CN106676902A - POE/polyester (polyolefin elastomer/polyester) composite umbrella fabric and preparation method thereof - Google Patents
POE/polyester (polyolefin elastomer/polyester) composite umbrella fabric and preparation method thereof Download PDFInfo
- Publication number
- CN106676902A CN106676902A CN201611266010.5A CN201611266010A CN106676902A CN 106676902 A CN106676902 A CN 106676902A CN 201611266010 A CN201611266010 A CN 201611266010A CN 106676902 A CN106676902 A CN 106676902A
- Authority
- CN
- China
- Prior art keywords
- poe
- cloth
- parts
- terylene
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to POE/polyester (polyolefin elastomer/polyester) composite umbrella fabric and a preparation method thereof and belongs to the technical field of textile fabrics. The preparation method comprises dyeing polyester yarn, warping, sizing, passing the sized yarn through molten POE so that the yarn is evenly coated with a POE layer, doubling the yarn, weaving, applying a layer of POE primer, carrying out anti-ultraviolet treatment by padding after the application of the primer, shaping, and inspecting the fabric to obtain the POE/polyester composite umbrella fabric. The POE/polyester composite umbrella fabric has the advantages that the strength is high, folds rarely occur, rainwater is easy to shake off, and the anti-ultraviolet effect is good.
Description
Technical field
The invention belongs to technical field of textile fabric, and in particular to a kind of compound umbrella cloth of POE/ terylene and its preparation side
Method.
Background technology
Umbrella is a necessary in people's life, and the cloth of umbrella mainly has 3 kinds, and cost is from low to high successively
For：Terylene, PG cloth, nylon.Wherein terylene cloth color is more gorgeous, but umbrella fabric is placed on after rubbing on hand, and folding line is obvious, no
Easily reduction, applies last layer elargol on terylene, is exactly our usually said elargol umbrellas, and the function of elargol cloth anti-ultraviolet is
It is reasonable, but after use time length, elargol is easily separated from where folding；PG cloth is called percussion cloth, anti-ultraviolet function, matter
The degree of stability of amount, the class of color are all more satisfactory but relatively costly, in being typically only used in the umbrella of top grade；Nylon cloth because
Affected larger by air humidity, umbrella cloth shrinks more serious, and the normal folding of umbrella cover is even influenced whether sometimes, so application now
It is less.And the Transparent umbrella for coming into vogue in recent years, it with POE or PVC plastic is fabric that its umbrella cover is, majority use for women and
It is easily damaged.
POE, polyolefin elastomer (Polyolefin elastomer) is DOW chemical companies of the U.S. with metallocene as catalysis
The thermoplastic elastomer (TPE) being distributed with narrow molecular weight distribution and uniform short-chain branch of agent, its main performance is dashed forward very much
Go out, in very many performance indications conventional elastomers have been exceeded, with superiority such as ageing-resistant, resistance to ozone, resistant to chemical media
Energy.Therefore, it is of the invention to consider the compound prepared umbrella cloth of POE and terylene so as to deform little, tensile strength greatly, do not tend to have folding line.
In addition, injury of the ultraviolet to human body is increasingly taken seriously, human body skin sunburn can be made aging, produce black
Element and mottle, more serious can also induce canceration, endanger human health.Also the parachute kit with rainwater brings interior or the vehicles into
Inconvenience storage, or get wet medicated clothing or ground of making dirty, it is uncomfortable.
The content of the invention
The invention aims to solve the deficiencies in the prior art, and provide a kind of compound umbrella cloth of POE/ terylene and its
Preparation method, the compound umbrella cloth of the POE/ terylene has intensity height, does not tend to have folding line, and rainwater is easily shaken off, and preventing ultraviolet effect
Good the advantages of.
The present invention is adopted the following technical scheme that：
The preparation method of the compound umbrella cloth of POE/ terylene, comprises the steps：
1) first spun polyester thread dyeed；
2) again the yarn after colouring carried out into warping, sizing；
3) yarn starched is worn from the POE under molten condition and draws and mistake, wrap up one layer of POE layer with making Yarn homogeneous；
4) by step 3) yarn that obtains carries out doubling, weaves cotton cloth；
5) to step 4) the cloth last layer POE primers that obtain；
6) and then by the cloth of first-class POE primers anti-ultraviolet process is carried out by padding method；
7) shaping, perching are finally carried out, obtains final product the compound umbrella cloth of the POE/ terylene.
