CN106702726A - Winter fashion womenswear and preparation method thereof - Google Patents
Winter fashion womenswear and preparation method thereof Download PDFInfo
- Publication number
- CN106702726A CN106702726A CN201710030381.1A CN201710030381A CN106702726A CN 106702726 A CN106702726 A CN 106702726A CN 201710030381 A CN201710030381 A CN 201710030381A CN 106702726 A CN106702726 A CN 106702726A
- Authority
- CN
- China
- Prior art keywords
- preparation
- coupling agent
- far
- far infrared
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a winter fashion womenswear and a preparation method thereof. The preparation method comprises the following steps: (1), preparing modified far infrared powder; (2), preparing far infrared antibacterial finishing liquid; (3), preparing far infrared antibacterial fabric; (4), tailoring and sewing, so as to obtain the winter fashion womenswear. The winter fashion womenswear and thee preparation method thereof inspect the inspect the optimum process condition of far infrared antibacterial finishing, do not add any toxic and harmful substance, strictly screen the far infrared antibacterial effects on all raw materials in the preparation technology, add a coupling agent to improve the interaction among the interfaces of the far infrared powder, the finishing liquid and the fabric, realize the effect of improving the far infrared emission rate and antibacterial performance, can activate the activity of biomacromolecules, promote and improve blood circulation, increase metabolism, improve the immunologic function of human body, and have a good healthcare function.
Description
Technical field
The present invention relates to a kind of women's dress, and in particular to a kind of winter Fashionable women dress and preparation method thereof.
Background technology
Dress ornament is the distinctive fruit of labour of the mankind, clothes as human civilization mark, it is that other are any that its status can be said
Material is all irreplaceable, wears clothes and is undoubtedly that the mankind are largest in the number of people, no matter be related to one of most wide life-form structure in face
It is people under which kind of Social Culture can wear clothes, or decorates the body of oneself in some way.Clothes go out
It is existing, accelerate the paces that the mankind stride forward to civilized society.
With the continuous improvement of living standard, used as the clothes of a human appearance part, its aesthetic value is also continuous
Improve, whether people are used selecting for clothes, and can be primarily to see it play a part of to maximize favourable factors and minimize unfavourable ones during dress, embody
The shortcomings and deficiencies of the one side of the beauty of human body, modification or improvement human body.Marx said:" progress of society is that the mankind pursue U.S.
Crystallization, people is also to mould oneself according to beautiful rule." different times aesthetical standard be change, and human body change not
Greatly, clothes assume responsibility for adapting to the responsibility of change.Clothes not passively internal characteristicses such as makings, mood of performance people, it can be with
Change the state of mind of people to a certain extent, guiding people adjust the mental state of oneself according to the hint of clothes theme.From certain
For planting in meaning, people creates clothes, and clothes have moulded people again in turn.Clothes are moulded to human body, mainly by clothes
Assembling structure embodies.One piece of fabric can not calculate clothes, only by this block fabric by certain pattern handling, according to human body
Build, aesthetic being attached on human body can just be called clothes.The secret of dress designing is that how to protrude and exaggerate human body
Graceful feature, reduces or eliminates the defect of build, and the purpose of beautification mankind itself is reached in perfect form.
The content of the invention
In view of the shortcomings of the prior art, the technical problem to be solved in the present invention be to provide a kind of winter Fashionable women dress and
Its preparation method.
To solve the above problems, the present invention is adopted the following technical scheme that:
A kind of preparation method of winter Fashionable women dress, comprises the following steps:
(1) far infrared powder of 1-10 weight portions is well mixed with the coupling agent of 0.2-2 weight portions, obtains modified remote red
Outer powder;
(2) by the aqueous polyurethane emulsion of modified far infrared powder and 5-20 weight portions, the dispersant of 1-5 weight portions,
The sodium sorbate of 0.2-2 weight portions, the water of 95-105 weight portions are well mixed, and obtain far-infrared anti-biotic dressing liquid;
(3) fabric is impregnated into 40-60min, fabric and far infrared in temperature is for 45-75 DEG C of far-infrared anti-biotic dressing liquid
The mass ratio of antibiotic finishing solution is 1:10-1:30, after dehydration, 80-200min is dried under the conditions of 30-60 DEG C, obtain far infrared
Antibiotic facing material;
(4) Far-infrared antibacterial fabric is cut, and routinely women's dress preparation technology sewing is obtained final product.
