower 2 layers, feed distribution is set uniformly to be adhered between grid cloth and be bonded firmly.
Beneficial effects of the present invention are:Reinforcing fiber magnesium-made fire-proof plate has environmental protection, and fire prevention, waterproof, insulation is not variable
Type, antisepsis;Product can do ventilation shaft, dalle, external wall insulation etc..
Specific embodiment
Detailed introduction will be done to the present invention below:
The preparation method of this reinforcing fiber magnesium-made fire-proof plate of the present invention, the process steps are as follows:Slurrying
Stirring pool is pumped into after 3 tons of magnesium sulfate and 1.6 tons of aquation slurries are put into pond, 120 kg magnesia, 25 kilograms of sawdust powders, 80 are added
Kilogram magnesium sulfate and 25 kilograms of bamboo fibres;Hopper upper strata is put into after stirring, the raw material for stirring flows into hopper lower net
In the template of lattice cloth (grid cloth is divided into upper and lower 2 layers, and feed distribution can be made uniformly to be adhered between grid cloth and be bonded firmly), then
By drum pressed sizing, just into reinforcing fiber magnesium-made fire-proof boards half-finished product, then by reinforcing fiber magnesium-made fire-proof sheet material half into
Product enter fog room, conserve the temperature of 40 DEG C of constant indoor temperature, and by the temperature control baking and curing shaping of 12 hours, after curing molding
Reinforcing fiber magnesium-made fire-proof plate is unified into the demoulding (sloughing template), finished room is finally entered and is put one week of maintenance, Ran Houjin
Row cutting, shaping is packed.
(1) reinforcing fiber magnesium-made fire-proof plate has good fire resistance, and fire resistance rating is A grades.
(2) reinforcing fiber magnesium-made fire-proof plate anticracking grout and alkali resistant glass fiber reticular cloth do protective facing, efficiently solve
Insulation surface layer it is empty, bulging, split problem., without cavity, wind suction prevention ability is strong, it is adaptable to multilayer structure for system.
(3) reinforcing fiber magnesium-made fire-proof plate good permeability, respiratory function is strong, and existing good water-proof function can have row again
Solve the moisture of heat-insulation layer.
(4) not only thermal conductivity factor (≤0.049W/m.K) is low for reinforcing fiber magnesium-made fire-proof plate, and heat-insulating property is stable, anti-
Compressive Strength is high.
(5) reinforcing fiber magnesium-made fire-proof plate comprehensive cost is relatively low, and speed of application is fast, it is easy to operate, and for environmental protection is built
Material, it is environmentally safe.
It is understood that it will be understood by those skilled in the art that being subject to technical scheme and inventive concept
The protection domain of appended claims of the invention should all be belonged to replacement or change.
Claims (2)
1. a kind of preparation method of reinforcing fiber magnesium-made fire-proof plate, it is characterised in that:The process steps are as follows:In slurrying pond
Be pumped into stirring pool after being put into 3 tons of magnesium sulfate and 1.6 tons of aquations slurry, add 120 kg magnesia, 25 kilograms of sawdust powders, 80 kilograms
Magnesium sulfate and 25 kilograms of bamboo fibres;Hopper upper strata is put into after stirring, the raw material for stirring flows into hopper lower floor grid cloth
Template in, it is then that reinforcing fiber is magnesia anti-just into reinforcing fiber magnesium-made fire-proof boards half-finished product then by drum pressed sizing
Fiery sheet material semi-finished product enter fog room, conserve the temperature of 40 DEG C of constant indoor temperature, and by the temperature control baking and curing shaping of 12 hours,
Reinforcing fiber magnesium-made fire-proof plate is unified into the demoulding after curing molding, finished room is finally entered and is put one week of maintenance, Ran Houjin
Row cutting, shaping is packed.
2. the preparation method of reinforcing fiber magnesium-made fire-proof plate according to claim 1, it is characterised in that:Grid cloth is divided into
Lower 2 layers, feed distribution is set uniformly to be adhered between grid cloth and be bonded firmly.