Further, the step 2) in the sizing agent of sizing include according to the following component of mass fraction meter：Ethylene
Alcohol polymer 30-40 parts, propenyl polymer 5-35 parts, sodium alginate 4-9 parts, sodium carboxymethyl cellulose 1-50 parts, polycyclic oxygen
Ethane 0.1-5 parts, carbamide 1-4 parts.
Further, the step 3) in obtained yarn thickness be 30D-50D.
Further, the step 4) in when weaving cotton cloth weaving method be warp knit, the fabric stability for obtaining is strong, wear-resisting,
Warp count:Weft count=2:1.
Further, the step 5) in the method for upper POE glue be frictioning, by fixing a roller bearing, moving cloth,
In roller gluing and rotate contact with cloth, so as to give cloth gluing.
Further, the step 6) in carry out anti-ultraviolet process when padding liquid include according to mass fraction meter
Following component：Nano zine oxide 5-8 parts, nano titanium oxide 2-7 parts, nano silicon 1-4 parts, aqueouss rosin resin emulsion
12-20 parts, eugenol 0.5-2 parts, amino silicone breast 6-13 parts, KG-500A waterproofing agent 7-15 parts, water 32-45 parts, concrete process side
Method be according to the quality proportioning, first by nano zine oxide, nano titanium oxide and nano silicon mix homogeneously, then by its
Sequentially add in water and stir with aqueouss rosin resin emulsion, amino silicone breast, be warming up to 35 DEG C, add eugenol and KG-
500A waterproofing agents stir, and natural cooling is obtained padding liquid, and cloth impregnated in wherein, and an immersing and rolling, pick-up rate is 80%,
Dry at 140 DEG C -150 DEG C.
The compound umbrella cloth of the POE/ terylene by obtained in the preparation method of above-mentioned POE/ terylene compound umbrella cloth.
Compared with prior art, its advantage is the present invention：The compound umbrella cloth of the POE/ terylene of the present invention has intensity
It is high, be difficult advantage creasy, spun polyester thread equably wraps up one layer of POE layer, enhances the intensity of yarn so as to deform it is little,
Folding line is not tended to have；Inherently more hydrophobic terylene is wrapped up after one layer of POE layer, and rainwater is less in its surface adhesion force, adds conjunction
The braiding thread count ratio of reason, firmly one gets rid of and do not have substantially rainwater and adhere to；In addition present invention uses Zinc Oxide, titanium dioxide and two
The various nano-powder interworkings of silicon oxide, and general coating is abandoned, and anti-ultraviolet process is carried out to cloth using padding method,
The anti-ultraviolet umbrella cloth of high-quality is obtained, UPF values reach 50+, and ultraviolet shielding rate is up to 99%, and nontoxic, safe to the human body, this
The product of invention is to integrate advantage.
Specific embodiment
With reference to specific embodiment, the present invention is described in further detail.
It will be understood to those of skill in the art that the following example is merely to illustrate the present invention, and should not be regarded as limiting this
Bright scope.
Embodiment 1
A kind of POE/ terylene is combined umbrella cloth, and its preparation method comprises the steps：
1) first spun polyester thread dyeed；
2) again the yarn after colouring carried out into warping, sizing, the sizing agent of wherein sizing is included according to mass fraction meter
Following component：30 parts of vinyl alcohol polymer, 5 parts of propenyl polymer, 4 parts of sodium alginate, 1 part of sodium carboxymethyl cellulose, polycyclic
0.1 part of oxidative ethane, 1 part of carbamide；
3) yarn starched is worn from the POE under molten condition and draws and mistake, wrap up one layer of POE layer with making Yarn homogeneous,
Obtained thickness of yarn is 30D-50D；
4) by step 3) yarn that obtains carries out doubling, weaves cotton cloth, and weaving method is warp knit when weaving cotton cloth, the fabric stability for obtaining
Strong, wear-resisting, the warp count of property:Weft count=2:1；
5) to step 4) the cloth last layer POE primers that obtain, coating method is frictioning, by fixing a roller bearing, is moved
Dynamic cloth, in roller gluing and rotate contact with cloth, so as to give cloth gluing；
6) and then by the cloth of first-class POE primers anti-ultraviolet process is carried out by padding method, carries out anti-ultraviolet process
When padding liquid include according to the following component of mass fraction meter：5 parts of nano zine oxide, 2 parts of nano titanium oxide, nano-silica
1 part of SiClx, 12 parts of aqueouss rosin resin emulsion, 0.5 part of eugenol, 6 parts of amino silicone breast, 7 parts of KG-500A waterproofing agents, 32 parts of water,
Concrete processing method is, according to the quality proportioning, first to mix nano zine oxide, nano titanium oxide and nano silicon
Uniformly, then by itself and aqueouss rosin resin emulsion, amino silicone breast sequentially add in water and stir, be warming up to 35 DEG C, add fourth
Fragrant phenol and KG-500A waterproofing agents stir, and natural cooling is obtained padding liquid, and cloth impregnated in wherein, an immersing and rolling, mangle
Rate is 80%, is dried at 140 DEG C；
7) shaping, perching are finally carried out, obtains final product the compound umbrella cloth of the POE/ terylene.
