CN106706458A - 电热套eva交联度测试方法 - Google Patents
电热套eva交联度测试方法 Download PDFInfo
- Publication number
- CN106706458A CN106706458A CN201611080446.5A CN201611080446A CN106706458A CN 106706458 A CN106706458 A CN 106706458A CN 201611080446 A CN201611080446 A CN 201611080446A CN 106706458 A CN106706458 A CN 106706458A
- Authority
- CN
- China
- Prior art keywords
- sample
- eva
- bag
- flask
- sample bag
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了电热套EVA交联度测试方法,准备仪器,先将不锈钢网洗净晾干，制成顶端开口并且要保证折起的两边能保证承装样品不漏，做好的试样袋要能放入烧瓶，称重量为W1；将已交联过的EVA胶样在不同部位用剪刀剪成小碎片进行取样，重W2；将试样包悬吊在有回流装置的烧瓶中，以二甲苯为溶剂，在1000ml烧瓶中要装750g溶剂，沸腾回流后，冷却取出试样袋后悬挂起来，以除去过量的溶剂，取出称量W3；最后测量交联度，本发明利用加热、降温、加热，并且循环的测试方法光伏组件EVA封装材料交联度的测试，可避免持续加热过程中添加剂对EVA交联后的网状结构造成破坏，提高测试数据的重复性和准确性。
Description
技术领域
本发明属于太阳能电池生产技术领域，尤其涉及电热套EVA交联度测试方法。
背景技术
在太阳能电池制造工艺中，常通过将背板、EVA胶、太阳能电池串、EVA胶和基片按顺序敷设在一起，之后放入层压机内通过层压工艺而形成太阳能电池组件。其中，所述EVA胶的作用是将所述太阳能电池串和背板以及基片牢固粘接在一起，并对所述太阳能电池串进行密封，因此，所述EVA胶需要具有较好的抗老化性能及较高的机械强度。
对制备好的EVA胶进行交联度的测试过程包括：将固化后的EVA胶切成微粒状，取0.4克装入铜筛袋里，并将所述铜筛袋放入二甲苯中煮沸5小时左右，之后取出铜筛袋放入干燥箱中干燥3小时，最后分离铜筛袋与交联后的EVA，通过称重计算出交联度，以上方法操作繁琐，且测量不准确。
发明内容
有鉴于此，本发明实施例提供了电热套EVA交联度测试方法，该方法可减少对EVA胶交联度的测试次数，从而可节省时间，节约成本。
电热套EVA交联度测试方法，它包括有以下操作步骤：
准备仪器：1)大口圆底的烧瓶及塞子，采用2～3只以测定500ml样品为宜或者采用6～8只以测定1000ml样品为宜；
2)加热套或恒温油槽，加热容器要求热容量足以加沸二甲苯，沸点为138～144℃；
3)回流冷凝管，且回流冷凝管带磨口或以软木塞和烧瓶连接；
4)真空烘箱附带能产生0.87Mpa真空度的真空源和装有能测150℃的热电偶；
5)120目不锈钢网；
6)干燥器；
分析步骤：1)先将不锈钢网洗净晾干，放入100-120℃的真空烘箱内烘干，冷却后截取60mm×120mm，对折成60mm×60mm的正方形，两侧边折进7.5mm，制成顶端开口的袋尺寸为45×60mm，并且要保证折起的两边能保证承装样品不漏，做好的试样袋要能放入烧瓶，称重量为W1；
2)将已交联过的EVA胶样在不同部位用剪刀剪成小碎片进行取样，在1/10000电子天平上准确称取试样0.14500～0.15500g，将样品放于已知重量的120目不锈钢网袋里，称重W2；
3)将试样包悬吊在有回流装置的烧瓶中，以二甲苯为溶剂，在1000ml烧瓶中要装750g溶剂，沸腾回流后，冷却取出试样袋后悬挂起来，以除去过量的溶剂，再放入真空烘箱中烘3h，取出试样袋于干燥器内冷却15min，取出称量W3；
4)计算交联度ρ＝(W3-W1)/(W2-W1)×100％
W1：不锈钢网袋三边封口一边开的袋重
W2：装有试样的袋重
W3：萃取与干燥后的试样袋重
5)通过多次实验，不锈钢网袋和未交联的EVA树脂不会影响此分析方法的准确性，萃取时间5h后，交联度变化小，交联剂用量增加，EVA的交联度也会上升，与实际工艺吻合，交联度每天测试1次，工作环境在：温度25±2℃，湿度：≤65％。
优选地，在二甲苯为溶剂沸腾回流5h后，回流速度为20～40滴/min，主要是为了防止试样的再度交联，加入1％左右的抗氧剂。
优选地，真空烘箱使用(温度141±20℃，真空度0.8Mpa)。
优选地，萃取剂二甲苯可多次使用，使用3次时应更换试剂，在更换二甲苯的同时，将烧瓶用无水乙醇冲洗，二甲苯是易燃溶剂，只能在通风柜内使用，要戴上防护用品。