Preferably, the far infrared powder is in medical stone powder, nano-zirconium carbide, nanometer silicon carbide, nano silicon
At least one.
It is further preferred that the far infrared powder is mixed by 55-65wt% medical stone powders and 35-45wt% nano-zirconium carbides
Conjunction is formed.
Preferably, the coupling agent consumption is 0.6-1 weight portions.
Preferably, the coupling agent is at least one in silane coupler, titanate coupling agent, aluminate coupling agent,
The silane coupler can be selected from diethylenetriamine base propyl trimethoxy silicane, 3- (oxygen of 2,3- epoxies third) propyl group trimethoxy
Base silane, the titanate coupling agent can be selected from isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters, the oil of isopropyl two
Sour acyloxy (dioctyl phosphoric acid acyloxy) titanate esters, the aluminate coupling agent can be selected from aluminate coupling agent 821, aluminic acid
Ester coupling agent DL-411.
It is further preferred that the coupling agent is titanate coupling agent.
It is further preferred that the coupling agent is the oleic acid acyloxy of isopropyl two (dioctyl phosphoric acid acyloxy) titanate esters.
Preferably, the dispersant is anionic surfactant, cationic surface active agent, amphion surface
At least one in activating agent, nonionic surfactant, the anionic surfactant can be selected from dodecyl sulphur
Sour sodium, cetyl benzenesulfonic acid sodium, the cationic surface active agent can be selected from Cetyltrimethylammonium bromide, 20
Dialkyl group trimethyl ammonium chloride, the zwitterionic surfactant dodecyldimethylammonium hydroxide inner salt, 3- sulfopropyl hexadecanes
Base diformazan glycine betaine, the nonionic surfactant can be Dodecyl Polyglucosides.
It is further preferred that the dispersant is nonionic surfactant.
It is further preferred that the dispersant is Dodecyl Polyglucosides.
Preferably, the fabric material is 100wt% wools.
Present invention also offers a kind of winter Fashionable women dress, it is prepared from using the above method.
Winter Fashionable women dress of the invention and preparation method thereof, has investigated the optimum process condition of far-infrared anti-biotic arrangement, no
Addition poisonous and harmful substances, to preparation technology in each raw material far-infrared anti-biotic effect is screened layer by layer, addition coupling
Agent increased far infrared powder and dressing liquid and the interfacial interaction of fabric, realize raising far infrared transmissivity and antibiotic property
The effect of energy, can activate the activity of large biological molecule, promote and improve blood circulation, increase metabolism, and raising human body is exempted from
Epidemic disease function, possesses good healthcare function.
Specific embodiment
Far infrared performance test methods:The use of instrument is IR-1 emissivity measurement instrument, 8-14 μm of spectral regions normal direction hair of measurement
Rate is penetrated, temperature during measurement is 25 DEG C.
Anti-microbial property test method:Using standard GB/T/T 20944.3-2008《The evaluation of antibacterial textile performance
3 parts:Succusion》Antibiotic property quantitative test is carried out, using color fastness to washing testing machine washing methods, after test washes 30 times
Far infrared fabric, with staphylococcus aureus ATCC No.6538 (gram-positive bacteria) as test strain.