Embodiment 2
A kind of POE/ terylene is combined umbrella cloth, and its preparation method comprises the steps：
1) first spun polyester thread dyeed；
2) again the yarn after colouring carried out into warping, sizing, the sizing agent of wherein sizing is included according to mass fraction meter
Following component：It is 35 parts of vinyl alcohol polymer, 25 parts of propenyl polymer, 6 parts of sodium alginate, 28 parts of sodium carboxymethyl cellulose, poly-
2.6 parts of oxirane, 3 parts of carbamide；
3) yarn starched is worn from the POE under molten condition and draws and mistake, wrap up one layer of POE layer with making Yarn homogeneous,
Obtained thickness of yarn is 30D-50D；
4) by step 3) yarn that obtains carries out doubling, weaves cotton cloth, and weaving method is warp knit when weaving cotton cloth, the fabric stability for obtaining
Strong, wear-resisting, the warp count of property:Weft count=2:1；
5) to step 4) the cloth last layer POE primers that obtain, coating method is frictioning, by fixing a roller bearing, is moved
Dynamic cloth, in roller gluing and rotate contact with cloth, so as to give cloth gluing；
6) and then by the cloth of first-class POE primers anti-ultraviolet process is carried out by padding method, carries out anti-ultraviolet process
When padding liquid include according to the following component of mass fraction meter：7 parts of nano zine oxide, 4 parts of nano titanium oxide, nano-silica
2 parts of SiClx, 15 parts of aqueouss rosin resin emulsion, 1 part of eugenol, 9 parts of amino silicone breast, 12 parts of KG-500A waterproofing agents, 38 parts of water,
Concrete processing method is, according to the quality proportioning, first to mix nano zine oxide, nano titanium oxide and nano silicon
Uniformly, then by itself and aqueouss rosin resin emulsion, amino silicone breast sequentially add in water and stir, be warming up to 35 DEG C, add fourth
Fragrant phenol and KG-500A waterproofing agents stir, and natural cooling is obtained padding liquid, and cloth impregnated in wherein, an immersing and rolling, mangle
Rate is 80%, is dried at 145 DEG C；
7) shaping, perching are finally carried out, obtains final product the compound umbrella cloth of the POE/ terylene.
Embodiment 3
A kind of POE/ terylene is combined umbrella cloth, and its preparation method comprises the steps：
1) first spun polyester thread dyeed；
2) again the yarn after colouring carried out into warping, sizing, the sizing agent of wherein sizing is included according to mass fraction meter
Following component：It is 40 parts of vinyl alcohol polymer, 35 parts of propenyl polymer, 9 parts of sodium alginate, 50 parts of sodium carboxymethyl cellulose, poly-
5 parts of oxirane, 4 parts of carbamide；
3) yarn starched is worn from the POE under molten condition and draws and mistake, wrap up one layer of POE layer with making Yarn homogeneous,
Obtained thickness of yarn is 30D-50D；
4) by step 3) yarn that obtains carries out doubling, weaves cotton cloth, and weaving method is warp knit when weaving cotton cloth, the fabric stability for obtaining
Strong, wear-resisting, the warp count of property:Weft count=2:1；
5) to step 4) the cloth last layer POE primers that obtain, coating method is frictioning, by fixing a roller bearing, is moved
Dynamic cloth, in roller gluing and rotate contact with cloth, so as to give cloth gluing；
6) and then by the cloth of first-class POE primers anti-ultraviolet process is carried out by padding method, carries out anti-ultraviolet process
When padding liquid include according to the following component of mass fraction meter：8 parts of nano zine oxide, 7 parts of nano titanium oxide, nano-silica
4 parts of SiClx, 20 parts of aqueouss rosin resin emulsion, 2 parts of eugenol, 13 parts of amino silicone breast, 15 parts of KG-500A waterproofing agents, 45 parts of water,
Concrete processing method is, according to the quality proportioning, first to mix nano zine oxide, nano titanium oxide and nano silicon
Uniformly, then by itself and aqueouss rosin resin emulsion, amino silicone breast sequentially add in water and stir, be warming up to 35 DEG C, add fourth
Fragrant phenol and KG-500A waterproofing agents stir, and natural cooling is obtained padding liquid, and cloth impregnated in wherein, an immersing and rolling, mangle
Rate is 80%, is dried at 150 DEG C；
7) shaping, perching are finally carried out, obtains final product the compound umbrella cloth of the POE/ terylene.