本发明的有益效果如下：本发明利用加热、降温、加热，并且循环的测试方法光伏组件EVA封装材料交联度的测试，可避免持续加热过程中添加剂对EVA交联后的网状结构造成破坏，提高测试数据的重复性和准确性。
具体实施方式
实施例一
电热套EVA交联度测试方法，它包括有以下操作步骤：
准备仪器：1)大口圆底的烧瓶及塞子，采用2～3只以测定500ml样品为宜或者采用6～8只以测定1000ml样品为宜；
2)加热套或恒温油槽，加热容器要求热容量足以加沸二甲苯，沸点为138～144℃；
3)回流冷凝管，且回流冷凝管带磨口或以软木塞和烧瓶连接；
4)真空烘箱附带能产生0.87Mpa真空度的真空源和装有能测150℃的热电偶；
5)120目不锈钢网；
6)干燥器；
分析步骤：1)先将不锈钢网洗净晾干，放入100-120℃的真空烘箱内烘干，冷却后截取60mm×120mm，对折成60mm×60mm的正方形，两侧边折进7.5mm，制成顶端开口的袋尺寸为45×60mm，并且要保证折起的两边能保证承装样品不漏，做好的试样袋要能放入烧瓶，称重量为W1；
2)将已交联过的EVA胶样在不同部位用剪刀剪成小碎片进行取样，在1/10000电子天平上准确称取试样0.14500～0.15500g，将样品放于已知重量的120目不锈钢网袋里，称重W2；
3)将试样包悬吊在有回流装置的烧瓶中，以二甲苯为溶剂，在1000ml烧瓶中要装750g溶剂，沸腾回流后，冷却取出试样袋后悬挂起来，以除去过量的溶剂，再放入真空烘箱中烘3h，取出试样袋于干燥器内冷却15min，取出称量W3；
4)计算交联度ρ＝(W3-W1)/(W2-W1)×100％
W1：不锈钢网袋三边封口一边开的袋重
W2：装有试样的袋重
W3：萃取与干燥后的试样袋重
5)通过多次实验，不锈钢网袋和未交联的EVA树脂不会影响此分析方法的准确性，萃取时间5h后，交联度变化小，交联剂用量增加，EVA的交联度也会上升，与实际工艺吻合，交联度每天测试1次，工作环境在：温度25±2℃，湿度：≤65％。
优选地，在二甲苯为溶剂沸腾回流5h后，回流速度为20～40滴/min，主要是为了防止试样的再度交联，加入1％左右的抗氧剂。
优选地，真空烘箱使用(温度141±20℃，真空度0.8Mpa)。
优选地，萃取剂二甲苯可多次使用，使用3次时应更换试剂，在更换二甲苯的同时，将烧瓶用无水乙醇冲洗，二甲苯是易燃溶剂，只能在通风柜内使用，要戴上防护用品。
Claims (4)
1.电热套EVA交联度测试方法，其特征在于，它包括有以下操作步骤：
准备仪器：1)大口圆底的烧瓶及塞子，采用2～3只以测定500ml样品为宜或者采用6～8只以测定1000ml样品为宜；
2)加热套或恒温油槽，加热容器要求热容量足以加沸二甲苯，沸点为138～144℃；
3)回流冷凝管，且回流冷凝管带磨口或以软木塞和烧瓶连接；
4)真空烘箱附带能产生0.87Mpa真空度的真空源和装有能测150℃的热电偶；
5)120目不锈钢网；
6)干燥器；
分析步骤：1)先将不锈钢网洗净晾干，放入100-120℃的真空烘箱内烘干，冷却后截取60mm×120mm，对折成60mm×60mm的正方形，两侧边折进7.5mm，制成顶端开口的袋尺寸为45×60mm，并且要保证折起的两边能保证承装样品不漏，做好的试样袋要能放入烧瓶，称重量为W1；
2)将已交联过的EVA胶样在不同部位用剪刀剪成小碎片进行取样，在1/10000电子天平上准确称取试样0.14500～0.15500g，将样品放于已知重量的120目不锈钢网袋里，称重W2；
3)将试样包悬吊在有回流装置的烧瓶中，以二甲苯为溶剂，在1000ml烧瓶中要装750g溶剂，沸腾回流后，冷却取出试样袋后悬挂起来，以除去过量的溶剂，再放入真空烘箱中烘3h，取出试样袋于干燥器内冷却15min，取出称量W3；
4)计算交联度ρ＝(W3-W1)/(W2-W1)×100％
W1：不锈钢网袋三边封口一边开的袋重
W2：装有试样的袋重
W3：萃取与干燥后的试样袋重
5)通过多次实验，不锈钢网袋和未交联的EVA树脂不会影响此分析方法的准确性，萃取时间5h后，交联度变化小，交联剂用量增加，EVA的交联度也会上升，与实际工艺吻合，交联度每天测试1次，工作环境在：温度25±2℃，湿度：≤65％。
2.根据权利要求1所述的电热套EVA交联度测试方法，其特征在于，在二甲苯为溶剂沸腾回流5h后，回流速度为20～40滴/min，主要是为了防止试样的再度交联，加入1％左右的抗氧剂。
3.根据权利要求1所述的电热套EVA交联度测试方法，其特征在于，真空烘箱使用温度141±20℃，真空度0.8Mpa。
4.根据权利要求1所述的电热套EVA交联度测试方法，其特征在于，萃取剂二甲苯可多次使用，使用3次时应更换试剂，在更换二甲苯的同时，将烧瓶用无水乙醇冲洗，二甲苯是易燃溶剂，只能在通风柜内使用，要戴上防护用品。