Embodiment 1-3
The preparation method of winter Fashionable women dress, comprises the following steps:
(1) by medical stone powder (the 2000 mesh wheat meals provided using Zhengzhou Yu Lan Environmental Protection Technology Co., Ltd of 1.8 weight portions
Stone flour), (article No. for using Shanghai Nai Ou nanosecond science and technology Co., Ltd to provide is NO-C-003- for the nano-zirconium carbide of 1.2 weight portions
2 zirconium carbide, average grain diameter is 800nm) with the coupling agent (coupling agent species is shown in Table 1) of 0.4 weight portion in high speed mixing machine
800 revs/min of stirring 10min are well mixed at a temperature of 80 DEG C, obtain modified far infrared powder;
(2) it is modified far infrared powder is (limited using Shenzhen's Jitian's chemical industry with the aqueous polyurethane emulsion of 12 weight portions
Company provide model F0401 anion-type water-thinned polyurethane emulsion, viscosity 300mpa.s), the dodecyl of 2 weight portions
Sodium sulphate, the sodium sorbate of 0.3 weight portion, the water of 100 weight portions are well mixed, and obtain far-infrared anti-biotic dressing liquid;
(3) by fabric, (article No. for using Hebei day Yi Fengda fine hair processing Co., Ltd to provide is the wool of RKB752100
Fabric, composition is 100wt% fine wools, and grammes per square metre is 570g/ ㎡) impregnated in the far-infrared anti-biotic dressing liquid that temperature is 65 DEG C
45min, fabric is 1 with the mass ratio of far-infrared anti-biotic dressing liquid:15, after dehydration, 120min is dried under the conditions of 60 DEG C, obtain
Far-infrared antibacterial fabric;
(4) Far-infrared antibacterial fabric is cut, and routinely women overcoat preparation technology sewing, obtain final product the winter
Fashionable women dress.
Table 1:Coupling agent species and Far-infrared antibacterial fabric the performance test results table
Wherein, the oleic acid acyloxy of isopropyl two (dioctyl phosphoric acid acyloxy) titanate esters, by the Nanjing Olympic limited public affairs of sincere chemical industry
Department provides, No. CAS:61417-49-0.
Found out by table 1, coupling agent is ideal using titante coupling agent far infrared and antibacterial effect.
Embodiment 4-13
The preparation method of winter Fashionable women dress, comprises the following steps:
(1) by medical stone powder (the 2000 mesh wheat meals provided using Zhengzhou Yu Lan Environmental Protection Technology Co., Ltd of 1.8 weight portions
Stone flour), (article No. for using Shanghai Nai Ou nanosecond science and technology Co., Ltd to provide is NO-C-003- for the nano-zirconium carbide of 1.2 weight portions
2 zirconium carbide, average grain diameter is 800nm) and the oleic acid acyloxy of isopropyl two (dioctyl phosphoric acid acyloxy) titanate esters (coupling agent
2) consumption is shown in Table that 800 revs/min of stirring 10min are well mixed at a temperature of 80 DEG C in the high speed mixing machine, obtains modified far-infrared powder
Body;
(2) it is modified far infrared powder is (limited using Shenzhen's Jitian's chemical industry with the aqueous polyurethane emulsion of 12 weight portions
Company provide model F0401 anion-type water-thinned polyurethane emulsion, viscosity 300mpa.s), the dodecyl of 2 weight portions
Sodium sulphate, the sodium sorbate of 0.3 weight portion, the water of 100 weight portions are well mixed, and obtain far-infrared anti-biotic dressing liquid;
(3) by fabric, (article No. for using Hebei day Yi Fengda fine hair processing Co., Ltd to provide is the wool of RKB752100
Fabric, composition is 100wt% fine wools, and grammes per square metre is 570g/ ㎡) impregnated in the far-infrared anti-biotic dressing liquid that temperature is 65 DEG C
45min, fabric is 1 with the mass ratio of far-infrared anti-biotic dressing liquid:15, after dehydration, 120min is dried under the conditions of 60 DEG C, obtain
Far-infrared antibacterial fabric;
(4) Far-infrared antibacterial fabric is cut, and routinely women overcoat preparation technology sewing, obtain final product the winter
Fashionable women dress.
Table 2:Coupling agent consumption and Far-infrared antibacterial fabric the performance test results table
Wherein, the oleic acid acyloxy of isopropyl two (dioctyl phosphoric acid acyloxy) titanate esters, by the Nanjing Olympic limited public affairs of sincere chemical industry
Department provides, No. CAS:61417-49-0.
Found out by table 2, the oleic acid acyloxy of isopropyl two (dioctyl phosphoric acid acyloxy) titanate coupling agent consumption is 0.8 weight
Far infrared and antibacterial effect are ideal during amount part, and consumption is the most reasonable.