The compound umbrella cloth of the POE/ terylene of the gained of the embodiment of the present invention 1 to 3 is carried out into performance test, and with price on market
30 yuan one is compared certain brand umbrella, as a result as shown in table 1 below：
The performance test data of the compound umbrella cloth of POE/ terylene of the gained of 1 embodiment of table 1 to 3
From in table, the POE/ terylene of the present invention is combined umbrella cloth intensity height, does not tend to have folding line, and rainwater is easily shaken off, and
Preventing ultraviolet effect is good, better than common like product on the market.
It should be understood by those skilled in the art that, the present invention is not restricted to the described embodiments, above-described embodiment and explanation
Merely illustrating the principles of the invention described in book, without departing from the spirit and scope of the present invention, the present invention also has
Various changes and modifications, these changes and improvements are both fallen within scope of the claimed invention.The claimed scope of the invention
By appending claims and its equivalent thereof.
Claims (7)
- The preparation method of the compound umbrella cloth of 1.POE/ terylene, it is characterised in that comprise the steps：1）First spun polyester thread is dyeed；2）Again the yarn after colouring is carried out into warping, sizing；3）The yarn starched is worn from the POE under molten condition and is drawn and mistake, wrap up one layer of POE layer with making Yarn homogeneous；4）By step 3）The yarn for obtaining carries out doubling, weaves cotton cloth；5）To step 4）The cloth last layer POE primers for obtaining；6）Then the cloth of first-class POE primers is carried out into anti-ultraviolet process by padding method；7）Shaping, perching are finally carried out, the compound umbrella cloth of the POE/ terylene is obtained final product.
- 2. POE/ terylene according to claim 1 is combined the preparation method of umbrella cloth, it is characterised in that the step 2）In The sizing agent of sizing is included according to the following component of mass fraction meter：Vinyl alcohol polymer 30-40 parts, propenyl polymer 5-35 Part, sodium alginate 4-9 parts, sodium carboxymethyl cellulose 1-50 parts, poly(ethylene oxide) 0.1-5 part, carbamide 1-4 parts.
- 3. POE/ terylene according to claim 1 is combined the preparation method of umbrella cloth, it is characterised in that the step 3）In The thickness of obtained yarn is 30D-50D.
- 4. POE/ terylene according to claim 1 is combined the preparation method of umbrella cloth, it is characterised in that the step 4）In When weaving cotton cloth weaving method be warp knit, warp count:Weft count=2:1.
- 5. POE/ terylene according to claim 1 is combined the preparation method of umbrella cloth, it is characterised in that the step 5）In The method of upper POE glue is frictioning, by fixing a roller bearing, moving cloth, and in roller gluing and rotation is contacted with cloth, so as to Give cloth gluing.
- 6. POE/ terylene according to claim 1 is combined the preparation method of umbrella cloth, it is characterised in that the step 6）In Carrying out padding liquid when anti-ultraviolet is processed is included according to the following component of mass fraction meter：Nano zine oxide 5-8 parts, nanometer two Titanium oxide 2-7 parts, nano silicon 1-4 parts, aqueouss rosin resin emulsion 12-20 part, eugenol 0.5-2 parts, amino silicone breast 6-13 parts, KG-500A waterproofing agent 7-15 parts, water 32-45 parts, concrete processing method is according to the quality proportioning, first by nanometer Zinc Oxide, nano titanium oxide and nano silicon mix homogeneously, then by itself and aqueouss rosin resin emulsion, amino silicone breast according to It is secondary be added to the water stir, be warming up to 35 DEG C, add eugenol and KG-500A waterproofing agents to stir, natural cooling is obtained Padding liquid, cloth impregnated in wherein, and an immersing and rolling, pick-up rate is 80%, dry at 140 DEG C -150 DEG C.
- 7. a kind of POE/ terylene by obtained in the preparation method of the compound umbrella cloth of the POE/ terylene described in claim 1 is combined umbrella Cloth.