Embodiment 14-19
The preparation method of winter Fashionable women dress, comprises the following steps:
(1) by medical stone powder (the 2000 mesh wheat meals provided using Zhengzhou Yu Lan Environmental Protection Technology Co., Ltd of 1.8 weight portions
Stone flour), (article No. for using Shanghai Nai Ou nanosecond science and technology Co., Ltd to provide is NO-C-003- for the nano-zirconium carbide of 1.2 weight portions
2 zirconium carbide, average grain diameter is 800nm) with the oleic acid acyloxy of isopropyl two (dioctyl phosphoric acid acyloxy) titanium of 0.8 weight portion
(by Nanjing Olympic, sincere Chemical Co., Ltd. provides acid esters, No. CAS:61417-49-0) in the high speed mixing machine 800 at a temperature of 80 DEG C
Rev/min stirring 10min is well mixed, and obtains modified far infrared powder;
(2) it is modified far infrared powder is (limited using Shenzhen's Jitian's chemical industry with the aqueous polyurethane emulsion of 12 weight portions
Company provide model F0401 anion-type water-thinned polyurethane emulsion, viscosity 300mpa.s), the dispersant of 2 weight portions
(dispersant is shown in Table 3), the sodium sorbate of 0.3 weight portion, the water of 100 weight portions are well mixed, and obtain far-infrared anti-biotic whole
Reason liquid;
(3) by fabric, (article No. for using Hebei day Yi Fengda fine hair processing Co., Ltd to provide is the wool of RKB752100
Fabric, composition is 100wt% fine wools, and grammes per square metre is 570g/ ㎡) impregnated in the far-infrared anti-biotic dressing liquid that temperature is 65 DEG C
45min, fabric is 1 with the mass ratio of far-infrared anti-biotic dressing liquid:15, after dehydration, 120min is dried under the conditions of 60 DEG C, obtain
Far-infrared antibacterial fabric;
(4) Far-infrared antibacterial fabric is cut, and routinely women overcoat preparation technology sewing, obtain final product the winter
Fashionable women dress.
Table 3:Dispersant and Far-infrared antibacterial fabric the performance test results table
Dispersant | Emissivity, % | Antibiotic rate, % | |
Embodiment 14 | Lauryl sodium sulfate | 92 | 91.3 |
Embodiment 15 | Cetyl benzenesulfonic acid sodium | 92 | 91.5 |
Embodiment 16 | Cetyltrimethylammonium bromide | 90 | 93.8 |
Embodiment 17 | INCROQUAT TMC-80 | 91 | 93.2 |
Embodiment 18 | Dodecyldimethylammonium hydroxide inner salt | 94 | 92.5 |
Embodiment 19 | Dodecyl Polyglucosides | 94 | 93.4 |
Found out by table 3, dispersant is ideal using nonionic far infrared and antibacterial effect.
Embodiment 20
The preparation method of winter Fashionable women dress, comprises the following steps:
(1) by medical stone powder (the 2000 mesh wheat meals provided using Zhengzhou Yu Lan Environmental Protection Technology Co., Ltd of 1.8 weight portions
Stone flour), (article No. for using Shanghai Nai Ou nanosecond science and technology Co., Ltd to provide is NO-C-003- for the nano-zirconium carbide of 1.2 weight portions
2 zirconium carbide, average grain diameter is 800nm) with the oleic acid acyloxy of isopropyl two (dioctyl phosphoric acid acyloxy) titanium of 0.8 weight portion
(by Nanjing Olympic, sincere Chemical Co., Ltd. provides acid esters, No. CAS:61417-49-0) in the high speed mixing machine 800 at a temperature of 80 DEG C
Rev/min stirring 10min is well mixed, and obtains modified far infrared powder;
(2) it is modified far infrared powder is (limited using Shenzhen's Jitian's chemical industry with the aqueous polyurethane emulsion of 12 weight portions
Company provide model F0401 anion-type water-thinned polyurethane emulsion, viscosity 300mpa.s), the dodecyl of 1 weight portion
Dimethyl betaine, the Dodecyl Polyglucosides of 1 weight portion, the sodium sorbate of 0.3 weight portion, the water of 100 weight portions mix equal
It is even, obtain far-infrared anti-biotic dressing liquid;
(3) by fabric, (article No. for using Hebei day Yi Fengda fine hair processing Co., Ltd to provide is the wool of RKB752100
Fabric, composition is 100wt% fine wools, and grammes per square metre is 570g/ ㎡) impregnated in the far-infrared anti-biotic dressing liquid that temperature is 65 DEG C
45min, fabric is 1 with the mass ratio of far-infrared anti-biotic dressing liquid:15, after dehydration, 120min is dried under the conditions of 60 DEG C, obtain
Far-infrared antibacterial fabric;Fabric performance testing result:Antibiotic rate 95.2%, emissivity, 94.8%;
(4) Far-infrared antibacterial fabric is cut, and routinely women overcoat preparation technology sewing, obtain final product the winter
Fashionable women dress.
Claims (10)
1. a kind of preparation method of winter Fashionable women dress, it is characterised in that comprise the following steps:
(1) far infrared powder of 1-10 weight portions is well mixed with the coupling agent of 0.2-2 weight portions, obtains modified far-infrared powder
Body;
(2) by the aqueous polyurethane emulsion of modified far infrared powder and 5-20 weight portions, the dispersant of 1-5 weight portions, 0.2-2 weights
Measure the sodium sorbate of part, the water of 95-105 weight portions to be well mixed, obtain far-infrared anti-biotic dressing liquid;
(3) fabric is impregnated into 40-60min, fabric and far-infrared anti-biotic in temperature is for 45-75 DEG C of far-infrared anti-biotic dressing liquid
The mass ratio of dressing liquid is 1:10-1:30, after dehydration, 80-200min is dried under the conditions of 30-60 DEG C, obtain far-infrared anti-biotic
Fabric;
(4) Far-infrared antibacterial fabric is cut, and routinely women's dress preparation technology sewing is obtained final product.
2. the preparation method of winter Fashionable women dress according to claim 1, it is characterised in that:The far infrared powder is wheat meal
At least one in stone flour, nano-zirconium carbide, nanometer silicon carbide, nano silicon.
3. the preparation method of winter Fashionable women dress according to claim 2, it is characterised in that:The far infrared powder is by 55-
65wt% medical stone powders and 35-45wt% nano-zirconium carbides are mixed.
4. the preparation method of winter Fashionable women dress according to claim 1, it is characterised in that:The coupling agent consumption is 0.6-
1 weight portion, the coupling agent is at least one in silane coupler, titanate coupling agent, aluminate coupling agent, the silane
Coupling agent can be selected from diethylenetriamine base propyl trimethoxy silicane, 3- (2,3- the third oxygen of epoxy) propyl trimethoxy silicane,
The titanate coupling agent can be selected from isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters, the oleic acid acyloxy of isopropyl two
(dioctyl phosphoric acid acyloxy) titanate esters, the aluminate coupling agent can be selected from aluminate coupling agent 821, aluminate coupling agent
DL-411。
5. the preparation method of winter Fashionable women dress according to claim 4, it is characterised in that:The coupling agent is titanate esters idol
Connection agent.
6. the preparation method of winter Fashionable women dress according to claim 5, it is characterised in that:The coupling agent is isopropyl two
Oleic acid acyloxy (dioctyl phosphoric acid acyloxy) titanate esters.
7. the preparation method of winter Fashionable women dress according to claim 1, it is characterised in that:The dispersant is anionic
In surfactant, cationic surface active agent, zwitterionic surfactant, nonionic surfactant at least one
Kind, the anionic surfactant can be selected from lauryl sodium sulfate, cetyl benzenesulfonic acid sodium, the cationic
Surfactant can be selected from Cetyltrimethylammonium bromide, INCROQUAT TMC-80, the amphion table
Face activating agent dodecyldimethylammonium hydroxide inner salt, 3- sulfopropyl etradecyldimethylamine glycine betaines, the nonionic surfactant
Can be Dodecyl Polyglucosides.
8. the preparation method of winter Fashionable women dress according to claim 7, it is characterised in that:The dispersant is nonionic table
Face activating agent.
9. the preparation method of winter Fashionable women dress according to claim 1, it is characterised in that:The fabric material is
100wt% wools.
10. a kind of winter Fashionable women dress, it is characterised in that:It is prepared from using method any one of claim 1-9.